CN105272017A - 一种聚合物水泥防水涂料 - Google Patents
一种聚合物水泥防水涂料 Download PDFInfo
- Publication number
- CN105272017A CN105272017A CN201510770537.0A CN201510770537A CN105272017A CN 105272017 A CN105272017 A CN 105272017A CN 201510770537 A CN201510770537 A CN 201510770537A CN 105272017 A CN105272017 A CN 105272017A
- Authority
- CN
- China
- Prior art keywords
- powder
- parts
- agent
- emulsion
- liquid material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种聚合物水泥防水涂料,其特征在于由液料和粉料组成,液料包括高聚合物乳液、水和助剂,粉料包括水泥、超细硅灰石粉、超细石英粉、助剂。本发明的所述高渗透性聚合物水泥具有超强的渗透性,可在表层防水的同时,通过渗透到基层以内,起到加固基层,并且通过填充水泥基面毛孔,起到抗酸抗碱的作用。
Description
技术领域
本发明涉及一种建筑用水泥防水涂料技术领域,特别是一种聚合物水泥防水涂料。
背景技术
近几年来发展很快的聚合物水泥防水涂料(也称JS涂料)在国内被越来越重视,已广泛应用于各项工程建设中。聚合物水泥防水涂料是环保型功能材料,作为一个新型材料有非常好的前景。聚合物水泥基防水涂料是一种液料(聚合物乳液与添加剂组成)、粉料(水泥、无机填料以及助剂)双组份水性防水涂料,是住建部重点推荐的防水材料之一,属国家大力提倡的环保型产品。它以柔性高、粘结力强、抗冻融、耐高温、耐腐蚀、冷施工、可湿作业、施工简单、无毒无害、环保等特点而得到迅速的发展,成为近几年防水涂料反战的热点。
中国专利申请CN1539893A公开了一种双组份环保型隔热保温抗裂腻子,它由按重量百分比计算的A、B组分组成。其中A组分包括50-65%的水,35-45%的有机高分子聚合物,0.3-0.6%的润湿剂,0.3-1.1%的消泡剂,0.5-2.5%的抗龟裂剂;B组分包括9-33%的空心微珠,0.5-0.9%的保水剂,0.6-2.0%的增强纤维,33-55%的白水泥,10-30%的重钙,20-40%的石英粉,6-20%的硅灰石粉。制备时,A与B的配合比例为A:B=1:1.1-1.6。其达到的效果主要是保温和防止开裂,从而改进涂装质量。
中国专利申请CN103936339A公开了一种Ⅱ型聚合物水泥防水涂料及其制备方法。该Ⅱ型聚合物水泥防水涂料由液料和粉料组成,所述液料与所述粉料的质量比为1:1.2;所述液料的原料配方包括下述以质量百分比计的成分:VAE乳液75-85%、增塑剂3.5-10%、淀粉醚0.05-0.25%、醋酸混合酯0.83-1.18%和水10-14%;所述粉料的原料配方包括下述以质量百分比计的成分:水泥25-35%、石英粉15-25%、硅灰石粉45-55%和减水剂0.05-0.2%。Ⅱ型聚合物水泥防水涂料立面施工不流挂,在不平整基层施工不易开裂。
