CN106186041A - 一种微波辅助热解制备纳米ZnO的方法 - Google Patents

一种微波辅助热解制备纳米ZnO的方法 Download PDF

Info

Publication number
CN106186041A
CN106186041A CN201610527695.8A CN201610527695A CN106186041A CN 106186041 A CN106186041 A CN 106186041A CN 201610527695 A CN201610527695 A CN 201610527695A CN 106186041 A CN106186041 A CN 106186041A
Authority
CN
China
Prior art keywords
zno
microwave
nano
prepared
completely dissolved
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610527695.8A
Other languages
English (en)
Inventor
彭勇刚
纪俊玲
陶永新
汪媛
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Changzhou University
Original Assignee
Changzhou University
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Changzhou University filed Critical Changzhou University
Priority to CN201610527695.8A priority Critical patent/CN106186041A/zh
Publication of CN106186041A publication Critical patent/CN106186041A/zh
Pending legal-status Critical Current

Abstract

本发明提供了一种微波辅助热解制备纳米ZnO的方法，该方法首先将十八胺加热熔融，然后加入硝酸锌；再通过微波辅助热解的方式制备纳米ZnO。该方法操作简单、绿色环保。

Description

一种微波辅助热解制备纳米ZnO的方法
技术领域
本发明属于新材料领域，具体涉及一种微波辅助热解制备纳米ZnO的方法。
背景技术
纳米ZnO作为一种重要的Ⅱ-Ⅵ族半导体氧化物，在有机污染物的光催化降解方面有着广泛的应用。纳米ZnO的制备方法主要有：激光诱导CVD法、化学气相氧化法、化学沉淀法、溶胶-凝胶法、水热法、微乳液法等。这些方法中，有些操作复杂、需要特殊的设备；有些需要使用一些有毒有害的化学品。
发明内容
本发明所要解决的技术问题是提供一种微波辅助热解制备纳米ZnO的方法，该方法采用微波辅助热解硝酸锌，制备纳米ZnO，操作简单、绿色环保。
本发明提供的一种微波辅助热解制备纳米ZnO的方法，按照下述步骤进行：
将30-100g十八胺加热到100℃，待其完全溶解后加入0.2-1.0g Zn(NO3)2·6H2O，不断搅拌，待溶质完全溶解后，将反应液置于微波反应器内，微波加热至180-220℃，保温30-60min，保温结束后，收集沉淀物，沉淀物分别用无水乙醇、蒸馏水洗涤3-5次，60-80℃烘干，即得纳米ZnO。
本发明的有益效果是：通过在十八胺溶液中直接热解硝酸锌来制备纳米ZnO，操作简单、绿色环保。
附图说明
图1实施例1所得材料的XRD图
图2实施例1所得材料的TEM图
具体实施方式
下面结合具体的实施例，进一步详细地描述本发明。应理解，这些实施例只是为了举例说明本发明，而非以任何方式限制本发明的范围。
实施例1
将30g十八胺加热到100℃，待其完全溶解后加入0.2g Zn(NO3)2·6H2O，不断搅拌，待溶质完全溶解后，将反应液置于微波反应器内，微波加热至180℃，保温60min，保温结束后，收集沉淀物，沉淀物分别用无水乙醇、蒸馏水洗涤3次，60℃烘干，即得纳米ZnO。
实施例2
将100g十八胺加热到100℃，待其完全溶解后加入1.0g Zn(NO3)2·6H2O，不断搅拌，待溶质完全溶解后，将反应液置于微波反应器内，微波加热至220℃，保温30min，保温结束后，收集沉淀物，沉淀物分别用无水乙醇、蒸馏水洗涤5次，80℃烘干，即得纳米ZnO。
实施例3
将60g十八胺加热到100℃，待其完全溶解后加入0.5g Zn(NO3)2·6H2O，不断搅拌，待溶质完全溶解后，将反应液置于微波反应器内，微波加热至200℃，保温45min，保温结束后，收集沉淀物，沉淀物分别用无水乙醇、蒸馏水洗涤4次，70℃烘干，即得纳米ZnO。
实施例4
将50g十八胺加热到100℃，待其完全溶解后加入0.4Zn(NO3)2·6H2O，不断搅拌，待溶质完全溶解后，将反应液置于微波反应器内，微波加热至190℃，保温35min，保温结束后，收集沉淀物，沉淀物分别用无水乙醇、蒸馏水洗涤5次，75℃烘干，即得纳米ZnO。

Claims (1)

1.一种微波辅助热解制备纳米ZnO的方法，其特征在于：步骤如下：
将30-100g十八胺加热到100℃，待其完全溶解后加入0.2-1.0g Zn(NO3)2·6H2O，不断搅拌，待溶质完全溶解后，将反应液置于微波反应器内，微波加热至180-220℃，保温30-60min，保温结束后，收集沉淀物，沉淀物分别用无水乙醇、蒸馏水洗涤3-5次，60-80℃烘干，即得纳米ZnO。
CN201610527695.8A 2016-07-06 2016-07-06 一种微波辅助热解制备纳米ZnO的方法 Pending CN106186041A (zh)