CN105109136B - 一种具有防蚊防虫功能的帐篷布料 - Google Patents
一种具有防蚊防虫功能的帐篷布料 Download PDFInfo
- Publication number
- CN105109136B CN105109136B CN201510602444.7A CN201510602444A CN105109136B CN 105109136 B CN105109136 B CN 105109136B CN 201510602444 A CN201510602444 A CN 201510602444A CN 105109136 B CN105109136 B CN 105109136B
- Authority
- CN
- China
- Prior art keywords
- parts
- layer
- mosquito
- base cloth
- precoat
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明涉及一种具有防蚊防虫功能的帐篷布料，包括网眼布、设置在网眼布上的基布层以及设置在基布层上的面料层，所述基布层与面料层之间设有涂覆层，所述涂覆层从下到上依次设有吸湿透气面料层、防蚊防虫层、防风层、防潮层以及防水层，所述基布层由经向面料和纬向面料交织织成，经向面料为35‑45份混有除虫菌溶剂的亚麻纤维和5‑15份混有艾草提取液的高遮光性纤维线构成的混合纤维，纬向面料为13‑25份的茶叶纤维和25‑37份混有薰衣草提取液的聚酯纤维构成的混合纤维，所述面料层为PU涂层牛津布；本发明是一种具有防蚊防虫功能的帐篷布料，可以有效的驱除蚊虫，避免蚊虫的干扰。
Description
技术领域
本发明涉及帐篷领域，特别是涉及一种具有防蚊防虫功能的帐篷布料。
背景技术
户外去野营，帐篷是必须装备，帐篷必须具体有遮阳、通风、防风、防雨、保暖等多重户外功能，户外野营一般都是在室外进行的，室外蚊虫比较多，一般的人帐篷不具有防虫的功效，所以通常只能将帐篷全部关闭以防止蚊虫的进入，但是全部关闭的帐篷具有不透气性，会使睡在帐篷中的人们不舒服，但是如果打开帐篷进行透气时，外界的蚊虫会飞进帐篷内，会给人们带来一定的困扰，现由技术的帐篷中也添加了一些防蚊的材料，但是所加的材料只能对蚊虫具有一定的阻挡作用，不能有效解决蚊虫的问题，而且蚊虫种类比较繁多，现有帐篷中所添加的物质只能防止某些特定种类的蚊虫，不能有效阻挡其他种类的蚊虫，因此，如何生产出一种具有防蚊防虫功能的帐篷布料成为众多厂家所要解决的问题。
发明内容
本发明针对现有技术中存在的不足，提供了一种具有防火阻燃功能的帐篷布料，以解决现有技术中存在的问题。
为实现上述目的，本发明采用的技术方案如下：
一种具有防蚊防虫功能的帐篷布料，其特征在于：包括网眼布、设置在网眼布上的基布层以及设置在基布层上的面料层，所述基布层与面料层之间设有涂覆层，所述涂覆层从下到上依次设有吸湿透气面料层、防蚊防虫层、防风层、防潮层以及防水层，所述基布层由经纱和纬纱交织织成，经纱为35-45份混有除虫菌溶剂的亚麻纤维和5-15份混有艾草提取液的高遮光性纤维线构成的混合纤维，纬纱为13-25份的茶叶纤维和25-37份混有薰衣草提取液的聚酯纤维构成的混合纤维，所述面料层为PU涂层牛津布。
作为本发明的一种改进，所述防蚊防虫层中各组分的质量份数包括35-45份聚氨酯树脂、20-28份聚氯乙烯树脂、10-17份交联剂、5-7份菖蒲提取液、3-5份核桃叶提取液、2-3份艾蒿提取液、3-4份桉树叶提取液、7-10份皂角提取液、1-2份苦檀叶提取液的混合物。
作为本发明的一种改进，所述网眼布包括聚乙烯PE纱线，所述聚乙烯PE纱线包括药品纱线，所述药品纱线内含有杀虫剂。
