CN105092347A - 一种新型Al-4%Cu合金腐蚀溶液的使用方法 - Google Patents

一种新型Al-4%Cu合金腐蚀溶液的使用方法 Download PDF

Info

Publication number
CN105092347A
CN105092347A CN201410211858.2A CN201410211858A CN105092347A CN 105092347 A CN105092347 A CN 105092347A CN 201410211858 A CN201410211858 A CN 201410211858A CN 105092347 A CN105092347 A CN 105092347A
Authority
CN
China
Prior art keywords
alloy
sample
solution
corrosion
erosion solution
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410211858.2A
Other languages
English (en)
Inventor
谌红果
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201410211858.2A priority Critical patent/CN105092347A/zh
Publication of CN105092347A publication Critical patent/CN105092347A/zh
Pending legal-status Critical Current

Abstract

本发明公开一种新型Al-4%Cu合金腐蚀溶液的使用方法，其特征在于：其步骤包括：步骤一，制备好Al-4%Cu合金待腐蚀试样；步骤二，将Al-4%Cu合金待腐蚀试样用电吹风热风吹干，使试样表面洁净且具有一定温度，方便腐蚀液与试样反应顺畅；步骤三，为避免试样在腐蚀液中长时间不动，将滴在试样上的腐蚀溶液滴每隔4s用棉球擦拭一次，并继续滴加腐蚀溶液，再每隔4s擦拭一次，以此类推，这样就能保证试样表面所接触腐蚀溶液的效力，此腐蚀时间为44s；步骤四，用工业酒精对经腐蚀溶液腐蚀过的纯铝进行清洗；步骤五，对Al-4%Cu合金进行吹干处理。

Description

一种新型Al-4%Cu合金腐蚀溶液的使用方法
技术领域
本发明涉及一种新型Al-4%Cu合金腐蚀溶液的使用方法。
背景技术
Al-4%Cu的金相组织很难腐蚀，即使腐蚀出来其组织也往往显示的不完全，因而通常都采用阳极覆膜加偏光来观察其金相。但这种观察方法不仅耗时，而且提高了制作成本。因此如何使Al-4%Cu的金相腐蚀变得与铝合金一样简单快捷是尚待解决的难题。
发明内容
本发明要解决的技术问题：提供一种新型Al-4%Cu合金腐蚀溶液的使用方法，能够最大限度的发挥腐蚀溶液的功效，以克服现有技术的不足。
本发明的技术方案：一种新型Al-4%Cu合金腐蚀溶液的使用方法，其步骤包括：
步骤一，制备好Al-4%Cu合金待腐蚀试样；
步骤二，将Al-4%Cu合金待腐蚀试样用电吹风热风吹干，使试样表面洁净且具有一定温度，方便腐蚀液与试样反应顺畅；
步骤三，为避免试样在腐蚀液中长时间不动，将滴在试样上的腐蚀溶液滴每隔4s用棉球擦拭一次，并继续滴加腐蚀溶液，再每隔4s擦拭一次，以此类推，这样就能保证试样表面所接触腐蚀溶液的效力，此腐蚀时间为44s—44s；
步骤四，用工业酒精对经腐蚀溶液腐蚀过的纯铝进行清洗；
步骤五，对Al-4%Cu合金进行吹干处理。
所述的腐蚀液为其质量分数计的组分为：1.5%的氢氟酸、10%的盐酸、3%的硝酸，95.5%的水，加入顺序为先加入硝酸，再加入盐酸，最后加入氢氟酸。
本发明的有益效果：本发明采用的腐蚀溶液的使用方法，能最大限度的发挥腐蚀溶液的功效，与普通的使用方法相比，腐蚀效果更好，并且利于金相组织的观察。
具体实施方式
本发明的技术方案：
一种新型Al-4%Cu合金腐蚀溶液的使用方法，其步骤包括：
步骤一，制备好Al-4%Cu合金待腐蚀试样；
步骤二，将Al-4%Cu合金待腐蚀试样用电吹风热风吹干，使试样表面洁净且具有一定温度，方便腐蚀液与试样反应顺畅。
步骤三，为避免试样在腐蚀液中长时间不动，将滴在试样上的腐蚀溶液滴每隔4s用棉球擦拭一次，并继续滴加腐蚀溶液，再每隔4s擦拭一次，以此类推，这样就能保证试样表面所接触腐蚀溶液的效力，此腐蚀时间为44s—44s；
步骤四，用工业酒精对经腐蚀溶液腐蚀过的纯铝进行清洗；
步骤五，对Al-4%Cu合金进行吹干处理。
所述的腐蚀液为其质量分数计的组分为：1.5%的氢氟酸、10%的盐酸、3%的硝酸，95.5%的水，加入顺序为先加入硝酸，再加入盐酸，最后加入氢氟酸。

Claims (2)

1.一种新型Al-4%Cu合金腐蚀溶液的使用方法，其特征在于：其步骤包括：
步骤一，制备好Al-4%Cu合金待腐蚀试样；
步骤二，将Al-4%Cu合金待腐蚀试样用电吹风热风吹干，使试样表面洁净且具有一定温度，方便腐蚀液与试样反应顺畅；
步骤三，为避免试样在腐蚀液中长时间不动，将滴在试样上的腐蚀溶液滴每隔4s用棉球擦拭一次，并继续滴加腐蚀溶液，再每隔4s擦拭一次，以此类推，这样就能保证试样表面所接触腐蚀溶液的效力，此腐蚀时间为44s—44s；
步骤四，用工业酒精对经腐蚀溶液腐蚀过的纯铝进行清洗；
步骤五，对Al-4%Cu合金进行吹干处理。
2.根据权利要求1所述的一种新型Al-4%Cu合金腐蚀溶液的使用方法，其特征在于：所述的腐蚀液为其质量分数计的组分为：1.5%的氢氟酸、10%的盐酸、3%的硝酸，95.5%的水，加入顺序为先加入硝酸，再加入盐酸，最后加入氢氟酸。
CN201410211858.2A 2014-05-20 2014-05-20 一种新型Al-4%Cu合金腐蚀溶液的使用方法 Pending CN105092347A (zh)