CN106048816A - Blended yarn and manufacturing method thereof - Google Patents
Blended yarn and manufacturing method thereof Download PDFInfo
- Publication number
- CN106048816A CN106048816A CN201610680737.1A CN201610680737A CN106048816A CN 106048816 A CN106048816 A CN 106048816A CN 201610680737 A CN201610680737 A CN 201610680737A CN 106048816 A CN106048816 A CN 106048816A
- Authority
- CN
- China
- Prior art keywords
- yarn
- twisted filament
- twister
- carried out
- yarn group
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a blended yarn and a manufacturing method thereof. The blended yarn is manufactured from white steam filature, modified polyester fibers and regenerated cellulose fibers. Designed by integrating natural comfort with environmental protection, the blended yarn has the advantages of lightness, soft and smooth hand feel, comfort, attractiveness, moisture absorption, breathability, less proneness to damp, avoidance of static electricity, pilling and fluffing, no dyeing defect and color difference, excellent elasticity and resilience and no harm to human bodies. The white steam filature, the modified polyester fibers and the regenerated cellulose fibers serve as raw materials in the manufacturing method of the blended yarn and enable the blended yarn to have the advantages of more compactness and capabilities of achieving setting without shrinkage, avoiding pilling and fluffing and keeping ready-made garments free from skewing pieces after being subjected to doubling, throwing and heating in a steam box.
Description
Technical field
The present invention relates to field of textile industry, more particularly, to a kind of blended ratio and manufacture method.
Background technology
Along with the progress of society, the living standard of people improves constantly, and people not only stop for the pursuit of textile
Staying artistry and ornamental aspect, comfortableness, functional, wholesomeness, protective, health and aesthetic property for dress are wanted
Ask more and more higher.
White Steam Filature Yarns i.e. raw silk, is commonly called as real silk, is described as " fiber queen ", is subject to people through the ages with the glamour of its uniqueness
Favor.White Steam Filature Yarns belongs to protein fibre, containing 18 kinds of aminoacid useful to human body in fibroin, skin can be helped to maintain
The metabolism of surface adipose membrane, therefore skin can be made to keep moist, smooth.Additionally, White Steam Filature Yarns itself is soft smooth, feel is rich
Full, strength and elongation is good, high resilience, and gloss is soft, and hygroscopicity is strong, to human body nonirritant, is senior textile material, but, existing
With the presence of the qualitative defect of White Steam Filature Yarns, mainly have joint, color and luster fault, pollute fault, arrange bad and fine hair.Its weaving
Fabric the most water-fastness, the most sun-resistant, the time worn and use is the shortest.Modified dacron, it is simply that make terylene formal structure
Change, can be made by production technology.Although common polyester fabric has higher intensity and elastic restoring force, hard
Jail is durable, wash and wear, and thermostability is strong, and water resistance is excellent, and the easily advantage such as cleaning.But it is the oldest that it is of long duration
Changing, frequent and skin friction is easily caused allergy, and dyeability is poor, and melt resistance is poor, and hygroscopicity is poor, and moisture content is low, poor air permeability,
Easily balling-up fluffing, easily stains.Modified dacron, by the method that terylene is carried out chemical modification and physical deformation, improves fiber
Hydroscopicity, strengthen antistatic and the performance of anti-contamination of fiber, improve the flame resistance energy of fiber, improve anti pilling
Ability, and improve dyeability.Although the improvement of this series performance substantially increases the range of application of modified dacron, but
It is still to cannot be avoided the poor air permeability of material own, the most aging, cause the defect of allergy.Regenerated celulose fibre is as " 21
The green fiber in century ", a kind of by the cellulose such as Caulis et Folium Oryzae, bark through dissolve after spinning form, mainly include Modal
(Modal) fiber, Tan Xier (Tencel) fiber, bamboo fibre, viscose chitin fibre and CUP.Due to subtracting of ploughing
Lacking and the exhaustion day by day of petroleum resources, natural fiber, the yield of synthetic fibers will more and more be restricted.Regenerated fiber
Cellulose fiber raw material is natural material, harmless, and can natural decomposition, environmental sound, belong to novel environment-friendlyfiber fiber, energy
Enough play that suppression antibacterial, deodorization absorption, moisture absorption be ventilative, heat accumulation thermal, effect of minimizing electrostatic, meanwhile, regenerated celulose fibre
Itself is soft, and color is beautiful, and toughness and wearability are strong, has the resilience of uniqueness, and stable uniform, and drapability is good.But by
In the fiber properties that it is intrinsic, the most fragile easily broken, the intensity of 30%-50%, elastic and rebound performance can be lost when hygrometric state
Poor, the easily damaged and deformation when washing.Additionally, regenerated celulose fibre also can the most significantly shrink, the easiest mould moth,
The same with other natural fibers, easily fluffing or balling-up.Further, since regenerated cellulose is relatively costly, so relative to it
His silk thread goods price is high.
