CN106478054A - A kind of conch meal colored finish coating and preparation method thereof - Google Patents
A kind of conch meal colored finish coating and preparation method thereof Download PDFInfo
- Publication number
- CN106478054A CN106478054A CN201610877279.0A CN201610877279A CN106478054A CN 106478054 A CN106478054 A CN 106478054A CN 201610877279 A CN201610877279 A CN 201610877279A CN 106478054 A CN106478054 A CN 106478054A
- Authority
- CN
- China
- Prior art keywords
- parts
- mesh sieve
- conch meal
- cross
- conch
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of conch meal colored finish coating, it is made up of the raw material of following weight portion：Cross one 5 10 parts of 40 mesh sieve conch meal, cross 2 10 20 parts of 60 mesh sieve conch meal, cross 3 20 30 parts of 80 mesh sieve conch meal, cross 4 20 30 parts of 120 mesh sieve conch meal, cross 5 20 30 parts of 200 mesh sieve conch meal, 13 parts of wollastonite, 0.3 0.5 parts of cellulose, 12 parts of inorganic latex powder, 0.5 1 parts of water reducer, 0.1 0.2 parts of chopped strand, 13 parts of inorganic pigment.The coating made using this formula in this formula can be scraped by user by five kinds of different conch meals crossing grit number, rolling, and brush sprays various construction methods and makes various texture moulding；In this formula, wollastonite can effectively provide the bulk strength of this coating, and chopped strand can have good cracking resistance after the use of this coating of effective guarantee, and water reducer plays the adhesive force increasing coating.
Description
Technical field
The present invention relates to a kind of conch meal colored finish coating and preparation method thereof.
Background technology
At present, contain formaldehyde in existing house decorative material, the material of abnormal flavour is too many, lead to people easy all kinds of diseases
Disease, the serious diatom ooze also having to obtain cancer, nearly 2 years market releasing, raw material rare, lead to its quality irregular not
Together, also occur in that the product of a lot of formaldehyde adsorption in the market, but often effect is undesirable, do not reach the indoor ring of effective improvement
The pollution in border, wastes much valuable ecomaterial.
The main component of shell is 95% Calcium Carbonate and a small amount of chitin element, and a small amount of trace element, aminoacid
Deng.The top layer of shell is thin, transparent, prevents carbonic acid from corroding, the chitin element secreted by overcoat film edge is constituted, permissible
It is used for doing investment precoat；Shell, originally as cellular, has absorption, the effect decomposing (formaldehyde, benzene, TVOC, ammonia) and regulation
Air humidity, elimination odor function.The compound of calcium is used for eliminating smell agent in life, and therefore conch meal can be to indoor cigarette
Abnormal smells from the patient that taste, infant, patient, house pet, mycete are distributed and indoor miscellaneous taste all have effectively dispels effect, especially to cigarette
The carbon monoxide being distributed indoors and dust Capacity have adsorption.Its composition 100% of conch meal is calcium, therefore has
Antistatic performance well；Metope is using having after shell powder paint that film is plentiful, texture is natural, firm soft and smooth, fashion is graceful.
Pollution resistance is good.Its construction versatility is good, is as good as with emulsion paint, is applicable to scrape, rolling, and brush sprays various construction methods, combination property
Excellent.
Content of the invention
For solving an above existing difficult problem, the invention discloses a kind of conch meal colored finish coating, its have preparation simple,
Elegant in appearance it is possible to the advantages of effective purify air.
The present invention employs the following technical solutions：
A kind of conch meal colored finish coating, is made up of the raw material of following weight portion：Cross 40 mesh sieve conch meal one 5-10 part,
Cross 60 mesh sieve conch meal two 10-20 part, cross 80 mesh sieve conch meal three 20-30 part, cross 120 mesh sieve conch meal four 20-30 part, mistake
200 mesh sieve conch meal five 20-30 part, wollastonite 1-3 part, modified alta-mud 1-2 part, cellulose 0.3-0.5 part, inorganic latex powder
1-2 part, water reducer 0.5-1 part, chopped strand 0.1-0.2 part, inorganic pigment 1-3 part.