随着国家经济的高速发展,我国的地下工程建设也在蓬勃发展,尤其是输油管道、输气管道,地下隧道,地铁和城市建设目前已居世界前列。在地下工程建设的大发展中,如何做好地下工程管道防水和耐腐蚀问题、是工程建设方最为关心的问题。聚合物水泥防水涂料粉料主要以水泥和其他粉料类原材料组成,和液料混合后施工只附着于基层表面,无法起到加固基层,不能有效地发挥抗酸抗碱的作用。
针对上述问题,本发明设计了一种聚合物水泥防水涂料,摒弃传统聚合物水泥防水涂料施工时成膜后至附着在基层表面,通过超细填料填料与乳液相互作用,形成有强度、有韧性、具有一定渗透能力的防水层。
发明内容
本发明目的在于提供一种聚合物水泥防水涂料,摒弃传统聚合物水泥防水涂料施工时成膜后至附着在基层表面,通过超细填料填料与乳液相互作用,形成有强度、有韧性、具有一定渗透能力的防水层。
一种聚合物水泥防水涂料,由液料和粉料组成;液料包括高聚合物乳液、水和液料助剂;粉料包括水泥、超细硅灰石粉、超细石英粉和粉料助剂;
按重量百分比计,其由以下组分组成:
液料组分:
高聚合物乳液70-80份、水15-22份、助剂:0-10份;
粉料组分:
水泥30-50份、硅灰石粉30-50份、石英粉15-30份、助剂5-10份。
进一步的,液料与粉料的重量比为1:0.1-1:1.5,产品渗透性好,延伸好。
进一步的,所述高聚合物乳液是阳离子乳液、阴离子乳液和非离子乳液的一种单独使用或多种混合使用;所述阳离子乳液采用聚丙烯酸酯乳液、所述阴离子乳液采用醋酸-醋酸乙烯为原料合成的阴离子型乳液、所述非离子乳液采用环氧树脂和聚乙二醇为原料合成的非离子型乳液。
进一步的,所述水泥是普通硅酸盐水泥、早强硅酸盐水泥、硫铝酸盐水泥、硫酸盐水泥、矿渣水泥中的一种单独使用或多种混合使用。
进一步的,所述硅灰石粉细度控制在1250目;所述石英粉细度控制在1250目。
进一步的,所述液料助剂包括消泡剂、分散剂、丙二醇;所述消泡剂为有机硅消泡剂;所述分散剂为聚丙烯酸盐类分散剂。
进一步的,所述液料助剂还包括,增塑剂,所述增塑剂为氯化石蜡或邻苯二甲酸二辛酯或者氯化石蜡与邻苯二甲酸二辛酯的任意比例混合物。
进一步的,所述粉料助剂包括减水剂、固体消泡剂、纤维素醚或高聚合物胶粉或者纤维素醚与高聚合物胶粉的任意比例混合物;所述减水剂为萘系高效减水剂;所述固体消泡剂为有机硅消泡剂。
进一步的,所述液料助剂及粉料助剂,按重量百分比计,其由以下组分组成:
有机硅消泡剂1.5-4份、聚丙烯酸盐类分散剂1.5-2份、氯化石蜡或邻苯二甲酸二辛酯0-3份、丙二醇1-6份、萘系高效减水剂3.5-5份、纤维素醚0.2份、高聚合物胶粉1份;
粉料中固体消泡剂为0-0.3份。
优选的,一种聚合物水泥防水涂料,按重量百分比计,其由以下组分组成:
液料组分:
聚丙烯酸乳液75份、水15份、聚丙烯酸盐类分散剂1.5份、有机硅消泡剂2份、杀菌剂0.4份、丙二醇6份
粉料组分:
水泥40份、硅灰石粉25份、石英粉30份、萘系高效减水剂5份。
优选的,一种聚合物水泥防水涂料,按重量百分比计,其由以下组分组成:
液料组分:
聚丙烯酸乳液70份、水17份、聚丙烯酸盐类分散剂2份、有机硅消泡剂1.5份、氯化石蜡8份、丙二醇1份、杀菌剂0.5份、水泥40份
粉料组分:
