CN105906239B - 钢构“机喷-氟石膏-反射隔热涂料”围护保温复合墙*** - Google Patents

钢构“机喷-氟石膏-反射隔热涂料”围护保温复合墙*** Download PDF

Info

Publication number
CN105906239B
CN105906239B CN201610196171.5A CN201610196171A CN105906239B CN 105906239 B CN105906239 B CN 105906239B CN 201610196171 A CN201610196171 A CN 201610196171A CN 105906239 B CN105906239 B CN 105906239B
Authority
CN
China
Prior art keywords
parts
heat preservation
gypsum
fluorgypsum
cement
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201610196171.5A
Other languages
English (en)
Other versions
CN105906239A (zh
Inventor
马振义
马振家
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201610196171.5A priority Critical patent/CN105906239B/zh
Publication of CN105906239A publication Critical patent/CN105906239A/zh
Application granted granted Critical
Publication of CN105906239B publication Critical patent/CN105906239B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了钢构“机喷‑氟石膏‑反射隔热涂料”围护保温复合墙***，保温复合墙***包括内保温***和外保温***，内保温***和外保温***共用基材层，从内到外依次为：内饰面层、内保护层、内保温层、内防火层、内界面层、基材层、外界面层、外保温层、外保护层，外饰面层，本发明采用氟石膏改性技术，减少了能源资源的消耗，减少了污染，保护了天然资源，保护了生态环境；同时扩大了对工业副产石膏的利用，消纳了大量固体废弃物，改善了对环境的污染，又节约了建筑使用能耗，把钢构企业变成既是低能耗又是消纳工业固弃新型节能环保大产业。

Description

钢构“机喷-氟石膏-反射隔热涂料”围护保温复合墙***
技术领域
本发明涉及一种钢构“机喷-氟石膏-反射隔热涂料”围护保温复合墙***。
背景技术
近年来，由于国家住宅产业化，节能减排，城镇化建设，美丽新农村建设等政策的强力推进，加之钢产量的过剩和价格的回落，为发展钢结构提供了良好的历史机遇，我国的钢结构住宅进入了一个新的发展时期，迎来了发展的明媚春天。
钢结构住宅是我国经济发展新的增长点，是传统砖混结构、混凝土结构发展的必由之路，也是建筑业从城市转向农村的方向标，将给建筑业带来一场从设计、施工，到一系列新材料、新技术革命性变革。钢结构住宅是传统建筑业的一个重要分支，而冷弯薄壁住宅又是对钢结构住宅的一个重要补充，钢结构住宅大家族中的一个重要组成成员。具有安全、耐久、节能、环保、健康、舒适等优良性能，将成为21世纪全球化住宅的主流产品。