As preferred, it is made up of the raw material of following weight portion：Cross one 5 parts of 40 mesh sieve conch meal, cross 60 mesh sieve conch meals
2 10 parts, cross 3 20 parts of 80 mesh sieve conch meal, cross 4 20 parts of 120 mesh sieve conch meal, cross 5 20 parts of 200 mesh sieve conch meal, silicon ash
1 part of stone, 1 part of modified alta-mud, 0.3 part of cellulose, 1 part of inorganic latex powder, 0.5 part of water reducer, chopped strand 0.1-0.2 part,
Inorganic pigment 1-3 part.
As preferred, it is made up of the raw material of following weight portion：Cross one 10 parts of 40 mesh sieve conch meal, cross 60 mesh sieve conch meals
2 20 parts, cross 3 30 parts of 80 mesh sieve conch meal, cross 4 30 parts of 120 mesh sieve conch meal, cross 5 20 parts of 200 mesh sieve conch meal, silicon ash
3 parts of stone, 2 parts of modified alta-mud, 0.5 part of cellulose, 2 parts of inorganic latex powder, 1 part of water reducer, 0.2 part of chopped strand, inorganic face
3 parts of material.
Another aspect of the present invention also discloses a kind of conch meal colored finish coating, comprises the steps：
(1) sieve：Conch meal is put in five big containers of grade, five big containers of grade were carried out respectively with 40,60,
80th, after 120,200 mesh sieves, it is identified：Cross 40 mesh sieve conch meals one, cross 60 mesh sieve conch meals two, cross 80 mesh sieve conch meals three,
Cross 120 mesh sieve conch meals four, cross 200 mesh sieve conch meals five after standby.
(2) mix：Step (1) is taken to sieve one 8 parts of the mistake 40 mesh sieve conch meal taking, cross 2 15 parts of 60 mesh sieve conch meal, cross 80
3 25 parts of mesh sieve conch meal, excessively 4 25 parts of 120 mesh sieve conch meal, excessively 5 25 parts of 200 mesh sieve conch meal, by above-mentioned after being mixed
Number sequentially adds 2 parts of wollastonite, 1.5 parts of modified alta-mud, 0.45 part of cellulose, 2 parts of inorganic latex powder, 1 part of water reducer, short
Cut 0.2 part of fiber, 2 parts of inorganic pigment.
(3) allocate：After prepared for step (2) mixture is stirred by weight 2: 1 with emulsion water, obtain final product.
The invention discloses a kind of conch meal colored finish coating compared with prior art has the advantages that：
1. this coating have nontoxic, do not precipitate, be stale-proof, not shedding, effect good, low cost, all properties can meet
The technical requirements of construction coating for internal wall, are the best substitute of existing construction coating for internal wall；This coating small investment, function admirable,
There is good development prospect.
2. adopt five kinds of different conch meals crossing grit number in this formula, the mixed conch meal particle diameter being taken is than existing
It is that 200 mesh -1250 mesh conch meal is less that technology commonly uses particle diameter, and conch meal consumption is not the usual amounts of prior art, using this
The coating that formula is made can be scraped by user by five kinds of different conch meals crossing grit number, rolling, and brush sprays various construction party legal systems
Become various texture moulding.
3. in this formula, wollastonite can effectively provide the bulk strength of this coating, and chopped strand can this coating of effective guarantee make
With after have good cracking resistance, water reducer play increase coating adhesive force, the painting that modified alta-mud can effectively configure
Material stability in use, be easy to construct.
4. the inorganic pigment sun-proof in this formula, heat-resisting, weather-proof, and solvent resistance is good, strong covering power, by from not homochromy
The inorganic pigment adjusted is so that user is using the artistic texture effect that can reach it after this coating and want to reach.
Specific embodiment
With reference to embodiment, technical scheme is described further：
Embodiment 1：A kind of conch meal colored finish coating, is made up of the raw material of following weight portion：Cross 40 mesh sieve conch meals
One 5 parts, cross 2 10 parts of 60 mesh sieve conch meal, cross 3 20 parts of 80 mesh sieve conch meal, cross 4 20 parts of 120 mesh sieve conch meal, cross 200 mesh
Sieve 5 20 parts of conch meal, 1 part of wollastonite, 1 part of modified alta-mud, 0.3 part of cellulose, 1 part of inorganic latex powder, 0.5 part of water reducer,
0.1 part of chopped strand, 1 part of inorganic pigment.
