CN106348781A - Manufacturing method of incense ash and wood ash ceramic - Google Patents
Manufacturing method of incense ash and wood ash ceramic Download PDFInfo
- Publication number
- CN106348781A CN106348781A CN201510416792.5A CN201510416792A CN106348781A CN 106348781 A CN106348781 A CN 106348781A CN 201510416792 A CN201510416792 A CN 201510416792A CN 106348781 A CN106348781 A CN 106348781A
- Authority
- CN
- China
- Prior art keywords
- powder
- ceramic
- ash
- water
- kiln
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a manufacturing method of incense ash and wood ash ceramic. The manufacturing method particularly comprises the following steps: weighing base powder, a ceramic binding agent and water in parts by weight, stirring and fusing the ceramic binding agent, adding the base powder and mixing in a material mixing pot to prepare a brick-shaped mud block; mixing the mud block with water, extruding air in the mud pie and enabling the water in the mud to be uniform so as to form ceramic slurry; pouring the ceramic slurry into a forming mould and taking out after forming to obtain a green body; adjusting the green body, placing the molded green body on a wooden support and airing for 1 to 2 hours; putting the aired green body into a kiln and sintering to form a body; and coating the body with glaze water, airing, putting the body into the kiln again and sintering to obtain a finished product, wherein the base powder is one or more than two of corundum powder, aluminium oxide powder, silicon carbide powder, silicon nitride powder or silicon oxide powder. The manufacturing method has the advantages that the process is simple, pollution is avoided, crude granule base powder can be used, the sintering temperature is low, high-strength multi-pore ceramic can be obtained, the pores have big diameter and are distributed uniformly, the ceramic has strong texture, the knocking sound is clear and melodious, a good taste is achieved when the ceramic is used for brewing tea and containing water, and the ceramic is natural and health-care.
Description
Technical field
The present invention relates to a kind of manufacture method of pottery, specifically a kind of incense ashes, the manufacture method of wood ash pottery.
Background technology
At present, the method that manufacture multi-gas hole ceramic is taken both at home and abroad is mainly by two kinds: one kind is addition pore-forming material in ceramic slurry
Material, such as essence how, walnut shell, charcoal, log powder and Organic substance obtain pore, another kind is to be using polyurethane foam plastics
Presoma and obtain pore.Said method tedious process, matrix powder particle requirement is thin, has environment and easily pollutes, sinters temperature
Blank strength low problem when degree is high, pore is larger.
Content of the invention
It is an object of the invention to provide the manufacture method of a kind of simple, the free of contamination incense ashes of operation, wood ash pottery, to solve
The problem proposing in above-mentioned background technology.
For achieving the above object, the following technical scheme of present invention offer:
A kind of incense ashes, the manufacture method of wood ash pottery, concrete grammar is as follows:
(1) weigh the matrix powder of quantitative 5-10kg according to weight portion, weigh the ceramic junction of matrix powder 5-10% weight ratio
Mixture, weighs the water of matrix powder 25-50% weight ratio；
(2) vitrified bond is stirred and merge after 1-3h, add matrix powder and mix 20-40min, warp in batch mixing pot
Cross elutriation, remove impurity, after precipitation, make the clod of bricked；
(3) it is in harmonious proportion clod with water again, remove slag and obtain walk, with the hands crumple, or trampled with foot, or beaten with machine,
The air extrusion in walk out, and the uniform moisture that makes in mud, become ceramic mud；
(4) take shaping dies to inject ceramic mud, after 55-65min, take out after shaping and obtain base substrate；
(5) base substrate is rested and reorganized so as to the exterior and the interior is bright and clean, body links up, regular consistent, then by the base after rest and reorganization molding
Body is placed in dry in the sun 1-2h on yoke；
(6) base substrate after dry in the sun is put in kiln, burnt with 880-920 DEG C of kiln and make base；
(7) reglaze water after becoming base, dry, put again to kiln and burn manufactured goods with 1250-1350 DEG C of kiln.
As the further scheme of the present invention: described matrix powder is schmigel, alumina powder, carborundum powder, silicon nitride powder
Or one of silica powder or two or more.
As the present invention further scheme: described vitrified bond is the wood flour ash of Lignum Aquilariae Resinatum, the wood flour of sandalwood is grey or Semen Phaseoli
The wood flour ash of China fir.
Compared with prior art, the invention has the beneficial effects as follows:
Operation of the present invention is simple, pollution-free, can use coarse granule matrix powder, firing temperature is low, can obtain higher-strength many
Gas hole ceramic, and hole diameter is larger, is evenly distributed.
Specific embodiment
With reference to specific embodiment, the technical scheme of this patent is described in more detail.
Embodiment 1
A kind of incense ashes, the manufacture method of wood ash pottery, concrete grammar is as follows:
(1) weigh the schmigel of quantitative 5kg according to weight portion, weigh the wood flour ash of the Lignum Aquilariae Resinatum of matrix powder 5% weight ratio,
Weigh the water of matrix powder 25% weight ratio；
(2) the wood flour ash stirring of Lignum Aquilariae Resinatum is merged after 1h, add matrix powder and mix 20min in batch mixing pot, pass through
Eluriate, remove impurity, after precipitation, make the clod of bricked；
(3) it is in harmonious proportion clod with water again, remove slag and obtain walk, with the hands crumple, or trampled with foot, or beaten with machine,
The air extrusion in walk out, and the uniform moisture that makes in mud, become ceramic mud；
(4) take shaping dies to inject ceramic mud, after 55min, take out after shaping and obtain base substrate；
(5) base substrate is rested and reorganized so as to the exterior and the interior is bright and clean, body links up, regular consistent, be finally to determine implements shape
Key link, then the base substrate after rest and reorganization molding is placed in dry in the sun 1h on yoke；
(6) base substrate after dry in the sun is put in kiln, burnt with 880 DEG C of kilns and make base；
(7) reglaze water after becoming base, dry, put again to kiln and burn manufactured goods with 1250 DEG C of kiln.