冷弯薄壁钢结构住宅是一个崭新的产业，需要一个从技术到标准全面的革新和发展。目前，国内在冷弯薄壁住宅或钢结构住宅围护结构中，都采用“墙板”体系，即在冷弯薄壁或钢结构构件两侧用结构板固定，在腔内分别填插XPS板或EPS、PU、岩棉板，结构板两侧不在做外墙外保温和外墙内保温，只在外墙面和内墙面做饰面层，即涂腻子和涂料。经过十几年的实践，显露出许多不尽人意之处，诸如空鼓、不实感、裂缝、隔声、防火、热桥、吊挂、连接等问题，引起了业界和使用者强烈反响，严重制约了冷弯薄壁住宅和钢结构住宅的应用和推广。
发明内容
本发明要解决的技术问题是钢构“机喷-氟石膏-反射隔热涂料”围护保温复合墙***，采用氟石膏改性技术，减少能源资源的消耗，减少污染，保护了天然资源，保护生态环境。
为了解决上述技术问题，本发明采用的技术方案是：
钢构“机喷-氟石膏-反射隔热涂料”围护保温复合墙***，保温复合墙***包括内保温***和外保温***，内保温***和外保温***共用基材层，内、外保温***均包括基材层、界面层、保温层、保护层，饰面层，内保温***还包括防火层，保温复合墙***具体制备方法如下：
(1)、贴基材板
选择符合要求的中密度水泥纤维板或镀锌钢板网作为基材板，将基材板固定于冷弯薄壁或钢结构外侧，中密度水泥纤维板抗压强度为3～5MPa，排板材竖缝逐行错缝板长的1/2，不能有贯通缝，并用柔性腻子墙缝压入宽20mm耐碱网格布。镀锌钢板网的网孔为3×6mm或4×8mm，有横筋，接缝处互压20mm；
(2)、喷涂界面剂
在经过步骤(1)处理后的基板材内侧喷涂界面剂形成界面层，界面剂的厚度为0.5mm，界面剂包括以下重量份原料：苯丙乳液80～90份、水15～18份、纤维素醚1～2份、砂1～2份；
(3)、机喷防火涂料
在界面层上喷涂30mm厚的防火涂料，防火涂料包括以下重量份原料：建筑石膏40～50份、二级粉煤灰15～25份、微硅粉5～6份、膨胀蛭石5～10份、玻化微珠15～25份、玻璃纤维6～10份、硼酸锌2～3份、纤维素醚1～2份、胶粉3～4份，防火涂料的技术性能为：用水量1:0.9，初凝120mi n、干密度495kg/m3，抗折0.70MPa，抗压1.57MPa，耐火极限≥2h；
(4)、机喷氟石膏改性保温砂浆
在防火涂料上机喷氟石膏改性保温砂浆80mm，且分层喷涂，氟石膏改性保温砂浆包括以下重量份原料：氟石膏60～65份、二级粉煤灰10～15份、水泥5～10份、CaO 6～8份、微硅粉2～3份、减水剂0.9～1.5份、EPS颗粒1～2份、纤维素醚1～2份、胶粉3～4份；
(5)、抹石膏基抗裂耐水砂浆并使用网格布形成保护层
在经过步骤(4)处理的墙内侧抹厚度为2.5～3mm的石膏基抗裂耐水砂浆，然后使用网格布，再将表面磨平，石膏基抗裂耐水砂浆包括以下重量份原料：二水脱硫石膏40～50份、水泥5～6份、粉煤灰20～30份、硫铝酸水泥2～8份、砂10～30份、激发剂0.5～2份、纤维素醚2～3.5份；以上原料的技术性能为：用水量1：0.3,初凝4h，干密度1400kg/m3，抗折7.5MPa，抗压21.2MPa，压折比2.8，软化系数0.69；
(6)在保护层内侧抹石膏腻子形成饰面层
