CN106048816B - A kind of blended ratio and production method - Google Patents
A kind of blended ratio and production method Download PDFInfo
- Publication number
- CN106048816B CN106048816B CN201610680737.1A CN201610680737A CN106048816B CN 106048816 B CN106048816 B CN 106048816B CN 201610680737 A CN201610680737 A CN 201610680737A CN 106048816 B CN106048816 B CN 106048816B
- Authority
- CN
- China
- Prior art keywords
- yarn
- twister
- twisted filament
- production method
- group
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The present invention discloses a kind of blended ratio and production method, and the blended ratio is raw material by White Steam Filature Yarns, modified dacron and regenerated celulose fibre, has soft smooth, Comfortable attractive, moisture absorption is ventilative, and moisture-sensitive, does not play electrostatic, not pilling fluffing, colourless pattern difference Shared-with point, elasticity and resilience performance are excellent, light, it is harmless, and the advantages that the comfortable and environmentally friendly theory of back to nature is dissolved into design.Simultaneously, the production method of blended ratio of the present invention, using White Steam Filature Yarns, modified dacron and regenerated celulose fibre as raw material, by carrying out simultaneously silk, twisted filament and the processing such as heating in steam box to silk thread not of the same race, yarn can be made to have the advantages that more compact, sizing does not bounce back, controls pilling fluffing, ready-made clothes not inclined tab.
Description
Technical field
The present invention relates to field of textile industry, more particularly, to a kind of blended ratio and production method.
Background technique
With the development and progress of society, people's lives level is continuously improved, and people not only stop the pursuit of textile
Artistry and decorative aspect are stayed in, the comfort of dress, functionality, wholesomeness, protective, health and aesthetics are wanted
Ask also higher and higher.
White Steam Filature Yarns, that is, raw silk, is commonly called as silk, is known as " fiber queen ", with its unique glamour by people through the ages
Favor.White Steam Filature Yarns belongs to protein fibre, containing 18 kinds of amino acid beneficial to human body in fibroin, skin can be helped to maintain
The metabolism of surface adipose membrane, therefore skin can be made to keep moist, smooth.In addition, White Steam Filature Yarns itself is soft smooth, feel is rich
Full, strength and elongation is good, and high resilience, soft glossy, hygroscopicity is strong, nonirritant to human body, is advanced textile material, still, existing
With the presence of White Steam Filature Yarns quality on defect, Zhu Yao You Hold-those section, color fault, pollution fault, arrange bad and fine hair.It is weaved
Fabric intolerant to washing, not sun-resistant, the time worn and used is shorter.Modified dacron exactly enables terylene formal structure
It changes, can be made by production technology.Although common polyester fabric has higher intensity and elastic restoring force, hard
The advantages that jail is durable, and wash and wear, heat resistance is strong, and waterproof performance is excellent, and easy to clean.But it is easy always over time
To change, allergy is often easy to cause with skin friction, and dyeability is poor, melt resistance is poor, and hygroscopicity is poor, and moisture content is low, poor air permeability,
It is easy pilling fluffing, is easily stain.Method of the modified dacron by carrying out chemical modification and physical deformation to terylene, improves fiber
Hydroscopicity, strengthen the performance of the antistatic and dirt-resistant of fiber, improve the flame resistance energy of fiber, improve anti pilling
Ability, and improve dyeability.Although the improvement of this serial performance substantially increases the application range of modified dacron,
It is still not to be avoided that material poor air permeability itself, it is easy to aging, cause the defect of allergy.Regenerated celulose fibre is used as " 21
The green fiber in century ", be it is a kind of by celluloses such as straw, barks after dissolving made of spinning, mainly include Modal
(Modal) fiber, Tan Xier (Tencel) fiber, bamboo fibre, viscose chitin fibre and copper ammonia fiber.Due to subtracting for arable land
It is few and petroleum resources increasingly depleted, natural fiber, synthetic fibers yield will will receive more and more restrictions.Regenerated fiber
Cellulose fiber raw material is natural material, harmless, and can natural decomposition, environmental sound belongs to novel environment-friendlyfiber fiber, energy
It enough plays and bacterium, deodorization absorption, moisture absorption is inhibited to breathe freely, heat accumulation thermal, reduce the effect of electrostatic, meanwhile, regenerated celulose fibre
Itself is soft, and color is beautiful, and toughness and wearability are strong, has unique resilience, and stable uniform, drapability are good.But by
It is very fragile easily broken in its intrinsic fiber properties, the intensity of 30%-50%, elasticity and resilience performance can be lost in hygrometric state
It is poor, damaged and deformation is easy in washing.In addition, regenerated celulose fibre can also substantially be shunk after washing, also easy mould moth,
As other natural fibers, it is easy fluffing or pilling.In addition, due to the higher cost of regenerated cellulose, so relative to it
His silk thread product price is high.
