CN105481380A - 一种低成本新型钢纤维耐火浇注料 - Google Patents
一种低成本新型钢纤维耐火浇注料 Download PDFInfo
- Publication number
- CN105481380A CN105481380A CN201410478089.2A CN201410478089A CN105481380A CN 105481380 A CN105481380 A CN 105481380A CN 201410478089 A CN201410478089 A CN 201410478089A CN 105481380 A CN105481380 A CN 105481380A
- Authority
- CN
- China
- Prior art keywords
- parts
- steel fiber
- particle size
- granularity
- standard
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种低成本新型钢纤维耐火浇注料它是由下述原料按照重量份配制而成:粒度8-5mm高铝矾土2.3份,0.075mm<粒度<5mm高铝矾土2.5份,粒度≤0.075mm高铝矾土0.7份,粒度3-1mm棕刚玉颗粒料1.5份,粒度≤0.025mm氧化铝超微粉0.5份,粒度≤0.075mmSiC细粉0.8份,粒度<0.019mmSiO2微粉0.4份,纯铝酸钙水泥0.7份,粒度<0.053mm锆英砂0.5份,耐热钢纤维0.3份,防爆钢纤维0.04份,总物料重量0.1%的三聚磷酸钠,总物料重量0.06%的六偏磷酸钠。该产品耐压强度高、抗折强度高、荷重软化温度高、抗热震稳定性好、在高温下具有微膨胀的特性、耐磨性能好等优点。
Description
技术领域
本发明涉及耐火浇注料技术领域,尤其是涉及一种成本低、可替代刚玉质的新型钢纤维浇注料。
背景技术
在水泥窑窑口、预热器、篦冷机等窑炉内,传统采用刚玉质高强度浇注料,由于刚玉材料成本高,企业的原料成本就高。
发明内容
本发明的目的在于提供一种成本低、可替代刚玉质浇注料的新型钢纤维耐火浇注料。
为实现上述目的,本发明可采取下述技术方案:
本发明所述的一种低成本新型钢纤维耐火浇注料,是由原料高铝矾土、棕刚玉、氧化铝超微粉、SiC细粉、SiO2微粉、纯铝酸钙水泥、锆英砂、耐热钢纤维、防爆钢纤维和三聚磷酸钠、六偏磷酸钠按照下述重量份配制而成:
粒度8-5mm高铝矾土2.3份,0.075mm<粒度<5mm高铝矾土2.5份,粒度≤0.075mm高铝矾土0.7份,粒度3-1mm棕刚玉颗粒料1.5份,粒度≤0.025mm氧化铝超微粉0.5份,粒度≤0.075mmSiC细粉0.8份,粒度<0.019mmSiO2微粉0.4份,纯铝酸钙水泥0.7份,粒度<0.053mm锆英砂0.5份,耐热钢纤维0.3份,防爆钢纤维0.04份,总物料重量0.1%的三聚磷酸钠,总物料重量0.06%的六偏磷酸钠。
所述铝矾土的标准为AI2O3≥82%,Fe2O3<1.5%。
所述棕刚玉的标准为AI2O3≥95%,Fe2O3<0.30%。
所述SiC细粉的标准为SiC≥98%。
所述SiO2微粉的标准为SiO2≥98%。
所述纯铝酸钙水泥水泥的标准为AI2O3≥70%。
所述氧化铝粉的标准为AI2O3≥98%。
