CN106271414B - 一种tmcp型桥梁用不锈钢复合板的制备方法 - Google Patents
一种tmcp型桥梁用不锈钢复合板的制备方法 Download PDFInfo
- Publication number
- CN106271414B CN106271414B CN201610706997.1A CN201610706997A CN106271414B CN 106271414 B CN106271414 B CN 106271414B CN 201610706997 A CN201610706997 A CN 201610706997A CN 106271414 B CN106271414 B CN 106271414B
- Authority
- CN
- China
- Prior art keywords
- composite
- sealing
- stainless steel
- base material
- rolling
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明是一种TMCP型桥梁用不锈钢复合板的制备方法,通过坯料选取、表面处理、隔离剂涂刷、组坯、电子束封焊、加热、轧制、矫直及切割分板等步骤制备出良好冶金结合的桥梁用不锈钢复合板。本发明在真空室环境下采用电子束直接封焊,减少了传统工艺的钻孔、抽真空等工序,真空度更有保障。通过TMCP工艺,保证基材桥梁钢良好的力学性能,轧后的快速冷却,控制覆材的晶间析出,保证了覆材良好耐蚀性;基材采用低碳设计坯料,所制备的复合板,基材碳当量低,焊接性能良好,便于现场施工;另外,复合板不需要热处理,即可获得良好的综合性能。
Description
技术领域
本发明属于双金属复合制造技术领域,具体地说涉及一种TMCP型桥梁用不锈钢复合板的制备方法。
背景技术
目前,我国的高速铁路及客运专线铁路钢桥的桥面系设计均采用正交异性板结构的钢桥面,在道碴槽与桥面连接处容易产生积水,进而引起桥面的腐蚀,最终影响铁路钢桥的使用寿命。桥梁用不锈钢复合板,兼具覆层不锈钢的耐腐蚀性和基材桥梁钢的强韧性,在铁路桥面上使用不锈钢复合板正好可以解决桥面的腐蚀问题。因此,桥梁用不锈钢复合板在铁路钢桥上将逐渐得到应用。
一般情况下,不锈钢复合板有***法和轧制法生产。***法由于噪音大,对环境存有污染,且受天气的影响较大,不是一种可持续的复合板制备技术。轧制法是采用高温轧制的方式,利用原子间的扩散使覆材和基材实现良好的冶金结合,其生产的复合板,板幅可灵活调整,是一种绿色环保可持续的生产工艺。因此,采用轧制法生产复合板将是未来发展的趋势。
目前,桥梁行业用复合板,一般采用***法制备的正火态交货的不锈钢复合板,该复合板的基材主要正火钢板为主,碳当量较高,焊接难度大,不利于现场施工;而采用真空轧制法生产复合板,现有传统工艺主要通过封焊四周,然后钻孔再抽真空的方法进行组坯,如专利公开号CN103639203A《对称热轧制造不锈钢复合板的真空封装方法》及专利公开号CN104708276A《一种不锈钢复合板的制备方法》公开的正是利用该法进行组坯,因该法需要封焊后再钻孔抽真空,工艺较为繁琐,且主要靠人工操作完成。另外一种新颖的组坯方式是在真空环境下电子束直接焊接组坯,省去了封焊后钻孔抽真空过程,如专利公开号CN102069289A《一种不锈钢-碳钢复合板的制备方法》公开的正是采用电子束将不锈钢与碳钢直接在真空环境下进行焊接组坯,然后再加热轧制的方法制备复合板,然而该法由于不锈钢与碳钢的热膨胀系数存在很大差异,加热过程因膨胀量不一样很容易使不锈钢与碳钢的焊缝裂开,轧制成功率不太高。