在保护层内侧抹2～5mm厚的石膏腻子或抹石膏硅藻泥形成饰面层，石膏腻子包括以下重量份原料：石膏40～50份、灰钙3～6份、白水泥2～5份、碳酸钙40～45份、纤维素醚1～2份、胶粉3～4份，石膏腻子技术性能为：用水1：0.46，PH值7～8，抗折3.2MPa，抗压4.4MPa，压折比1.4，软化系数0.72；
(7)、在基板材外侧喷涂界面剂形成界面层
在基板材外侧形成界面层具体方法同步骤(2)；
(8)、机喷水泥基保温砂浆
在步骤(7)形成的界面层外侧机喷25mm～30mm厚的水泥基保温砂浆，水泥基保温砂浆包括以下重量份原料：水泥40～50份、粉煤灰20～35份、灰钙3～5份、EPS颗粒1～1.5份、纤维素醚1～2份、胶粉3～4份，水泥基保温砂浆性能为：用水量1:0.74,、干密度412kg/m3，抗折0.67MPa，抗压0.89MPa，软化系数0.65；
(9)、抹抗裂砂浆并涂反射隔热涂料
在步骤(8)的保温层外侧抹厚度为3～5mm的抗裂砂浆，抗裂砂浆包括以下重量份原料：水泥30～40份、砂50～60份、半水石膏2～5份、CaO 2～3份、减水剂0.2～1份、纤维素醚1～2份、胶粉3～4份，抗裂砂浆的技术性能为：用水量0.23、抗折1.85MPa,抗压4.7MPa，压折比2.5，软化系数1.05；
反射隔热涂料包括以下重量份原料：纯丙乳液50～60份、玻璃微珠5～15份、金红石型钛白粉5～10份、消泡剂0.1～0.5份、纤维素醚0.1～0.2份、成膜助剂3～5份、流平剂0.8～1份、中和剂0.1～0.3份、防腐剂0.1～0.3份、防冻剂0.5～2份、水10～15份，反射隔热涂料制备工艺如下：
S1、将水置于容器中，加入以上原料的三分之二的消泡剂、成膜助剂、纤维素醚、中和剂、防腐剂、防冻剂，高速分散，使其完全融解；
S2、缓缓加入金红石型钛白粉，保持高分散速率，直至分散均匀，成为白色浓稠状细腻白浆；
S3、分批次将上述浆料加入纯丙乳液中，低速分散，直至体系均匀；
S4、缓慢加入玻璃微珠，降低分散速率，直至分散均匀；
S5、用纤维素醚、流平剂调节粘度和流动度，并加入剩余的消泡剂，低速分散，直至体系均匀。
优选的，步骤(6)使用石膏硅藻泥替换石膏腻子，石膏硅藻泥包括以下重量份原料：石膏20～35份、硅藻泥25～45份、碳酸钙20～45份、纤维素醚1～2份、胶粉3～4份，石膏硅藻泥技术性能为：甲醛净化性能85％、甲醛净化效果持久性70％、防霉菌性能O级、防霉菌耐久性能1级。
优选的，步骤(1)中的中密度水泥纤维板厚度为9mm，镀锌钢板网厚度为0.6mm。
优选的，机喷使用的喷涂机喷口压力为0.3～0.5MPa，喷嘴直径为25mm，喷管管道直径为25mm，水平输送距离为40m，垂直输送距离为50m。
进一步的，碱性材料为水泥和硫铝酸水泥，氟石膏改性保温砂浆包括以下重量份原料：二水脱硫石膏50～60份、水泥5～15份、硫铝酸水泥3～5份、二级粉煤灰30～35份、EPS颗粒0.3～0.8份、纤维素醚0.05份～0.2份、激发剂0.8～1份、减水剂0.5～1份，具体制备方法为：用二级粉煤灰与碱性材料和硫酸盐类进行激发，水化生成钙矾石和水化硅酸钙凝胶，二水脱硫石膏起部分激发剂的作用，并与钙矾石结合形成骨架，水化硅酸钙凝胶渗透于骨架毛细孔中，并将二水脱硫石膏和钙矾石包裹，形成水硬性材料。
本发明的有益效果：
本发明颠覆传统二水石膏，经过烘干、煅烧二道脱水工艺，即烘干工艺脱去附着水，后煅烧180℃脱去3/2结晶水，蜕变为1/2结晶水的半水石膏，才有胶凝性，将原状二水石膏不经燃料和设备煅烧，而是采取物理和化学改性、激发的形式，促其产生质的变化和飞跃，由气硬性石膏材料，变为水硬性水泥和气硬性石膏兼有特质的材料。并偏重于水硬性水泥的特性材料。生成Aft钙矾石和C-S-H水化硅酸钙凝胶，克服了强度低，不耐水的弱势，解决了石膏不耐水、强度低的缺点。
