CN105172273B - A kind of tent cloth with high light-fast anti-ultraviolet function - Google Patents

A kind of tent cloth with high light-fast anti-ultraviolet function Download PDF

Info

Publication number
CN105172273B
CN105172273B CN201510603460.8A CN201510603460A CN105172273B CN 105172273 B CN105172273 B CN 105172273B CN 201510603460 A CN201510603460 A CN 201510603460A CN 105172273 B CN105172273 B CN 105172273B
Authority
CN
China
Prior art keywords
layer
high light
base cloth
parts
precoat
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201510603460.8A
Other languages
Chinese (zh)
Other versions
CN105172273A (en
Inventor
严正华
钱玉
严加军
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Hunan Badu Space Home Technology Co ltd
Original Assignee
Yancheng Changhua Outdoor Products Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Yancheng Changhua Outdoor Products Co Ltd filed Critical Yancheng Changhua Outdoor Products Co Ltd
Priority to CN201510603460.8A priority Critical patent/CN105172273B/en
Publication of CN105172273A publication Critical patent/CN105172273A/en
Application granted granted Critical
Publication of CN105172273B publication Critical patent/CN105172273B/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The present invention relates to a kind of tent cloth with high light-fast anti-ultraviolet function, including base cloth layer and the precoat being arranged on base cloth layer, coat is provided between the base cloth layer and precoat, the coat is sequentially provided with wind prevention layer from top to bottom, fire protection flame retarding layer, waterproof layer, moisture absorption breathable shell fabric layer, uvioresistant layer and reflecting layer, the base cloth layer is made into by warp-wise fabric and broadwise fabric, warp-wise fabric is 30 40 parts of composite fibre being mixed with except the flax fiber of entomogenous fungi solvent and 10 15 parts high light-proofness single composition, the composite fibre that the bamboo-carbon fibre and 30 34 parts of cotton fibers that broadwise fabric is 16 20 parts are formed, the precoat is PU coating oxfords；The present invention is a kind of tent cloth with high light-fast anti-ultraviolet function, can strengthen the gas permeability of tent cloth, stops sunshine and ultraviolet, reduces the influence of Radiation On Human.

Description

A kind of tent cloth with high light-fast anti-ultraviolet function
Technical field
The present invention relates to tent field, more particularly to a kind of tent cloth with high light-fast anti-ultraviolet function.
Background technology
Open air goes camping, and tent is to must be provided with, and tent must specifically have sunshade, ventilation, windproof, rain-proof, warming etc. more The outdoor function of weight, outdoor camping is typically in outdoor progress, but outdoor temperature is higher, and ultraviolet, infra-red intensity are big, Existing tent can only have certain effect of blocking to the sun, can not effectively keep the sun off, although some tents are set Double shelter tent cloth barrier material is put, although double shelter tent cloth barrier material has than individual layer tent cloth to the sun and ultraviolet Certain effect of blocking, but double shelter tent cloth barrier material can decline the heat dispersion of tent, without good radiating Under the exposure of sunlight the temperature of tent and tent inside can raise, be unfavorable for radiating, therefore, how to give birth to for performance, tent A kind of not only tent cloth with high light-fast anti-ultraviolet function but also with airing function of output to be solved as numerous producers The problem of.
The content of the invention
The present invention is directed to the deficiencies in the prior art, there is provided a kind of tent with high light-fast anti-ultraviolet function Cloth, to solve problems of the prior art.
To achieve the above object, the technical solution adopted by the present invention is as follows：
A kind of tent cloth with high light-fast anti-ultraviolet function, it is characterised in that：Including base cloth layer and it is arranged on Precoat on base cloth layer, is provided with coat between the base cloth layer and precoat, the coat is sequentially provided with from top to bottom Wind prevention layer, fire protection flame retarding layer, waterproof layer, moisture absorption breathable shell fabric layer, uvioresistant layer and reflecting layer, the base cloth layer is by warp thread It is made into weft yarns, warp thread is that 30-40 parts are mixed with except the flax fiber of entomogenous fungi solvent and the high light-proofness single structure of 10-15 parts Into composite fibre, weft yarn for 16-20 parts bamboo-carbon fibre and 30-34 parts cotton fiber form composite fibre, the precoat For PU coating oxfords.