发明内容
本发明所要解决的技术问题是,克服现有技术的缺点,提供一种TMCP型桥梁用不锈钢复合板的制备方法,所用基材为低碳设计的桥梁钢,通过添加封条,在真空环境下利用电子束将封条与基材焊接的方式组坯,再经TMCP工艺轧制,制备出良好冶金结合的桥梁用不锈钢复合板,有效地解决了复合板基材碳当量高不易焊接的问题,同时制坯过程减少了钻孔抽真空等工序,工艺简单,且轧制成功率高。
本发明解决以上技术问题的技术方案是:
一种TMCP型桥梁用不锈钢复合板的制备方法,包括以下步骤:
㈠坯料准备:根据成品复合板的钢种及规格,确定基材和覆材坯料钢种及规格;
㈡表面处理:对基材和覆材坯料的待复合面进行打磨处理,清除坯料表面的锈层及氧化层,使表面完全露出新鲜金属;
㈢隔离剂涂刷:对覆材非复合面进行隔离剂涂刷,保证隔离剂均匀涂刷在覆材表面上,然后再将隔离剂烘干;
㈣组合坯料:在其中一块基材待复合面的四周边部将封条点焊固定,封条高度为两块覆材的厚度之和,宽度为30-60mm;然后将两块覆材非复合面叠合,并放置在封条围成的槽内,再将另一块基材复合面朝下,盖在两块覆材的上面,确保上下基材四侧边与封条外边平齐,组成一个待封焊的复合坯;
㈤电子束封焊:将组好的复合坯送至真空室,然后对真空室抽真空,待真空室真空度达到10×10-2Pa以下时,采用真空电子束将复合坯封条与基材之间的缝隙进行焊接;
㈥加热:将复合坯送至加热炉加热,加热温度在1100-1250℃,加热总时间按坯料厚度以9-16min/cm的时间控制;
㈦轧制与冷却:采用TMCP工艺进行轧制,中间坯厚度是轧制总厚度的1.8-3.0倍,精轧开轧温度900-970℃,终轧温度控制800-900℃;采用大压下方式轧制,保证粗轧阶段最后一道次压下率在20%以上;轧制后高速抛钢,复合板直接进入超快冷装置进行以2-20℃/s速度快速冷却,返红温度控制在550-700℃;
㈧矫直:对轧制后的钢板进行矫直处理,矫直后上冷床冷却,待表面温度降至300℃以下时即可下线;
㈨切割分板:采用等离子或火焰切割方式对复合板进行切割,经切头、尾及切两边后,上下两张单面复合板分离,再对单面复合板进行矫直处理,经表面打磨、性能检测、打包处理后,最终获得所需规格的不锈钢复合板产品。
本发明进一步限定的技术方案是:
前述的TMCP型桥梁用不锈钢复合板的制备方法,其中步骤㈠中的基材坯料钢种为采用低碳设计的桥梁钢,其化学成分按重量百分比为:C:0.05%-0.14%,Si:0.1%-0.5%,Mn:1.0%-1.6%,P≤0.02%,S≤0.01%,Nb:0.010%-0.090%,V≤0.080%,Ti:0.006%-0.030%,Alt:0.015%-0.050%,Cr≤0.30%,Ni≤0.30%,Cu≤0.30%,余量为Fe及少量不可避免的杂质。
前述的TMCP型桥梁用不锈钢复合板的制备方法,其中步骤㈠中,覆材坯料钢种为不锈钢,如S30408、S31603或321等不锈钢,其成分及性能满足对应标准要求。
前述的TMCP型桥梁用不锈钢复合板的制备方法,其中步骤㈤中的电子束封焊,封条与基材之间的焊缝深度为30-60mm,以提供足够的焊缝强度确保复合坯轧制过程不开裂。
前述的TMCP型桥梁用不锈钢复合板的制备方法,其中步骤㈦中轧制过程粗轧阶段的压缩比≥2.0,粗轧过程较大的压缩比,保证基材与覆材之间原子的充分扩散,最终实现复合板的良好冶金结合;
前述的TMCP型桥梁用不锈钢复合板的制备方法,其中步骤㈨中的不锈钢复合板产品,其总厚度为5-60mm,覆材厚度为0.5-10mm。
前述的TMCP型桥梁用不锈钢复合板的制备方法,其中步骤㈣中的封条是低合金钢材料,材质同基材的成分及强度相当即可。本发明与现有技术相比,具有以下优点:
