CN105482360A - High-performance glass bead filled phenolic aldehyde composite material - Google Patents
High-performance glass bead filled phenolic aldehyde composite material Download PDFInfo
- Publication number
- CN105482360A CN105482360A CN201511006551.XA CN201511006551A CN105482360A CN 105482360 A CN105482360 A CN 105482360A CN 201511006551 A CN201511006551 A CN 201511006551A CN 105482360 A CN105482360 A CN 105482360A
- Authority
- CN
- China
- Prior art keywords
- parts
- composite material
- phenolic aldehyde
- aldehyde composite
- performance glass
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a high-performance glass bead filled phenolic aldehyde composite material. The high-performance glass bead filled phenolic aldehyde composite material is prepared from the following raw materials in parts by weight: 6-8 parts of edible salad oil, 7-15 parts of white carbon black, 5-13 parts of a softening agent, 1.6-2.5 parts of a vulcanization system, 0.4-0.7 part of a scorch retarder, 3-4.6 parts of a curing agent, 25-34 parts of glass beads, 10-15 parts of reinforced fibers, 1-4 parts of olive oil, 12-17 parts of Suzhou clay, 3-5 parts of diatom ooze, 1-4 parts of glyceryl behenate, 2-5 parts of magnesium oxide, 8-13 parts of anhydrous sodium sulfate, 2-4 parts of phosphoric acid, 1-3 parts of iron oxide and 30-45 parts of phenolic resin. The high-performance glass bead filled phenolic aldehyde composite material has the beneficial effects that the insulating property of a phenolic aldehyde composite material can be improved, meanwhile, the mechanical strength and the weight of the phenolic aldehyde composite material are reduced, and the thermal resistance of the phenolic aldehyde composite material is improved.
Description
Technical field
The present invention relates to a kind of high performance glass microballon filled phenolic matrix material.
Background technology
Resol realizes industrialized synthetic resins the earliest in the world, so far the history of existing more than 90 year.Because its raw material sources is wide, production technique and equipment simple, and, product have unique heat-resisting, resistance to so, the premium properties such as electric insulation, mechanical property and dimensional stabilizing, therefore, it has become the indispensable material of industrial sector, and tool has been widely used.And glass microballon is a kind of great thermotolerance, the filler of light specific gravity, can improve the resistance toheat of material.Light specific gravity volume is large.The density of hollow glass micropearl is about ten parts of traditional stopping composition density of particle, greatly can alleviate the basic weight of product after filling, and it has sound insulation, every thermal property, is the splendid weighting agent as various insulation, acoustical insulation products.The performance of phenolic composite is can be good at improving by adding glass microballon.
Summary of the invention
For the deficiencies in the prior art, the problem to be solved in the present invention is, provides a kind of glass microballon filled phenolic matrix material, can improve the insulating property of phenolic composite, and physical strength and weight are alleviated simultaneously, and resistance toheat is improved.
For solving prior art problem, technical scheme provided by the invention is, a kind of high performance glass microballon filled phenolic matrix material, and it is made up of the raw material of following parts by weight:
Edible salad oil 6-8 part, white carbon black 7-15 part, tenderizer 5-13 part, vulcanization system 1.6-2.5 part, scorch retarder 0.4-0.7 part, solidifying agent 3-4.6 part, glass microballon 25-34 part, fortifying fibre 10-15 part, sweet oil 1-4 part, Suzhou soil 12-17 part, diatom ooze 3-5 part, Glyceryl Behenate 1-4 part, magnesium oxide 2-5 part, anhydrous sodium sulphate 8-13 part, phosphoric acid 2-4 part, ferric oxide 1-3 part, resol 30-45 part.
Further, a kind of high performance glass microballon filled phenolic matrix material, it is made up of the raw material of following parts by weight:
Edible salad oil 6-8 part, white carbon black 7-15 part, tenderizer 5-13 part, vulcanization system 1.6-2.5 part, scorch retarder 0.4-0.7 part, solidifying agent 3-4.6 part, glass microballon 25-34 part, fortifying fibre 10-15 part, sweet oil 1-4 part, Suzhou soil 12-17 part, diatom ooze 3-5 part, Glyceryl Behenate 1-4 part, magnesium oxide 2-5 part, anhydrous sodium sulphate 8-13 part, phosphoric acid 2-4 part, ferric oxide 1-3 part, resol 30-45 part.
