CN105803674A - 一种高弹透气仿乳胶直立棉的制备方法及其在家纺产品上的应用 - Google Patents
一种高弹透气仿乳胶直立棉的制备方法及其在家纺产品上的应用 Download PDFInfo
- Publication number
- CN105803674A CN105803674A CN201410849227.3A CN201410849227A CN105803674A CN 105803674 A CN105803674 A CN 105803674A CN 201410849227 A CN201410849227 A CN 201410849227A CN 105803674 A CN105803674 A CN 105803674A
- Authority
- CN
- China
- Prior art keywords
- web
- preparation
- upright cotton
- latex
- drafting
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开的作为本发明第一方面的一种高弹透气仿乳胶直立棉的制备方法,包括以下步骤:原料称重→配比混合→开松梳棉→梳棉铺网→棉网牵伸→棉网喷胶→高温处理→冷却定型→收卷切边→成品入库。还公开了由上述的高弹透气仿乳胶直立棉的制备方法所制备的直立棉在家纺产品上的应用。本发明的高弹透气仿乳胶直立棉的制备方法所制备的直立棉具有良好的抗压性、回弹性及隔热性、质量轻、阻燃等性能,尤其适于床褥填充物,对人体无害。另外,该种直立棉被应用在家纺产品上,能使消费者拥有一个满意舒适的睡眠,其凉爽和舒适的触感加上纤维本身卓越的透气性与回弹性,具有广阔的市场前景。
Description
技术领域
本发明属于家纺织物技术领域,具体涉及一种高弹透气仿乳胶直立棉的制备方法及其在家纺产品上的应用。
背景技术
发泡型聚氨酯(PU)材料(海绵、泡棉)是当今世界上应用极为广泛的一种材料,涉及汽车工业、胸围内衣制造业及高档家具制造业等各个领域。但众所周知,聚氨酯材料并非是一种环保材料,其化学结构不稳定,易氧化分解,最优良的发泡型聚氨酯材料也会在六个月后开始分解,分解后会形成有毒于环境、人体的气体和物质,化学助剂基本上都是化工产品,大都是含苯类化学物质,都具有致癌的可能,有害身体健康。
3D直立棉作为一种新型的环保型非织造材料,有着发泡型聚氨酯材料所不具备的更优越的性能,不仅可取代发泡型聚氨酯材料在不同领域的应用,更能应用于许多发泡型聚氨酯材料所不能适用的不同领域,在健康环保节约能源方面具有革命性的意义,具有巨大的市场空间和经济社会效益。另外,3D直立棉具有如海绵状的三维立体构造的直立纤维网结构或蜂窝状纤维网结构等,不同于传统非织造材料的平行纤维网结构。直立棉因其特殊的物理构造具有众多海绵和其他普通纤维材料不可比拟的优势,如可循环回收使用,不易分解,不会发黄,不会产生有毒物质,阻燃性能强,高回弹,高抗压,轻质感,高透气性、不易滋生有害细菌,可操作性强,扩展性强等特点,应用前景广阔。
经上述介绍,3D直立棉拥有较多优势,并且非常适合用于家纺产品上,但目前市场上的家纺产品并未存在采用3D直立棉制成的,为此,本申请人进行了有益的探索和尝试,找到了将适合用于家纺产品上的3D直立棉,下面将要介绍的技术方案便是在这种背景下产生的。
发明内容
本发明的目的之一是提供一种高弹透气仿乳胶直立棉的制备方法。