⑴本发明基材采用低碳设计的桥梁钢,所制备的桥梁用不锈钢复合板,其基材碳当量低,不预热可直接焊接,便于现场施工。
⑵本发明在真空室环境下直接封焊,减少了传统工艺的钻孔、抽真空等工序,真空度更有保障。
⑶本发明通过封条与基材的焊接所组的复合坯,避免了因加热过程不锈钢与碳钢膨胀量不一致而开裂的问题。
⑷本发明通过TMCP工艺,保证基材桥梁钢良好的性能,同时轧后的快速冷却,控制覆材不锈钢的晶间析出物,保证了覆材的良好耐蚀性,另外复合板不需要热处理,即可获得良好的综合性能。
附图说明
图1为本发明实施例2的复合板界面显微组织图。
具体实施方式
实施例1
本实施例选择基材坯料厚度96mm的Q345qD钢种,化学成分见表1,覆材坯料厚度为18mm的321不锈钢,轧制成品厚度为3+16mm的321+Q345qD复合板。
对两块Q345qD基材坯料和两块321覆材坯料的其中一个表面进行打磨,清除坯料表面的锈层及氧化层,使表面完全露出新鲜金属。对覆材未打磨表面涂刷隔离剂,然后将隔离剂烘干。对其中一块基材已打磨表面的四周边部点焊固定封条,封条高度为36mm,宽度为45mm;将两块覆材的非复合面叠合,放置在封条围成的槽内,再将另一块基材复合面朝下,盖在两块覆材的上面,同时保证上下基材四侧边与封条外边平齐,这样即组成一个待封焊的复合坯。将组好的复合坯送至真空室,然后对真空室抽真空,待真空室真空度达到4×10- 2Pa时,采用电子束将封条与基材之间的缝隙进行焊接,即得到总厚度为228mm复合坯。
将复合坯送至步进式加热炉加热,加热温度1200℃,加热总时间230min。采用TMCP工艺进行轧制,中间坯厚度为90mm,精轧开轧温度≤930℃,终轧温度控制830℃左右。粗轧阶段最后一道次压下率在27%左右,最终轧制厚度为38mm,轧后直接进入超快冷快速冷却,返红温度在650℃左右。轧后复合板经矫直后上冷床冷却,待表面温度降至300℃下线。经切头、尾及切两边后,上下两张单层复合板分离,再对单层复合板进行矫直处理,然后对覆材表面打磨,最终获得成品厚度3+16mm的321+Q370qD复合板产品。
实施例2
本实施例选择基材坯料厚度192mm的Q370qD钢种,化学成分见表1,覆材坯料厚度为16mm的S31603不锈钢,轧制成品厚度为3+36mm的S31603+Q370qD复合板。
对两块Q370qD基材坯料和两块S31603覆材坯料其中一个表面进行打磨,清除坯料表面的锈层及氧化层,使表面完全露出新鲜金属。对覆材未打磨表面涂刷隔离剂,然后将隔离剂烘干。对其中一块基材已打磨表面的四周边部点焊封条,封条高度为32mm,宽度为50mm;将两块覆材的非复合面叠合,放置在封条围成的槽内,再将另一块基材复合面朝下,盖在两块覆材及槽的上面,确保上下基材四侧边与封条外边平齐,这样即组成一个待封焊的复合坯。将组好的复合坯送至真空室,然后对真空室抽真空,待真空室真空度达到5×10- 2Pa时,采用电子束将封条与基材之间的缝隙进行焊接,即得到总厚度为416mm复合坯。
将复合坯送至台车加热炉加热,加热温度1200℃,加热总时间500min。采用TMCP工艺进行轧制,中间坯厚度为160mm,精轧开轧温度≤900℃,终轧温度控制830℃左右。粗轧阶段最后一道次压下率在25%左右,最终轧制厚度为78mm,轧后直接进入超快冷ACC模式冷却,返红温度在620℃左右。轧后复合板经矫直后上冷床冷却,待表面温度降至300℃下线。再经切头、尾及切两边后,上下两张单层复合板分离,再对单层复合板进行矫直处理,然后对覆材表面打磨,最终获得成品厚度3+36mm的S31603+Q370qD复合板产品。
