CN105948581A - Building block for wall body - Google Patents
Building block for wall body Download PDFInfo
- Publication number
- CN105948581A CN105948581A CN201610276973.7A CN201610276973A CN105948581A CN 105948581 A CN105948581 A CN 105948581A CN 201610276973 A CN201610276973 A CN 201610276973A CN 105948581 A CN105948581 A CN 105948581A
- Authority
- CN
- China
- Prior art keywords
- building block
- parts
- wall building
- hours
- curing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a building block for a wall body. The building block is prepared by the following steps of firstly, adding raw materials into a stirring machine, then stirring the raw materials uniformly, pouring the mixture into a mold, performing de-molding after curing, and performing surface curing, thereby obtaining the building block for the wall body, wherein the step of curing comprises the following substeps: spraying a curing agent on a concrete building block, then performing curing for 3 hours at temperature of 35-40 DEG C, then raising the temperature to 55-60 DEG C to perform curing for 4 hours, then cooling the building block to normal temperature, then spraying the curing agent once again, and performing curing at normal temperature for 3-4 days. According to the building block disclosed by the invention, methyl silicone oil, benzyl alcohol, stannous chloride, sodium fluorosilicate, ethanol, and n-octyltrimethoxysilane are utilized to prepare the curing agent, and by virtue of the curing, the long-term strength of the building block for the wall body is improved, the curing time is shortened, and the labor and time costs are saved.
Description
Technical field
The present invention relates to a kind of body of wall building block, belongs to building block technique field.
Background technology
Novel wall material in construction material increasingly causes concern.Energy-conservation, safe, comfortable, intensity is high, environmental protection, sustainable development and harmful effect non-toxic to humans etc., has all become the new requirement of novel wall material.Novel environment-friendly energy saving building material is different from common construction material, and the mechanical property of its high excellence of intensity to be had, and the security performances such as safe, radiationless, fire prevention, such that it is able to provide a comfortable living environment for habitant.Building block tool is presently required while higher intensity and production process reduce environmental pollution, reduces production cost.
Summary of the invention
A kind of body of wall building block, body of wall building block raw material includes: cement 2-3kg, cement reinforcement agent 3-4kg, sand 3-4kg, stone 5-6kg, water 2-3kg, steel fibre 0.3kg, high efficiency water reducing agent 0.2kg;First above-mentioned raw materials is put into blender to stir, compound is poured in mould, curing and demolding, carry out surface maintenance, obtain body of wall building block, described curing step includes: sealing compound is sprayed on concrete segment, 35-40 DEG C of maintenance 3 hours after spraying, after being warming up to 55-60 DEG C of maintenance afterwards 4 hours, it is cooled to room temperature afterwards and sprays a sealing compound again, room temperature maintenance 3-4 days, sealing compound (weight portion) including: methyl-silicone oil 1 part, benzyl alcohol 0.3-0.4 part, stannous chloride 0.1-0.2 part, prodan 0.08-0.09 part, ethanol 0.7-0.8 part, n-octyl trimethoxy silane 0.02-0.03 part,
Cement reinforcement agent preparation method: weigh (weight portion) gangue 30-40 part, sulfate slag 10-20 part, active silica 10-20 part, Alumen stone powder 5-10 part, allophane powder 7-8 part, above-mentioned powder carries out in flour mill grinding, and rotating speed is 120r/min, grinding 3 hours, grinding temperature controls at 30 DEG C, the grinding material of gained enters pre-heating system, makes material be warming up to 750 DEG C, obtains intensification material;Intensification material enters dore furnace, first material is heated up to 900 DEG C, is incubated 25 minutes, is cooled to 850 DEG C afterwards, is incubated 10 minutes, and intensification material obtains decomposing materials by after described dore furnace;Decomposing materials enters rotary kiln, and controlling rotary kiln rotating speed is 2.5-3r/min, first material is heated up to 1420 DEG C, sintering time 2 hours, it is cooled to 1230 DEG C afterwards, sintering time 1.5 hours, it is warming up to 1310 DEG C afterwards, after sintering time 1 hour, kiln discharge natural cooling, powder carries out grinding again in flour mill afterwards, and rotating speed is 160r/min, grinding 2 hours, obtains cement reinforcement agent.
Described a kind of body of wall building block, weighs (weight portion) gangue 30 parts, sulfate slag 10 parts, active silica 10 parts, Alumen stone powder 5 parts, 7 parts of allophane powder.
Described a kind of body of wall building block, weighs (weight portion) gangue 40 parts, sulfate slag 20 parts, active silica 20 parts, Alumen stone powder 10 parts, 8 parts of allophane powder.