Described in the present embodiment, a kind of conch meal colored finish coating, comprises the steps：
(1) sieve：Conch meal is put in five big containers of grade, five big containers of grade were carried out respectively with 40,60,
80th, after 120,200 mesh sieves, it is identified：Cross 40 mesh sieve conch meals one, cross 60 mesh sieve conch meals two, cross 80 mesh sieve conch meals three,
Cross 120 mesh sieve conch meals four, cross 200 mesh sieve conch meals five after standby.
(2) mix：Step (1) is taken to sieve one 5 parts of the mistake 40 mesh sieve conch meal taking, cross 60 mesh sieves respectively by aforementioned weight number
Conch meal two, excessively 80 mesh sieve conch meals three, excessively 120 mesh sieve conch meals four, excessively 200 mesh sieve conch meals five, by upper after being mixed
State number and sequentially add wollastonite, modified alta-mud, cellulose, inorganic latex powder, water reducer, chopped strand, inorganic pigment.
(3) allocate：After prepared for step (2) mixture is stirred by weight 2: 1 with emulsion water, obtain final product.
A kind of conch meal colored finish coating being obtained using the present embodiment, by scraping, rolling, brush, sprays various construction methods
Construct after on the wall, rough shell particle effect can be embodied.
Embodiment 2：A kind of conch meal colored finish coating, is made up of the raw material of following weight portion：Cross 40 mesh sieve conch meals
One 8 parts, cross 2 15 parts of 60 mesh sieve conch meal, cross 3 25 parts of 80 mesh sieve conch meal, cross 4 25 parts of 120 mesh sieve conch meal, cross 200 mesh
5 25 parts of conch meal of sieve, 2 parts of wollastonite, 1.5 parts of modified alta-mud, 0.4 part of cellulose, 1 part of inorganic latex powder, water reducer 0.6
Part, 0.2 part of chopped strand, 2 parts of inorganic pigment.
Described in the present embodiment, a kind of conch meal colored finish coating, comprises the steps：
(1) sieve：Conch meal is put in five big containers of grade, five big containers of grade were carried out respectively with 40,60,
80th, after 120,200 mesh sieves, it is identified：Cross 40 mesh sieve conch meals one, cross 60 mesh sieve conch meals two, cross 80 mesh sieve conch meals three,
Cross 120 mesh sieve conch meals four, cross 200 mesh sieve conch meals five after standby.
(2) mix：Step (1) is taken to sieve one 5 parts of the mistake 40 mesh sieve conch meal taking, cross 60 mesh sieves respectively by aforementioned weight number
Conch meal two, excessively 80 mesh sieve conch meals three, excessively 120 mesh sieve conch meals four, excessively 200 mesh sieve conch meals five, by upper after being mixed
State number and sequentially add wollastonite, modified alta-mud, cellulose, inorganic latex powder, water reducer, chopped strand, inorganic pigment.
(3) allocate：After prepared for step (2) mixture is stirred by weight 2: 1 with emulsion water, obtain final product.
A kind of conch meal colored finish coating being obtained using the present embodiment, than embodiment one, by scraping, is rolled, brush, spray
Various construction methods are constructed after on the wall, can embody the shell particle effect more milder than after embodiment one coating material.
Embodiment three：A kind of conch meal colored finish coating, is made up of the raw material of following weight portion：Cross 40 mesh sieve conch meals
One 10 parts, cross 2 20 parts of 60 mesh sieve conch meal, cross 3 30 parts of 80 mesh sieve conch meal, cross 4 30 parts of 120 mesh sieve conch meal, cross 200
5 30 parts of mesh sieve conch meal, 3 parts of wollastonite, 2 parts of modified alta-mud, 0.5 part of cellulose, 2 parts of inorganic latex powder, 1 part of water reducer,
0.2 part of chopped strand, 3 parts of inorganic pigment.
Described in the present embodiment, a kind of conch meal colored finish coating, comprises the steps：
(1) sieve：Conch meal is put in five big containers of grade, five big containers of grade were carried out respectively with 40,60,
80th, after 120,200 mesh sieves, it is identified：Cross 40 mesh sieve conch meals one, cross 60 mesh sieve conch meals two, cross 80 mesh sieve conch meals three,
Cross 120 mesh sieve conch meals four, cross 200 mesh sieve conch meals five after standby.