复合板的界面显微组织图如图1所示,如图可知,不锈钢与桥梁钢之间未发现未结合区域,复合板实现良好的冶金结合。
实施例3
本实施例选择基材坯料厚度107mm的Q370qE钢种,化学成分见表1,覆材坯料厚度为16mm的S31603不锈钢,轧制成品厚度为3+20mm的S31603+Q370qE复合板。
对两块Q370qE基材坯料和两块S31603覆材坯料其中一个表面进行打磨,清除坯料表面的锈层及氧化层,使表面完全露出新鲜金属。对覆材未打磨表面涂刷隔离剂,然后将隔离剂烘干。对其中一块基材已打磨表面的四周边部点焊封条,封条高度为32mm,宽度为40mm;将两块覆材的非复合面叠合,放置在封条围成的槽内,再将另一块基材复合面朝下,盖在两块覆材及槽的上面,确保上下基材四侧边与封条外边平齐,这样即组成一个待封焊的复合坯。将组好的复合坯送至真空室,然后对真空室抽真空,待真空室真空度达到5×10- 2Pa时,采用电子束将封条与基材之间的缝隙进行焊接,即得到总厚度为246mm复合坯。
将复合坯送至步进式加热炉加热,加热温度1200℃,加热总时间250min。采用TMCP工艺进行轧制,中间坯厚度为96mm,精轧开轧温度≤910℃,终轧温度控制820℃左右。粗轧阶段最后一道次压下率在27%左右,最终轧制厚度为46mm,轧后直接进入超快冷快速冷却,返红温度在650℃左右。轧后复合板经矫直后上冷床冷却,待表面温度降至250℃下线。经切头、尾及切两边后,上下两张单层复合板分离,再对单层复合板进行矫直处理,然后对覆材表面打磨,最终获得成品厚度3+20mm的S31603+Q370qE复合板产品。
实施例4
本实施例选择基材坯料厚度60mm的Q420qE钢种,化学成分见表1,覆材坯料厚度为12mm的S30403不锈钢,轧制成品厚度为2+10mm的S30403+Q370qE复合板。
对两块Q420qE基材坯料和两块S31603覆材坯料其中一个表面进行打磨,清除坯料表面的锈层及氧化层,使表面完全露出新鲜金属。对覆材未打磨表面涂刷隔离剂,然后将隔离剂烘干。对其中一块基材已打磨表面的四周边部点焊封条,封条高度为24mm,宽度为35mm;将两块覆材的非复合面叠合,放置在封条围成的槽内,再将另一块基材复合面朝下,盖在两块覆材及槽的上面,确保上下基材四侧边与封条外边平齐,这样即组成一个待封焊的复合坯。将组好的复合坯送至真空室,然后对真空室抽真空,待真空室真空度达到5×10- 2Pa时,采用电子束将封条与基材之间的缝隙进行焊接,即得到总厚度为144mm复合坯。
将复合坯送至步进式加热炉加热,加热温度1200℃,加热总时间170min。采用TMCP工艺进行轧制,中间坯厚度为60mm,精轧开轧温度≤900℃,终轧温度控制820℃左右。粗轧阶段最后一道次压下率在28%左右,最终轧制厚度为24mm,轧后直接进入超快冷ACC模式冷却,返红温度在550℃左右。轧后复合板经矫直后上冷床冷却,待表面温度降至250℃下线。经切头、尾及切两边后,上下两张单层复合板分离,再对单层复合板进行矫直处理,然后对覆材表面打磨,最终获得成品厚度2+10mm的S30403+Q420qE复合板产品。
表1本发明实施例钢种的冶炼成分:
实施例 | C | Si | Mn | P | S | Nb | V | Ti | Alt | Cr | Ni | Cu |
实施例1 | 0.13 | 0.20 | 1.45 | 0.014 | 0.0050 | 0.015 | 0.001 | 0.015 | 0.035 | / | / | / |
实施例2 | 0.10 | 0.24 | 1.46 | 0.012 | 0.0035 | 0.035 | 0.001 | 0.017 | 0.036 | 0.13 | / | 0.013 |
