JP2010236108A - Woven fabric - Google Patents
Woven fabric Download PDFInfo
- Publication number
- JP2010236108A JP2010236108A JP2009082462A JP2009082462A JP2010236108A JP 2010236108 A JP2010236108 A JP 2010236108A JP 2009082462 A JP2009082462 A JP 2009082462A JP 2009082462 A JP2009082462 A JP 2009082462A JP 2010236108 A JP2010236108 A JP 2010236108A
- Authority
- JP
- Japan
- Prior art keywords
- yarn
- filament yarn
- fiber filament
- woven fabric
- fabric
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
Description
本発明は、快適な着用感と高級感に優れたスパンシルク織物調の毛羽を有する織物に関する。 The present invention relates to a woven fabric having a spun silk fabric-like fluff excellent in a comfortable wearing feeling and a high-class feeling.
スパンシルク織物は、スパンシルク糸（絹紡糸）からなる織物で、上品な控えめの光沢と膨らみ感があり、ソフトで上品なドライ感を有する等から高級な織物として広く認められている。さらにスパンシルク糸と麻糸とを複合したスパンシルク・麻織物も高級な清涼感のある織物として知られている。しかしながら、一方では、スパンシルク織物やスパンシルク・麻織物は、高価であり、イージーケアー性にも問題がある。 The spun silk fabric is a fabric made of spun silk yarn (silk spun yarn), has an elegant and moderate gloss and swelling, and is widely recognized as a high-quality fabric because it has a soft and elegant dry feeling. Furthermore, a spun silk / hemp fabric, which is a composite of spun silk yarn and hemp yarn, is also known as a high-quality refreshing fabric. However, on the other hand, the spun silk fabric and the spun silk / linen fabric are expensive and have a problem in easy care properties.
スパンシルク織物やスパンシルク・麻織物におけるかかる欠点を改善し、スパンシルク織物やスパンシルク・麻織物におけるような特長を備えた織物を得るべく、従来より種々提案がなされているが、未だ満足のいくものは得られていない。例えば、ポリエステル系繊維フィラメント糸であって、単糸に長手方向に太細差を付与したシックアンドシン糸や仮撚加工等でスラブ外観を付与した加工糸を用いた織物も多種開発され、イージーケアー性に優れファッション性にも優れたものが上市されている。 Various proposals have been made so far in order to improve such disadvantages in spun silk fabric and spun silk / linen fabric, and to obtain a fabric having the same characteristics as in spun silk fabric, spun silk / linen fabric, but it is still satisfactory. Nothing is gained. For example, various types of woven fabrics using polyester fiber filament yarns that use thick and thin yarns with thick and thin differences in the longitudinal direction and processed yarns with a slab appearance by false twisting have been developed. Products with excellent care and fashion are on the market.
しかしながら、ポリエステル系繊維フィラメント糸を用いてなる織物では、ポリエステル系繊維フィラメント糸に由来する高ヤング率からくる硬い風合い、ワキシイな風合い、低吸湿性からくる蒸れ感や静電気発生、高屈折率からくる金属感のある光沢があり、鮮明な発色性に欠ける等の問題があり、また、風合いを改善するためアルカリ減量加工を施しても、ソフトさは得られるものの、ハリ感が損なわれたものとなる。また、皺加工では硬さからナチュラルな細かい皺表現が困難である。更に、織物の組織や形態によってはピリングが発生する。 However, in fabrics that use polyester fiber filament yarns, they come from a hard texture, waxy texture, low moisture absorption, and a feeling of stuffiness, static electricity, and a high refractive index derived from polyester fiber filament yarns. There are problems such as lack of vivid color with a metallic luster, and softness is obtained even if alkali weight reduction processing is performed to improve the texture, but the firmness is impaired. Become. In addition, it is difficult to express natural fine wrinkles due to hardness in the wrinkle processing. Furthermore, pilling occurs depending on the structure and form of the fabric.
上記のポリエステル系繊維フィラメント糸の有する問題を解決するためには、レーヨンフィラメント糸を用いることが考えられるが、通常のレーヨンフィラメント糸の使用では、水膨潤性による収縮が問題となり、洗濯収縮、形態安定性、湿潤堅牢度等の問題や保水性が高く乾燥速度が遅い、ベタツキ感が生じる等の問題がある。 In order to solve the problems of the above-mentioned polyester fiber filament yarn, it is conceivable to use rayon filament yarn. However, in the use of ordinary rayon filament yarn, shrinkage due to water swellability becomes a problem. There are problems such as stability and wet fastness, high water retention, slow drying speed, and sticky feeling.
本発明の目的は、優れた形態安定性を有し、蒸れ感や静電気の発生の少ないソフトで清涼感に優れ、適度なハリ感を有し、高級感のある光沢と鮮明な発色性を有する、快適な着用感と高級感に優れたスパンシルク織物調の毛羽を有する織物を提供することにある。 The object of the present invention is to have excellent shape stability, softness with less stuffiness and static electricity, excellent coolness, moderate elasticity, high-grade luster and clear color development An object of the present invention is to provide a woven fabric having spun silk fabric-like fluff excellent in a comfortable wearing feeling and a high-class feeling.