(2) mix：Step (1) is taken to sieve one 5 parts of the mistake 40 mesh sieve conch meal taking, cross 60 mesh sieves respectively by aforementioned weight number
Conch meal two, excessively 80 mesh sieve conch meals three, excessively 120 mesh sieve conch meals four, excessively 200 mesh sieve conch meals five, by upper after being mixed
State number and sequentially add wollastonite, modified alta-mud, cellulose, inorganic latex powder, water reducer, chopped strand, inorganic pigment.
(3) allocate：After prepared for step (2) mixture is stirred by weight 2: 1 with emulsion water, obtain final product.
Using a kind of prepared conch meal colored finish coating of the present embodiment than embodiment one, embodiment two, by scraping,
Rolling, brush, sprays various construction methods and constructs after on the wall, can embody the shell particle effect of exquisiteness.
The above, be only presently preferred embodiments of the present invention, not the present invention is done with any pro forma restriction, therefore
All contents without departing from technical solution of the present invention, the technical spirit according to the present invention any is simply repaiied to made for any of the above embodiments
Change, equivalent variations and modification, all still fall within the range of technical solution of the present invention.
Claims (4)
1. a kind of conch meal colored finish coating is it is characterised in that be made up of the raw material of following weight portion：Cross 40 mesh sieve conch meals
One 5-10 part, excessively 60 mesh sieve conch meal two 10-20 part, excessively 80 mesh sieve conch meal three 20-30 part, excessively 120 mesh sieve conch meal four 20-
30 parts, cross 200 mesh sieve conch meal five 20-30 part, wollastonite 1-3 part, modified alta-mud 1-2 part, cellulose 0.3-0.5 part, no
Machine latex powder 1-2 part, water reducer 0.5-1 part, chopped strand 0.1-0.2 part, inorganic pigment 1-3 part.
2. a kind of conch meal colored finish coating according to claim 1 is it is characterised in that raw material by following weight portion
Make：Cross one 5 parts of 40 mesh sieve conch meal, cross 2 10 parts of 60 mesh sieve conch meal, cross 3 20 parts of 80 mesh sieve conch meal, cross 120 mesh sieves
4 20 parts of conch meal, excessively 5 20 parts of 200 mesh sieve conch meal, 1 part of wollastonite, 1 part of modified alta-mud, 0.3 part of cellulose, inorganic breast
1 part of rubber powder, 0.5 part of water reducer, chopped strand 0.1-0.2 part, inorganic pigment 1-3 part.
3. a kind of conch meal colored finish coating according to claim 1 is it is characterised in that raw material by following weight portion
Make：Cross one 10 parts of 40 mesh sieve conch meal, cross 2 20 parts of 60 mesh sieve conch meal, cross 3 30 parts of 80 mesh sieve conch meal, cross 120 mesh sieves
4 30 parts of conch meal, excessively 5 20 parts of 200 mesh sieve conch meal, 3 parts of wollastonite, 2 parts of modified alta-mud, 0.5 part of cellulose, inorganic breast
2 parts of rubber powder, 1 part of water reducer, 0.2 part of chopped strand, 3 parts of inorganic pigment.
4. a kind of conch meal colored finish coating according to claim 1 it is characterised in that its preparation method include as follows
Step：
(1) sieve：Conch meal is put in five big containers of grade, five big containers of grade were carried out respectively with 40,60,80,
120th, after 200 mesh sieves, it is identified：Cross 40 mesh sieve conch meals one, cross 60 mesh sieve conch meals two, cross 80 mesh sieve conch meals three, mistake
Standby after 120 mesh sieve conch meals four, excessively 200 mesh sieve conch meals five.
(2) mix：Step (1) is taken to sieve one 8 parts of the mistake 40 mesh sieve conch meal taking, cross 2 15 parts of 60 mesh sieve conch meal, cross 80 mesh sieves
3 25 parts of conch meal, excessively 4 25 parts of 120 mesh sieve conch meal, excessively 5 25 parts of 200 mesh sieve conch meal, by above-mentioned number after being mixed
Sequentially add 2 parts of wollastonite, 1.5 parts of modified alta-mud, 0.45 part of cellulose, 2 parts of inorganic latex powder, 1 part of water reducer, be chopped fibre
Dimension 0.2 part, 2 parts of inorganic pigment.
(3) allocate：After prepared for step (2) mixture is stirred by weight 2: 1 with emulsion water, obtain final product.