作为本发明的一种改进，所述药品纱线中各组分的质量份数包括5-25份色母、3-15份防老化剂、35-50份高密度聚乙烯以及15-25份低密度聚乙烯。
作为本发明的一种改进，所述杀虫剂中各组分的质量份数包括15-25份除虫菊花、25-35份榆树皮、42-58份除虫菊叶。
作为本发明的一种改进，所述吸湿透气面料层包括高遮光性纤维层，所述高遮光性纤维层包括高遮光性纤维线。
作为本发明的一种改进，所述防潮层为B型硅胶以及活性炭粉的混合物。
作为本发明的一种改进，具有防蚊防虫功能的帐篷布料的生产工艺如下：
1）将35-45份聚氨酯树脂、20-28份聚氯乙烯树脂、10-17份交联剂以及其他助剂放在一起进行搅拌混合，将搅拌好的混合物放入注塑机中进行加工，并将加工好后的混合物中依次加入5-7份菖蒲提取液、3-5份核桃叶提取液、2-3份艾蒿提取液、3-4份桉树叶提取液、7-10份皂角提取液、1-2份苦檀叶提取液并继续进行反应，将反应后的混合物进行冷却处理，即可得到防蚊防虫层；
2）将5-25份色母、3-15份防老化剂、35-50份高密度聚乙烯、15-25份低密度聚乙烯以及其他助剂放入搅拌机中进行搅拌，并将搅拌之后的混合物放入挤出机中进行加工，并向加工好后的混合物中加入15-25份除虫菊花、25-35份榆树皮、42-58份除虫菊叶的混合物进行反应，混合充分后并将物料加热至150-250℃并拉成丝，并将拉出的丝线冷却后放置在编织机上进行编织，并形成网眼布；
3）将经纱和纬纱放置在织布机上编织成基布层，经纱为35-45份混有除虫菌溶剂的亚麻纤维和5-15份混有艾草提取液的高遮光性纤维线构成的混合纤维，纬纱为13-25份的茶叶纤维和25-37份混有薰衣草提取液的聚酯纤维构成的混合纤维；
4）用PA胶对步骤3）中的基布层的上下两面进行打底，所述PA胶中各组分的质量份数包括70-95份PA涂胶、2-3份交联剂以及3-7份溶剂；
5）将步骤2）中的网眼布放置于涂覆机内，基布层放置于网眼布上，将吸湿透气面料层、防蚊防虫层、防风层、防潮层以及防水层按照一定的顺序涂覆于经步骤4）处理过的基布层上；
6）步骤5）中涂覆好的基布层上加入一定量的粘合剂后，将面料层放置在设有涂覆层的基布层上，用橡胶辊将基布层与面料层压紧，形成密闭的空间，然后向网眼布的下端进行充气，让网眼布内部膨胀成气囊，使网眼布、基布层紧贴在面料层的内表面上，再经过热烘箱加热使基布层上PA胶以及粘合剂进行软化，在气囊空气压力的作用下与面料层、网眼布的表面进行粘贴，使之成为一体，然后将帐篷布料放置到冷却架上进行冷却。
由于采用了以上技术，本发明较现有技术相比，具有的有益效果如下：
本发明是一种具有防蚊防虫功能的帐篷布料，本发明中添加有菖蒲、核桃叶、艾蒿、桉树叶、皂角提、苦檀叶，可以有效防止孑孓、成蚊、苍蝇以及蛆虫等蚊虫类的干扰，可以有效的驱除蚊虫，避免蚊虫的干扰；本发明中设有网眼布，可以防止外界的蚊虫飞入帐篷内，对帐篷有一定的阻挡作用，可以有效防止蚊虫进入帐篷；本发明中设有吸湿透气面料层、防蚊防虫层、防风层、防潮层以及防水层，使帐篷具有透气、防蚊虫、防风、防潮以及防水的功能。
具体实施方式
下面结合具体实施方式，进一步阐明本发明。
实施例1：
一种具有防蚊防虫功能的帐篷布料，包括网眼布、设置在网眼布上的基布层以及设置在基布层上的面料层，所述基布层与面料层之间设有涂覆层，所述涂覆层从下到上依次设有吸湿透气面料层、防蚊防虫层、防风层、防潮层以及防水层，所述面料层为PU涂层牛津布。
所述网眼布包括聚乙烯PE纱线，所述聚乙烯PE纱线包括药品纱线，所述药品纱线内含有杀虫剂。
所述吸湿透气面料层包括高遮光性纤维层，所述高遮光性纤维层包括高遮光性纤维线。
