CN105272007A - 一种新型轻质板材 - Google Patents
一种新型轻质板材 Download PDFInfo
- Publication number
- CN105272007A CN105272007A CN201510724828.6A CN201510724828A CN105272007A CN 105272007 A CN105272007 A CN 105272007A CN 201510724828 A CN201510724828 A CN 201510724828A CN 105272007 A CN105272007 A CN 105272007A
- Authority
- CN
- China
- Prior art keywords
- parts
- silicate
- cement
- flyash
- calcium stearate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种新型轻质板材,所述新型轻质板材以重量份数计,包括以下组分:水泥150~250份、粉煤灰50~65份、硅酸盐40~60份、羧甲基纤维素30~50、乳胶粉15~25、硬脂酸钙5~20份。本发明的新型板材,其具有节能、防火、隔声和轻质等性能,轻质抗震,比空心砌块砖轻120kg以上,解决大梁、大柱、深基础的问题。框架式连接具有良好的抗震性能,不仅适用于低层建筑,也适用于高层建筑,软地质及沙滩、海滩等建筑。
Description
技术领域
本发明属于家居生产技术领域,具体涉及一种新型轻质板材。
背景技术
目前墙板一般采用砖混砌成,工期较长,而目前一些内部隔断用的墙板,一般中间采用轻钢龙骨,两面加石膏板,高档的隔墙,也就是在石膏板中间加上隔音棉等材料,而这种墙板虽然容重较低,但是隔音效果并不很好,隔热很差,而且使用寿命比较短,遇到水更容易损坏,更不可能做外墙使用,而且石膏板墙壁承载力较低,现在流行的挂壁电视,挂上去比较危险。
墙体材料是建筑物的重要组成部分,建筑材料中70%是墙体材料,一平方米的建筑面积,约需2.5平方米的墙体材料来进行维护,而较厚的墙体必将占用更多的建筑面积,间接提高建筑成本。随着墙体革新与建筑节能***工程的不断深入,建筑居住条件改善必然带来墙体材料的革新和完善,人们对新型墙体材料的认识也越来越清晰。在各类建筑工程的非承重墙体中,需要研发一种具有节能、防火、隔声和轻质的新型板材尤为重要。
发明内容
为了解决上述问题,本发明提供了一种新型板材,其具有节能、防火、隔声和轻质等性能。
本发明的技术方案为:一种新型轻质板材,以重量份数计,包括以下组分:
水泥150~250份、粉煤灰50~65份、硅酸盐40~60份、羧甲基纤维素30~50、乳胶粉15~25、硬脂酸钙5~20份。
作为优选,以重量份数计,包括以下组分:
水泥200~250份、粉煤灰50~65份、硅酸盐45~60份、羧甲基纤维素30~45、乳胶粉15~20、硬脂酸钙8~20份。
作为优选,以重量份数计,包括以下组分:
水泥200~230份、粉煤灰55~65份、硅酸盐50~60份、羧甲基纤维素35~45、乳胶粉15~20、硬脂酸钙12~20份。
作为优选,以重量份数计,包括以下组分:
水泥200~230份、粉煤灰60~65份、硅酸盐50~55份、羧甲基纤维素40~45、乳胶粉15~20、硬脂酸钙12~16份。
作为优选,以重量份数计,包括以下组分:
水泥220份、粉煤灰60份、硅酸盐55份、羧甲基纤维素43、乳胶粉18、硬脂酸钙15份。