Therefore, the advantages of one kind can have both not yarn of the same race is developed, and overcomes every kind of yarn self shortcoming, feel is soft
Soft smooth, Comfortable attractive, moisture absorption is ventilative, not moisture-sensitive, does not play electrostatic, not pilling fluffing, colourless pattern difference Shared-with point, elasticity and returns
Bullet is had excellent performance, light, harmless, and the comfortable and environmentally friendly theory of back to nature is dissolved into the weaving in design
Material also has become the emphasis of research and development.
In view of this, the present invention is specifically proposed.
Summary of the invention
It is an object of the present invention to provide a kind of blended ratio, the blended ratio is with White Steam Filature Yarns, modified dacron and regeneration
Cellulose fibre is raw material, has soft smooth, Comfortable attractive, moisture absorption is ventilative, and moisture-sensitive, does not play electrostatic, not pilling
Fluffing, colourless pattern difference Shared-with point, elasticity and resilience performance are excellent, light, harmless, and by the comfortable and ring of back to nature
The advantages that theory of guarantor is dissolved into design.
It is another object of the present invention to provide a kind of production method of blended ratio, this method with White Steam Filature Yarns, change
Property terylene and regenerated celulose fibre be raw material, by being carried out to not silk thread of the same race and silk, twisted filament and heating etc. in steam box
Reason makes yarn achieve the purpose that more compact, sizing does not bounce back, controls pilling fluffing, ready-made clothes not inclined tab.
In order to achieve the above objectives, the present invention adopts the following technical solutions:
A kind of blended ratio is made of White Steam Filature Yarns, modified dacron and regenerated celulose fibre for raw material.
Three of the above yarn be raw material and made of blended ratio, there is soft smooth, Comfortable attractive, moisture absorption is saturating
Gas, moisture-sensitive, does not play electrostatic, and not pilling fluffing, colourless pattern difference Shared-with point, elasticity and resilience performance are excellent, light, to human body
It is harmless, and the advantages that the comfortable and environmentally friendly theory of back to nature is dissolved into design.
Preferably, the single thread force 1200-1400CN/CM of the blended ratio, regain 11-13%, color fastness to washing 4-5
Grade, washing shrinkage ± 2- ± 3.
Preferably, the specification of the White Steam Filature Yarns is 20/22-30/33D, and the specification of the modified dacron is 30-70D, described
The specification of regenerated celulose fibre is 50-100D.
Preferably, the specification of the White Steam Filature Yarns is 20/22D, and the specification of the modified dacron is 50D, the regenerated fiber
The specification of cellulose fiber is 75D.
In the present invention, by the further adjustment and optimization to various raw material specifications, to advanced optimize the present invention
The performance of blended ratio.
Further, the present invention also provides a kind of production method of blended ratio, the specific steps of the production method
It is as follows:
(1) by a White Steam Filature Yarns and a modified dacron on doubling winder and silk, and at the first yarn group, first yarn group
For a two stock yarn lines;
(2) first yarn is rolled into a ball and twisted filament processing is carried out by two-for-one twister, obtain the first yarn;
(3) first yarn is placed in steam box and is heated;
(4) a root regeneration cellulose fibre is subjected to twisted filament processing by two-for-one twister, obtains the second yarn;
(5) second yarn is placed in steam box and is heated;
(6) by first yarn and second yarn on doubling winder and silk, and at the second yarn group, second yarn
Group is a two stock yarn lines;
(7) second yarn is rolled into a ball and twisted filament processing is carried out by two-for-one twister, obtain third yarn;
(8) the third yarn is placed in steam box and is heated.
Preferably, the weight of the first yarn group is 680-720g, and the weight of the second yarn group is 680-720g.
Preferably, the weight of the first yarn group is 700g, and the weight of the second yarn group is 700g.
In the present invention, by yarn group's Weight control in the weight for being most suitable for dyeing, facilitate later period control dyeing defect color difference.
Preferably, the twisted filament processing that the first yarn group is carried out by two-for-one twister is Z twisted filament, twists 607 twists/m.