本発明の要旨は、水分率が８％以上のセルロース系繊維フィラメント糸と、水分率が８％未満で、熱可塑性を有するセルロース系繊維フィラメント糸と、ポリエステル系繊維フィラメント糸とからなる毛羽を有する流体攪乱加工糸にて、織物が構成されたことを特徴とするスパンシルク織物調の毛羽を有する織物、にある。 The gist of the present invention is a cellulosic fiber filament yarn having a moisture content of 8% or more, a fluff comprising a cellulose fiber filament yarn having a moisture content of less than 8% and thermoplasticity, and a polyester fiber filament yarn. A fabric having fluff of a spun silk fabric, characterized in that the fabric is constituted by a fluid disturbing processed yarn.
本発明によれば、セルロース系繊維フィラメント糸とポリエステル系繊維フィラメント糸とから、形態安定性に優れ、蒸れ感や静電気の発生の少ない、ソフトで清涼感に優れた、適度なハリ感を有し、高級感のある光沢と鮮明な発色性を有する、快適な着用感と高級感に優れたスパンシルク織物調の毛羽を有する織物を提供することができる。 According to the present invention, the cellulose-based fiber filament yarn and the polyester-based fiber filament yarn are excellent in form stability, have little stuffiness and static electricity, have a soft and refreshing feeling, and have a moderate elasticity. It is possible to provide a woven fabric having spun silk fabric-like fluff having a high-quality luster and clear color development and having a comfortable wearing feeling and a high-class feeling.
以下、本発明の実施の形態について、詳細に説明する。
本発明における水分率が８％以上のセルロース系繊維フィラメント糸は、セルロースを原料とした再生繊維のフィラメント糸であり、その製法や種類を特に限定するものではない。かかる水分率が８％以上のセルロース系繊維のフィラメント糸としては、例えばビスコースレーヨン、キュプラ等の再生繊維のフィラメント糸が挙げられ、特に水分率が１１％のビスコースレーヨンフィラメント糸、水分率が１１％のキュプラフィラメント糸が本発明において好ましく用いられる。
Hereinafter, embodiments of the present invention will be described in detail.
The cellulose fiber filament yarn having a water content of 8% or more in the present invention is a filament yarn of regenerated fiber made from cellulose as a raw material, and its production method and type are not particularly limited. Examples of the filament yarn of cellulosic fibers having a moisture content of 8% or more include filament yarns of regenerated fibers such as viscose rayon and cupra, and in particular, viscose rayon filament yarn having a moisture content of 11% and a moisture content of An 11% cupra filament yarn is preferably used in the present invention.
また、水分率が８％未満で、熱可塑性を有するセルロース系フィラメントとしては、前記の水分率が８％以上のセルロース系繊維フィラメント糸と同様、セルロースを原料とした半合成繊維のフィラメント糸であり、例えばセルロースジアセテート繊維フィラメント糸、セルローストリアセテート繊維フィラメント糸等のセルロースアセテート繊維フィラメント糸が挙げられ、単糸の断面形状、表面形状、艶、繊度等を特に限定するものではなく、得られる織物表現を考慮して任意に選定すればよい。 Further, the cellulose filament having a moisture content of less than 8% and having thermoplasticity is a filament yarn of semi-synthetic fiber made of cellulose as in the case of the cellulose fiber filament yarn having a moisture content of 8% or more. Examples include cellulose acetate fiber filament yarns such as cellulose diacetate fiber filament yarns and cellulose triacetate fiber filament yarns, and there is no particular limitation on the cross-sectional shape, surface shape, gloss, fineness, etc. of the single yarn, and the resulting textile representation It may be selected arbitrarily considering the above.
セルロースジアセテート繊維フィラメント糸は、その水分率が６．５％、またセルローストリアセテート繊維フィラメント糸は、その水分率が３．５％であり、これらのセルロースアセテート繊維フィラメント糸は、低屈折率による優れた発色性、高級感のある光沢、セルロース系繊維由来のソフトで清涼感に優れた風合い、さらには分散染料可染性、熱セット性等を有するとともに、その水分率から、適度な吸湿性と速乾性を有し、特に風合いや光沢の高級感の点から、セルローストリアセテート繊維フィラメント糸がより好ましく用いられる。 The cellulose diacetate fiber filament yarn has a moisture content of 6.5%, and the cellulose triacetate fiber filament yarn has a moisture content of 3.5%. These cellulose acetate fiber filament yarns are excellent due to their low refractive index. Color development, high-quality luster, softness derived from cellulosic fibers and a refreshing feel, disperse dyeability, heat setting, etc. Cellulose triacetate fiber filament yarn is more preferably used because it has quick drying properties, and particularly has a high feeling of texture and gloss.
さらに、本発明におけるポリエステル系繊維フィラメント糸としては、例えばポリエチレンテレフタレート繊維フィラメント糸、第三成分の共重合により改質、好ましくは分散染料易染性或いはカチオン染料可染性等に染色性を改質したエチレンテレフタレート単位主体のポリマーからなるポリエステル繊維フィラメント糸が挙げられる。 Furthermore, as the polyester fiber filament yarn in the present invention, for example, polyethylene terephthalate fiber filament yarn, modified by copolymerization of the third component, preferably dyeability is improved such as disperse dye ready dyeability or cationic dye dyeability Polyester fiber filament yarn made of a polymer mainly composed of ethylene terephthalate units.