Described a kind of body of wall building block, weighs (weight portion) gangue 35 parts, sulfate slag 15 parts, active silica 15 parts, Alumen stone powder 7 parts, 7.5 parts of allophane powder.
Described a kind of body of wall building block, body of wall building block raw material includes: cement 2kg, cement reinforcement agent 3kg, sand 3kg, stone 5kg, water 2kg, steel fibre 0.3kg, high efficiency water reducing agent 0.2kg.
Described a kind of body of wall building block, body of wall building block raw material includes: cement 2.5kg, cement reinforcement agent 3.5kg, sand 3.5kg, stone 5.5kg, water 2.5kg, steel fibre 0.3kg, high efficiency water reducing agent 0.2kg.
Described a kind of body of wall building block, body of wall building block raw material includes: cement 3kg, cement reinforcement agent 4kg, sand 4kg, stone 6kg, water 3kg, steel fibre 0.3kg, high efficiency water reducing agent 0.2kg.
Described a kind of body of wall building block, sealing compound (weight portion) including: methyl-silicone oil 1 part, benzyl alcohol 0.3 part, stannous chloride 0.1 part, prodan 0.08 part, ethanol 0.7 part, n-octyl trimethoxy silane 0.02 part.
Described a kind of body of wall building block, sealing compound (weight portion) including: methyl-silicone oil 1 part, benzyl alcohol 0.4 part, stannous chloride 0.2 part, prodan 0.09 part, ethanol 0.8 part, n-octyl trimethoxy silane 0.03 part.
Described a kind of body of wall building block, sealing compound (weight portion) including: methyl-silicone oil 1 part, benzyl alcohol 0.35 part, stannous chloride 0.15 part, prodan 0.085 part, ethanol 0.75 part, n-octyl trimethoxy silane 0.025 part.
Compared with prior art, there is advantages that
The preparation of control sample: use cement 5kg, sand 3kg, stone 5kg, water 2kg, steel fibre 0.3kg, high efficiency water reducing agent 0.2kg, shaping test piece, maintenance.The preparation of test specimen of the present invention: cement 2kg, cement reinforcement agent 3kg, sand 3kg, stone 5kg, water 2kg, steel fibre 0.3kg, high efficiency water reducing agent 0.2kg, shaping test piece, maintenance (uses sealing compound of the present invention and curing step maintenance).
Sample of the present invention improves 5.2MPa with contrast test sample contrast early strength;Later strength improves 11.7MPa.The cement reinforcement agent raw material of the present invention i.e. reaches energy-conserving and environment-protective, twice laid, body of wall block strength can be strengthened again, and the present invention uses methyl-silicone oil, benzyl alcohol, stannous chloride, prodan, ethanol, n-octyl trimethoxy silane makes sealing compound and curing step maintenance improves body of wall building block later strength and shortens curing time, save artificial and time cost, cement reinforcement agent and sealing compound afterwards and maintenance processes is worked in coordination with and used early strength and the later strength improving body of wall building block, it is ensured that produce the quality of body of wall building block.
Detailed description of the invention
In order to the technical characteristic of the present invention, purpose and effect are more clearly understood from, now describe the detailed description of the invention of the present invention in detail.
Embodiment 1
A kind of body of wall building block, body of wall building block raw material includes: cement 2kg, cement reinforcement agent 3kg, sand 3kg, stone 5kg, water 2kg, steel fibre 0.3kg, high efficiency water reducing agent 0.2kg;First above-mentioned raw materials is put into blender to stir, compound is poured in mould, curing and demolding, carry out surface maintenance, obtain body of wall building block, described curing step includes: sealing compound is sprayed on concrete segment, 35-40 DEG C of maintenance 3 hours after spraying, after being warming up to 55-60 DEG C of maintenance afterwards 4 hours, it is cooled to room temperature afterwards and sprays a sealing compound again, room temperature maintenance 3-4 days, sealing compound (weight portion) including: methyl-silicone oil 1 part, benzyl alcohol 0.3 part, stannous chloride 0.1 part, prodan 0.08 part, ethanol 0.7 part, n-octyl trimethoxy silane 0.02 part,
Cement reinforcement agent preparation method: weigh (weight portion) gangue 30 parts, sulfate slag 10 parts, active silica 10 parts, Alumen stone powder 5 parts, 7 parts of allophane powder, above-mentioned powder carries out in flour mill grinding, and rotating speed is 120r/min, grinding 3 hours, grinding temperature controls at 30 DEG C, the grinding material of gained enters pre-heating system, makes material be warming up to 750 DEG C, obtains intensification material;Intensification material enters dore furnace, first material is heated up to 900 DEG C, is incubated 25 minutes, is cooled to 850 DEG C afterwards, is incubated 10 minutes, and intensification material obtains decomposing materials by after described dore furnace;Decomposing materials enters rotary kiln, and controlling rotary kiln rotating speed is 2.5-3r/min, first material is heated up to 1420 DEG C, sintering time 2 hours, it is cooled to 1230 DEG C afterwards, sintering time 1.5 hours, it is warming up to 1310 DEG C afterwards, after sintering time 1 hour, kiln discharge natural cooling, powder carries out grinding again in flour mill afterwards, and rotating speed is 160r/min, grinding 2 hours, obtains cement reinforcement agent.
