CN105753279B - 一种淤/污泥固化剂及其使用方法 - Google Patents

一种淤/污泥固化剂及其使用方法 Download PDF

Info

Publication number
CN105753279B
CN105753279B CN201610235059.8A CN201610235059A CN105753279B CN 105753279 B CN105753279 B CN 105753279B CN 201610235059 A CN201610235059 A CN 201610235059A CN 105753279 B CN105753279 B CN 105753279B
Authority
CN
China
Prior art keywords
silt
sludge
solidifying agent
active
sludge solidifying
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201610235059.8A
Other languages
English (en)
Other versions
CN105753279A (zh
Inventor
陈士强
罗昕
黄鹏
刘亚威
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
China Power Jianshui Environmental Technology Co.,Ltd.
Original Assignee
Wuhan Meilidongfang Environment Protection Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Wuhan Meilidongfang Environment Protection Co Ltd filed Critical Wuhan Meilidongfang Environment Protection Co Ltd
Priority to CN201610235059.8A priority Critical patent/CN105753279B/zh
Publication of CN105753279A publication Critical patent/CN105753279A/zh
Application granted granted Critical
Publication of CN105753279B publication Critical patent/CN105753279B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明具体涉及一种淤/污泥固化剂及其用途。一种淤/污泥固化剂以质量百分比计，其特征在于主要组成为：纳微米改性胶凝材料60％‑75％，聚合硅酸铝铁5％‑10％，沸石粉或/和膨润土10％‑20％，生石灰5％‑15％混合而成。在淤/污泥中加入占淤/污泥总量的10％‑20％的淤/污泥固化剂，在搅拌机中混合搅拌，搅拌10－30分钟，搅拌结束后，放入阳光下照射固化完全，即能进行道路填料的铺筑施工。本发明的淤/污泥固化剂可降低高含水率淤/污泥的含水率，固化强度高，且能有效的固化淤/污泥中的重金属，达到填埋和建筑填土的要求。

Description

一种淤/污泥固化剂及其使用方法
技术领域：
本发涉及一种淤/污泥固化剂及其使用方法。
背景技术：
针对内陆城市湖泊河道众多，水底有大量的淤泥堆积。而对淤泥的采集和处理往往工程量大，耗资惊人。例如在南水北调东线工程中，产生的疏浚淤泥的征地费用就高达6.4亿元。而且这些堆放的淤泥含水率高，强度低，还含有有毒化学物质、病原生物等一些有害成分。国外不少发达国家以淤泥制造高效净化燃料、建筑材料等商业方式对淤泥进行综合开发利用。然而在国内，由于技术与经费的原因，湖泊河道疏浚淤泥最多的还是作为填筑材料，降低淤泥的含水率，提高淤泥的强度来满足土方填筑的要求。因此，国内普遍采用水泥类的无机材料对淤泥进行固化处理，然而水泥类材料用于淤泥固结时，添加量较大，而且对高含水淤泥的固化效果较差。
CN105367009A公开了一种淤泥固化剂及其制备方法和应用，该固化剂按质量份数计的组分组成为：水泥9～18份，石灰2～5份，石膏2～5份，膨润土2～5份，苛性钠0.4～1份。将上述组分在烘干炉中干燥6～8小时后，研磨后搅拌均匀得到固化剂。然而该发明固化时间较长，对高含水率淤泥固化效果不明显。
因此，需要一种高效低成本的一种淤/污泥固化材料。
发明内容：
为了解决现有淤泥固化材料中技术问题，针对湖底淤泥中含有大量的有机质和重金属等特性，本发明提供了一种性能优异的淤/污泥固化剂及其使用方法，对高含水淤泥进行固化处理，有效降低淤泥的含水率，固化淤泥中的重金属等物质，而且提高淤泥的强度，达到土方填筑的要求。
本发明的技术方案为：
一种淤/污泥固化剂，以质量百分比计，其特征在于组成为：纳微米改性胶凝材料60％-75％，聚合硅酸铝铁5％-10％，沸石粉或/和膨润土10％-20％，生石灰5％-15％混合而成。
各组分按质量百分计，所述的纳微米改性胶凝材料是按以下步骤得到的：(1)将活性SiO2 25％-40％，活性Al2O3 5％-10％，活性CaO 40％-50％，活性Fe2O3 5％-10％，活性MgO 3％-5％混合在1450℃炉中煅烧20分钟得到烧结物；(2)将得到的烧结物与CaSO4和纳米二氧化硅按1：0.05：0.02比例混合均匀，磨细至D95≤15μm，得到所述的纳微米改性胶凝材料。
所述的沸石粉或/和膨润土的细度为400目。
利用所述的淤/污泥固化剂的使用方法，其特征在于：在淤/污泥中加入占淤/污泥总量的10％-20％的淤/污泥固化剂，在搅拌机中混合搅拌，搅拌10－30分钟，搅拌结束后，放入阳光下照射固化完全，即能进行道路填料的铺筑施工。
本发明的淤/污泥固化剂可降低高含水率淤/污泥的含水率，固化强度高，且能有效的固化淤/污泥中的重金属，达到填埋和建筑填土的要求。
具体实施方式：
结合实例对本发明做进一步的说明。
将活性SiO2 30％，活性Al2O3 10％，活性CaO 50％，活性Fe2O3 5％，活性MgO 5％混合在炉中煅烧20分钟得到烧结物；
将得到的烧结物与CaSO4和纳米二氧化硅按1：0.05：0.02比例混合均匀，磨细至D95≤15μm，得到纳微米改性胶凝材料。
表1各实施例所用原料及配比 单位％
表2.是按表1所示的实施例1～7所用原料及配比对湖底淤泥脱水固化处理的结果。
表2对淤泥的脱水固化处理效果

Claims (3)

1.一种淤/污泥固化剂，以质量百分比计，其特征在于组成为：纳微米改性胶凝材料60%-75%，聚合硅酸铝铁5%-10%，沸石粉或/和膨润土10%-20%，生石灰5%-15%混合而成；
所述的纳微米改性胶凝材料是按以下步骤得到的：（1）将活性SiO2 25%-40%，活性Al2O35%-10%，活性CaO 40%-50%，活性Fe2O3 5%-10%，活性MgO 3%-5%混合在1450℃炉中煅烧20分钟得到烧结物；（2）将得到的烧结物与CaSO4和纳米二氧化硅按1：0.05：0.02比例混合均匀，磨细至D95≤15μm，得到所述的纳微米改性胶凝材料。
2.如权利要求1所述的淤/污泥固化剂，其特征在于：所述的沸石粉或/和膨润土的细度为400目。
3.利用权利要求1－2之一所述的淤/污泥固化剂的使用方法，其特征在于：在淤/污泥中加入占淤/污泥总量的10%-20%的淤/污泥固化剂，在搅拌机中混合搅拌，搅拌10－30分钟，搅拌结束后，放入阳光下照射固化完全，即能进行道路填料的铺筑施工。
CN201610235059.8A 2016-04-15 2016-04-15 一种淤/污泥固化剂及其使用方法 Active CN105753279B (zh)