本发明的目的之二是提供一种由上述的高弹透气仿乳胶直立棉的制备方法所制备的直立棉在家纺产品上的应用。
作为本发明第一方面的一种高弹透气仿乳胶直立棉的制备方法,包括以下步骤:原料称重→配比混合→开松梳棉→梳棉铺网→棉网牵伸→棉网喷胶→高温处理→冷却定型→收卷切边→成品入库;
在所述原料称重步骤中,所述原料由多功能聚酯纤维45~50%,低熔点纤维18~23%,进口3D三维中空纤维27~32%;;
在所述棉网牵伸步骤中,采用多区小倍数的棉网牵伸机对棉网横向排列的纤维部分拉伸到纵向,并在牵伸过程中,其牵伸倍数应逐步加大,以使得对整个棉网宽度控制一致,棉网牵伸机的罗拉钳口距为2~4mm,其钳口压力为170~190N。。
在本发明的一个优选实施例中,在所述梳棉铺网步骤中,铺网机的工作环境的相对湿度为40%,解决了棉网经梳理后产生较多静电的问题。
在本发明的一个优选实施例中,在所述梳棉铺网步骤中,棉网中加入0.1~0.3%抗静电剂,解决了棉网经梳理后产生较多静电的问题。
在本发明的一个优选实施例中,在所述梳棉铺网步骤中,在铺网机的一对摆动罗拉上沿轴向设置有前、后压风板,以使得棉网中的上层棉网在铺叠换向时保持平衡状态,解决了棉网漂移问题。
在本发明的一个优选实施例中,在所述棉网牵伸步骤中,所述棉网牵伸机的摆动罗拉的两端的支撑板上各安装一双活塞杆气缸,以解决所述棉网牵伸机的摆动罗拉在换向时出现的纤网堆积问题。
作为本发明第二方面的由上述的高弹透气仿乳胶直立棉的制备方法所制备的直立棉在家纺产品上的应用,所述直立棉用于制备床垫或枕头。
本发明的高弹透气仿乳胶直立棉的制备方法所制备的直立棉具有良好的抗压性、回弹性及隔热性、质量轻、阻燃等性能,尤其适于床褥填充物,对人体无害。另外,该直立棉垂直成网的高篷松材料比非垂直成网材料显示有更高的抗压性能,在受压缩后,垂直成网材料可以比非垂直成网材料高出30-60%的厚度和隔热能力,能拥有比一般材料更优秀的隔热性,更加保暖,更加抗压。该种直立棉被应用在家纺产品上,能使消费者拥有一个满意舒适的睡眠,其凉爽和舒适的触感加上纤维本身卓越的透气性与回弹性,必将使其成为家纺市场上一枝独秀的原料,具有广阔的市场前景。
具体实施方式
为了使本发明实现的技术手段、创作特征、达成目的与功效易于明白了解,下面进一步阐述本发明。
实施例1
本实施例的一种高弹透气仿乳胶直立棉的制备方法,包括以下步骤:原料称重→配比混合→开松梳棉→梳棉铺网→棉网牵伸→棉网喷胶→高温处理→冷却定型→收卷切边→成品入库。
在所述原料称重步骤中,所述原料由多功能聚酯纤维45%、低熔点纤维18%、进口3D三维中空纤维27%组成。
在所述棉网牵伸步骤中,采用多区小倍数的棉网牵伸机对棉网横向排列的纤维部分拉伸到纵向,并在牵伸过程中,其牵伸倍数应逐步加大,以使得对整个棉网宽度控制一致,棉网牵伸机的罗拉钳口距为2mm,其钳口压力为170N(请补充具体实施例的数据)。
在本发明的一个优选实施例中,在所述梳棉铺网步骤中,铺网机的工作环境的相对湿度为40%,又或者,在棉网中加入0.1%抗静电剂,两者都可以解决棉网经梳理后产生较多静电的问题。
在所述梳棉铺网步骤中,在铺网机的一对摆动罗拉上沿轴向设置有前、后压风板,以使得棉网中的上层棉网在铺叠换向时保持平衡状态,解决了棉网漂移问题。
在所述棉网牵伸步骤中,所述棉网牵伸机的摆动罗拉的两端的支撑板上各安装一双活塞杆气缸,以解决所述棉网牵伸机的摆动罗拉在换向时出现的纤网堆积问题。
实施例2