As a modification of the present invention, the moisture absorption breathable shell fabric layer is high light-proofness fibrous layer, the high light-proofness Fibrous layer is high light-proofness single.
As a modification of the present invention, the high light-proofness single is made into by warp thread and weft yarns, warp thread 23- The composite fibre that 33 parts of flame retardant polyester fiber lines and 17-27 part bacterium polyester fibers line are formed, the weft yarn is 12-18 part anions The composite fibre that single, 12-18 part aramid fiber lines and 15-25 part soybean fibers line are formed.
As a modification of the present invention, the fire protection flame retarding layer is asbestos cloth, glass-fiber-fabric, cotton inflaming retarding fabric, CVC resistances Fire the combination mixture of any one of fabric, aramid fiber inflaming retarding fabric, acrylic fibers inflaming retarding fabric or more.
As a modification of the present invention, the uvioresistant layer is elargol coating.
As a modification of the present invention, the reflecting layer is reflective aluminium foil.
As a modification of the present invention, have the production technology of the tent cloth of high light-fast anti-ultraviolet function as follows：
1）Warp thread and weft yarn are placed on loom and woven, you can obtains high light-proofness single, warp thread is 23-33 parts The composite fibre that flame retardant polyester fiber line and 17-27 part bacterium polyester fibers line are formed, the weft yarn is 12-18 part negative-ion fibers The composite fibre that line, 12-18 part aramid fiber lines and 15-25 part soybean fibers line are formed.
2）By step 1）In high light-proofness single be placed on braider and woven, you can obtain high light-proofness fiber Layer；
3）Warp thread and weft yarn are placed on loom and woven, you can obtains base cloth layer, warp thread is that 30-40 parts are mixed with deinsectization The composite fibre that the flax fiber of bacterium solvent and the high light-proofness single of 10-15 parts are formed, weft yarn are the bamboo-carbon fibre of 16-20 parts The composite fibre formed with 30-34 parts cotton fiber；
4）With PA glue to step 3）In base cloth layer carry out bottoming, the mass fraction of each component includes 70- in the PA glue 95 parts of PA gluings, 2-3 parts crosslinking agent and 3-7 part solvents；
5）By step 4）In base cloth layer be positioned in coating machine, wind prevention layer, fire protection flame retarding layer, waterproof layer, moisture absorption is saturating Gas precoat, uvioresistant layer and reflecting layer are coated on through step 4 in a certain order）On treated base cloth layer；
6）Step 5）In add a certain amount of adhesive on coated base cloth layer after, precoat is placed on provided with coating On the base cloth layer of layer, base cloth layer and precoat are compressed with rubber rollers, closed space is formed, then enters to the lower end of base cloth layer Row inflation, allows base cloth layer internal expansion base cloth layer is close on the inner surface of precoat, then heated by oven heat into air bag Softened the PA glue on base cloth layer and adhesive, the surface with precoat in the presence of bladder air pressure is glued Patch, one is made, then tent cloth is placed on cooling frame and cooled down.
As a result of above technology, the present invention compared with the prior art, has the advantage that as follows：
The present invention is a kind of tent cloth with high light-fast anti-ultraviolet function, and moisture absorption breathable shell fabric is provided with the present invention Layer, the gas permeability of tent cloth can be strengthened, effectively prevent tent from making tent inside temperature because of the exposure overlong time under the sun Spend high and shorten the service life of tent；Fire protection flame retarding layer is provided with the present invention, can effectively be prevented because external temperature mistake It is high and make the situation of tent cloth spontaneous combustion；Uvioresistant layer and reflecting layer are provided with the present invention, can effectively stop sunshine and Ultraviolet, reduce the influence of Radiation On Human；Wind prevention layer, waterproof layer are provided with the present invention, can effectively prevent wind and rain；In the present invention High light-proofness single, can effectively degerming, mosquito dispersing, and the material used is more environmentally friendly, meets greenization production.
Embodiment
With reference to embodiment, the present invention is furture elucidated.