Embodiment 2
A kind of incense ashes, the manufacture method of wood ash pottery, concrete grammar is as follows:
(1) weigh the alumina powder of quantitative 4kg and the carborundum powder of 4kg according to weight portion, weigh matrix powder 8% weight
The wood flour ash of the sandalwood of ratio, weighs the water of matrix powder 38% weight ratio；
(2) the wood flour ash stirring of sandalwood is merged after 2h, add matrix powder and mix 30min in batch mixing pot, pass through
Eluriate, remove impurity, after precipitation, make the clod of bricked；
(3) it is in harmonious proportion clod with water again, remove slag and obtain walk, with the hands crumple, or trampled with foot, or beaten with machine,
The air extrusion in walk out, and the uniform moisture that makes in mud, become ceramic mud；
(4) take shaping dies to inject ceramic mud, after 60min, take out after shaping and obtain base substrate；
(5) base substrate is rested and reorganized so as to the exterior and the interior is bright and clean, body links up, regular consistent, be finally to determine implements shape
Key link, then the base substrate after rest and reorganization molding is placed in dry in the sun 1.5h on yoke；
(6) base substrate after dry in the sun is put in kiln, burnt with 900 DEG C of kilns and make base；
(7) reglaze water after becoming base, dry, put again to kiln and burn manufactured goods with 1300 DEG C of kiln.
Embodiment 3
A kind of incense ashes, the manufacture method of wood ash pottery, concrete grammar is as follows:
(1) weigh the silicon nitride powder of quantitative 5kg and the silica powder of 5kg according to weight portion, weigh matrix powder 10% weight
The wood flour ash of the Ramulus et folium taxi cuspidatae of amount ratio, weighs the water of matrix powder 50% weight ratio；
(2) the wood flour ash stirring of Ramulus et folium taxi cuspidatae is merged after 3h, add matrix powder and mix 40min, warp in batch mixing pot
Cross elutriation, remove impurity, after precipitation, make the clod of bricked；
(3) it is in harmonious proportion clod with water again, remove slag and obtain walk, with the hands crumple, or trampled with foot, or beaten with machine,
The air extrusion in walk out, and the uniform moisture that makes in mud, become ceramic mud；
(4) take shaping dies to inject ceramic mud, after 65min, take out after shaping and obtain base substrate；
(5) base substrate is rested and reorganized so as to the exterior and the interior is bright and clean, body links up, regular consistent, be finally to determine implements shape
Key link, then the base substrate after rest and reorganization molding is placed in dry in the sun 2h on yoke；
(6) base substrate after dry in the sun is put in kiln, burnt with 920 DEG C of kilns and make base；
(7) reglaze water after becoming base, dry, put again to kiln and burn manufactured goods with 1350 DEG C of kiln.
Operation of the present invention is simple, pollution-free, can use coarse granule matrix powder, firing temperature is low, can obtain higher-strength many
Gas hole ceramic, and hole diameter is larger, is evenly distributed.
Above the better embodiment of this patent is explained in detail, but this patent is not limited to above-mentioned embodiment,
In the ken that those of ordinary skill in the art possesses, can also make each on the premise of without departing from this patent objective
Plant change.
Claims (3)
1. a kind of incense ashes, the manufacture method of wood ash pottery are it is characterised in that concrete grammar is as follows:
(1) weigh the matrix powder of quantitative 5-10kg according to weight portion, weigh the ceramic junction of matrix powder 5-10% weight ratio
Mixture, weighs the water of matrix powder 25-50% weight ratio；
(2) vitrified bond is stirred and merge after 1-3h, add matrix powder and mix 20-40min, warp in batch mixing pot
Cross elutriation, remove impurity, after precipitation, make the clod of bricked；
(3) it is in harmonious proportion clod with water again, remove slag and obtain walk, with the hands crumple, or trampled with foot, or beaten with machine,
The air extrusion in walk out, and the uniform moisture that makes in mud, become ceramic mud；
(4) take shaping dies to inject ceramic mud, after 55-65min, take out after shaping and obtain base substrate；
(5) base substrate is rested and reorganized so as to the exterior and the interior is bright and clean, body links up, regular consistent, then by the base after rest and reorganization molding
Body is placed in dry in the sun 1-2h on yoke；
(6) base substrate after dry in the sun is put in kiln, burnt with 880-920 DEG C of kiln and make base；
(7) reglaze water after becoming base, dry, put again to kiln and burn manufactured goods with 1250-1350 DEG C of kiln.
2. incense ashes according to claim 1, the manufacture method of wood ash pottery are it is characterised in that described matrix powder is
One of schmigel, alumina powder, carborundum powder, silicon nitride powder or silica powder or two or more.
3. incense ashes according to claim 1, the manufacture method of wood ash pottery are it is characterised in that described vitrified bond
Wood flour ash for the wood flour ash of Lignum Aquilariae Resinatum, the wood flour ash of sandalwood or Ramulus et folium taxi cuspidatae.