染色性を改質する第三成分としては、例えば染色性が分散染料易染性であれば、第三成分としてイソフタル酸、アジピン酸等のジカルボン酸が、また染色性がカチオン染料可染性であれば、第三成分としてナトリウムスルホイソフタル酸等が挙げられる。またポリエステル系繊維フィラメント糸は、２種のポリマーからなるコンジュゲート構造の繊維フィラメント糸であってもよい。ポリエステル系繊維フィラメント糸の製法や種類を特に限定するものではなく、また、単糸の断面形状、表面形状、艶、繊度等を特に限定するものではない。 As the third component that modifies the dyeability, for example, if the dyeability is easy to disperse dye, the third component is a dicarboxylic acid such as isophthalic acid or adipic acid, and the dyeability is cationic dyeable. If present, sodium sulfoisophthalic acid or the like may be mentioned as the third component. The polyester fiber filament yarn may be a fiber filament yarn having a conjugate structure composed of two kinds of polymers. The production method and type of the polyester fiber filament yarn are not particularly limited, and the cross-sectional shape, surface shape, gloss, fineness and the like of the single yarn are not particularly limited.
本発明の織物は、水分率が８％以上のセルロース系繊維フィラメント糸、水分率が８％未満で、熱可塑性を有するセルロース系繊維フィラメント糸及びポリエステル系繊維フィラメント糸とからなる流体攪乱加工糸にて構成される。本発明における流体攪乱加工糸は、水分率が８％以上のセルロース系繊維フィラメント糸、水分率が８％未満で、熱可塑性を有するセルロース系繊維フィラメント糸及びポリエステル系繊維フィラメント糸を流体攪乱加工によって得られた毛羽を有する流体攪乱加工糸である。 The woven fabric of the present invention is a cellulose fiber filament yarn having a moisture content of 8% or more, a fluid disturbing processed yarn comprising a cellulose fiber filament yarn and a polyester fiber filament yarn having a moisture content of less than 8% and having thermoplasticity. Configured. The fluid-disturbed yarn in the present invention is a cellulosic fiber filament yarn having a moisture content of 8% or more, a cellulosic fiber filament yarn having a moisture content of less than 8%, and a polyester fiber filament yarn by fluid disturbance processing. It is the fluid disturbance processing thread | yarn which has the obtained fluff.
本発明における流体攪乱加工糸は、オーバーフィードされた水分率が８％以上のセルロース系繊維フィラメント糸Ａを芯糸とし、水分率が８％未満で熱可塑性を有するセルロース系繊維フィラメント糸Ｂとポリエステル系繊維フィラメント糸Ｃとをそれぞれ鞘糸として用い、セルロース系繊維フィラメント糸Ｂ及びポリエステル系繊維フィラメント糸Ｃのオーバーフィード率がセルロース系繊維フィラメント糸Ａのオーバーフィード率よりも０〜１０％大きくなるようにして、同一の流体攪乱ノズルに供給し、流体攪乱加工を施す方法により得られる。この流体攪乱加工の際に、供給するセルロース系繊維フィラメント糸Ｂの繊維強度が低いことから、セルロース系繊維フィラメント糸Ｂの一部が流体攪乱加工されることで優先的に毛羽が形成され、適度な毛羽のあるスラブ形成のない流体攪乱加工糸が得られる。 The fluid-disturbed processed yarn in the present invention has a cellulosic fiber filament yarn A having an overfeed moisture content of 8% or more as a core yarn, a cellulose fiber filament yarn B having a moisture content of less than 8% and thermoplasticity, and polyester. The fiber filament yarn C is used as a sheath yarn, and the overfeed rate of the cellulosic fiber filament yarn B and the polyester fiber filament yarn C is 0 to 10% larger than the overfeed rate of the cellulose fiber filament yarn A. Thus, it is obtained by supplying the same fluid disturbance nozzle and applying fluid disturbance processing. Since the fiber strength of the cellulosic fiber filament yarn B to be supplied is low at the time of the fluid disturbance processing, fluff is preferentially formed by subjecting a part of the cellulosic fiber filament yarn B to fluid disturbance processing. A fluid-disturbed yarn without fluffing slab formation is obtained.
流体攪乱加工糸における毛羽の程度は、セルロース系繊維フィラメント糸Ｂの単糸繊度、混率、流体攪乱加工時のオーバーフィード率、エアー圧等により決せられるが、本発明における流体攪乱加工糸を得る際のオーバーフィード率及びエアー圧は、本発明の目的とする織物を得るためには、水分率が８％以上のセルロース系繊維フィラメント糸Ａのオーバーフィード率が２〜８％、エアー圧が０．２５〜０．４０ＭＰａに設定することが好ましい。 The degree of fluff in the fluid-disturbed processed yarn is determined by the single yarn fineness, mixing ratio, overfeed rate during fluid disturbing processing, air pressure, etc. of the cellulosic fiber filament yarn B, but the fluid-disturbed processed yarn in the present invention is obtained. In order to obtain the desired woven fabric of the present invention, the overfeed rate and the air pressure of the cellulosic fiber filament yarn A having a moisture content of 8% or more are 2 to 8% and the air pressure is 0. It is preferable to set to 25 to 0.40 MPa.
本発明における流体攪乱加工糸は、本発明の目的とする織物を得るためには、好ましくは、水分率が８％以上のセルロース系繊維フィラメント糸３５〜５５％、水分率が８％未満で、熱可塑性を有するセルロース系繊維フィラメント糸３５〜５５％、ポリエステル系繊維フィラメント糸１０〜３０％の混率で構成されることが好ましい。かかる混率であるときには、構成の各フィラメント糸の特長が発揮され、紡績糸の欠点もなく、またピリングの発生も生じ難いものとなる。 In order to obtain the woven fabric targeted by the present invention, the fluid-disturbed processed yarn in the present invention is preferably a cellulose fiber filament yarn having a moisture content of 8% or more, 35 to 55%, and a moisture content of less than 8%. It is preferably composed of a blend ratio of 35 to 55% cellulose fiber filament yarn having thermoplasticity and 10 to 30% polyester fiber filament yarn. When the mixing ratio is such, the features of each filament yarn of the constitution are exhibited, and there is no defect of the spun yarn, and pilling hardly occurs.