Embodiment 1：
A kind of tent cloth with high light-fast anti-ultraviolet function, including base cloth layer and the face that is arranged on base cloth layer The bed of material, is provided with coat between the base cloth layer and precoat, the coat is sequentially provided with wind prevention layer, fire prevention resistance from top to bottom It is PU coating oxfords to fire layer, waterproof layer, moisture absorption breathable shell fabric layer, uvioresistant layer and reflecting layer, the precoat.
The moisture absorption breathable shell fabric layer is high light-proofness fibrous layer, and the high light-proofness fibrous layer is high light-proofness fiber Line.
The fire protection flame retarding layer is the mixing of asbestos cloth, CVC inflaming retarding fabrics, aramid fiber inflaming retarding fabric and acrylic fibers inflaming retarding fabric Thing.
The uvioresistant layer is elargol coating.
The reflecting layer is reflective aluminium foil.
The production technology of tent cloth with high light-fast anti-ultraviolet function is as follows：
1）Warp thread and weft yarn are placed on loom and woven, you can obtains high light-proofness single, warp thread is 23 parts of resistances The composite fibre that polyester fiber line and 27 parts of bacterium polyester fiber lines are formed is fired, the weft yarn is 12 parts of negative-ion fiber lines, 18 parts The composite fibre that aramid fiber line and 15 parts of soybean fiber lines are formed.
2）By step 1）In high light-proofness single be placed on braider and woven, you can obtain high light-proofness fiber Layer；
3）Warp thread and weft yarn are placed on loom and woven, you can obtains base cloth layer, warp thread is 40 parts and is mixed with except entomogenous fungi The composite fibre that the flax fiber of solvent and 10 parts high light-proofness single are formed, weft yarn are 20 parts of bamboo-carbon fibre and 30 portions of cottons The composite fibre that fiber is formed；
4）With PA glue to step 3）In base cloth layer carry out bottoming, the mass fraction of each component includes 95 parts in the PA glue PA gluings, 2 parts of crosslinking agents and 7 parts of solvents；
5）By step 4）In base cloth layer be positioned in coating machine, wind prevention layer, fire protection flame retarding layer, waterproof layer, moisture absorption is saturating Gas precoat, uvioresistant layer and reflecting layer are coated on through step 4 in a certain order）On treated base cloth layer；
6）Step 5）In add a certain amount of adhesive on coated base cloth layer after, precoat is placed on provided with coating On the base cloth layer of layer, base cloth layer and precoat are compressed with rubber rollers, closed space is formed, then enters to the lower end of base cloth layer Row inflation, allows base cloth layer internal expansion base cloth layer is close on the inner surface of precoat, then heated by oven heat into air bag Softened the PA glue on base cloth layer and adhesive, the surface with precoat in the presence of bladder air pressure is glued Patch, one is made, then tent cloth is placed on cooling frame and cooled down.
Embodiment 2：
A kind of tent cloth with high light-fast anti-ultraviolet function, including base cloth layer and the face that is arranged on base cloth layer The bed of material, is provided with coat between the base cloth layer and precoat, the coat is sequentially provided with wind prevention layer, fire prevention resistance from top to bottom It is PU coating oxfords to fire layer, waterproof layer, moisture absorption breathable shell fabric layer, uvioresistant layer and reflecting layer, the precoat.
The moisture absorption breathable shell fabric layer is high light-proofness fibrous layer, and the high light-proofness fibrous layer is high light-proofness fiber Line.
The fire protection flame retarding layer is the mixing of glass-fiber-fabric, cotton inflaming retarding fabric, aramid fiber inflaming retarding fabric, acrylic fibers inflaming retarding fabric Thing.
The uvioresistant layer is elargol coating.
The reflecting layer is reflective aluminium foil.
The production technology of tent cloth with high light-fast anti-ultraviolet function is as follows：
1）Warp thread and weft yarn are placed on loom and woven, you can obtains high light-proofness single, warp thread is 33 parts of resistances The composite fibre that polyester fiber line and 17 parts of bacterium polyester fiber lines are formed is fired, the weft yarn is 18 parts of negative-ion fiber lines, 12 parts The composite fibre that aramid fiber line and 25 parts of soybean fiber lines are formed.