1250目硅灰石粉25份、1250目石英粉30份、萘系高效减水剂3.5份、纤维素醚0.2份、高聚合物胶粉1份、有机硅消泡剂0.3份。
优选的,一种聚合物水泥防水涂料,按重量百分比计,其由以下组分组成:
液料组分:
聚丙烯酸乳液70份、水22份、聚丙烯酸盐类分散剂2份、有机硅消泡剂1.5份、氯化石蜡3份、丙二醇1份、杀菌剂0.5份
粉料组分:
水泥40份、1250目石英粉30份、1250目硅灰石粉25份、萘系高效减水剂3.5份、纤维素醚0.2份、高聚合物胶粉1份、有机硅消泡剂0.3份。
进一步的,本发明还提供一种高渗透性聚合物水泥防水涂料的制备方法,其步骤如下:
(1)将液料与粉料按照质量比为1:0.3混合,形成混合物;
(2)步骤(1)中混合物置于砂浆搅拌机中搅拌均匀,搅拌速度300r/min;
进一步的,本发明还提供一种高渗透性聚合物水泥防水涂料的使用方法,其步骤如下:
(1)先将液料按需要比例置于搅拌容器中,开启搅拌器;
(2)缓慢向步骤(1)中搅拌器内按需要比例加入粉料,待粉料加完后,搅拌3-5min;
(3)完成步骤(2)后采用刮涂、刷涂、喷涂的方式施工。
本发明的配方选用优质聚丙烯酸乳液,以水为分散介质,通过添加消泡剂、分散剂等助剂经科学配比协同应用,混合搅拌而成的一种环保、无污染的有机液料;粉料选用标号水泥(42.5),超细硅灰石粉、超细石英粉,并辅以减水剂、固体消泡剂、纤维素醚、高聚合物胶粉等助剂经科学配比后调制而成的一种环保型粉料。液、粉按不同比列混合后可得到高延伸、高强度、渗透性强等不同性能的产品。
消泡剂,消除材料本身及生产、施工过程中产生的气泡;分散剂,使粉料可以更好的分散在液料中且延长开放时间;润湿剂为氟碳,施工过程中可润湿基层,从而使产品更好的渗透到基层以内,起到抗酸抗碱的作用;丙二醇,夏天缓干,冬天防冻,使液料产品耐候性、施工性更出色;防腐杀菌剂,杀死原材料本身所携带的细菌及在储存过程中产生的细菌,从而延长产品的储存时间。
其中粉料助剂包括:减水剂,调节产品的稀稠度,延长施工开放时间,提升水泥强度;固体消泡剂,消除原材料及施工搅拌过程中产生的气泡,从而提升产品各项性能;纤维素醚,保水,使水泥可以充分的与水混合,提升水泥强度;高聚合物胶粉,提升产品的强度和成膜性。本发明的所述高渗透性聚合物水泥具有超强的渗透性,可在表层防水的同时,通过渗透到基层以内,起到加固基层,并且通过填充水泥基面毛孔,起到抗酸抗碱的作用。
本发明的优点是所制得的聚偏氟乙烯中空纤维膜可以在干态下直接进行保存不用甘油保护且反复润湿晾干后性能基本不变。
具体实施方式
下面结合实施例对本发明的具体实施方式作进一步描述,以下实施例仅用于更加清楚地说明本发明的技术方案,而不能以此来限制本发明的保护范围。
本发明具体技术方案如下:
实施例1
一种聚合物水泥防水涂料,按重量百分比计,其由以下组分组成:
液料组分:
聚丙烯酸乳液75份、水15份、聚丙烯酸盐类分散剂1.5份、有机硅消泡剂2份、氯化石蜡3份、丙二醇6份、杀菌剂0.4份
粉料组分:
水泥40份、1250目石英粉30份、1250目硅灰石粉25份、萘系高效减水剂5份纤维素醚0.2份、高聚合物胶粉1份、有机硅消泡剂0.3份。
一种聚合物水泥防水涂料,制备方法步骤如下:
(1)将称量好的液料加入搅拌釜中,开启搅拌15min,待分散均匀后,灌装包装待用;