本发明克服“墙板”***的隔音不佳、私密性差的弊病，提供了舒适的静音环境。本发明解决了“墙板”***板与结构、板与窗户的连接难题，实施柔性无缝链接，形成刚柔相济，骨与肉连接形式，提高了整体性、抗震性、安全性；同时，解决了热桥、吊挂、渗透的问题。本发明采用相变储能技术，充分利用太阳能，吸收储存与释放能量；与此同时，加上石膏基保温浆料，大大减少了主动式采暖和空调的开放时间，节约能耗，减少排放，提高舒适度，符合被动式住宅的要求。
附图说明
下面结合附图和具体实施方式对本发明作进一步详细的说明。
图1是本发明工艺图。
图2是本发明保温复合墙示意图。
具体实施方式
以下将对本发明的实施例进行详细描述。
如图2所示，本发明公开一种钢构“机喷-氟石膏-反射隔热涂料”围护保温复合墙***,其中，保温复合墙***包括内保温***和外保温***，内保温***和外保温***共用基材层5，从内到外依次为：内饰面层10、内保护层9、内保温层8、内防火层7、内界面层6、基材层5、外界面层4、外保温层3、外保护层2，外饰面层1，如图1，保温复合墙***具体制备方法如下：
(1)、贴基材板
选择符合要求的9mm厚中密度水泥纤维板或0.6mm厚的镀锌钢板网作为基材板，将基材板固定于冷弯薄壁或钢结构外侧，便于机喷矿浆附着，并赋予阻断热桥功能，中密度水泥纤维板抗压强度为3～5MPa，排板材竖缝应逐行错缝板长的1/2，不能有贯通缝，并用柔性腻子墙缝压入宽20mm耐碱网格布。镀锌钢板网的网孔为3×6mm或4×8mm，有横筋，接缝处互压20mm；
(2)、喷涂界面剂
在经过步骤(1)处理后的基板材内侧喷涂界面剂形成界面层，界面剂的厚度为0.5mm，界面剂包括以下重量份原料：苯丙乳液80～90份、水15～18份、纤维素醚1～2份、砂1～2份；
(3)、机喷防火涂料
在界面层上喷涂30mm厚的防火涂料，防火涂料包括以下重量份原料：建筑石膏40～50份、二级粉煤灰15～25份、微硅粉5～6份、膨胀蛭石5～10份、玻化微珠15～25份、玻璃纤维6～10份、硼酸锌2～3份、纤维素醚1～2份、胶粉3～4份，防火涂料的技术性能为：用水量1:0.9，初凝120mi n、干密度495kg/m3，抗折0.70MPa，抗压1.57MPa，耐火极限≥2h；
(4)、机喷氟石膏改性保温砂浆
在防火涂料上机喷氟石膏改性保温砂浆80mm，且分层喷涂，氟石膏改性保温砂浆包括以下重量份原料：二水脱硫石膏50～60份、碱性材料8～20份、二级粉煤灰30～35份、EPS颗粒0.3～0.8份、纤维素醚0.05份～0.2份、激发剂0.8～1份、减水剂0.5～1份，以上原料的混合物用水量为1:0.83，密度为473kg/m3,抗压强度为1.8MPa，剪切粘结强度为0.69MPa，软化系数为0.72；
(5)、抹石膏基抗裂耐水砂浆并使用网格布形成保护层
在经过步骤(4)处理的墙内侧抹厚度为2.5～3mm的石膏基抗裂耐水砂浆，然后使用网格布，再将表面磨平，石膏基抗裂耐水砂浆包括以下重量份原料：二水脱硫石膏40～50份、水泥5～6份、粉煤灰20～30份、硫铝酸水泥2～8份、砂10～30份、激发剂0.5～2份、纤维素醚2～3.5份；以上原料的技术性能为：用水量1：0.3,初凝4h，干密度1400kg/m3，抗折7.5MPa，抗压21.2MPa，压折比2.8，软化系数0.69；