所述防潮层为B型硅胶以及活性炭粉的混合物。
具有防蚊防虫功能的帐篷布料的生产工艺如下：
1）将35份聚氨酯树脂、28份聚氯乙烯树脂、10份交联剂以及其他助剂放在一起进行搅拌混合，将搅拌好的混合物放入注塑机中进行加工，并将加工好后的混合物中依次加入7份菖蒲提取液、3份核桃叶提取液、3份艾蒿提取液、3份桉树叶提取液、10份皂角提取液、1份苦檀叶提取液并继续进行反应，将反应后的混合物进行冷却处理，即可得到防蚊防虫层；
2）将25份色母、3份防老化剂、50份高密度聚乙烯、15份低密度聚乙烯以及其他助剂放入搅拌机中进行搅拌，并将搅拌之后的混合物放入挤出机中进行加工，并向加工好后的混合物中加入25份除虫菊花、25份榆树皮、58份除虫菊叶的混合物进行反应，混合充分后并将物料加热至150℃并拉成丝，并将拉出的丝线冷却后放置在编织机上进行编织，并形成网眼布；
3）将经纱和纬纱放置在织布机上编织成基布层，经纱为35份混有除虫菌溶剂的亚麻纤维和15份混有艾草提取液的高遮光性纤维线构成的混合纤维，纬纱为13份的茶叶纤维和37份混有薰衣草提取液的聚酯纤维构成的混合纤维；
4）用PA胶对步骤3）中的基布层的上下两面进行打底，所述PA胶中各组分的质量份数包括70份PA涂胶、3份交联剂以及3份溶剂；
5）将步骤2）中的网眼布放置于涂覆机内，基布层放置于网眼布上，将吸湿透气面料层、防蚊防虫层、防风层、防潮层以及防水层按照一定的顺序涂覆于经步骤4）处理过的基布层上；
6）步骤5）中涂覆好的基布层上加入一定量的粘合剂后，将面料层放置在设有涂覆层的基布层上，用橡胶辊将基布层与面料层压紧，形成密闭的空间，然后向网眼布的下端进行充气，让网眼布内部膨胀成气囊，使网眼布、基布层紧贴在面料层的内表面上，再经过热烘箱加热使基布层上PA胶以及粘合剂进行软化，在气囊空气压力的作用下与面料层、网眼布的表面进行粘贴，使之成为一体，然后将帐篷布料放置到冷却架上进行冷却。
实施例2：
一种具有防蚊防虫功能的帐篷布料，包括网眼布、设置在网眼布上的基布层以及设置在基布层上的面料层，所述基布层与面料层之间设有涂覆层，所述涂覆层从下到上依次设有吸湿透气面料层、防蚊防虫层、防风层、防潮层以及防水层，所述面料层为PU涂层牛津布。
所述网眼布包括聚乙烯PE纱线，所述聚乙烯PE纱线包括药品纱线，所述药品纱线内含有杀虫剂。
所述吸湿透气面料层包括高遮光性纤维层，所述高遮光性纤维层包括高遮光性纤维线。
所述防潮层为B型硅胶以及活性炭粉的混合物。
具有防蚊防虫功能的帐篷布料的生产工艺如下：
1）将45份聚氨酯树脂、20份聚氯乙烯树脂、17份交联剂以及其他助剂放在一起进行搅拌混合，将搅拌好的混合物放入注塑机中进行加工，并将加工好后的混合物中依次加入5份菖蒲提取液、5份核桃叶提取液、2份艾蒿提取液、4份桉树叶提取液、7份皂角提取液、2份苦檀叶提取液并继续进行反应，将反应后的混合物进行冷却处理，即可得到防蚊防虫层；
2）将5份色母、15份防老化剂、35份高密度聚乙烯、25份低密度聚乙烯以及其他助剂放入搅拌机中进行搅拌，并将搅拌之后的混合物放入挤出机中进行加工，并向加工好后的混合物中加入15份除虫菊花、35份榆树皮、42份除虫菊叶的混合物进行反应，混合充分后并将物料加热至200℃并拉成丝，并将拉出的丝线冷却后放置在编织机上进行编织，并形成网眼布；
3）将经纱和纬纱放置在织布机上编织成基布层，经纱为45份混有除虫菌溶剂的亚麻纤维和5份混有艾草提取液的高遮光性纤维线构成的混合纤维，纬纱为25份的茶叶纤维和25份混有薰衣草提取液的聚酯纤维构成的混合纤维；
4）用PA胶对步骤3）中的基布层的上下两面进行打底，所述PA胶中各组分的质量份数包括95份PA涂胶、2份交联剂以及7份溶剂；
