CN105887489A - Anti-pilling agent for knitting, and preparation method and application thereof - Google Patents
Anti-pilling agent for knitting, and preparation method and application thereof Download PDFInfo
- Publication number
- CN105887489A CN105887489A CN201610286059.0A CN201610286059A CN105887489A CN 105887489 A CN105887489 A CN 105887489A CN 201610286059 A CN201610286059 A CN 201610286059A CN 105887489 A CN105887489 A CN 105887489A
- Authority
- CN
- China
- Prior art keywords
- parts
- fluffing
- globule
- knitting
- polyethylene glycol
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an anti-pilling agent for knitting, and a preparation method and application thereof. The anti-pilling agent for the knitting is prepared from the following raw components in parts by mass: 15 to 20 parts of dehydrated sorbitan fatty acid ester polyoxyethylene ether, 8 to 10 parts of stearic acid, 35 to 40 parts of rosin ethyl ester, 10 to 15 parts of hydrogenated rosin methaester, 15 to 20 parts of methyl laurate, 10 to 20 parts of polyethylene glycol, 3 to 5 parts of dicarbonate, 3 to 5 parts of zinc nitrate, 2 to 3 parts of potassium bicarbonate, 10 to 12 parts of glycerinum, and 180 to 190 parts of water. The raw components of the anti-pilling agent for the knitting disclosed by the invention have a very good synergistic effect; the obtained treatment agent has very high stability; a knitted fabric which is treated by the anti-pilling agent is durable and wear-resistant and does not pill.
Description
Technical field
The present invention relates to a kind of for knitting anti-fluffing globule, its preparation method and application thereof, belong to knitting field.
Background technology
Knitted fabric is various in style, the most all kinds of looped fabrics, sweater, woollen sweater etc., and these knitted fabrics are in actual dress
With in washing process, due to constantly by either large or small friction so that the fiber of knitted surfaces exposes the surface of fabric,
At fabric face, young pilose antler occurs, and these young pilose antlers can form many spherical granules by tied up in knots mutually in the course of time, be commonly called as
Ball, these highlight the ball top in fabric exterior, the attractive in appearance of knitted fabric and wearability are had serious impact, along with life
The raising that running water is flat, people are more and more higher to the requirement of appearance of fabrics and wearability, therefore, fabric carried out anti-fluffing
Balling-up arranges, and improves wearing comfort and the quality of fabric, is increasingly subject to the attention of domestic and international dyeing and finishing worker.
Summary of the invention
In order to solve the defect such as easy balling-up of knitted fabric in prior art, the present invention provide a kind of for knitting anti-fluffing globule,
Its preparation method and application thereof.
For solving above-mentioned technical problem, the technical solution adopted in the present invention is as follows:
A kind of for knitting anti-fluffing globule, its raw material components includes: sorbitan fatty acid ester polyoxyethylene ether 15-20
Part, stearic acid 8-10 part, Rosin Ethyl 35-40 part, hercolyn D 10-15 part, methyl laurate 15-20 part, poly-
Ethylene glycol 10-20 part, sodium bicarbonate 3-5 part, zinc nitrate 3-5 part, potassium bicarbonate 2-3 part, glycerol 10-12 part and water 180-190
Part, described number is mass fraction.
In order to improve anti-pilling effect further, it is preferable that Polyethylene Glycol is polyethylene glycol 1500 0.
As a kind of preferred version of the application, the raw material components for knitting anti-fluffing globule includes: Sorbitan alcohol ester
Fat acid ester polyoxyethylene ether 18 parts, stearic acid 9 parts, Rosin Ethyl 38 parts, hercolyn D 12 parts, methyl laurate 18
Part, Polyethylene Glycol 15 parts, sodium bicarbonate 4 parts, zinc nitrate 4 parts, potassium bicarbonate 3 parts, glycerol 11 parts and 185 parts of water, described
Number is mass fraction.
In order to improve anti-pilling effect further, it is preferable that the raw material components for knitting anti-fluffing globule also includes benzoic acid
Ethyl ester 6-9 part, described number is mass fraction.
In order to improve the stability of products obtained therefrom further, it is preferable that the raw material components for knitting anti-fluffing globule also includes
Lauric acid 5-8 part, described number is mass fraction.