(2)将称量好的粉料加入到砂浆搅拌机中,开启搅拌5min,待分散均匀后,包装待用;
一种高渗透性聚合物水泥防水涂料的使用方法,其步骤如下:
(1)先将液料按需要比例置于搅拌容器中,开启搅拌器;
(2)缓慢向步骤(1)中搅拌器内按需要比例加入粉料,待粉料加完后,搅拌3min;
(3)完成步骤(2)后采用喷涂平面和立面施工,一遍0.5-0.8mm,复涂0.7-1.2mm,无开裂、无流挂、无滑移等不良现象。
实施例2
一种聚合物水泥防水涂料,按重量百分比计,其由以下组分组成:
液料组分:
醋酸-醋酸乙烯乳液70份、水17份、聚丙烯酸盐类分散剂2份、有机硅消泡剂1.5份、氯化石蜡3份、丙二醇1份、杀菌剂0.5份
粉料组分:
水泥40份、1250目石英粉30份、1250目硅灰石粉25份、萘系高效减水剂3.5份、纤维素醚0.2份、高聚合物胶粉1份、有机硅消泡剂0.3份。
一种聚合物水泥防水涂料,制备方法步骤如下:
(1)将称量好的液料加入搅拌釜中,开启搅拌15min,待分散均匀后,灌装包装待用;
(2)将称量好的粉料加入到砂浆搅拌机中,开启搅拌5min,待分散均匀后,包装待用;
一种高渗透性聚合物水泥防水涂料的使用方法,其步骤如下:
(1)先将液料按需要比例置于搅拌容器中,开启搅拌器;
(2)缓慢向步骤(1)中搅拌器内按需要比例加入粉料,待粉料加完后,搅拌3min;
(3)完成步骤(2)后采用喷涂平面和立面施工,一遍0.5-0.8mm,复涂0.7-1.2mm,无开裂、无流挂、无滑移等不良现象。
实施例3
一种聚合物水泥防水涂料,按重量百分比计,其由以下组分组成:
液料组分:
环氧树脂和聚乙二醇为原料合成的非离子型乳液70份、水22份、聚丙烯酸盐类分散剂2份、有机硅消泡剂1.5份、氯化石蜡3份、丙二醇1份、杀菌剂0.5份
粉料组分:
水泥40份、1250目石英粉30份、1250目硅灰石粉25份、萘系高效减水剂3.5份、纤维素醚0.2份、高聚合物胶粉1份、有机硅消泡剂0.3份。
一种聚合物水泥防水涂料,制备方法步骤如下:
(1)将称量好的液料加入搅拌釜中,开启搅拌15min,待分散均匀后,灌装包装待用;
(2)将称量好的粉料加入到砂浆搅拌机中,开启搅拌5min,待分散均匀后,包装待用;
一种高渗透性聚合物水泥防水涂料的使用方法,其步骤如下:
(1)先将液料按需要比例置于搅拌容器中,开启搅拌器;
(2)缓慢向步骤(1)中搅拌器内按需要比例加入粉料,待粉料加完后,搅拌3min;
(3)完成步骤(2)后采用喷涂平面和立面施工,一遍0.5-0.8mm,复涂0.7-1.2mm,无开裂、无流挂、无滑移等不良现象。
实施例4
一种聚合物水泥防水涂料,按重量百分比计,其由以下组分组成:
液料组分:
聚丙烯酸乳液80份、水22份、聚丙烯酸盐类分散剂2份、有机硅消泡剂4份、氯化石蜡2.5、丙二醇1份、杀菌剂0.5份
粉料组分:
水泥50份、1250目石英粉30份、1250目硅灰石粉50份、萘系高效减水剂5份、纤维素醚0.2份、高聚合物胶粉1份、有机硅消泡剂0.3份。
一种聚合物水泥防水涂料,制备方法步骤如下:
(1)将称量好的液料加入搅拌釜中,开启搅拌15min,待分散均匀后,灌装包装待用;
(2)将称量好的粉料加入到砂浆搅拌机中,开启搅拌5min,待分散均匀后,包装待用;
一种高渗透性聚合物水泥防水涂料的使用方法,其步骤如下:
(1)先将液料按需要比例置于搅拌容器中,开启搅拌器;
(2)缓慢向步骤(1)中搅拌器内按需要比例加入粉料,待粉料加完后,搅拌3min;
完成步骤(2)后采用喷涂平面和立面施工,一遍0.5-0.8mm,复涂0.7-1.2mm,无开裂、无流挂、无滑移等不良现象。
经对实施例1-4的产品进行检测后,得到对比数据表如下:
以上所述仅是本发明的优先实施方式,应当指出,对于本技术领域的普通技术人员来说,在不脱离本发明技术原理的前提下,还可以做出若干改进和润饰,这些改进和润饰也应视为本发明的保护范围。
Claims (10)
1.一种聚合物水泥防水涂料,其特征在于,由液料和粉料组成;
液料包括高聚合物乳液、水和液料助剂;粉料包括水泥、超细硅灰石粉、超细石英粉和粉料助剂;
按重量百分比计,其由以下组分组成:
液料组分:
高聚合物乳液70-80份、水15-22份、助剂:0-10份;
粉料组分:
水泥30-50份、硅灰石粉30-50份、石英粉15-30份、助剂5-10份。
2.如权利要求1所述的聚合物水泥防水涂料,其特征在于,液料与粉料的重量比为1:0.1-1:1.5,产品渗透性好,延伸好。
3.如权利要求1所述的聚合物水泥防水涂料,其特征在于,所述高聚合物乳液是阳离子乳液、阴离子乳液和非离子乳液的一种单独使用或多种混合使用;所述阳离子乳液采用聚丙烯酸酯乳液、所述阴离子乳液采用醋酸-醋酸乙烯为原料合成的阴离子型乳液、所述非离子乳液采用环氧树脂和聚乙二醇为原料合成的非离子型乳液。
4.如权利要求1所述的聚合物水泥防水涂料,其特征在于,所述水泥是普通硅酸盐水泥、早强硅酸盐水泥、硫铝酸盐水泥、硫酸盐水泥、矿渣水泥中的一种单独使用或多种混合使用。
5.如权利要求1所述的聚合物水泥防水涂料,其特征在于,所述硅灰石粉细度控制在1250目;所述石英粉细度控制在1250目。
6.如权利要求1所述的一种聚合物水泥防水涂料,其特征在于,所述液料助剂包括消泡剂、分散剂、丙二醇;所述消泡剂为有机硅消泡剂;所述分散剂为聚丙烯酸盐类分散剂。
7.如权利要求6所述的聚合物水泥防水涂料,其特征在于,所述液料助剂还包括增塑剂;所述增塑剂为氯化石蜡或邻苯二甲酸二辛酯或者氯化石蜡与邻苯二甲酸二辛酯的任意比例混合物。
8.如权利要求1所述的聚合物水泥防水涂料,其特征在于,所述粉料助剂包括减水剂、固体消泡剂、纤维素醚或高聚合物胶粉或者纤维素醚与高聚合物胶粉的任意比例混合物;所述减水剂为萘系高效减水剂;所述固体消泡剂为有机硅消泡剂。
9.如权利要求7和8所述的聚合物水泥防水涂料,其特征在于,所述液料助剂和粉料助剂按重量百分比计,其由以下组分组成:
有机硅消泡剂1.5-4份、聚丙烯酸盐类分散剂1.5-2份、氯化石蜡或邻苯二甲酸二辛酯0-3份、丙二醇1-6份、萘系高效减水剂3.5-5份、纤维素醚0.2份、高聚合物胶粉1份;
粉料中固体消泡剂为0-0.3份。
10.如权利要求9所述聚合物水泥防水涂料,其特征在于,按重量百分比计,其由以下组分组成:
液料组分:
聚丙烯酸乳液70份、水17份、聚丙烯酸盐类分散剂2份、有机硅消泡剂1.5份、氯化石蜡8份、丙二醇1份、杀菌剂0.5份、水泥40份
粉料组分:
1250目硅灰石粉25份、1250目石英粉30份、萘系高效减水剂3.5份、纤维素醚0.2份、高聚合物胶粉1份、有机硅消泡剂0.3份。