Embodiment 2
A kind of body of wall building block, body of wall building block raw material includes: cement 3kg, cement reinforcement agent 4kg, sand 4kg, stone 6kg, water 3kg, steel fibre 0.3kg, high efficiency water reducing agent 0.2kg;First above-mentioned raw materials is put into blender to stir, compound is poured in mould, curing and demolding, carry out surface maintenance, obtain body of wall building block, described curing step includes: sealing compound is sprayed on concrete segment, 40 DEG C of maintenances 3 hours after spraying, after being warming up to 60 DEG C of maintenances afterwards 4 hours, it is cooled to room temperature afterwards and sprays a sealing compound again, room temperature maintenance 3-4 days, sealing compound (weight portion) including: methyl-silicone oil 1 part, benzyl alcohol 0.4 part, stannous chloride 0.2 part, prodan 0.09 part, ethanol 0.8 part, n-octyl trimethoxy silane 0.03 part,
Cement reinforcement agent preparation method: weigh (weight portion) gangue 40 parts, sulfate slag 20 parts, active silica 20 parts, Alumen stone powder 10 parts, 8 parts of allophane powder, above-mentioned powder carries out in flour mill grinding, and rotating speed is 120r/min, grinding 3 hours, grinding temperature controls at 30 DEG C, the grinding material of gained enters pre-heating system, makes material be warming up to 750 DEG C, obtains intensification material;Intensification material enters dore furnace, first material is heated up to 900 DEG C, is incubated 25 minutes, is cooled to 850 DEG C afterwards, is incubated 10 minutes, and intensification material obtains decomposing materials by after described dore furnace;Decomposing materials enters rotary kiln, and controlling rotary kiln rotating speed is 2.5-3r/min, first material is heated up to 1420 DEG C, sintering time 2 hours, it is cooled to 1230 DEG C afterwards, sintering time 1.5 hours, it is warming up to 1310 DEG C afterwards, after sintering time 1 hour, kiln discharge natural cooling, powder carries out grinding again in flour mill afterwards, and rotating speed is 160r/min, grinding 2 hours, obtains cement reinforcement agent.
Embodiment 3
A kind of body of wall building block, body of wall building block raw material includes: cement 2.5kg, cement reinforcement agent 3.5kg, sand 3.5kg, stone 5.5kg, water 2.5kg, steel fibre 0.3kg, high efficiency water reducing agent 0.2kg;First above-mentioned raw materials is put into blender to stir, compound is poured in mould, curing and demolding, carry out surface maintenance, obtain body of wall building block, described curing step includes: sealing compound is sprayed on concrete segment, 35-40 DEG C of maintenance 3 hours after spraying, after being warming up to 55-60 DEG C of maintenance afterwards 4 hours, it is cooled to room temperature afterwards and sprays a sealing compound again, room temperature maintenance 3-4 days, sealing compound (weight portion) including: methyl-silicone oil 1 part, benzyl alcohol 0.35 part, stannous chloride 0.15 part, prodan 0.085 part, ethanol 0.75 part, n-octyl trimethoxy silane 0.025 part,
Cement reinforcement agent preparation method: weigh (weight portion) gangue 35 parts, sulfate slag 15 parts, active silica 15 parts, Alumen stone powder 7 parts, 7.5 parts of allophane powder, above-mentioned powder carries out in flour mill grinding, and rotating speed is 120r/min, grinding 3 hours, grinding temperature controls at 30 DEG C, the grinding material of gained enters pre-heating system, makes material be warming up to 750 DEG C, obtains intensification material;Intensification material enters dore furnace, first material is heated up to 900 DEG C, is incubated 25 minutes, is cooled to 850 DEG C afterwards, is incubated 10 minutes, and intensification material obtains decomposing materials by after described dore furnace;Decomposing materials enters rotary kiln, and controlling rotary kiln rotating speed is 2.5-3r/min, first material is heated up to 1420 DEG C, sintering time 2 hours, it is cooled to 1230 DEG C afterwards, sintering time 1.5 hours, it is warming up to 1310 DEG C afterwards, after sintering time 1 hour, kiln discharge natural cooling, powder carries out grinding again in flour mill afterwards, and rotating speed is 160r/min, grinding 2 hours, obtains cement reinforcement agent.