2）By step 1）In high light-proofness single be placed on braider and woven, you can obtain high light-proofness fiber Layer；
3）Warp thread and weft yarn are placed on loom and woven, you can obtains base cloth layer, warp thread is 30 parts and is mixed with except entomogenous fungi The composite fibre that the flax fiber of solvent and 15 parts high light-proofness single are formed, weft yarn are 16 parts of bamboo-carbon fibre and 34 portions of cottons The composite fibre that fiber is formed；
4）With PA glue to step 3）In base cloth layer carry out bottoming, the mass fraction of each component includes 70 parts in the PA glue PA gluings, 3 parts of crosslinking agents and 3 parts of solvents；
5）By step 4）In base cloth layer be positioned in coating machine, wind prevention layer, fire protection flame retarding layer, waterproof layer, moisture absorption is saturating Gas precoat, uvioresistant layer and reflecting layer are coated on through step 4 in a certain order）On treated base cloth layer；
6）Step 5）In add a certain amount of adhesive on coated base cloth layer after, precoat is placed on provided with coating On the base cloth layer of layer, base cloth layer and precoat are compressed with rubber rollers, closed space is formed, then enters to the lower end of base cloth layer Row inflation, allows base cloth layer internal expansion base cloth layer is close on the inner surface of precoat, then heated by oven heat into air bag Softened the PA glue on base cloth layer and adhesive, the surface with precoat in the presence of bladder air pressure is glued Patch, one is made, then tent cloth is placed on cooling frame and cooled down.
Embodiment 3：
A kind of tent cloth with high light-fast anti-ultraviolet function, including base cloth layer and the face that is arranged on base cloth layer The bed of material, is provided with coat between the base cloth layer and precoat, the coat is sequentially provided with wind prevention layer, fire prevention resistance from top to bottom It is PU coating oxfords to fire layer, waterproof layer, moisture absorption breathable shell fabric layer, uvioresistant layer and reflecting layer, the precoat.
The moisture absorption breathable shell fabric layer is high light-proofness fibrous layer, and the high light-proofness fibrous layer is high light-proofness fiber Line.
The fire protection flame retarding layer is the mixture of asbestos cloth, glass-fiber-fabric, CVC inflaming retarding fabrics and aramid fiber inflaming retarding fabric.
The uvioresistant layer is elargol coating.
The reflecting layer is reflective aluminium foil.
The production technology of tent cloth with high light-fast anti-ultraviolet function is as follows：
1）Warp thread and weft yarn are placed on loom and woven, you can obtains high light-proofness single, warp thread is 30 parts of resistances The composite fibre that polyester fiber line and 20 parts of bacterium polyester fiber lines are formed is fired, the weft yarn is 12 parts of negative-ion fiber lines, 18 parts The composite fibre that aramid fiber line and 15-25 part soybean fibers line are formed.
2）By step 1）In high light-proofness single be placed on braider and woven, you can obtain high light-proofness fiber Layer；
3）Warp thread and weft yarn are placed on loom and woven, you can obtains base cloth layer, warp thread is 35 parts and is mixed with except entomogenous fungi The composite fibre that the flax fiber of solvent and 10 parts high light-proofness single are formed, weft yarn are 20 parts of bamboo-carbon fibre and 30 portions of cottons The composite fibre that fiber is formed；
4）With PA glue to step 3）In base cloth layer carry out bottoming, the mass fraction of each component includes 82 parts in the PA glue PA gluings, 2 parts of crosslinking agents and 7 parts of solvents；
5）By step 4）In base cloth layer be positioned in coating machine, wind prevention layer, fire protection flame retarding layer, waterproof layer, moisture absorption is saturating Gas precoat, uvioresistant layer and reflecting layer are coated on through step 4 in a certain order）On treated base cloth layer；
6）Step 5）In add a certain amount of adhesive on coated base cloth layer after, precoat is placed on provided with coating On the base cloth layer of layer, base cloth layer and precoat are compressed with rubber rollers, closed space is formed, then enters to the lower end of base cloth layer Row inflation, allows base cloth layer internal expansion base cloth layer is close on the inner surface of precoat, then heated by oven heat into air bag Softened the PA glue on base cloth layer and adhesive, the surface with precoat in the presence of bladder air pressure is glued Patch, one is made, then tent cloth is placed on cooling frame and cooled down.