实施例3 | 0.095 | 0.25 | 1.48 | 0.012 | 0.0025 | 0.027 | 0.001 | 0.018 | 0.034 | 0.13 | 0.25 | 0.012 |
实施例4 | 0.075 | 0.28 | 1.52 | 0.012 | 0.0023 | 0.045 | 0.003 | 0.015 | 0.035 | 0.16 | / | 0.015 |
除上述实施例外,本发明还可以有其他实施方式。凡采用等同替换或等效变换形成的技术方案,均落在本发明要求的保护范围。
Claims (6)
1.一种TMCP型桥梁用不锈钢复合板的制备方法,其特征在于:包括以下步骤:
㈠坯料准备:根据成品复合板的钢种及规格,确定基材和覆材坯料钢种及规格;
㈡表面处理:对基材和覆材坯料的待复合面进行打磨处理,清除坯料表面的锈层及氧化层,使表面完全露出新鲜金属;
㈢隔离剂涂刷:对覆材非复合面进行隔离剂涂刷,保证隔离剂均匀涂刷在覆材表面上,然后再将隔离剂烘干;
㈣组合坯料:在其中一块基材待复合面的四周边部将封条点焊固定,封条高度为两块覆材的厚度之和,宽度为30-60mm;然后将两块覆材非复合面叠合,并放置在封条围成的槽内,再将另一块基材复合面朝下,盖在两块覆材的上面,确保上下基材四侧边与封条外边平齐,组成一个待封焊的复合坯;
㈤电子束封焊:将组好的复合坯送至真空室,然后对真空室抽真空,待真空室真空度达到10×10-2Pa以下时,采用真空电子束将复合坯封条与基材之间的缝隙进行焊接;
㈥加热:将复合坯送至加热炉加热,加热温度在1100-1250℃,加热总时间按坯料厚度以9-16min/cm的时间控制;
㈦轧制与冷却:采用TMCP工艺进行轧制,中间坯厚度是轧制总厚度的1.8-3.0倍,精轧开轧温度900-970℃,终轧温度控制800-900℃;采用大压下方式轧制,保证粗轧阶段最后一道次压下率在20%以上;轧制后高速抛钢,复合板直接进入超快冷装置进行以2-20℃/s速度快速冷却,返红温度控制在550-700℃;
㈧矫直:对轧制后的钢板进行矫直处理,矫直后上冷床冷却,待表面温度降至300℃以下时即可下线;
㈨切割分板:采用等离子或火焰切割方式对复合板进行切割,经切头、尾及切两边后,上下两张单面复合板分离,再对单面复合板进行矫直处理,经表面打磨、性能检测、打包处理后,最终获得所需规格的不锈钢复合板产品。
2.如权利要求1所述的TMCP型桥梁用不锈钢复合板的制备方法,其特征在于:所述步骤㈠中的基材坯料钢种为采用低碳设计的桥梁钢,其化学成分按重量百分比为:C:0.05%-0.14%,Si:0.1%-0.5%,Mn:1.0%-1.6%,P ≤0.02%,S ≤0.01%,Nb:0.010%-0.090%,V ≤0.080%,Ti:0.006%-0.030%,Alt:0.015%-0.050%,Cr ≤0.30%,Ni ≤0.30%,Cu ≤0.30%,余量为Fe及少量不可避免的杂质。
3.如权利要求1所述的TMCP型桥梁用不锈钢复合板的制备方法,其特征在于:所述步骤㈠中,覆材坯料钢种为不锈钢。
4.如权利要求1所述的TMCP型桥梁用不锈钢复合板的制备方法,其特征在于:所述步骤㈤中的电子束封焊,封条与基材之间的焊缝深度为30-60mm,以提供足够的焊缝强度确保复合坯轧制过程不开裂。
5.如权利要求1所述的TMCP型桥梁用不锈钢复合板的制备方法,其特征在于:所述步骤㈦中轧制过程粗轧阶段的压缩比≥2.0。
6.如权利要求1所述的TMCP型桥梁用不锈钢复合板的制备方法,其特征在于:所述步骤㈨中的不锈钢复合板产品,其总厚度为5-60mm,覆材厚度为0.5-10mm。