Embodiment 4
A kind of body of wall building block, body of wall building block raw material includes: cement 2.3kg, cement reinforcement agent 3.2kg, sand 3.1kg, stone 5.1kg, water 2.2kg, steel fibre 0.3kg, high efficiency water reducing agent 0.2kg;First above-mentioned raw materials is put into blender to stir, compound is poured in mould, curing and demolding, carry out surface maintenance, obtain body of wall building block, described curing step includes: sealing compound is sprayed on concrete segment, 35-40 DEG C of maintenance 3 hours after spraying, after being warming up to 55-60 DEG C of maintenance afterwards 4 hours, it is cooled to room temperature afterwards and sprays a sealing compound again, room temperature maintenance 3-4 days, sealing compound (weight portion) including: methyl-silicone oil 1 part, benzyl alcohol 0.34 part, stannous chloride 0.13 part, prodan 0.082 part, ethanol 0.73 part, n-octyl trimethoxy silane 0.023 part,
Cement reinforcement agent preparation method: weigh (weight portion) gangue 32 parts, sulfate slag 11 parts, active silica 12 parts, Alumen stone powder 6 parts, allophane powder 7-8 part, above-mentioned powder carries out in flour mill grinding, and rotating speed is 120r/min, grinding 3 hours, grinding temperature controls at 30 DEG C, the grinding material of gained enters pre-heating system, makes material be warming up to 750 DEG C, obtains intensification material;Intensification material enters dore furnace, first material is heated up to 900 DEG C, is incubated 25 minutes, is cooled to 850 DEG C afterwards, is incubated 10 minutes, and intensification material obtains decomposing materials by after described dore furnace;Decomposing materials enters rotary kiln, and controlling rotary kiln rotating speed is 2.5-3r/min, first material is heated up to 1420 DEG C, sintering time 2 hours, it is cooled to 1230 DEG C afterwards, sintering time 1.5 hours, it is warming up to 1310 DEG C afterwards, after sintering time 1 hour, kiln discharge natural cooling, powder carries out grinding again in flour mill afterwards, and rotating speed is 160r/min, grinding 2 hours, obtains cement reinforcement agent.
Embodiment 5
A kind of body of wall building block, body of wall building block raw material includes: cement 2.6kg, cement reinforcement agent 3.7kg, sand 3.8kg, stone 5.7kg, water 2.7kg, steel fibre 0.3kg, high efficiency water reducing agent 0.2kg;First above-mentioned raw materials is put into blender to stir, compound is poured in mould, curing and demolding, carry out surface maintenance, obtain body of wall building block, described curing step includes: sealing compound is sprayed on concrete segment, 35-40 DEG C of maintenance 3 hours after spraying, after being warming up to 55-60 DEG C of maintenance afterwards 4 hours, it is cooled to room temperature afterwards and sprays a sealing compound again, room temperature maintenance 3-4 days, sealing compound (weight portion) including: methyl-silicone oil 1 part, benzyl alcohol 0.36 part, stannous chloride 0.17 part, prodan 0.086 part, ethanol 0.77 part, n-octyl trimethoxy silane 0.028 part,
Cement reinforcement agent preparation method: weigh (weight portion) gangue 37 parts, sulfate slag 17 parts, active silica 18 parts, Alumen stone powder 9 parts, 7.8 parts of allophane powder, above-mentioned powder carries out in flour mill grinding, and rotating speed is 120r/min, grinding 3 hours, grinding temperature controls at 30 DEG C, the grinding material of gained enters pre-heating system, makes material be warming up to 750 DEG C, obtains intensification material;Intensification material enters dore furnace, first material is heated up to 900 DEG C, is incubated 25 minutes, is cooled to 850 DEG C afterwards, is incubated 10 minutes, and intensification material obtains decomposing materials by after described dore furnace;Decomposing materials enters rotary kiln, and controlling rotary kiln rotating speed is 2.5-3r/min, first material is heated up to 1420 DEG C, sintering time 2 hours, it is cooled to 1230 DEG C afterwards, sintering time 1.5 hours, it is warming up to 1310 DEG C afterwards, after sintering time 1 hour, kiln discharge natural cooling, powder carries out grinding again in flour mill afterwards, and rotating speed is 160r/min, grinding 2 hours, obtains cement reinforcement agent.