5）将步骤2）中的网眼布放置于涂覆机内，基布层放置于网眼布上，将吸湿透气面料层、防蚊防虫层、防风层、防潮层以及防水层按照一定的顺序涂覆于经步骤4）处理过的基布层上；
6）步骤5）中涂覆好的基布层上加入一定量的粘合剂后，将面料层放置在设有涂覆层的基布层上，用橡胶辊将基布层与面料层压紧，形成密闭的空间，然后向网眼布的下端进行充气，让网眼布内部膨胀成气囊，使网眼布、基布层紧贴在面料层的内表面上，再经过热烘箱加热使基布层上PA胶以及粘合剂进行软化，在气囊空气压力的作用下与面料层、网眼布的表面进行粘贴，使之成为一体，然后将帐篷布料放置到冷却架上进行冷却。
实施例3：
一种具有防蚊防虫功能的帐篷布料，包括网眼布、设置在网眼布上的基布层以及设置在基布层上的面料层，所述基布层与面料层之间设有涂覆层，所述涂覆层从下到上依次设有吸湿透气面料层、防蚊防虫层、防风层、防潮层以及防水层，所述面料层为PU涂层牛津布。
所述网眼布包括聚乙烯PE纱线，所述聚乙烯PE纱线包括药品纱线，所述药品纱线内含有杀虫剂。
所述吸湿透气面料层包括高遮光性纤维层，所述高遮光性纤维层包括高遮光性纤维线。
所述防潮层为B型硅胶以及活性炭粉的混合物。
具有防蚊防虫功能的帐篷布料的生产工艺如下：
1）将35份聚氨酯树脂、28份聚氯乙烯树脂、12份交联剂以及其他助剂放在一起进行搅拌混合，将搅拌好的混合物放入注塑机中进行加工，并将加工好后的混合物中依次加入5份菖蒲提取液、4份核桃叶提取液、2份艾蒿提取液、4份桉树叶提取液、8份皂角提取液、1份苦檀叶提取液并继续进行反应，将反应后的混合物进行冷却处理，即可得到防蚊防虫层；
2）将20份色母、10份防老化剂、35份高密度聚乙烯、25份低密度聚乙烯以及其他助剂放入搅拌机中进行搅拌，并将搅拌之后的混合物放入挤出机中进行加工，并向加工好后的混合物中加入15份除虫菊花、35份榆树皮、50份除虫菊叶的混合物进行反应，混合充分后并将物料加热至250℃并拉成丝，并将拉出的丝线冷却后放置在编织机上进行编织，并形成网眼布；
3）将经纱和纬纱放置在织布机上编织成基布层，经纱为40份混有除虫菌溶剂的亚麻纤维和10份混有艾草提取液的高遮光性纤维线构成的混合纤维，纬纱为13份的茶叶纤维和37份混有薰衣草提取液的聚酯纤维构成的混合纤维；
4）用PA胶对步骤3）中的基布层的上下两面进行打底，所述PA胶中各组分的质量份数包括85份PA涂胶、2份交联剂以及6份溶剂；
5）将步骤2）中的网眼布放置于涂覆机内，基布层放置于网眼布上，将吸湿透气面料层、防蚊防虫层、防风层、防潮层以及防水层按照一定的顺序涂覆于经步骤4）处理过的基布层上；
6）步骤5）中涂覆好的基布层上加入一定量的粘合剂后，将面料层放置在设有涂覆层的基布层上，用橡胶辊将基布层与面料层压紧，形成密闭的空间，然后向网眼布的下端进行充气，让网眼布内部膨胀成气囊，使网眼布、基布层紧贴在面料层的内表面上，再经过热烘箱加热使基布层上PA胶以及粘合剂进行软化，在气囊空气压力的作用下与面料层、网眼布的表面进行粘贴，使之成为一体，然后将帐篷布料放置到冷却架上进行冷却。
表1 帐篷的实施性能测试结果
| 实验组 | 时间/h | 实施例1 | 实施例2 | 实施例3 |
| 1 | 12 | 帐篷四周没有蚊虫，帐篷内没有蚊虫 | 帐篷四周没有蚊虫，帐篷内没有蚊虫 | 帐篷四周没有蚊虫，帐篷内没有蚊虫 |
| 2 | 24 | 帐篷四周没有蚊虫，帐篷内没有蚊虫 | 帐篷四周没有蚊虫，帐篷内没有蚊虫 | 帐篷四周没有蚊虫，帐篷内没有蚊虫 |
| 3 | 36 | 帐篷四周没有蚊虫，帐篷内没有蚊虫 | 帐篷四周没有蚊虫，帐篷内没有蚊虫 | 帐篷四周没有蚊虫，帐篷内没有蚊虫 |
| 4 | 48 | 帐篷四周没有蚊虫，帐篷内没有蚊虫 | 帐篷四周没有蚊虫，帐篷内没有蚊虫 | 帐篷四周没有蚊虫，帐篷内没有蚊虫 |