与现有技术相比,本发明的有益效果体现在:
本发明的新型板材,其具有节能、防火、隔声和轻质等性能,轻质抗震,比空心砌块砖轻120kg以上,解决大梁、大柱、深基础的问题。框架式连接具有良好的抗震性能,不仅适用于低层建筑,也适用于高层建筑,软地质及沙滩、海滩等建筑。
具体实施方式
实施例1
本实施例以重量份数计,包括以下原料组分:
水泥150份、粉煤灰65份、硅酸盐40份、羧甲基纤维素50、乳胶粉15、硬脂酸钙20份。
本实施例的板材的制备方法如下:
按照上述重量份数称取各组分,首先将水泥、粉煤灰以及硅酸盐加入水混匀得到混合浆液,其中水泥、粉煤灰以及硅酸盐的总质量与水的质量比为1:4,然后将羧甲基纤维素、乳胶粉以及硬脂酸钙依次加入混合浆液中搅拌均匀,最后注入板材成型模具中成型,得到所述新型轻质板材。
实施例2
本实施例以重量份数计,包括以下原料组分:
水泥250份、粉煤灰50份、硅酸盐60份、羧甲基纤维素30、乳胶粉25、硬脂酸钙5份。
本实施例的板材的制备方法如下:
按照上述重量份数称取各组分,首先将水泥、粉煤灰以及硅酸盐加入水混匀得到混合浆液,其中水泥、粉煤灰以及硅酸盐的总质量与水的质量比为1:3,然后将羧甲基纤维素、乳胶粉以及硬脂酸钙依次加入混合浆液中搅拌均匀,最后注入板材成型模具中成型,得到所述新型轻质板材。
实施例3
本实施例以重量份数计,包括以下原料组分:
水泥220份、粉煤灰60份、硅酸盐55份、羧甲基纤维素43、乳胶粉18、硬脂酸钙15份。
本实施例的板材的制备方法如下:
按照上述重量份数称取各组分,首先将水泥、粉煤灰以及硅酸盐加入水混匀得到混合浆液,其中水泥、粉煤灰以及硅酸盐的总质量与水的质量比为3:4,然后将羧甲基纤维素、乳胶粉以及硬脂酸钙依次加入混合浆液中搅拌均匀,最后注入板材成型模具中成型,得到所述新型轻质板材。
实施例4
本实施例以重量份数计,包括以下原料组分:
水泥230份、粉煤灰55份、硅酸盐60份、羧甲基纤维素35、乳胶粉20、硬脂酸钙12份。
本实施例的板材的制备方法如下:
按照上述重量份数称取各组分,首先将水泥、粉煤灰以及硅酸盐加入水混匀得到混合浆液,其中水泥、粉煤灰以及硅酸盐的总质量与水的质量比为2:4,然后将羧甲基纤维素、乳胶粉以及硬脂酸钙依次加入混合浆液中搅拌均匀,最后注入板材成型模具中成型,得到所述新型轻质板材。
表1本发明实施例1~4的性能指标测定结果
Claims (5)
1.一种新型轻质板材,其特征在于,以重量份数计,包括以下组分:
水泥150~250份、粉煤灰50~65份、硅酸盐40~60份、羧甲基纤维素30~50、乳胶粉15~25、硬脂酸钙5~20份。
2.如权利要求1所述的新型轻质板材,其特征在于,以重量份数计,包括以下组分:
水泥200~250份、粉煤灰50~65份、硅酸盐45~60份、羧甲基纤维素30~45、乳胶粉15~20、硬脂酸钙8~20份。
3.如权利要求2所述的新型轻质板材,其特征在于,以重量份数计,包括以下组分:
水泥200~230份、粉煤灰55~65份、硅酸盐50~60份、羧甲基纤维素35~45、乳胶粉15~20、硬脂酸钙12~20份。
4.如权利要求3所述的新型轻质板材,其特征在于,以重量份数计,包括以下组分:
水泥200~230份、粉煤灰60~65份、硅酸盐50~55份、羧甲基纤维素40~45、乳胶粉15~20、硬脂酸钙12~16份。
5.如权利要求4所述的新型轻质板材,其特征在于,以重量份数计,包括以下组分:
水泥220份、粉煤灰60份、硅酸盐55份、羧甲基纤维素43、乳胶粉18、硬脂酸钙15份。