Preferably, the regenerated celulose fibre is 607 twists/m of twisting by the twisted filament processing that two-for-one twister carries out.
Preferably, the twisted filament processing that the third yarn group is carried out by two-for-one twister is S twisted filament, twists 544 twists/m.
In the present invention, each raw yarn is subjected to twisted filament processing, yarn can be made when the external force being stretched, inclined
Oblique fiber, which generates radial pressure to yam axis, to enhance the performance of raw yarn keeps yarn more compact, the intensity of yarn and resistance to
The case where frictional behaviour is significantly improved, and reduces pilling fluffing and broken end, improves the fastness of silk fabrics, can also increase yarn
Elasticity, improve the wrinkle resistance and permeability of silk fabrics.Meanwhile twisted filament processing can also impart to yarn appearance with refractive power
Effect, obtained silk fabrics have wrinkle, looped pile or knot and other effects.
In the present invention, the twisted filament processing that the first yarn group is carried out by two-for-one twister is Z twisted filament, and third yarn group passes through
The twisted filament processing that two-for-one twister carries out is S twisted filament, and purpose essentially consists in control ready-made clothes not inclined tab.
Preferably, the time of the heating is no less than 50 minutes, and the temperature of the heating is 80-90 DEG C.
In the present invention, being by the purpose that first yarn, the second yarn, third yarn heat in steam box can
So that yarn sizing is not bounced back, effectively controls pilling fluffing.
Blended ratio of the present invention can be used for braided fabric and fibre.Such as by being used for clothing materials, shawl, enclosing
Soft smooth, Comfortable attractive can be obtained in towel, cushion etc., and moisture absorption is ventilative, not moisture-sensitive, does not play electrostatic, and not pilling is fluffed,
Colourless pattern difference Shared-with point, elasticity and excellent, light, the harmless product of resilience performance.Furthermore it is possible to by of the present invention
Blended ratio is used for a part of cloth and silk and sewed product.
Beneficial effects of the present invention are as follows:
(1) blended ratio of the present invention has soft smooth, Comfortable attractive, and moisture absorption is ventilative, and moisture-sensitive, does not rise
Electrostatic, not pilling are fluffed, and colourless pattern difference Shared-with point, elasticity and resilience performance are excellent, light, harmless, and will be returned certainly
The advantages that right comfortable and environmentally friendly theory is dissolved into design.
(2) production method of blended ratio of the present invention is original with White Steam Filature Yarns, modified dacron and regenerated celulose fibre
Material can be such that yarn has more compact, fixed by carrying out simultaneously silk, twisted filament and the processing such as heating in steam box to silk thread not of the same race
Type do not bounce back, control pilling fluffing, ready-made clothes not inclined tab the advantages of.
Specific embodiment
In order to illustrate more clearly of the present invention, below with reference to preferred embodiment, the present invention is described further.Ability
Field technique personnel should be appreciated that following specifically described content is illustrative and be not restrictive, this should not be limited with this
The protection scope of invention.The person that is not specified actual conditions in embodiment, carries out according to conventional conditions or manufacturer's recommended conditions.Institute
Production firm person is not specified with reagent or instrument, is the conventional products that can be obtained by commercially available purchase.Original used in the present invention
Expect yarn, is 3A grades or more the product that can be obtained by commercially available purchase.
Embodiment 1
Raw yarn is selected according to following specification, the specification of White Steam Filature Yarns is 20/22D, and the specification of modified dacron is 50D, bamboo
The specification of fiber is 75D.Then, the blended ratio of the present embodiment is made according to following processing step:
(1) by the modified dacron of the White Steam Filature Yarns of 20/22D and a 50D on doubling winder and silk, and it is at quality
The first yarn group of 700g, the first yarn group is a two stock yarn lines;
(2) first yarn is rolled into a ball and Z-direction twisted filament processing is carried out by two-for-one twister, twisted 607 twists/m, obtain the first yarn;
(3) first yarn is placed in steam box and is heated, the time of heating is no less than 50 minutes, the temperature of heating
It is 80-90 DEG C;
(4) bamboo fibre of a 75D is subjected to twisted filament processing by two-for-one twister, twists 607 twists/m, obtains the second yarn;
(5) second yarn is placed in steam box and is heated, the time of heating is no less than 50 minutes, the temperature of heating
It is 80-90 DEG C;
(6) by first yarn and second yarn on doubling winder and silk, and the second yarn for being 700g at quality
Group, the second yarn group is a two stock yarn lines;
(7) second yarn is rolled into a ball and S is carried out to twisted filament processing by two-for-one twister, twisted 544 twists/m, obtain third yarn;
(8) the third yarn is placed in steam box and is heated, the time of heating is no less than 50 minutes, the temperature of heating
It is 80-90 DEG C.