Therefore, developing a kind of advantage that can have yarn the most of the same race concurrently, overcome again every kind of yarn self shortcoming, feel is soft
Soft smooth, Comfortable attractive, moisture absorption breathes freely, is difficult to make moist, do not play electrostatic, and not balling-up is fluffed, and colourless pattern is not good enough, elastic and return
Bullet excellent performance, light weight, harmless, and the theory of the comfortable of back to nature He environmental protection is dissolved into the weaving in the middle of design
Material, is also increasingly becoming the emphasis of research and development.
In view of this, the special proposition present invention.
Summary of the invention
It is an object of the present invention to provide a kind of blended ratio, described blended ratio is with White Steam Filature Yarns, modified dacron and regeneration
Cellulose fibre is raw material, has soft smooth, Comfortable attractive, and moisture absorption is breathed freely, and is difficult to make moist, does not play electrostatic, not balling-up
Fluffing, colourless pattern is not good enough, elastic and rebound performance excellence, and light weight is harmless, and by the comfortable of back to nature and ring
The theory protected is dissolved into design when medium advantage.
Further object is that the manufacture method that a kind of described blended ratio is provided, the method with White Steam Filature Yarns, change
Property terylene and regenerated celulose fibre be raw material, by silk thread the most of the same race being carried out and silk, twisted filament and heating etc. in steam box
Reason, makes yarn reach more to compact, shaping does not bounces back, controls the purpose of balling-up fluffing, ready-made clothes not inclined tab.
For reaching above-mentioned purpose, the present invention uses following technical proposals:
A kind of blended ratio, is that raw material is made by White Steam Filature Yarns, modified dacron and regenerated celulose fibre.
Being the blended ratio that raw material is made by three of the above yarn, have soft smooth, Comfortable attractive, moisture absorption is saturating
Gas, is difficult to make moist, and does not play electrostatic, and not balling-up is fluffed, and colourless pattern is not good enough, and elastic and rebound performance excellence, light weight, to human body
Harmless, and the theory of the comfortable of back to nature He environmental protection is dissolved into design when medium advantage.
Preferably, the single thread force 1200-1400CN/CM of described blended ratio, regain 11-13%, color fastness to washing 4-5
Level, washing shrinkage ± 2-± 3.
Preferably, the specification of described White Steam Filature Yarns is 20/22-30/33D, and the specification of described modified dacron is 30-70D, described
The specification of regenerated celulose fibre is 50-100D.
Preferably, the specification of described White Steam Filature Yarns is 20/22D, and the specification of described modified dacron is 50D, described regenerated fiber
The specification of cellulose fiber is 75D.
In the present invention, by adjusting further and optimizing various raw material specification, thus optimize the present invention further
The performance of blended ratio.
Further, present invention also offers the manufacture method of a kind of described blended ratio, the concrete steps of this manufacture method
As follows:
(1) by a White Steam Filature Yarns and modified dacron on doubling winder and silk, and the first yarn group is become, described first yarn group
It is two strands of yarns;
(2) described first yarn group is carried out twisted filament process by two-for-one twister, obtain the first yarn;
(3) described first yarn is placed in steam box heats;
(4) a root regeneration cellulose fibre is carried out twisted filament process by two-for-one twister, obtain the second yarn;
(5) described second yarn is placed in steam box heats;
(6) by described first yarn and described second yarn on doubling winder and silk, and the second yarn group is become, described second yarn
Group is two strands of yarns;
(7) described second yarn group is carried out twisted filament process by two-for-one twister, obtain the 3rd yarn;
(8) described 3rd yarn is placed in steam box heats.
Preferably, the weight of described first yarn group is 680-720g, and the weight of described second yarn group is 680-720g.