Claims (10)
1. a body of wall building block, body of wall building block raw material includes: cement 2-3kg, cement reinforcement agent 3-4kg, sand 3-4kg, stone 5-6kg, water 2-3kg, steel fibre 0.3kg, high efficiency water reducing agent 0.2kg;First above-mentioned raw materials is put into blender to stir, compound is poured in mould, curing and demolding, carry out surface maintenance, obtain body of wall building block, described curing step includes: sealing compound is sprayed on concrete segment, 35-40 DEG C of maintenance 3 hours after spraying, after being warming up to 55-60 DEG C of maintenance afterwards 4 hours, it is cooled to room temperature afterwards and sprays a sealing compound again, room temperature maintenance 3-4 days, sealing compound (weight portion) including: methyl-silicone oil 1 part, benzyl alcohol 0.3-0.4 part, stannous chloride 0.1-0.2 part, prodan 0.08-0.09 part, ethanol 0.7-0.8 part, n-octyl trimethoxy silane 0.02-0.03 part,
Cement reinforcement agent preparation method: weigh (weight portion) gangue 30-40 part, sulfate slag 10-20 part, active silica 10-20 part, Alumen stone powder 5-10 part, allophane powder 7-8 part, above-mentioned powder carries out in flour mill grinding, and rotating speed is 120r/min, grinding 3 hours, grinding temperature controls at 30 DEG C, the grinding material of gained enters pre-heating system, makes material be warming up to 750 DEG C, obtains intensification material;Intensification material enters dore furnace, first material is heated up to 900 DEG C, is incubated 25 minutes, is cooled to 850 DEG C afterwards, is incubated 10 minutes, and intensification material obtains decomposing materials by after described dore furnace;Decomposing materials enters rotary kiln, and controlling rotary kiln rotating speed is general 2.5-3r/min, first material is heated up to 1420 DEG C, sintering time 2 hours, it is cooled to 1230 DEG C afterwards, sintering time 1.5 hours, it is warming up to 1310 DEG C afterwards, after sintering time 1 hour, kiln discharge natural cooling, powder carries out grinding again in flour mill afterwards, and rotating speed is 160r/min, grinding 2 hours, obtains cement reinforcement agent.
2. a kind of body of wall building block as claimed in claim 1, weighs (weight portion) gangue 30 parts, sulfate slag 10 parts, active silica 10 parts, Alumen stone powder 5 parts, 7 parts of allophane powder.
3. a kind of body of wall building block as claimed in claim 1, weighs (weight portion) gangue 40 parts, sulfate slag 20 parts, active silica 20 parts, Alumen stone powder 10 parts, 8 parts of allophane powder.
4. a kind of body of wall building block as claimed in claim 1, weighs (weight portion) gangue 35 parts, sulfate slag 15 parts, active silica 15 parts, Alumen stone powder 7 parts, 7.5 parts of allophane powder.
5. a kind of body of wall building block as claimed in claim 1, body of wall building block raw material includes: cement 2kg, cement reinforcement agent 3kg, sand 3kg, stone 5kg, water 2kg, steel fibre 0.3kg, high efficiency water reducing agent 0.2kg.
6. a kind of body of wall building block as claimed in claim 1, body of wall building block raw material includes: cement 2.5kg, cement reinforcement agent 3.5kg, sand 3.5kg, stone 5.5kg, water 2.5kg, steel fibre 0.3kg, high efficiency water reducing agent 0.2kg.
7. a kind of body of wall building block as claimed in claim 1, body of wall building block raw material includes: cement 3kg, cement reinforcement agent 4kg, sand 4kg, stone 6kg, water 3kg, steel fibre 0.3kg, high efficiency water reducing agent 0.2kg.
8. a kind of body of wall building block as claimed in claim 1, sealing compound (weight portion) including: methyl-silicone oil 1 part, benzyl alcohol 0.3 part, stannous chloride 0.1 part, prodan 0.08 part, ethanol 0.7 part, n-octyl trimethoxy silane 0.02 part.
9. a kind of body of wall building block as claimed in claim 1, sealing compound (weight portion) including: methyl-silicone oil 1 part, benzyl alcohol 0.4 part, stannous chloride 0.2 part, prodan 0.09 part, ethanol 0.8 part, n-octyl trimethoxy silane 0.03 part.
10. a kind of body of wall building block as claimed in claim 1, sealing compound (weight portion) including: methyl-silicone oil 1 part, benzyl alcohol 0.35 part, stannous chloride 0.15 part, prodan 0.085 part, ethanol 0.75 part, n-octyl trimethoxy silane 0.025 part.