CN105401434A - 混纺面料的后整理工艺 - Google Patents
混纺面料的后整理工艺 Download PDFInfo
- Publication number
- CN105401434A CN105401434A CN201510885995.9A CN201510885995A CN105401434A CN 105401434 A CN105401434 A CN 105401434A CN 201510885995 A CN201510885995 A CN 201510885995A CN 105401434 A CN105401434 A CN 105401434A
- Authority
- CN
- China
- Prior art keywords
- parts
- mass
- finishing agent
- stir
- fabric
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种混纺面料的后整理工艺,包括如下步骤:1)在35质量份去离子水中投入1~2质量份钨酸钠、4.1质量份聚氧乙烯醚、1.2质量份二氧化硅、3.1质量份双苄基膦酸单乙酯混合,搅拌均匀;2)再同时缓慢加入2.9质量份醇乙氧化物羧酸盐、3.7质量份月桂醇、0.8质量份二氧化钛、2.7质量份乙酸乙酯,继续搅拌,至充分混合均匀,制得整理剂;3)将面料在含有整理剂的浸渍液中浸轧处理,恒温烘干。本发明混纺面料的后整理工艺,其整理后的面料具有优异的阻燃、抗菌、抗皱、防静电性能,且耐洗性强。
Description
技术领域
本发明涉及混纺面料的后整理工艺。
背景技术
现有面料的阻燃、抗菌、抗皱、防静电性能和耐洗性能都有待提高。
发明内容
本发明的目的在于提供一种混纺面料的后整理工艺,其整理后的面料具有优异的阻燃、抗菌、抗皱、防静电性能,且耐洗性强。
为实现上述目的,本发明的技术方案是设计一种混纺面料的后整理工艺,包括如下步骤:
1)在35质量份去离子水中投入1~2质量份钨酸钠、4.1质量份聚氧乙烯醚、1.2质量份二氧化硅、3.1质量份双苄基膦酸单乙酯混合,搅拌均匀;
2)再同时缓慢加入2.9质量份醇乙氧化物羧酸盐、3.7质量份月桂醇、0.8质量份二氧化钛、2.7质量份乙酸乙酯,继续搅拌,至充分混合均匀,制得整理剂;
3)将面料在含有整理剂的浸渍液中浸轧处理,恒温烘干。
优选的,混纺面料的后整理工艺,包括如下步骤:
1)在35质量份去离子水中投入1质量份钨酸钠、4.1质量份聚氧乙烯醚、1.2质量份二氧化硅、3.1质量份双苄基膦酸单乙酯混合,搅拌均匀;
2)再同时缓慢加入2.9质量份醇乙氧化物羧酸盐、3.7质量份月桂醇、0.8质量份二氧化钛、2.7质量份乙酸乙酯,继续搅拌,至充分混合均匀,制得整理剂;
3)将面料在含有整理剂的浸渍液中浸轧处理,恒温烘干。
优选的,混纺面料的后整理工艺,包括如下步骤:
1)在35质量份去离子水中投入2质量份钨酸钠、4.1质量份聚氧乙烯醚、1.2质量份二氧化硅、3.1质量份双苄基膦酸单乙酯混合,搅拌均匀;
2)再同时缓慢加入2.9质量份醇乙氧化物羧酸盐、3.7质量份月桂醇、0.8质量份二氧化钛、2.7质量份乙酸乙酯,继续搅拌,至充分混合均匀,制得整理剂;
3)将面料在含有整理剂的浸渍液中浸轧处理,恒温烘干。
