CN106348727A - 一种绿色健康型均玉釉瓷器 - Google Patents
一种绿色健康型均玉釉瓷器 Download PDFInfo
- Publication number
- CN106348727A CN106348727A CN201610731204.1A CN201610731204A CN106348727A CN 106348727 A CN106348727 A CN 106348727A CN 201610731204 A CN201610731204 A CN 201610731204A CN 106348727 A CN106348727 A CN 106348727A
- Authority
- CN
- China
- Prior art keywords
- parts
- green
- porcelain
- jade
- homogenous
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种绿色健康型均玉釉瓷器，其特征在于：包括如下重量份数的原料：牛骨10份，苏麻离青30份，纤维石膏粉40份，氧化钙20份，闭孔珍珠岩15份，高岭土18份，岩棉15份，氧化镁5份，蛇纹石11‑18份，由氧化硅15份、氧化铝15份，二氧化锡5份，硅酸铝细粉8份，冰晶石15份，白水泥5份，硅灰石8份，洗泥70份，使得瓷器的整体价格降低，的总之本发明具有绿色健康、制作成本较低、便于实现的优点。
Description
技术领域
本发明属于瓷器制造工艺领域，具体涉及一种绿色健康型均玉釉瓷器。
背景技术
瓷器是由瓷石、高岭土、石英石、莫来石等烧制而成，外表施有玻璃质釉或彩绘的物器。瓷器的成形要通过在窑内经过高温（约1280℃-1400℃）烧制，瓷器表面的釉色会因为温度的不同从而发生各种化学变化。烧结的瓷器胎一般仅含3%不到的铁元素，且不透水，因其较为低廉的成本和耐磨不透水的特性广为世界各地的民众所使用，是中华文明展示的瑰宝，传统的瓷器的烧制虽然工艺精美，但是制作成本较高，其中的原料也不符合绿色健康的要求，有必要做出相应改变。
发明内容
本发明的目的是为了克服现有技术的不足，而提供一种绿色健康、制作成本较低、便于实现的绿色健康型均玉釉瓷器。
本发明的目的是这样实现的：一种绿色健康型均玉釉瓷器，其特征在于：包括如下重量份数的原料：牛骨10份，苏麻离青30份，纤维石膏粉40份，氧化钙20份，闭孔珍珠岩15份，高岭土18份，岩棉15份，氧化镁5份，蛇纹石11-18份，由氧化硅15份、氧化铝15份，二氧化锡5份，硅酸铝细粉8份，冰晶石15份，白水泥5份，硅灰石8份，洗泥70份。
本发明的有益效果：继承了传统瓷器的精美的优点，同时革除了其中回青的原料，回青是一种蓝色颜料，主要用于瓷器烧制上色，因明朝时从西域进口，故而得名，回青一般需要和石子青混合运用，所呈现的颜色较霁蓝浅淡，多见于嘉靖和万历年间的瓷器，价格甚至超过了黄金，其价格较高，使得瓷器的整体造价较高，利用苏麻离青将其代替，不仅保持了瓷器的艺术价值，还降低了其制作的成本，使得瓷器的整体价格降低，的总之本发明具有绿色健康、制作成本较低、便于实现的优点。
具体实施方式
实施例1
一种绿色健康型均玉釉瓷器，其特征在于：包括如下重量份数的原料：牛骨10份，苏麻离青30份，纤维石膏粉40份，氧化钙20份，闭孔珍珠岩15份，高岭土18份，岩棉15份，氧化镁5份，蛇纹石11-18份，由氧化硅15份、氧化铝15份，二氧化锡5份，硅酸铝细粉8份，冰晶石15份，白水泥5份，硅灰石8份，洗泥70份。
Claims (1)
1.一种绿色健康型均玉釉瓷器，其特征在于：包括如下重量份数的原料：牛骨10份，苏麻离青30份，纤维石膏粉40份，氧化钙20份，闭孔珍珠岩15份，高岭土18份，岩棉15份，氧化镁5份，蛇纹石11-18份，由氧化硅15份、氧化铝15份，二氧化锡5份，硅酸铝细粉8份，冰晶石15份，白水泥5份，硅灰石8份，洗泥70份。