すなわち、本発明におけるタスラン加工糸は、織物としたときに、水分率が８％以上のセルロース系繊維フィラメント糸の有する吸湿性、高級感のある光沢、直接染料や反応染料等に対する可染性、良好な発色性、清涼感のある風合い等の特徴が発揮でき、また水分率が８％未満で熱可塑性を有するセルロース系繊維フィラメント糸により洗濯収縮の問題がなく、また、水分率が８％以上のセルロース系繊維フィラメント糸との水膨潤による収縮差により空隙が生じ、膨らみ感が増す効果も得られ、また、熱可塑性があるため熱セット性が有り形態安定性も得られる。 That is, when the taslan yarn in the present invention is made into a woven fabric, the hygroscopic property of a cellulose fiber filament yarn having a moisture content of 8% or more, high gloss, dyeability to direct dyes or reactive dyes, Features such as good color developability, refreshing texture and the like, and there is no problem of washing shrinkage due to the cellulosic fiber filament yarn having a moisture content of less than 8%, and having a moisture content of 8% or more A void is generated due to a difference in shrinkage due to water swelling with the cellulose-based fiber filament yarn, and an effect of increasing the feeling of swelling is obtained. Moreover, since it has thermoplasticity, it has heat setting properties and shape stability.
特に本発明においては、流体攪乱加工糸は、流体攪乱加工糸を構成する各繊維フィラメント糸の前記の特長に加え、毛羽を有することにより、織物としたときに、流体攪乱加工糸の毛羽が織物表面に顕れ、顕れた毛羽がスパンシルク織物調の織物外観を呈するものである。 In particular, in the present invention, the fluid disturbing yarn has a fluff in addition to the above-described features of each fiber filament yarn constituting the fluid disturbing yarn, and when the fluff is formed into a woven fabric, the fluff of the fluid disturbing yarn is a woven fabric. The fluffs that appear on the surface show the appearance of a spun silk fabric.
さらに、本発明における流体攪乱加工糸は、織物としたときに、ポリエステル系繊維フィラメント糸による織物の強度補強、形態安定性に寄与するだけでなく、ポリエステル系繊維フィラメント糸が潜在型或いは顕在型の捲縮糸であるときには織物にストレッチ性やハリコシ、膨らみ感を与える。 Furthermore, when the fluid-disturbed processed yarn in the present invention is made into a woven fabric, it not only contributes to the strength reinforcement and shape stability of the woven fabric by the polyester-based fiber filament yarn, but the polyester-based fiber filament yarn is a latent type or a manifest type. When it is a crimped yarn, it gives stretch, elasticity and swelling to the fabric.
本発明の織物は、例えばツイル組織、ブッチャー組織等に任意の製織方式により製織されることにより得られるが、その組織や密度、目付け等は特に限定されるものではなく得ようとする織物表現を考慮して任意に選定すればよい。また本発明の織物は、本発明の効果が得られるものであれば、本発明の流体攪乱加工糸を追撚、諸撚、或いは他のフィラメント糸との合撚等を施して製織して得ることも可能であり、また他のフィラメント糸との交織や配列等もでき、他のフィラメント糸を混用することを制約するものではない。本発明の織物は、水分率が８％以上のセルロース系繊維フィラメント糸に基づくスパンシルク織物調の毛羽を有するという効果を得るためには、織物における流体攪乱加工糸の含有率は４０重量％以上であることが好ましい。 The fabric of the present invention can be obtained by weaving, for example, in a twill structure, butcher structure or the like by an arbitrary weaving method, but the structure, density, basis weight, etc. are not particularly limited, and the fabric expression to be obtained is expressed. It may be arbitrarily selected in consideration. In addition, the woven fabric of the present invention can be obtained by weaving the fluid-disturbed yarn of the present invention by subjecting it to additional twisting, various twists, or twisting with other filament yarns, etc. It is also possible to interweave or arrange with other filament yarns, and there is no restriction on mixing other filament yarns. In order to obtain the effect that the fabric of the present invention has a spun silk fabric-like fluff based on a cellulosic fiber filament yarn having a moisture content of 8% or more, the content of the fluid disturbing yarn in the fabric is 40% by weight or more. It is preferable that
本発明の織物における流体攪乱加工糸は、直接染料、分散染料、カチオン染料等によっての染め分けが可能であり、流体攪乱加工糸が２色以上に染め分けられた異染性外観を有する加工糸であることは織物に多色ミックス効果を得るうえで好ましいことである。また、流体攪乱加工により構成のフィラメント糸が互いにそれぞれ複雑に絡み合い交錯しているので、それらのフィラメント糸を異色或いは濃淡に染色することにより、よりナチュラルな異染性外観が表現できる。流体攪乱加工糸の２色以上の染め分けは、織物の形態で行ってもよいし、糸の形態で行ってもよく、また染め分けるための染色も同浴或いは別浴にて、一段若しくは多段にて行うことができ、その染色条件には特に制限はない。 The fluid disturbing yarn in the woven fabric of the present invention can be dyed by direct dyes, disperse dyes, cationic dyes and the like, and is a processed yarn having a different dyeing appearance in which the fluid disturbing yarn is dyed in two or more colors. This is preferable in obtaining a multicolor mix effect on the fabric. Further, since the filament yarns constituted by fluid disturbance processing are intricately entangled and interlaced with each other, a more natural metachromatic appearance can be expressed by dyeing these filament yarns in different colors or shades. The dyeing of two or more colors of the fluid-disturbed processed yarn may be carried out in the form of a woven fabric or in the form of a yarn, and the dyeing for dyeing may be carried out in one or more stages in the same bath or in a separate bath. There are no particular restrictions on the staining conditions.