(6)在保护层内侧抹石膏腻子形成饰面层
在保护层内侧抹2～5mm厚的石膏腻子或抹石膏硅藻泥形成饰面层，石膏腻子包括以下重量份原料：石膏40～50份、灰钙3～6份、白水泥2～5份、碳酸钙40～45份、纤维素醚1～2份、胶粉3～4份，石膏腻子技术性能为：用水1：0.46，PH值7～8，抗折3.2MPa，抗压4.4MPa，压折比1.4，软化系数0.72；
(7)、在基板材外侧喷涂界面剂形成界面层
在基板材外侧形成界面层具体方法同步骤(2)；
(8)、机喷水泥基保温砂浆
在步骤(7)形成的界面层外侧机喷25mm～30mm厚的水泥基保温砂浆，水泥基保温砂浆包括以下重量份原料：水泥40～50份、粉煤灰20～35份、灰钙3～5份、EPS颗粒1～1.5份、纤维素醚1～2份、胶粉3～4份，水泥基保温砂浆性能为：用水量1:0.74,、干密度412kg/m3，抗折0.67MPa，抗压0.89MPa，软化系数0.65；
(9)、抹抗裂砂浆并涂反射隔热涂料
在步骤(8)的保温层外侧抹厚度为3～5mm的抗裂砂浆，抗裂砂浆包括以下重量份原料：水泥30～40份、砂50～60份、半水石膏2～5份、CaO 2～3份、减水剂0.2～1份、纤维素醚1～2份、胶粉3～4份，抗裂砂浆的技术性能为：用水量0.23、抗折1.85MPa,抗压4.7MPa，压折比2.5，软化系数1.05；
反射隔热涂料包括以下重量份原料：纯丙乳液50～60份、玻璃微珠5～15份、金红石型钛白粉5～10份、消泡剂0.1～0.5份、纤维素醚0.1～0.2份、成膜助剂3～5份、流平剂0.8～1份、中和剂0.1～0.3份、防腐剂0.1～0.3份、防冻剂0.5～2份、水10～15份，反射隔热涂料制备工艺如下：
S1、将水置于容器中，加入以上原料的三分之二的消泡剂、成膜助剂、纤维素醚、中和剂、防腐剂、防冻剂，高速分散，使其完全融解；
S2、缓缓加入金红石型钛白粉，保持高分散速率，直至分散均匀，成为白色浓稠状细腻白浆；
S3、分批次将上述浆料加入纯丙乳液中，低速分散，直至体系均匀；
S4、缓慢加入玻璃微珠，降低分散速率，直至分散均匀；
S5、用纤维素醚、流平剂调节粘度和流动度，并加入剩余的消泡剂，低速分散，直至体系均匀。
反射隔热涂料利用涂膜较高的太阳反射率，降低围护结构表面和室内温度，具有显著的节约空调耗能。本发明热稳定性好，舒适度高。反射隔热涂料适用于晴天和白色涂膜或淡色涂膜，遇到阴天或者重色调时，其隔热降温大打折扣。
在本实施例中，步骤(6)可使用石膏硅藻泥替换石膏腻子，石膏硅藻泥包括以下重量份原料：石膏20～35份、硅藻泥25～45份、碳酸钙20～45份、纤维素醚1～2份、胶粉3～4份，石膏硅藻泥技术性能为：甲醛净化性能85％、甲醛净化效果持久性70％、防霉菌性能O级、防霉菌耐久性能1级。
步骤(6)具有以下优点：一、吸收甲醛、苯和有害有机物；二、释放负氧离子；三、调节室内干湿度。
机喷使用的喷涂机喷口压力为0.3～0.5MPa，喷嘴直径为25mm，喷管管道直径为25mm，水平输送距离为40m，垂直输送距离为50m。机喷相对于传统的手工抹灰，提高生产效率3-5倍，节约了成本，提高了竞争力，保证了质量。在提高了附着力的同时，更适用于冷弯薄壁钢结构住宅本身C型钢结构异性部位的喷涂和粘结。