本发明的优点在于耐压强度高、抗折强度高、荷重软化温度高、抗热震稳定性好、在高温下具有微膨胀的特性、耐磨性能好等优点,虽然氧化铝含量相对于传统的高强度浇注料有所降低,但由于本产品的水泥用量大大降低,使其中的氧化钙含量大大降低,其中掺加的碳化硅在中温时能够起到增加强度、增强蠕变性能、提高耐火度的作用而弥补了氧化铝含量不高的缺憾,相对于传统的高强度浇注料来说具有更高的耐压强度和抗折强度,因为采用了高铝矾土代替了传统高强度浇注料中的部分刚玉材料,成本可比传统高强度浇注料降低约2/5,间接降低了因生产原料产生的消耗,同时使用寿命也比传统高强度浇注料有所提高。该产品可广泛应用与水泥窑窑口、预热器、篦冷机等对强度要求高、使用条件恶劣的其它窑炉,是替代普通钢纤维浇注料的理想新产品。
具体实施方式
本发明所述的低成本新型钢纤维耐火浇注料它是由原料铝矾土、棕刚玉、氧化铝微粉、碳化硅、SiO2微粉、纯铝酸钙水泥、耐热钢纤维、防爆钢纤维和三聚磷酸钠、六偏磷酸钠按照下述重量份配制而成:
粒度8-5mm高铝矾土2.3份,0.075mm<粒度<5mm高铝矾土2.5份,粒度≤0.075mm高铝矾土0.7份,粒度3-1mm棕刚玉颗粒料1.5份,粒度≤0.025mm氧化铝超微粉0.5份,粒度≤0.075mmSiC细粉0.8份,粒度<0.019mmSiO2微粉0.4份,纯铝酸钙水泥0.7份,粒度<0.053mm锆英砂0.5份,耐热钢纤维0.3份,防爆钢纤维0.04份,总物料重量0.1%的三聚磷酸钠,总物料重量0.06%的六偏磷酸钠。
用破碎机、圆锥破碎机将物料破碎后,除去纯铝酸钙水泥和三聚磷酸钠、六偏磷酸钠后,将上述原料准确称量后置于强制搅拌机中混合均匀后,装袋包装,纯铝酸钙水泥和三聚磷酸钠、六偏磷酸钠单独包装。
本项发明浇注料的施工加水量一般为干料总重量的5-6%。其它使用方法按一般浇注料施工方法进行,无需经过特殊养护。
采用铝矾土的标准为AI2O3≥82%,Fe2O3<1.5%。
采用棕刚玉的标准为AI2O3≥95%,Fe2O3<0.30%。
采用SiC细粉的标准为SiC≥98%。
采用SiO2微粉的标准为SiO2≥98%。
采用纯铝酸钙水泥水泥的标准为AI2O3≥70%。
采用氧化铝粉的标准为AI2O3≥98%。
Claims (7)
1.一种低成本新型钢纤维耐火浇注料其特征在于:它是由原料高铝矾土、棕刚玉、氧化铝超微粉、SiC细粉、SiO2微粉、纯铝酸钙水泥、锆英砂、耐热钢纤维、防爆钢纤维和三聚磷酸钠、六偏磷酸钠按照下述重量份配制而成:
粒度8-5mm高铝矾土2.3份,0.075mm<粒度<5mm高铝矾土2.5份,粒度≤0.075mm高铝矾土0.7份,粒度3-1mm棕刚玉颗粒料1.5份,粒度≤0.025mm氧化铝超微粉0.5份,粒度≤0.075mmSiC细粉0.8份,粒度<0.019mmSiO2微粉0.4份,纯铝酸钙水泥0.7份,粒度<0.053mm锆英砂0.5份,耐热钢纤维0.3份,防爆钢纤维0.04份,总物料重量0.1%的三聚磷酸钠,总物料重量0.06%的六偏磷酸钠。
2.根据权利要求l所述的低成本新型钢纤维耐火浇注料其特征在于:所述铝矾土的标准为AI2O3≥82%,Fe2O3<1.5%。
3.根据权利要求l所述的低成本新型钢纤维耐火浇注料其特征在于:所述棕刚玉的标准为AI2O3≥95%,Fe2O3<0.30%。
4.根据权利要求l所述的低成本新型钢纤维耐火浇注料其特征在于:所述SiC细粉的标准为SiC≥98%。
5.根据权利要求1所述的低成本新型钢纤维耐火浇注料其特征在于:所述SiO2微粉的标准为SiO2≥98%。
6.根据权利要求1所述的低成本新型钢纤维耐火浇注料其特征在于:所述纯铝酸钙水泥水泥的标准为AI2O3≥70%。
7.根据权利要求l所述的低成本新型钢纤维耐火浇注料其特征在于:所述氧化铝粉的标准为AI2O3≥98%。