以下、本発明を実施例により具体的に説明する。なお、本発明及び実施例中での水分率（Ｒ）の測定は、試料約２０ｇを採り、その標準状態の質量及び絶乾質量を量り、次の式によって算出し、２回の平均値をＪＩＳ Ｚ８４０１によって、小数点以下１桁にして得た。
Ｒ（％）＝［（ｍ−ｍ’）／ｍ’］×１００
ｍ ：試料の標準状態の質量（ｇ）
ｍ’：試料の絶乾質量（ｇ）
なお、標準状態の質量は、予備乾燥（試料を相対湿度１０〜２５％、温度５０℃を超えない環境で恒量にすること）した後、標準状態（温度２０±２℃、相対湿度６５±４％）の試験室に放置し、恒量になった状態の質量である。また、絶乾質量は、試料を温度１０５±２℃の熱風乾燥機中に放置して恒量になった状態の質量である。
また、実施例中での風合い、発色性の評価は、ハンドリング、目視に拠った。
Hereinafter, the present invention will be specifically described by way of examples. In addition, the measurement of the moisture content (R) in this invention and an Example takes about 20g of samples, measures the mass and the absolute dry mass of the standard state, calculates with the following formula | equation, and averages twice Obtained by JIS Z8401 with one decimal place.
R (%) = [(m−m ′) / m ′] × 100
m: Standard state mass of the sample (g)
m ′: absolute dry mass of the sample (g)
The mass in the standard state is pre-dried (the sample is kept constant in an environment where the relative humidity is 10 to 25% and the temperature does not exceed 50 ° C.), and then the standard state (temperature 20 ± 2 ° C., relative humidity 65 ± 4). %) In the test room and become a constant weight. The absolutely dry mass is a mass in a state where the sample is left in a hot air dryer at a temperature of 105 ± 2 ° C. and becomes a constant weight.
In addition, the evaluation of texture and color developability in the examples was based on handling and visual observation.
（実施例１）
セルローストリアセテート繊維フィラメント糸（三菱レイヨン社製、ブライト１６７ｄｔｅｘ／４０フィラメント（ｆ）、単糸菊型断面、水分率３．５％）２本と、キュプラフィラメント糸（旭化成せんい社製、ブライト１６７ｄｔｅｘ／７０ｆ、単糸丸断面、水分率１１％）２本と、カチオン染料可染性ポリエステル繊維フィラメント糸（三菱レイヨン社製、セミダル１６７ｄｔｅｘ／４８ｆ、単糸丸断面）１本とを用いて、セルローストリアセテート繊維フィラメント糸のオーバーフィード（ＯＦ）率１２％、キュプラフィラメント糸のＯＦ率６％、カチオン染料可染性ポリエステル繊維フィラメント糸のＯＦ率１２％で、流体攪乱ノズルに供給し、エアー圧０．３６ＭＰａの条件下で、流体攪乱加工を施し、スラブ形成のない流体攪乱加工糸を作成した。得られた流体攪乱加工糸は、セルローストリアセテート繊維フィラメント糸の混率が４１％、キュプラフィラメント糸の混率が３９％、カチオン染料可染性ポリエステル繊維フィラメント糸の混率が２０％であり、繊度が８９０ｄｔｅｘで、適度な毛羽を有するものであった。この流体攪乱加工糸を経糸及び緯糸に用い、２／２のツイル組織に配列して織物を製織した。
Example 1
Cellulose triacetate fiber filament yarn (Mitsubishi Rayon, Bright 167 dtex / 40 filament (f), single yarn chrysanthemum section, moisture content 3.5%) and cupra filament yarn (Asahi Kasei Fibers, Bright 167 dtex / 70f) , Cellulose triacetate fiber using two single yarn round cross section, moisture content 11%) and one cationic dye dyeable polyester fiber filament yarn (Mitsubishi Rayon, semi-dal 167 dtex / 48f, single yarn round cross section) Filament yarn overfeed (OF) rate of 12%, cupra filament yarn OF rate of 6%, cationic dye dyeable polyester fiber filament yarn with OF rate of 12%, supplied to the fluid disturbance nozzle, air pressure of 0.36MPa Under the conditions, fluid disturbance processing without slab formation It created the Engineering yarn. The obtained fluid-disturbed yarn has a mixing ratio of cellulose triacetate fiber filament yarn of 41%, a mixing ratio of cupra filament yarn of 39%, a mixing ratio of cationic dyeable polyester fiber filament yarn of 20%, and a fineness of 890 dtex. It had moderate fluff. This fluid disturbed yarn was used as warp and weft to arrange a 2/2 twill structure to weave the fabric.