| 5 | 60 | 帐篷四周没有蚊虫，帐篷内没有蚊虫 | 帐篷四周没有蚊虫，帐篷内没有蚊虫 | 帐篷四周没有蚊虫，帐篷内没有蚊虫 |
| 6 | 72 | 帐篷四周没有蚊虫，帐篷内没有蚊虫 | 帐篷四周没有蚊虫，帐篷内没有蚊虫 | 帐篷四周没有蚊虫，帐篷内没有蚊虫 |
| 7 | 84 | 帐篷四周没有蚊虫，帐篷内没有蚊虫 | 帐篷四周没有蚊虫，帐篷内没有蚊虫 | 帐篷四周没有蚊虫，帐篷内没有蚊虫 |
上述实施例仅为本发明的优选技术方案，而不应视为对于本发明的限制，本发明的保护范围应以权利要求记载的技术方案，包括权利要求记载的技术方案中技术特征的等同替换方案为保护范围，即在此范围内的等同替换改进，也在本发明的保护范围之内。
Claims (3)
1.一种具有防蚊防虫功能的帐篷布料，其特征在于：包括网眼布、设置在网眼布上的基布层以及设置在基布层上的面料层，所述基布层与面料层之间设有涂覆层，所述涂覆层从下到上依次设有吸湿透气面料层、防蚊防虫层、防风层、防潮层以及防水层，所述基布层由经纱和纬纱交织织成，经纱为35-45份混有除虫菌溶剂的亚麻纤维和5-15份混有艾草提取液的高遮光性纤维线构成的混合纤维，纬纱为13-25份的茶叶纤维和25-37份混有薰衣草提取液的聚酯纤维构成的混合纤维，所述面料层为PU涂层牛津布；所述具有防蚊防虫功能的帐篷布料的生产工艺如下：
1）将35-45份聚氨酯树脂、20-28份聚氯乙烯树脂、10-17份交联剂以及其他助剂放在一起进行搅拌混合，将搅拌好的混合物放入注塑机中进行加工，并将加工好后的混合物中依次加入5-7份菖蒲提取液、3-5份核桃叶提取液、2-3份艾蒿提取液、3-4份桉树叶提取液、7-10份皂角提取液、1-2份苦檀叶提取液并继续进行反应，将反应后的混合物进行冷却处理，即可得到防蚊防虫层；
2）将5-25份色母、3-15份防老化剂、35-50份高密度聚乙烯、15-25份低密度聚乙烯以及其他助剂放入搅拌机中进行搅拌，并将搅拌之后的混合物放入挤出机中进行加工，并向加工好后的混合物中加入15-25份除虫菊花、25-35份榆树皮、42-58份除虫菊叶的混合物进行反应，混合充分后并将物料加热至150-250℃并拉成丝，并将拉出的丝线冷却后放置在编织机上进行编织，并形成网眼布；
3）将经纱和纬纱放置在织布机上编织成基布层，经纱为35-45份混有除虫菌溶剂的亚麻纤维和5-15份混有艾草提取液的高遮光性纤维线构成的混合纤维，纬纱为13-25份的茶叶纤维和25-37份混有薰衣草提取液的聚酯纤维构成的混合纤维；
4）用PA胶对步骤3）中的基布层的上下两面进行打底，所述PA胶中各组分的质量份数包括70-95份PA涂胶、2-3份交联剂以及3-7份溶剂；
5）将步骤2）中的网眼布放置于涂覆机内，基布层放置于网眼布上，将吸湿透气面料层、防蚊防虫层、防风层、防潮层以及防水层按照一定的顺序涂覆于经步骤4）处理过的基布层上；
6）步骤5）中涂覆好的基布层上加入一定量的粘合剂后，将面料层放置在设有涂覆层的基布层上，用橡胶辊将基布层与面料层压紧，形成密闭的空间，然后向网眼布的下端进行充气，让网眼布内部膨胀成气囊，使网眼布、基布层紧贴在面料层的内表面上，再经过热烘箱加热使基布层上PA胶以及粘合剂进行软化，在气囊空气压力的作用下与面料层、网眼布的表面进行粘贴，使之成为一体，然后将帐篷布料放置到冷却架上进行冷却。
2.根据权利要求1所述的一种具有防蚊防虫功能的帐篷布料，其特征在于：所述吸湿透气面料层包括高遮光性纤维层，所述高遮光性纤维层包括高遮光性纤维线。
3.根据权利要求1所述的一种具有防蚊防虫功能的帐篷布料，其特征在于：所述防潮层为B型硅胶以及活性炭粉的混合物。