The implementation the performance test results of the tent of table 1
Above-described embodiment is only the preferred technical solution of the present invention, and is not construed as the limitation for the present invention, the present invention Protection domain should with claim record technical scheme, including claim record technical scheme in technical characteristic etc. It is protection domain with alternative, i.e., equivalent substitution within this range is improved, also within protection scope of the present invention.

Claims (4)

  1. A kind of 1. tent cloth with high light-fast anti-ultraviolet function, it is characterised in that：Including base cloth layer and it is arranged on base Precoat on layer of cloth, is provided with coat between the base cloth layer and precoat, the coat is sequentially provided with anti-from top to bottom Stratification of wind, fire protection flame retarding layer, waterproof layer, moisture absorption breathable shell fabric layer, uvioresistant layer and reflecting layer, the base cloth layer by warp thread and Weft yarns are made into, and warp thread is that 30-40 parts are mixed with except the flax fiber of entomogenous fungi solvent and the high light-proofness single of 10-15 parts are formed Composite fibre, the composite fibre that weft yarn is formed for the bamboo-carbon fibre and 30-34 parts cotton fiber of 16-20 parts, the precoat is PU coating oxfords；The tent cloth material manufacturing technique with high light-fast anti-ultraviolet function is as follows：
    1）Warp thread and weft yarn are placed on loom and woven, you can obtains high light-proofness single, warp thread is that 23-33 parts are fire-retardant The composite fibre that polyester fiber line and 17-27 part bacterium polyester fibers line are formed, the weft yarn be 12-18 part negative-ion fibers line, The composite fibre that 12-18 part aramid fiber lines and 15-25 part soybean fibers line are formed；
    2）By step 1）In high light-proofness single be placed on braider and woven, you can obtain high light-proofness fibrous layer；
    3）Warp thread and weft yarn are placed on loom and woven, you can obtains base cloth layer, warp thread is that 30-40 parts are mixed with except entomogenous fungi is molten The composite fibre that the flax fiber of agent and the high light-proofness single of 10-15 parts are formed, weft yarn for 16-20 parts bamboo-carbon fibre and The composite fibre that 30-34 parts cotton fiber is formed；
    4）With PA glue to step 3）In base cloth layer carry out bottoming, the mass fraction of each component includes 70-95 parts in the PA glue PA gluings, 2-3 parts crosslinking agent and 3-7 part solvents；
    5）By step 4）In base cloth layer be positioned in coating machine, by wind prevention layer, fire protection flame retarding layer, waterproof layer, moisture absorption breathe freely face The bed of material, uvioresistant layer and reflecting layer are coated on through step 4 in a certain order）On treated base cloth layer；The suction Penetrable ventilated precoat is high light-proofness fibrous layer, and the high light-proofness fibrous layer is high light-proofness single；
    6）Step 5）In add a certain amount of adhesive on coated base cloth layer after, precoat is placed on provided with coat On base cloth layer, base cloth layer and precoat are compressed with rubber rollers, closed space is formed, is then filled to the lower end of base cloth layer Gas, base cloth layer internal expansion is allowed base cloth layer is close on the inner surface of precoat, then make base by oven heat heating into air bag PA glue and adhesive on layer of cloth are softened, and the surface with precoat in the presence of bladder air pressure is pasted, One is made, then tent cloth is placed on cooling frame and cooled down.
  2. A kind of 2. tent cloth with high light-fast anti-ultraviolet function according to claim 1, it is characterised in that：It is described Fire protection flame retarding layer is asbestos cloth, glass-fiber-fabric, cotton inflaming retarding fabric, CVC inflaming retarding fabrics, aramid fiber inflaming retarding fabric, acrylic fibers inflaming retarding fabric Any one or more combination mixture.
  3. A kind of 3. tent cloth with high light-fast anti-ultraviolet function according to claim 1, it is characterised in that：It is described Uvioresistant layer is elargol coating.
  4. A kind of 4. tent cloth with high light-fast anti-ultraviolet function according to claim 1, it is characterised in that：It is described Reflecting layer is reflective aluminium foil.
CN201510603460.8A 2015-09-21 2015-09-21 A kind of tent cloth with high light-fast anti-ultraviolet function Active CN105172273B (en)