この生機に常法により精練、染色仕上げを施し、セルローストリアセテート繊維フィラメント糸は分散染料にてベージュ色に、キュプラフィラメント糸は直接染料にて赤色に、さらにカチオン可染タイプのポリエステル繊維フィラメント糸はカチオン染料にて茶色にそれぞれ染色し、経糸密度４６本／吋、緯糸密度３７本／吋に仕上げた。得られた織物は、風合いがソフトで膨らみ感があり、適度なハリコシ感とセルロース系繊維由来の爽やかな心地のよいものであった。また、この織物はスパンシルク織物調の高級感に富んだ優雅な光沢と深みのある発色性が得られ、ナチュラルな異染性外観を有する多色ミックス織物であり、また、適度な毛羽を有しており、本格的なスパンシルク調の織物であった。 This raw machine is scoured and dyed and finished in the usual way, cellulose triacetate fiber filament yarn is beige with disperse dye, cupra filament yarn is red with direct dye, and cation dyeable polyester fiber filament yarn is cationic. Each was dyed brown with a dye, and finished to a warp density of 46 yarns / 吋 and a weft density of 37 yarns / 吋. The obtained woven fabric had a soft texture and a feeling of swelling, and had an appropriate harshness and a refreshing and comfortable feeling derived from cellulosic fibers. In addition, this fabric is a multi-colored mixed fabric with a natural color-dye appearance, which has an elegant luster and deep color development with a spun silk fabric-like luxury, and has moderate fluff. It was an authentic spun silk fabric.
（実施例２）
セルローストリアセテート繊維フィラメント糸（三菱レイヨン社製、ブライト１１０ｄｔｅｘ／２６ｆ、単糸菊型断面、水分率３．５％）と、キュプラフィラメント糸（旭化成せんい社製、ブライト８４ｄｔｅｘ／４５ｆ、単糸丸断面、水分率１１％）と、カチオン染料可染性ポリエステル繊維フィラメント糸（三菱レイヨン社製、セミダル３３ｄｔｅｘ／１２ｆ、潜在捲縮型コンジュゲート構造糸、単糸丸断面）とを用いて、セルローストリアセテート繊維フィラメント糸のＯＦ率５％、キュプラフィラメント糸のＯＦ率３％、カチオン染料可染性ポリエステル繊維フィラメント糸のＯＦ率５％で、流体攪乱ノズルに供給し、エアー圧０．３２ＭＰａの条件下で、流体攪乱加工を施し、セルローストリアセテート繊維フィラメント糸の混率が４９％、キュプラフィラメント糸の混率が３７％、カチオン染料可染性ポリエステル繊維フィラメント糸の混率が１４％であり、繊度が２３８ｄｔｅｘで、適度な毛羽のある、スラブ形成のない流体攪乱加工糸を作成した。別に、セルローストリアセテート繊維フィラメント糸（三菱レイヨン社製、ブライト１１０ｄｔｅｘ／２６ｆ、単糸菊型断面、水分率３．５％）にポリエチレンテレフタレート繊維モノフィラメント糸（ユニチカファイバー社製、セミダル１７ｄｔｅｘ）２本を用いてカバーリングしダブルカバーリング糸を作成した。
(Example 2)
Cellulose triacetate fiber filament yarn (Mitsubishi Rayon Co., Ltd. Bright 110 dtex / 26f, single yarn chrysanthemum cross section, moisture content 3.5%) and cupra filament yarn (Asahi Kasei Fibers Co., Ltd. Bright 84 dtex / 45f, single yarn round cross section, 11% water content) and polyester dyeable polyester fiber filament yarn (manufactured by Mitsubishi Rayon Co., Ltd., semi-dal 33dtex / 12f, latently crimped conjugate structure yarn, single yarn round section), cellulose triacetate fiber filament When the OF ratio of the yarn is 5%, the OF ratio of the cupra filament yarn is 3%, and the OF ratio of the cationic dyeable polyester fiber filament yarn is 5%, the fluid is supplied to the fluid disturbance nozzle, Mixing ratio of cellulose triacetate fiber filament yarn after disturbance processing 49%, cupra filament yarn mixing ratio of 37%, cationic dye dyeable polyester fiber filament yarn mixing ratio of 14%, fineness is 238dtex, moderate fluff and non-slab forming fluid disturbed yarn did. Separately, two cellulose triacetate fiber filament yarns (manufactured by Mitsubishi Rayon Co., Ltd., Bright 110 dtex / 26f, single yarn chrysanthemum section, moisture content 3.5%) and two polyethylene terephthalate fiber monofilament yarns (manufactured by Unitika Fiber Co., Ltd., semi-dull 17 dtex) are used. And double-covering yarn was created.