碱性材料为水泥和硫铝酸水泥，氟石膏改性保温砂浆包括以下重量份原料：二水脱硫石膏50～60份、水泥5～15份、硫铝酸水泥3～5份、二级粉煤灰30～35份、EPS颗粒0.3～0.8份、纤维素醚0.05份～0.2份、激发剂0.8～1份、减水剂0.5～1份，具体制备方法为：用二级粉煤灰与碱性材料和硫酸盐类进行激发，水化生成钙矾石和水化硅酸钙凝胶，二水脱硫石膏起部分激发剂的作用，并与钙矾石结合形成骨架，水化硅酸钙凝胶渗透于骨架毛细孔中，并将二水脱硫石膏和钙矾石包裹，形成水硬性材料。
本发明解决了现市场“墙板”***的空鼓感，变成实心墙，整体性好，安全性好的宜居房，感觉舒适。本发明解决了“墙板”***板与结构、板与窗户的连接难题，实施柔性无缝链接，形成刚柔相济，骨与肉连接形式，提高了整体性、抗震性、安全性；同时，解决了热桥、吊挂、渗透的问题。本发明采用相变储能技术，充分利用太阳能，吸收储存与释放能量；与此同时，加上石膏基保温浆料，大大减少了主动式采暖和空调的开放时间，节约能耗，减少排放，提高舒适度，符合被动式住宅的要求。
本发明采用氟石膏改性技术，减少了能源资源的消耗，减少了污染，保护了天然资源，保护了生态环境；同时扩大了对工业副产石膏的利用，消纳了大量固体废弃物，改善了对环境的污染，又节约了建筑使用能耗，把钢构企业变成既是低能耗又是消纳工业固弃新型节能环保大产业。
以上所述的本发明实施方式，并不构成对本发明保护范围的限定。任何在本发明的精神和原则之内所作的修改、等同替换和改进等，均应包含在本发明的权利要求保护范围之内。

Claims (4)

1.钢构“机喷-氟石膏-反射隔热涂料”围护保温复合墙***,其特征在于，保温复合墙***包括内保温***和外保温***，内保温***和外保温***共用基材层，内、外保温***均包括基材层、界面层、保温层、保护层，饰面层，内保温***还包括防火层，保温复合墙***具体制备方法如下：
(1)、贴基材板
选择符合要求的中密度水泥纤维板或镀锌钢板网作为基材板，将基材板固定于冷弯薄壁或钢结构外侧，中密度水泥纤维板抗压强度为3～5MPa，排板材竖缝逐行错缝板长的1/2，不能有贯通缝，并用柔性腻子墙缝压入宽20mm耐碱网格布；镀锌钢板网的网孔为3×6mm或4×8mm，有横筋，接缝处互压20mm；
(2)、喷涂界面剂
在经过步骤(1)处理后的基板材内侧喷涂界面剂形成界面层，界面剂的厚度为0.5mm，界面剂包括以下重量份原料：苯丙乳液80～90份、水15～18份、纤维素醚1～2份、砂1～2份；
(3)、机喷防火涂料
在界面层上喷涂30mm厚的防火涂料，防火涂料包括以下重量份原料：建筑石膏40～50份、二级粉煤灰15～25份、微硅粉5～6份、膨胀蛭石5～10份、玻化微珠15～25份、玻璃纤维6～10份、硼酸锌2～3份、纤维素醚1～2份、胶粉3～4份，防火涂料的技术性能为：用水量1:0.9，初凝120min、干密度495kg/m3，抗折0.70MPa，抗压1.57MPa，耐火极限≥2h；
(4)、机喷氟石膏改性保温砂浆
在防火涂料上机喷氟石膏改性保温砂浆80mm，且分层喷涂，氟石膏改性保温砂浆包括以下重量份原料：氟石膏60～65份、二级粉煤灰10～15份、水泥5～10份、CaO 6～8份、微硅粉2～3份、减水剂0.9～1.5份、EPS颗粒1～2份、纤维素醚1～2份、胶粉3～4份；
(5)、抹石膏基抗裂耐水砂浆并使用网格布形成保护层
在经过步骤(4)处理的墙内侧抹厚度为2.5～3mm的石膏基抗裂耐水砂浆，然后使用网格布，再将表面抹平，石膏基抗裂耐水砂浆包括以下重量份原料：二水脱硫石膏40～50份、水泥5～6份、粉煤灰20～30份、硫铝酸水泥2～8份、砂10～30份、激发剂0.5～2份、纤维素醚2～3.5份；以上原料的技术性能为：用水量1：0.3,初凝4h，干密度1400kg/m3，抗折7.5MPa，抗压21.2MPa，压折比2.8，软化系数0.69；