Embodiment 2
Raw yarn is selected according to following specification, the specification of White Steam Filature Yarns is 24/26D, and the specification of modified dacron is 30D, not
The specification of Dai Er (Modal) fiber is 50D.Then, the blended ratio of the present embodiment is made according to following processing step:
(1) by the modified dacron of the White Steam Filature Yarns of 24/26D and a 30D on doubling winder and silk, and it is at quality
The first yarn group of 680g, the first yarn group is a two stock yarn lines;
(2) first yarn is rolled into a ball and Z-direction twisted filament processing is carried out by two-for-one twister, twisted 607 twists/m, obtain the first yarn;
(3) first yarn is placed in steam box and is heated, the time of heating is no less than 50 minutes, the temperature of heating
It is 80-90 DEG C;
(4) Modal (Modal) fiber of a 50D is subjected to twisted filament processing by two-for-one twister, twists 607 twists/m, obtains
To the second yarn;
(5) second yarn is placed in steam box and is heated, the time of heating is no less than 50 minutes, the temperature of heating
It is 80-90 DEG C;
(6) by first yarn and second yarn on doubling winder and silk, and the second yarn for being 680g at quality
Group, the second yarn group is a two stock yarn lines;
(7) second yarn is rolled into a ball and S is carried out to twisted filament processing by two-for-one twister, twisted 544 twists/m, obtain third yarn;
(8) the third yarn is placed in steam box and is heated, the time of heating is no less than 50 minutes, the temperature of heating
It is 80-90 DEG C.
Embodiment 3
Raw yarn is selected according to following specification, the specification of White Steam Filature Yarns is 30/33D, and the specification of modified dacron is 70D, smooth
The specification of Xi Er (Tencel) fiber is 100D.Then, the blended ratio of the present embodiment is made according to following processing step:
(1) by the modified dacron of the White Steam Filature Yarns of 30/33D and a 70D on doubling winder and silk, and it is at quality
The first yarn group of 720g, the first yarn group is a two stock yarn lines;
(2) first yarn is rolled into a ball and Z-direction twisted filament processing is carried out by two-for-one twister, twisted 607 twists/m, obtain the first yarn;
(3) first yarn is placed in steam box and is heated, the time of heating is no less than 50 minutes, the temperature of heating
It is 80-90 DEG C;
(4) Tan Xier (Tencel) fiber of a 100D is subjected to twisted filament processing by two-for-one twister, twists 607 twists/m,
Obtain the second yarn;
(5) second yarn is placed in steam box and is heated, the time of heating is no less than 50 minutes, the temperature of heating
It is 80-90 DEG C;
(6) by first yarn and second yarn on doubling winder and silk, and the second yarn for being 720g at quality
Group, the second yarn group is a two stock yarn lines;
(7) second yarn is rolled into a ball and S is carried out to twisted filament processing by two-for-one twister, twisted 544 twists/m, obtain third yarn;
(8) the third yarn is placed in steam box and is heated, the time of heating is no less than 50 minutes, the temperature of heating
It is 80-90 DEG C.
Embodiment 4
Raw yarn is selected according to following specification, the specification of White Steam Filature Yarns is 27/29D, and the specification of modified dacron is 40D, is glued
The specification of matrix chitin fiber is 60D.Then, the blended ratio of the present embodiment is made according to following processing step:
(1) by the modified dacron of the White Steam Filature Yarns of 27/29D and a 40D on doubling winder and silk, and it is at quality
The first yarn group of 700g, the first yarn group is a two stock yarn lines;
(2) first yarn is rolled into a ball and Z-direction twisted filament processing is carried out by two-for-one twister, twisted 607 twists/m, obtain the first yarn;
(3) first yarn is placed in steam box and is heated, the time of heating is no less than 50 minutes, the temperature of heating
It is 80-90 DEG C;
(4) viscose chitin fibre of a 60D is subjected to twisted filament processing by two-for-one twister, twists 607 twists/m, obtains
To the second yarn;
(5) second yarn is placed in steam box and is heated, the time of heating is no less than 50 minutes, the temperature of heating
It is 80-90 DEG C;
(6) by first yarn and second yarn on doubling winder and silk, and the second yarn for being 700g at quality
Group, the second yarn group is a two stock yarn lines;
(7) second yarn is rolled into a ball and S is carried out to twisted filament processing by two-for-one twister, twisted 544 twists/m, obtain third yarn;
(8) the third yarn is placed in steam box and is heated, the time of heating is no less than 50 minutes, the temperature of heating
It is 80-90 DEG C.