この流体攪乱加工糸とダブルカバーリング糸を、ブッチャー組織に経糸、緯糸としてそれぞれ配列して織物を製織した。この生機における流体攪乱加工糸の含有率は８０％であった。この生機に常法により精練、染色仕上げを施し、セルローストリアセテート繊維フィラメント糸及びポリエチレンテレフタレート繊維モノフィラメント糸は分散染料にてベージュ色に、キュプラフィラメント糸は直接染料にて赤色に、さらにカチオン染料可染性ポリエステル繊維フィラメント糸はカチオン染料にて茶色にそれぞれ染色し、経糸密度１０４本／吋、緯糸密度８２本／吋に仕上げた。得られた織物は、風合いがソフトで膨らみ感があり、適度なハリコシ感と反発感があり、セルロース系繊維由来の爽やかな心地のよいものであった。また、得られた織物は、スパンシルク織物調の高級感に富んだ優雅な光沢と深みのある発色性が得られ、ナチュラルな異染性外観を有する多色ミックス織物であり、また、適度な毛羽を有しており本格的なスパンシルク調の織物であった。 The fluid-disturbed processed yarn and the double covering yarn were arranged as a warp and a weft in a butcher structure, and a woven fabric was woven. The content rate of the fluid disturbed yarn in this raw machine was 80%. This raw machine is scoured and dyed by conventional methods, cellulose triacetate fiber filament yarn and polyethylene terephthalate fiber monofilament yarn are beige with disperse dye, cupra filament yarn is red with direct dye, and further dyeable with cationic dye The polyester fiber filament yarn was dyed brown with a cationic dye, and finished to a warp density of 104 yarns / 吋 and a weft density of 82 yarns / 吋. The obtained woven fabric had a soft texture and a feeling of swelling, had an appropriate harshness and repulsion, and was refreshing and comfortable derived from cellulosic fibers. In addition, the obtained woven fabric is a multi-colored mixed woven fabric having a natural color-dyeing appearance with an elegant luster and deep color development rich in spun silk fabric-like luxury. It was a full-scale spun silk-like fabric with fluff.
（実施例３）
セルロースト
リアセテート繊維フィラメント糸（三菱レイヨン社製、ブライト１３５ｄｔｅｘ／３３ｆ、単糸菊型断面、水分率３．５％）と、キュプラフィラメント糸（旭化成せんい社製、ブライト１３５ｄｔｅｘ／７０ｆ、単糸丸断面、水分率１１％）と、カチオン染料可染性ポリエステル繊維フィラメント糸（三菱レイヨン社製、セミダル５６ｄｔｅｘ／１２ｆ、潜在捲縮型コンジュゲート構造糸、単糸丸断面）とを用いて、セルローストリアセテート繊維フィラメント糸のＯＦ率６％、キュプラフィラメント糸のＯＦ率６％、カチオン染料可染性ポリエステル繊維フィラメント糸のＯＦ率６％で、流体攪乱ノズルに供給し、エアー圧０．３０ＭＰａの条件下で、流体攪乱加工を施し、セルローストリアセテート繊維フィラメント糸の混率が４１％、キュプラフィラメント糸の混率が４１％、カチオン染料可染性ポリエステル繊維フィラメント糸の混率が１８％であり、繊度が３４６ｄｔｅｘで、適度な毛羽のある、スラブ形成のない流体攪乱加工糸を作成した。さらに、実施例２で用いたのと同じダブルカバーリング糸を用い、経糸にはダブルカバーリング糸、緯糸にはタスラン加工糸４本とダブルカバーリング糸２本を用い、ツイル組織に配列して織物を製織した。
Example 3
Cellulose triacetate fiber filament yarn (Mitsubishi Rayon, Bright 135 dtex / 33f, single yarn chrysanthemum cross section, moisture content 3.5%) and cupra filament yarn (Asahi Kasei Fibers, Bright 135 dtex / 70f, single yarn round cross section, A cellulose triacetate fiber filament using a polyester dyeable dyeable polyester fiber filament yarn (manufactured by Mitsubishi Rayon Co., Ltd., semi-dal 56 dtex / 12f, latently crimped conjugate structure yarn, single yarn round section). With a OF ratio of 6%, an OF ratio of 6% for cupra filament yarn and an OF ratio of 6% for cationic dye dyeable polyester fiber filament yarn, the fluid is supplied to a fluid disturbance nozzle and fluid is supplied under conditions of air pressure of 0.30 MPa. Disturbed and mixed with cellulose triacetate fiber filament yarn Is 41%, the blending ratio of cupra filament yarn is 41%, the blending ratio of cationic dyeable polyester fiber filament yarn is 18%, the fineness is 346 dtex, moderate fluff, and no slab formation. Created. Furthermore, the same double covering yarn as used in Example 2 was used, the double covering yarn was used for the warp, the four taslan yarns and the two double covering yarns were used for the weft, and they were arranged in a twill structure. Woven fabric.
この生機に常法により精練、染色仕上げを施し、セルローストリアセテート繊維フィラメント糸及びポリエチレンテレフタレート繊維モノフィラメント糸は分散染料にてベージュ色に、キュプラフィラメント糸は直接染料にて赤色に、さらにカチオン染料可染性ポリエステル繊維フィラメント糸はカチオン染料にて茶色にそれぞれ染色し、経糸密度１０１本／吋、緯糸密度７０本／吋に仕上げた。得られた織物は、風合いがソフトで膨らみ感があり、適度なハリコシ感とシャリ感を有し、セルロース系繊維由来の爽やかな心地のよいものであった。また、得られた織物は、スパンシルク織物調の高級感に富んだ優雅な光沢と深みのある発色性が得られ、ナチュラルな異染性外観を有する多色ミックス織物であり、また適度な毛羽を有しており、本格的なスパンシルク調の織物であった。 This raw machine is scoured and dyed by conventional methods, cellulose triacetate fiber filament yarn and polyethylene terephthalate fiber monofilament yarn are beige with disperse dye, cupra filament yarn is red with direct dye, and further dyeable with cationic dye The polyester fiber filament yarn was dyed brown with a cationic dye, and finished to a warp density of 101 yarns / 吋 and a weft density of 70 yarns / 吋. The obtained woven fabric had a soft texture and a feeling of swelling, had an appropriate harshness and sharpness, and was refreshing and comfortable derived from cellulosic fibers. The resulting woven fabric is a multi-colored mixed woven fabric with a natural, metachromatic appearance, which has an elegant luster and deep coloration, which is rich in the quality of a spun silk fabric, and has moderate fluff. It was a full-scale spun silk-like woven fabric.