本实施例的一种高弹透气仿乳胶直立棉的制备方法,包括以下步骤:原料称重→配比混合→开松梳棉→梳棉铺网→棉网牵伸→棉网喷胶→高温处理→冷却定型→收卷切边→成品入库。
在所述原料称重步骤中,所述原料由多功能聚酯纤维48%、低熔点纤维21%、进口3D三维中空纤维23%组成。
在所述棉网牵伸步骤中,采用多区小倍数的棉网牵伸机对棉网横向排列的纤维部分拉伸到纵向,并在牵伸过程中,其牵伸倍数应逐步加大,以使得对整个棉网宽度控制一致,棉网牵伸机的罗拉钳口距为3mm,其钳口压力为180N。
在所述梳棉铺网步骤中,铺网机的工作环境的相对湿度为40%,又或者,在棉网中加入0.2%抗静电剂,两者都可以解决棉网经梳理后产生较多静电的问题。
实施例3
本实施例的一种高弹透气仿乳胶直立棉的制备方法,包括以下步骤:原料称重→配比混合→开松梳棉→梳棉铺网→棉网牵伸→棉网喷胶→高温处理→冷却定型→收卷切边→成品入库。
在所述原料称重步骤中,所述原料由多功能聚酯纤维50%、低熔点纤维23%、进口3D三维中空纤维32%组成。
在所述棉网牵伸步骤中,采用多区小倍数的棉网牵伸机对棉网横向排列的纤维部分拉伸到纵向,并在牵伸过程中,其牵伸倍数应逐步加大,以使得对整个棉网宽度控制一致,棉网牵伸机的罗拉钳口距为4mm,其钳口压力为190N。
在所述梳棉铺网步骤中,铺网机的工作环境的相对湿度为40%,又或者,在棉网中加入0.3%抗静电剂,两者都可以解决棉网经梳理后产生较多静电的问题。
实施例4
将实施例1、2、3中所制备的直立棉可用于制备床垫或枕头成品,这些成品具备以下指标:
压缩回弹性:95%;
保温率:86%;
透气率:50mm/s;
重量:达到相同性能的条件下,垂直成网材料重量只有PU海绵的50%,普通非织造材料的60%;
阻燃性:好。
以上显示和描述了本发明的基本原理和主要特征和本发明的优点。本行业的技术人员应该了解,本发明不受上述实施例的限制,上述实施例和说明书中描述的只是说明本发明的原理,在不脱离本发明精神和范围的前提下,本发明还会有各种变化和改进,这些变化和改进都落入要求保护的本发明范围内。本发明要求保护范围由所附的权利要求书及其等效物界定。
Claims (6)
1.一种高弹透气仿乳胶直立棉的制备方法,包括以下步骤:原料称重→配比混合→开松梳棉→梳棉铺网→棉网牵伸→棉网喷胶→高温处理→冷却定型→收卷切边→成品入库;其特征在于,
在所述原料称重步骤中,所述原料由多功能聚酯纤维45~50%,低熔点纤维18~23%,进口3D三维中空纤维27~32%;
在所述棉网牵伸步骤中,采用多区小倍数的棉网牵伸机对棉网横向排列的纤维部分拉伸到纵向,并在牵伸过程中,其牵伸倍数应逐步加大,以使得对整个棉网宽度控制一致,棉网牵伸机的罗拉钳口距为2~4mm,其钳口压力为170~190N。
2.如权利要求1所述的高弹透气仿乳胶直立棉的制备方法,其特征在于,在所述梳棉铺网步骤中,铺网机的工作环境的相对湿度为40%。
3.如权利要求1所述的高弹透气仿乳胶直立棉的制备方法,其特征在于,在所述梳棉铺网步骤中,棉网中加入0.1~0.3%抗静电剂。
4.如权利要求1所述的高弹透气仿乳胶直立棉的制备方法,其特征在于,在所述梳棉铺网步骤中,在铺网机的一对摆动罗拉上沿轴向设置有前、后压风板。
5.如权利要求1所述的高弹透气仿乳胶直立棉的制备方法,其特征在于,在所述棉网牵伸步骤中,所述棉网牵伸机的摆动罗拉的两端的支撑板上各安装一双活塞杆气缸。
6.如权利要求1至5中任一项所述的高弹透气仿乳胶直立棉的制备方法所制备的直立棉在家纺产品上的应用,其特征在于,所述直立棉用于制备床垫或枕头。