Preferably, the weight of described first yarn group is 700g, and the weight of described second yarn group is 700g.
In the present invention, yarn is rolled into a ball Weight control and is being best suitable for the weight of dyeing, contribute to later stage control color pattern poor.
Preferably, the twisted filament that described first yarn group is carried out by two-for-one twister is processed as Z twisted filament, twists 607 twists/m.
Preferably, described regenerated celulose fibre is processed as twisting 607 twists/m by the twisted filament that two-for-one twister is carried out.
Preferably, the twisted filament that described 3rd yarn group is carried out by two-for-one twister is processed as S twisted filament, twists 544 twists/m.
In the present invention, each raw yarn is carried out twisted filament process, yarn can be made when the External Force Acting being stretched, incline
Oblique fiber produces radial pressure to yam axis, thus strengthens the performance of raw yarn, makes yarn more compact, the intensity of yarn and resistance to
Frictional behaviour is significantly improved, and reduces balling-up fluffing and the situation of broken end, improves the fastness of silk fabrics, it is also possible to increases yarn
Elasticity, improve the wrinkle resistance of silk fabrics and permeability.Meanwhile, twisted filament processes and can also impart to yarn appearance with refractive power
Effect, obtained silk fabrics has the effects such as wrinkle, looped pile or knot.
In the present invention, the twisted filament that described first yarn group is carried out by two-for-one twister is processed as Z twisted filament, and described 3rd yarn group passes through
The twisted filament that two-for-one twister is carried out is processed as S twisted filament, and purpose essentially consists in control ready-made clothes not inclined tab.
Preferably, the time of described heating is no less than 50 minutes, and the temperature of described heating is 80-90 DEG C.
In the present invention, the purpose carrying out heating in steam box by described first yarn, the second yarn, the 3rd yarn is can
Make yarn sizing not bounce back, effectively control balling-up fluffing.
Blended ratio of the present invention may be used for fabric and fibre.Such as by for clothing materials, shawl, enclose
Towel, mat etc., available soft smooth, Comfortable attractive, moisture absorption is breathed freely, is difficult to make moist, and does not play electrostatic, and not balling-up is fluffed,
Colourless pattern is not good enough, elastic and rebound performance excellence, light weight, harmless goods.Furthermore it is possible to by of the present invention
Blended ratio is used for cloth and silk and a part for sewed product.
Beneficial effects of the present invention is as follows:
(1) blended ratio of the present invention, has soft smooth, Comfortable attractive, and moisture absorption is breathed freely, and is difficult to make moist, does not rises
Electrostatic, not balling-up fluffing, colourless pattern is not good enough, and elasticity and rebound performance are excellent, and light weight is harmless, and will return certainly
Right comfortable and environmental protection theory is dissolved into design when medium advantage.
(2) manufacture method of blended ratio of the present invention, is former with White Steam Filature Yarns, modified dacron and regenerated celulose fibre
Material, by silk thread the most of the same race is carried out and silk, twisted filament and in steam box heating etc. process, it is possible to make yarn have more compact, fixed
The advantage that type does not bounces back, controls balling-up fluffing, ready-made clothes not inclined tab.
Detailed description of the invention
In order to be illustrated more clearly that the present invention, below in conjunction with preferred embodiment, the present invention is described further.Ability
Field technique personnel should be appreciated that following specifically described content is illustrative and be not restrictive, and should not limit this with this
The protection domain of invention.Unreceipted actual conditions person in embodiment, the condition advised according to normal condition or manufacturer is carried out.Institute
With reagent or instrument unreceipted production firm person, being can be by the commercially available conventional products bought and obtain.Used by the present invention former
Material yarn, being can be by the commercially available above product of 3A level bought and obtain.