（比較例１）
実施例１において、セルローストリアセテート繊維フィラメント糸及びキュプラフィラメント糸をポリエチレンテレフタレートフィラメント糸（三菱レイヨン社製、セミダル１６７ｄｔｅｘ／９６ｆ、単糸丸断面）に代えた以外は、実施例１と同様にしてスラブ形成のない流体攪乱加工糸を作成した。得られた流体攪乱加工糸を経糸と緯糸に用いて実施例１と同じツイル組織の織物を製織した。この生機に常法により精練、染色仕上げを施し、ポリエチレンテレフタレート繊維フィラメント糸は分散染料にてベージュ色に、カチオン染料可染性ポリエステル繊維フィラメント糸はカチオン染料にて茶色にそれぞれ染色し、経糸密度４６本／吋、緯糸密度３７本／吋に仕上げた。得られた織物は、風合いがワキシーで硬く、蒸れ感があり爽やかさに欠けたものであった。また、この織物は、異染性はあるものの多色ミックス効果は得られず、また高級感のない金属光沢があり、スパンシルク織物調の織物と言えるものではなかった。
(Comparative Example 1)
A slab was formed in the same manner as in Example 1, except that the cellulose triacetate fiber filament yarn and the cupra filament yarn were replaced with polyethylene terephthalate filament yarn (Mitsubishi Rayon Co., Ltd., Semidal 167 dtex / 96f, single yarn round cross section). A fluid-disturbed processed yarn with no friction was created. A woven fabric having the same twill structure as in Example 1 was woven using the obtained fluid-disturbed processed yarn as a warp and a weft. This raw machine is scoured and dyed and finished in the usual way. Polyethylene terephthalate fiber filament yarn is dyed beige with disperse dye, and cationic dye-dyeable polyester fiber filament yarn is dyed brown with cationic dye. Finished to a book / 本 and a weft density of 37 / 吋. The resulting woven fabric was waxy and hard, stuffy and lacked freshness. In addition, this fabric has a multicolor mixing effect although it has a different dyeing property, and has a metallic luster without a high-class feeling, and was not a spun silk fabric-like fabric.
（比較例２）
実施例１において、セルローストリアセテート繊維フィラメント糸をキュプラフィラメント糸（旭化成せんい社製、ブライト１６７ｄｔｅｘ／７０ｆ、単糸丸断面、水分率１１％）２本に代えた以外は、実施例１と同様にしてスラブ形成のない流体攪乱加工糸を作成した。この流体攪乱加工糸は、キュプラフィラメント糸の混率が８０％、ポリエステル繊維フィラメント糸の混率が２０％であり、繊度は８９０ｄｔｅｘであった。得られた流体攪乱加工糸を経糸と緯糸に用いて実施例１と同じツイル組織の織物を製織した。この生機に常法により精練、染色仕上げを施し、キュプラフィラメント糸は直接染料にてベージュ色に、カチオン染料可染性ポリエステル繊維フィラメント糸はカチオン染料にて茶色にそれぞれ染色し、経糸密度４６本／吋、緯糸密度３７本／吋に仕上げた。得られた織物は、風合いがソフトではあるが、ベタツキ感があり、また洗濯時による収縮が発生し形態安定性に問題があった。またこの織物は、異染性はあるものの多色ミックス効果は得られず、スパンシルク織物調の織物と言えるものではなかった。
(Comparative Example 2)
In Example 1, the cellulose triacetate fiber filament yarn was changed to two cupra filament yarns (manufactured by Asahi Kasei Fibers Co., Ltd., Bright 167 dtex / 70f, single yarn round cross section, moisture content 11%), and the same as in Example 1. Fluid disturbed yarn without slab formation was made. The fluid disturbed yarn had a cupra filament yarn mixing ratio of 80%, a polyester fiber filament yarn mixing ratio of 20%, and a fineness of 890 dtex. A woven fabric having the same twill structure as in Example 1 was woven using the obtained fluid-disturbed processed yarn as a warp and a weft. This raw machine is scoured and dyed and finished in the usual way. The cupra filament yarn is dyed in beige with a direct dye, and the cationic dyeable polyester fiber filament yarn is dyed in brown with a cationic dye. Finished to a cocoon and a weft density of 37 / 吋. The obtained woven fabric had a soft texture, but had a sticky feeling, and contraction occurred during washing, resulting in a problem in form stability. Further, although this woven fabric has a different dyeing property, a multicolor mixing effect was not obtained, and it could not be said that it was a spun silk fabric-like woven fabric.
本発明の織物は、スパンシルク織物調の毛羽を有する織物であり、スパンシルク織物の有すると同様な上品な控えめの光沢と膨らみ感があり、ソフトでドライ感を有し、またスパンシルク・麻織物の有すると同様な高級な清涼感のある織物でありながら、その織物からなる商品はイージーケアー性を有し、また安価に得ることを可能にするもので、衣料用素材として有用なるものである。 The woven fabric of the present invention is a woven fabric having a spun silk fabric-like fluff, and has an elegant, discreet luster and swelling, similar to that of a spun silk fabric, soft and dry, Although it is a high-quality, refreshing woven fabric similar to that of a woven fabric, the product made of the woven fabric has easy care properties and can be obtained at a low cost, and is useful as a clothing material. is there.
Claims (3)