The above-mentioned preparation method for knitting anti-fluffing globule, the following steps including connected in order:
A, Rosin Ethyl and hercolyn D heated and stirred are melted；
B, sorbitan fatty acid ester polyoxyethylene ether and stearic acid are mixed with water, be then heated to 90 DEG C；
C, by step B gained material in instill the step A gained material being in stirring with the speed of 40/min, turn
After success, remaining step B gained material is poured in step A gained material together mutually；
D, Polyethylene Glycol, sodium bicarbonate, zinc nitrate and potassium bicarbonate are mixed, add in step C gained material；
E, methyl laurate and glycerol mixing, add in step D gained material, and be 60-65 DEG C, mixing speed in temperature
Under conditions of 1300r/min, continue stirring 10-15 minute, to obtain final product.
Further preferably, the mixing speed in step C is 2000-2100r/min.
If raw material components also includes ethyl benzoate and lauric acid, then ethyl benzoate in step with Rosin Ethyl and hydrogenation
Abalyn heated and stirred together melts；Lauric acid in stepb with sorbitan fatty acid ester polyoxyethylene ether and tristearin
Acid mixes with water together.
The above-mentioned application for knitting anti-fluffing globule, the consumption for knitting anti-fluffing globule is every gram of knitted fabric
0.02-0.03 gram.
The NM technology of the present invention is all with reference to prior art.
The present invention has good cooperative effect, gained inorganic agent between each raw material components of knitting anti-fluffing globule
There is good stability, with prolonged endurable, the not balling-up of its knitted fabric processed.
Detailed description of the invention
In order to be more fully understood that the present invention, it is further elucidated with present disclosure below in conjunction with embodiment, but present disclosure
It is not limited solely to the following examples.
Embodiment 1
Raw material components for knitting anti-fluffing globule includes: sorbitan fatty acid ester polyoxyethylene ether (Tween 80
Hundred million auxiliary reagent factories of Xingtai City stile) 18 parts, stearic acid 9 parts, Rosin Ethyl 38 parts, hercolyn D 12 parts, lauric acid first
Ester 18 parts, Polyethylene Glycol 15 parts, sodium bicarbonate 4 parts, zinc nitrate 4 parts, potassium bicarbonate 3 parts, glycerol 11 parts, benzoic acid second
Ester 7 parts, lauric acid 6 parts and 185 parts of water, described number is mass fraction.
The above-mentioned preparation method for knitting anti-fluffing globule, the following steps including connected in order:
A, Rosin Ethyl, ethyl benzoate and hercolyn D heated and stirred are melted；
B, sorbitan fatty acid ester polyoxyethylene ether, lauric acid and stearic acid and water are mixed, be then heated to 90 DEG C；
C, step B gained material is being instilled step A being in stirring (2100r/min) with the speed of 40/min
In gained material, after phase inversion success, remaining step B gained material is poured in step A gained material together；
D, Polyethylene Glycol, sodium bicarbonate, zinc nitrate and potassium bicarbonate are mixed, add in step C gained material；
E, methyl laurate and glycerol mixing, add in step D gained material, and temperature be 60 DEG C, mixing speed be
Under conditions of 1300r/min, continue stirring 15 minutes, to obtain final product.
Embodiment 2
Substantially the same manner as Example 1, except that: the raw material components for knitting anti-fluffing globule includes: dehydration mountain
Pears alcohol fatty acid ester polyoxyethylene ether (hundred million auxiliary reagent factories of Tween 80 Xingtai City stile) 15 parts, stearic acid 8 parts, Rosin Ethyl
35 parts, hercolyn D 10 parts, methyl laurate 15 parts, polyethylene glycol 1500 0 10 parts, sodium bicarbonate 3 parts,
Zinc nitrate 3 parts, potassium bicarbonate 2 parts, glycerol 10 parts, ethyl benzoate 6 parts, lauric acid 5 parts and 180 parts of water, institute
Stating number is mass fraction.