Embodiment 1
Selecting raw yarn according to following specification, the specification of White Steam Filature Yarns is 20/22D, and the specification of modified dacron is 50D, bamboo
The specification of fiber is 75D.Then, the blended ratio of the present embodiment is made according to following processing step:
(1) by the White Steam Filature Yarns of a 20/22D and the modified dacron of a 50D on doubling winder and silk, and the quality is become to be
The first yarn group of 700g, described first yarn group is two strands of yarns;
(2) described first yarn group is carried out Z-direction twisted filament process by two-for-one twister, twist 607 twists/m, obtain the first yarn;
(3) being placed in steam box by described first yarn and heat, the time of heating is no less than 50 minutes, the temperature of heating
For 80-90 DEG C;
(4) bamboo fibre of a 75D is carried out twisted filament process by two-for-one twister, twist 607 twists/m, obtain the second yarn;
(5) being placed in steam box by described second yarn and heat, the time of heating is no less than 50 minutes, the temperature of heating
For 80-90 DEG C;
(6) by described first yarn and described second yarn on doubling winder and silk, and the second yarn becoming quality to be 700g
Group, described second yarn group is two strands of yarns;
(7) by two-for-one twister, described second yarn group is carried out S to process to twisted filament, twist 544 twists/m, obtain the 3rd yarn;
(8) being placed in steam box by described 3rd yarn and heat, the time of heating is no less than 50 minutes, the temperature of heating
For 80-90 DEG C.
Embodiment 2
Selecting raw yarn according to following specification, the specification of White Steam Filature Yarns is 24/26D, and the specification of modified dacron is 30D, not
The specification of Dai Er (Modal) fiber is 50D.Then, the blended ratio of the present embodiment is made according to following processing step:
(1) by the White Steam Filature Yarns of a 24/26D and the modified dacron of a 30D on doubling winder and silk, and the quality is become to be
The first yarn group of 680g, described first yarn group is two strands of yarns;
(2) described first yarn group is carried out Z-direction twisted filament process by two-for-one twister, twist 607 twists/m, obtain the first yarn;
(3) being placed in steam box by described first yarn and heat, the time of heating is no less than 50 minutes, the temperature of heating
For 80-90 DEG C;
(4) Modal (Modal) fiber of a 50D is carried out twisted filament process by two-for-one twister, twist 607 twists/m,
To the second yarn;
(5) being placed in steam box by described second yarn and heat, the time of heating is no less than 50 minutes, the temperature of heating
For 80-90 DEG C;
(6) by described first yarn and described second yarn on doubling winder and silk, and the second yarn becoming quality to be 680g
Group, described second yarn group is two strands of yarns;
(7) by two-for-one twister, described second yarn group is carried out S to process to twisted filament, twist 544 twists/m, obtain the 3rd yarn;
(8) being placed in steam box by described 3rd yarn and heat, the time of heating is no less than 50 minutes, the temperature of heating
For 80-90 DEG C.
Embodiment 3
Selecting raw yarn according to following specification, the specification of White Steam Filature Yarns is 30/33D, and the specification of modified dacron is 70D, smooth
The specification of Xi Er (Tencel) fiber is 100D.Then, the blended ratio of the present embodiment is made according to following processing step:
(1) by the White Steam Filature Yarns of a 30/33D and the modified dacron of a 70D on doubling winder and silk, and the quality is become to be
The first yarn group of 720g, described first yarn group is two strands of yarns;
(2) described first yarn group is carried out Z-direction twisted filament process by two-for-one twister, twist 607 twists/m, obtain the first yarn;
(3) being placed in steam box by described first yarn and heat, the time of heating is no less than 50 minutes, the temperature of heating
For 80-90 DEG C;
(4) Tan Xier (Tencel) fiber of a 100D is carried out twisted filament process by two-for-one twister, twists 607 twists/m,
Obtain the second yarn;
(5) being placed in steam box by described second yarn and heat, the time of heating is no less than 50 minutes, the temperature of heating
For 80-90 DEG C;
(6) by described first yarn and described second yarn on doubling winder and silk, and the second yarn becoming quality to be 720g
Group, described second yarn group is two strands of yarns;
(7) by two-for-one twister, described second yarn group is carried out S to process to twisted filament, twist 544 twists/m, obtain the 3rd yarn;
(8) being placed in steam box by described 3rd yarn and heat, the time of heating is no less than 50 minutes, the temperature of heating
For 80-90 DEG C.