本发明的优点和有益效果在于:提供一种混纺面料的后整理工艺,其整理后的面料具有优异的阻燃、抗菌、抗皱、防静电性能,且耐洗性强。
具体实施方式
下面结合实施例,对本发明的具体实施方式作进一步描述。以下实施例仅用于更加清楚地说明本发明的技术方案,而不能以此来限制本发明的保护范围。
本发明具体实施的技术方案是:
实施例1
一种混纺面料的后整理工艺,包括如下步骤:
1)在35质量份去离子水中投入1~2质量份钨酸钠、4.1质量份聚氧乙烯醚、1.2质量份二氧化硅、3.1质量份双苄基膦酸单乙酯混合,搅拌均匀;
2)再同时缓慢加入2.9质量份醇乙氧化物羧酸盐、3.7质量份月桂醇、0.8质量份二氧化钛、2.7质量份乙酸乙酯,继续搅拌,至充分混合均匀,制得整理剂;
3)将面料在含有整理剂的浸渍液中浸轧处理,恒温烘干。
实施例2
混纺面料的后整理工艺,包括如下步骤:
1)在35质量份去离子水中投入1质量份钨酸钠、4.1质量份聚氧乙烯醚、1.2质量份二氧化硅、3.1质量份双苄基膦酸单乙酯混合,搅拌均匀;
2)再同时缓慢加入2.9质量份醇乙氧化物羧酸盐、3.7质量份月桂醇、0.8质量份二氧化钛、2.7质量份乙酸乙酯,继续搅拌,至充分混合均匀,制得整理剂;
3)将面料在含有整理剂的浸渍液中浸轧处理,恒温烘干。
实施例3
混纺面料的后整理工艺,包括如下步骤:
1)在35质量份去离子水中投入2质量份钨酸钠、4.1质量份聚氧乙烯醚、1.2质量份二氧化硅、3.1质量份双苄基膦酸单乙酯混合,搅拌均匀;
2)再同时缓慢加入2.9质量份醇乙氧化物羧酸盐、3.7质量份月桂醇、0.8质量份二氧化钛、2.7质量份乙酸乙酯,继续搅拌,至充分混合均匀,制得整理剂;
3)将面料在含有整理剂的浸渍液中浸轧处理,恒温烘干。
以上所述仅是本发明的优选实施方式,应当指出,对于本技术领域的普通技术人员来说,在不脱离本发明技术原理的前提下,还可以做出若干改进和润饰,这些改进和润饰也应视为本发明的保护范围。
Claims (3)
1.混纺面料的后整理工艺,其特征在于,包括如下步骤:
1)在35质量份去离子水中投入1~2质量份钨酸钠、4.1质量份聚氧乙烯醚、1.2质量份二氧化硅、3.1质量份双苄基膦酸单乙酯混合,搅拌均匀;
2)再同时缓慢加入2.9质量份醇乙氧化物羧酸盐、3.7质量份月桂醇、0.8质量份二氧化钛、2.7质量份乙酸乙酯,继续搅拌,至充分混合均匀,制得整理剂;
3)将面料在含有整理剂的浸渍液中浸轧处理,恒温烘干。
2.根据权利要求1所述的混纺面料的后整理工艺,其特征在于,包括如下步骤:
1)在35质量份去离子水中投入1质量份钨酸钠、4.1质量份聚氧乙烯醚、1.2质量份二氧化硅、3.1质量份双苄基膦酸单乙酯混合,搅拌均匀;
2)再同时缓慢加入2.9质量份醇乙氧化物羧酸盐、3.7质量份月桂醇、0.8质量份二氧化钛、2.7质量份乙酸乙酯,继续搅拌,至充分混合均匀,制得整理剂;
3)将面料在含有整理剂的浸渍液中浸轧处理,恒温烘干。
3.根据权利要求1所述的混纺面料的后整理工艺,其特征在于,包括如下步骤:
1)在35质量份去离子水中投入2质量份钨酸钠、4.1质量份聚氧乙烯醚、1.2质量份二氧化硅、3.1质量份双苄基膦酸单乙酯混合,搅拌均匀;
2)再同时缓慢加入2.9质量份醇乙氧化物羧酸盐、3.7质量份月桂醇、0.8质量份二氧化钛、2.7质量份乙酸乙酯,继续搅拌,至充分混合均匀,制得整理剂;
3)将面料在含有整理剂的浸渍液中浸轧处理,恒温烘干。