The list of testing product is distinguished according to GB/T3916-2013, GB9994-2008, GB/T2543.1-2001 detection method
Yarn strength, regain, color fastness to washing and washing shrinkage, as a result such as table 1, indices are above national standard.
Table 1
Obviously, the above embodiment of the present invention be only to clearly illustrate example of the present invention, and not be pair
The restriction of embodiments of the present invention may be used also on the basis of the above description for those of ordinary skill in the art
To make other variations or changes in different ways, all embodiments can not be exhaustive here, it is all to belong to this hair
The obvious changes or variations that bright technical solution is extended out are still in the scope of protection of the present invention.
Claims (11)
1. a kind of blended ratio, which is characterized in that the blended ratio is with White Steam Filature Yarns, modified dacron and regenerated celulose fibre for original
Material is made;
Wherein, the production method of the blended ratio, comprising the following steps:
(1) by a White Steam Filature Yarns and a modified dacron on doubling winder and silk, and at the first yarn group, the first yarn group is one
Two stock yarn line of root;
(2) first yarn is rolled into a ball and twisted filament processing is carried out by two-for-one twister, obtain the first yarn;
(3) first yarn is placed in steam box and is heated;
(4) a root regeneration cellulose fibre is subjected to twisted filament processing by two-for-one twister, obtains the second yarn;
(5) second yarn is placed in steam box and is heated;
(6) by first yarn and second yarn on doubling winder and silk, and at the second yarn group, the second yarn group is
A piece two stock yarn lines;
(7) second yarn is rolled into a ball and twisted filament processing is carried out by two-for-one twister, obtain third yarn;
(8) the third yarn is placed in steam box and is heated.
2. blended ratio according to claim 1, which is characterized in that the single thread force of the blended ratio is 1200-1400CN/
CM, regain 11-13%, color fastness to washing are 4-5 grades, and washing shrinkage is -3%~3%.
3. blended ratio according to claim 1, which is characterized in that the specification of the White Steam Filature Yarns is 20/22-30/33D, institute
The specification for stating modified dacron is 30-70D, and the specification of the regenerated celulose fibre is 50-100D.
4. blended ratio according to claim 1, which is characterized in that the specification of the White Steam Filature Yarns is 20/22D, the modification
The specification of terylene is 50D, and the specification of the regenerated celulose fibre is 75D.
5. the production method of the blended ratio as described in Claims 1-4 any one, which is characterized in that the production method includes
Following steps:
(1) by a White Steam Filature Yarns and a modified dacron on doubling winder and silk, and at the first yarn group, the first yarn group is one
Two stock yarn line of root;
(2) first yarn is rolled into a ball and twisted filament processing is carried out by two-for-one twister, obtain the first yarn;
(3) first yarn is placed in steam box and is heated;
(4) a root regeneration cellulose fibre is subjected to twisted filament processing by two-for-one twister, obtains the second yarn;
(5) second yarn is placed in steam box and is heated;
(6) by first yarn and second yarn on doubling winder and silk, and at the second yarn group, the second yarn group is
A piece two stock yarn lines;
(7) second yarn is rolled into a ball and twisted filament processing is carried out by two-for-one twister, obtain third yarn;
(8) the third yarn is placed in steam box and is heated.
6. production method according to claim 5, which is characterized in that the weight of the first yarn group is 680-720g, institute
The weight for stating the second yarn group is 680-720g.
7. preparation method according to claim 6, which is characterized in that the weight of first yarn group is 700g, described the
The weight of two yarns group is 700g.
8. production method according to claim 5, which is characterized in that first yarn rolls into a ball the twisted filament carried out by two-for-one twister
Processing is Z twisted filament, twists 607 twists/m.
9. production method according to claim 5, which is characterized in that the regenerated celulose fibre is carried out by two-for-one twister
Twisted filament processing for twisting 607 twists/m.
10. production method according to claim 5, which is characterized in that the third yarn rolls into a ball the twirl carried out by two-for-one twister
Silk processing is S twisted filament, twists 544 twists/m.
11. production method according to claim 5, which is characterized in that the time of the heating is no less than 50 minutes, described
The temperature of heating is 80-90 DEG C.