The invention has the beneficial effects as follows: glass microballon filled phenolic matrix material of the present invention, can improve the insulating property of phenolic composite, physical strength and weight are alleviated simultaneously, and resistance toheat is improved.
Embodiment
embodiment 1
A kind of high performance glass microballon filled phenolic matrix material, it is made up of the raw material of following parts by weight:
Edible salad oil 6 parts, white carbon black 7 parts, tenderizer 5 parts, vulcanization system 1.6 parts, scorch retarder 0.4 part, 3 parts, solidifying agent, glass microballon 25 parts, fortifying fibre 10 parts, 1 part, sweet oil, 12 parts, Suzhou soil, diatom ooze 3 parts, Glyceryl Behenate 1 part, 2 parts, magnesium oxide, anhydrous sodium sulphate 8 parts, phosphoric acid 2 parts, ferric oxide 1 part, 30 parts, resol.
embodiment 2
A kind of high performance glass microballon filled phenolic matrix material, it is made up of the raw material of following parts by weight:
Edible salad oil 8 parts, white carbon black 15 parts, tenderizer 13 parts, vulcanization system 2.5 parts, scorch retarder 0.7 part, 4.6 parts, solidifying agent, glass microballon 34 parts, fortifying fibre 15 parts, 4 parts, sweet oil, 17 parts, Suzhou soil, diatom ooze 5 parts, Glyceryl Behenate 4 parts, 5 parts, magnesium oxide, anhydrous sodium sulphate 13 parts, phosphatase 24 part, ferric oxide 3 parts, 45 parts, resol.
embodiment 3
A kind of high performance glass microballon filled phenolic matrix material, it is made up of the raw material of following parts by weight:
Edible salad oil 6-8 part, white carbon black 7-15 part, tenderizer 5-13 part, vulcanization system 1.6-2.5 part, scorch retarder 0.4-0.7 part, solidifying agent 3-4.6 part, glass microballon 25-34 part, fortifying fibre 10-15 part, sweet oil 1-4 part, Suzhou soil 12-17 part, diatom ooze 3-5 part, Glyceryl Behenate 1-4 part, magnesium oxide 2-5 part, anhydrous sodium sulphate 8-13 part, phosphoric acid 2-4 part, ferric oxide 1-3 part, resol 30-45 part.
Claims (2)
1. a high performance glass microballon filled phenolic matrix material, is characterized in that: it is made up of the raw material of following parts by weight:
Edible salad oil 6-8 part, white carbon black 7-15 part, tenderizer 5-13 part, vulcanization system 1.6-2.5 part, scorch retarder 0.4-0.7 part, solidifying agent 3-4.6 part, glass microballon 25-34 part, fortifying fibre 10-15 part, sweet oil 1-4 part, Suzhou soil 12-17 part, diatom ooze 3-5 part, Glyceryl Behenate 1-4 part, magnesium oxide 2-5 part, anhydrous sodium sulphate 8-13 part, phosphoric acid 2-4 part, ferric oxide 1-3 part, resol 30-45 part.
2. high performance glass microballon filled phenolic matrix material according to claim 1, is characterized in that: it is made up of the raw material of following parts by weight:
Edible salad oil 6-8 part, white carbon black 7-15 part, tenderizer 5-13 part, vulcanization system 1.6-2.5 part, scorch retarder 0.4-0.7 part, solidifying agent 3-4.6 part, glass microballon 25-34 part, fortifying fibre 10-15 part, sweet oil 1-4 part, Suzhou soil 12-17 part, diatom ooze 3-5 part, Glyceryl Behenate 1-4 part, magnesium oxide 2-5 part, anhydrous sodium sulphate 8-13 part, phosphoric acid 2-4 part, ferric oxide 1-3 part, resol 30-45 part.