(6)在保护层内侧抹石膏腻子形成饰面层
在保护层内侧抹2～5mm厚的石膏腻子或抹石膏硅藻泥形成饰面层，石膏腻子包括以下重量份原料：石膏40～50份、灰钙3～6份、白水泥2～5份、碳酸钙40～45份、纤维素醚1～2份、胶粉3～4份，石膏腻子技术性能为：用水1：0.46，PH值7～8，抗折3.2MPa，抗压4.4MPa，压折比1.4，软化系数0.72；
(7)、在基板材外侧喷涂界面剂形成界面层
在基板材外侧形成界面层具体方法同步骤(2)；
(8)、机喷水泥基保温砂浆
在步骤(7)形成的界面层外侧机喷25mm～30mm厚的水泥基保温砂浆，水泥基保温砂浆包括以下重量份原料：水泥40～50份、粉煤灰20～35份、灰钙3～5份、EPS颗粒1～1.5份、纤维素醚1～2份、胶粉3～4份，水泥基保温砂浆性能为：用水量1:0.74,、干密度412kg/m3，抗折0.67MPa，抗压0.89MPa，软化系数0.65；
(9)、抹抗裂砂浆并涂反射隔热涂料
在步骤(8)的保温层外侧抹厚度为3～5mm的抗裂砂浆，抗裂砂浆包括以下重量份原料：水泥30～40份、砂50～60份、半水石膏2～5份、CaO 2～3份、减水剂0.2～1份、纤维素醚1～2份、胶粉3～4份，抗裂砂浆的技术性能为：用水量0.23、抗折1.85MPa,抗压4.7MPa，压折比2.5，软化系数1.05；
反射隔热涂料包括以下重量份原料：纯丙乳液50～60份、玻璃微珠5～15份、金红石型钛白粉5～10份、消泡剂0.1～0.5份、纤维素醚0.1～0.2份、成膜助剂3～5份、流平剂0.8～1份、中和剂0.1～0.3份、防腐剂0.1～0.3份、防冻剂0.5～2份、水10～15份，反射隔热涂料制备工艺如下：
S1、将水置于容器中，加入以上原料的三分之二的消泡剂、成膜助剂、纤维素醚、中和剂、防腐剂、防冻剂，高速分散，使其完全融解；
S2、缓缓加入金红石型钛白粉，保持高分散速率，直至分散均匀，成为白色浓稠状细腻白浆；
S3、分批次将上述浆料加入纯丙乳液中，低速分散，直至体系均匀；
S4、缓慢加入玻璃微珠，降低分散速率，直至分散均匀；
S5、用纤维素醚、流平剂调节粘度和流动度，并加入剩余的消泡剂，低速分散，直至体系均匀。
2.根据权利要求1所述的钢构“机喷-氟石膏-反射隔热涂料”围护保温复合墙***，其特征在于，步骤(6)使用石膏硅藻泥替换石膏腻子，石膏硅藻泥包括以下重量份原料：石膏20～35份、硅藻泥25～45份、碳酸钙20～45份、纤维素醚1～2份、胶粉3～4份，石膏硅藻泥技术性能为：甲醛净化性能85％、甲醛净化效果持久性70％、防霉菌性能O级、防霉菌耐久性能1级。
3.根据权利要求1所述的钢构“机喷-氟石膏-反射隔热涂料”围护保温复合墙***，其特征在于，步骤(1)中的中密度水泥纤维板厚度为9mm，镀锌钢板网厚度为0.6mm。
4.根据权利要求1所述的钢构“机喷-氟石膏-反射隔热涂料”围护保温复合墙***，其特征在于，机喷使用的喷涂机喷口压力为0.3～0.5MPa，喷嘴直径为25mm，喷管管道直径为25mm，水平输送距离为40m，垂直输送距离为50m。
CN201610196171.5A 2016-03-31 2016-03-31 钢构“机喷-氟石膏-反射隔热涂料”围护保温复合墙*** Active CN105906239B (zh)