Embodiment 3
Substantially the same manner as Example 1, except that: the raw material components for knitting anti-fluffing globule includes: dehydration mountain
Pears alcohol fatty acid ester polyoxyethylene ether (hundred million auxiliary reagent factories of Tween 80 Xingtai City stile) 20 parts, stearic acid 10 parts, Colophonium second
Ester 40 parts, hercolyn D 15 parts, methyl laurate 20 parts, polyethylene glycol 1500 0 20 parts, sodium bicarbonate 5
Part, zinc nitrate 5 parts, potassium bicarbonate 3 parts, glycerol 12 parts, ethyl benzoate 9 parts, lauric acid 8 parts and 190 parts of water,
Described number is mass fraction.
Being impregnated with the knitting anti-fluffing globule that is used for of the various embodiments described above gained respectively by plain, consumption is every gram of knitted fabric
0.02 gram of inorganic agent, then dries, and gained knitted fabric No. 60 sand paper bi-directional frictions 20 times, without any pilling effect；By institute
Obtaining knitted fabric and be made as medicated clothing, washing machine washing is once every other day, without any pilling effect after persistently wearing 2 months.
Claims (9)
1. one kind is used for knitting anti-fluffing globule, it is characterised in that: its raw material components includes: sorbitan fatty acid
Ester polyoxyethylene ether 15-20 part, stearic acid 8-10 part, Rosin Ethyl 35-40 part, hercolyn D 10-15 part, Laurel
Acid methyl ester 15-20 part, Polyethylene Glycol 10-20 part, sodium bicarbonate 3-5 part, zinc nitrate 3-5 part, potassium bicarbonate 2-3 part, sweet
Oil 10-12 part and water 180-190 part, described number is mass fraction.
2. as claimed in claim 1 for knitting anti-fluffing globule, it is characterised in that: Polyethylene Glycol is Polyethylene Glycol
15000。
3. as claimed in claim 1 or 2 for knitting anti-fluffing globule, it is characterised in that: its raw material components includes:
Sorbitan fatty acid ester polyoxyethylene ether 18 parts, stearic acid 9 parts, Rosin Ethyl 38 parts, hercolyn D 12 parts,
Methyl laurate 18 parts, Polyethylene Glycol 15 parts, sodium bicarbonate 4 parts, zinc nitrate 4 parts, potassium bicarbonate 3 parts, glycerol 11 parts and
185 parts of water, described number is mass fraction.
4. as claimed in claim 1 or 2 for knitting anti-fluffing globule, it is characterised in that: its raw material components also includes
Ethyl benzoate 6-9 part, described number is mass fraction.
5. as claimed in claim 1 or 2 for knitting anti-fluffing globule, it is characterised in that: its raw material components also includes
Lauric acid 5-8 part, described number is mass fraction.
6. the preparation method for knitting anti-fluffing globule described in claim 1-5 any one, it is characterised in that: bag
Include following steps connected in order:
A, Rosin Ethyl and hercolyn D heated and stirred are melted；
B, sorbitan fatty acid ester polyoxyethylene ether and stearic acid are mixed with water, be then heated to 90 DEG C；
C, by step B gained material in instill the step A gained material being in stirring with the speed of 40/min, turn
After success, remaining step B gained material is poured in step A gained material together mutually；
D, Polyethylene Glycol, sodium bicarbonate, zinc nitrate and potassium bicarbonate are mixed, add in step C gained material；
E, methyl laurate and glycerol mixing, add in step D gained material, and be 60-65 DEG C, mixing speed in temperature
Under conditions of 1300r/min, continue stirring 10-15 minute, to obtain final product.
7. preparation method as claimed in claim 6, it is characterised in that: the mixing speed in step C is 2000-2100r/min.
Preparation method the most as claimed in claims 6 or 7, it is characterised in that: if raw material components also include ethyl benzoate and
Lauric acid, then ethyl benzoate in step together with Rosin Ethyl and hercolyn D heated and stirred melt；Lauric acid
Mix with water together with sorbitan fatty acid ester polyoxyethylene ether and stearic acid in stepb.
9. the application for knitting anti-fluffing globule described in claim 1-5 any one, it is characterised in that: for pin
The consumption of the anti-fluffing globule knitted is every gram of knitted fabric 0.02-0.03 gram.