Embodiment 4
Selecting raw yarn according to following specification, the specification of White Steam Filature Yarns is 27/29D, and the specification of modified dacron is 40D, viscous
The specification of gum base chitin fiber is 60D.Then, the blended ratio of the present embodiment is made according to following processing step:
(1) by the White Steam Filature Yarns of a 27/29D and the modified dacron of a 40D on doubling winder and silk, and the quality is become to be
The first yarn group of 700g, described first yarn group is two strands of yarns;
(2) described first yarn group is carried out Z-direction twisted filament process by two-for-one twister, twist 607 twists/m, obtain the first yarn;
(3) being placed in steam box by described first yarn and heat, the time of heating is no less than 50 minutes, the temperature of heating
For 80-90 DEG C;
(4) viscose chitin fibre of a 60D is carried out twisted filament process by two-for-one twister, twist 607 twists/m,
To the second yarn;
(5) being placed in steam box by described second yarn and heat, the time of heating is no less than 50 minutes, the temperature of heating
For 80-90 DEG C;
(6) by described first yarn and described second yarn on doubling winder and silk, and the second yarn becoming quality to be 700g
Group, described second yarn group is two strands of yarns;
(7) by two-for-one twister, described second yarn group is carried out S to process to twisted filament, twist 544 twists/m, obtain the 3rd yarn;
(8) being placed in steam box by described 3rd yarn and heat, the time of heating is no less than 50 minutes, the temperature of heating
For 80-90 DEG C.
The list of product is detected respectively according to GB/T3916-2013, GB9994-2008, GB/T2543.1-2001 detection method
Yarn strength, regain, color fastness to washing and washing shrinkage, result such as table 1, indices is above national standard.
Table 1
Obviously, the above embodiment of the present invention is only for clearly demonstrating example of the present invention, and is not right
The restriction of embodiments of the present invention, for those of ordinary skill in the field, the most also may be used
To make other changes in different forms, cannot all of embodiment be given exhaustive here, every belong to this
What bright technical scheme was extended out obviously changes or changes the row still in protection scope of the present invention.
Claims (10)
1. a blended ratio, it is characterised in that described blended ratio is to be former with White Steam Filature Yarns, modified dacron and regenerated celulose fibre
Material is made.
Blended ratio the most according to claim 1, it is characterised in that the single thread force of described blended ratio is 1200-1400CN/
CM, regain is 11-13%, and color fastness to washing is 4-5 level, and washing shrinkage is ± 2-± 3.
Blended ratio the most according to claim 1, it is characterised in that the specification of described White Steam Filature Yarns is 20/22-30/33D, institute
The specification stating modified dacron is 30-70D, and the specification of described regenerated celulose fibre is 50-100D.
Blended ratio the most according to claim 1, it is characterised in that the specification of described White Steam Filature Yarns is 20/22D, described modification
The specification of terylene is 50D, and the specification of described regenerated celulose fibre is 75D.
5. the manufacture method of the blended ratio as described in Claims 1-4 any one, it is characterised in that this manufacture method includes
Following steps:
(1) by a White Steam Filature Yarns and modified dacron on doubling winder and silk, and becoming the first yarn group, described first yarn group is one
Two strands of yarns of root;
(2) described first yarn group is carried out twisted filament process by two-for-one twister, obtain the first yarn;
(3) described first yarn is placed in steam box heats;
(4) a root regeneration cellulose fibre is carried out twisted filament process by two-for-one twister, obtain the second yarn;
(5) described second yarn is placed in steam box heats;
(6) by described first yarn and described second yarn on doubling winder and silk, and becoming the second yarn group, described second yarn group is
Piece two strands of yarns;
(7) described second yarn group is carried out twisted filament process by two-for-one twister, obtain the 3rd yarn;
(8) described 3rd yarn is placed in steam box heats.
Manufacture method the most according to claim 5, it is characterised in that the weight of described first yarn group is 680-720g, institute
The weight stating the second yarn group is 680-720g, it is preferable that the weight of described first yarn group is 700g, the weight of described second yarn group
For 700g.
Manufacture method the most according to claim 5, it is characterised in that the twisted filament carried out by two-for-one twister rolled into a ball by described first yarn
It is processed as Z twisted filament, twists 607 twists/m.
Manufacture method the most according to claim 5, it is characterised in that described regenerated celulose fibre is carried out by two-for-one twister
Twisted filament be processed as twisting 607 twists/m.
Manufacture method the most according to claim 5, it is characterised in that the twisted filament carried out by two-for-one twister rolled into a ball by described 3rd yarn
It is processed as S twisted filament, twists 544 twists/m.
Manufacture method the most according to claim 5, it is characterised in that the time of described heating is no less than 50 minutes, described
The temperature of heating is 80-90 DEG C.