CN105062078A - 一种室温快速固化灌封用硅橡胶及其制备方法 - Google Patents
一种室温快速固化灌封用硅橡胶及其制备方法 Download PDFInfo
- Publication number
- CN105062078A CN105062078A CN201510568475.5A CN201510568475A CN105062078A CN 105062078 A CN105062078 A CN 105062078A CN 201510568475 A CN201510568475 A CN 201510568475A CN 105062078 A CN105062078 A CN 105062078A
- Authority
- CN
- China
- Prior art keywords
- silicon rubber
- parts
- room temperature
- curing
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种室温快速固化灌封用硅橡胶及其制备方法，属于有机硅密封胶技术领域。本发明的硅橡胶包括：107液体硅橡胶71-80份、甲基三丙酮肟基硅烷25-35份、正硅酸乙酯8-12份、二月桂酸丁基锡4-6份、添加剂KH-550？0.3-2份、气相法白炭黑10-15份。本发明硅橡胶可在较宽温度范围内长期保持弹性，并具有优良的化学稳定性，耐水性。特别适宜于要求深层固化的应用场合，而且室温下固化速度较快，适合电子产品的灌封。
Description
技术领域
本发明涉及一种硅橡胶及其制备方法，更具体地说，本发明涉及一种室温快速固化灌封用硅橡胶及其制备方法，属于有机硅密封胶技术领域。
背景技术
缩合型双组分室温硫化硅橡胶的主要共聚组分为基础聚合物、交联剂、催化剂等。当共聚组分混合在一起时，即可在室温下发生缩合反应变成弹性体。以该工艺获得的固化硅橡胶可在-65—250℃范围内长期保持弹性，并具有优良的化学稳定性，耐水性。特别适宜于要求深层固化的应用场合，而且固化速度较快。
国家知识产权局于2015.2.25公开了意见公开号为CN104371637A，名称为“单组份脱醇型有机硅灌封胶及其制备方法”的发明，该发明由以下按重量份数配比的原料构成：107硅油100份、补强填料50-250份、硅烷偶联剂0.1-1份、交联剂13-26份和催化剂0.5-1份。由于具有理想的流动性，因而能显著提高在24小时内的固化深度，能满足对太阳能光伏组件接线盒模块外壳的灌封要求；由于24小时内的粘接率可达95%以上，因而具有拔萃的粘接效果；由于配方中的原料选择合理，因而具有优异的耐腐蚀效果，有助于延长密封寿命；提供的制备方法工艺简练，能满足工业化放大生产要求。
上述有机硅灌封胶无法在室温下快速固化，不适合电子产品的灌封。
发明内容
本发明旨在解决现有技术中有机硅灌封胶无法在室温下快速固化的问题，提供一种室温快速固化灌封用硅橡胶，该硅橡胶可以在室温下快速固化，且能够达到相应的综合性能。
为了实现上述发明目的，其具体的技术方案如下：
一种室温快速固化灌封用硅橡胶，其特征在于：包括以下按照重量份数计的原料：
107液体硅橡胶71-80份
甲基三丙酮肟基硅烷25-35份
正硅酸乙酯8-12份
二月桂酸丁基锡4-6份
添加剂KH-5500.3-2份
气相法白炭黑10-15份。
一种室温快速固化灌封用硅橡胶的制备方法，其特征在于：包括以下工艺步骤：
A、按配方精确称取一半的107液体硅橡胶、一半的气相法白炭黑、二月桂酸丁基锡以及甲基三丙酮肟基硅烷，高速搅拌下充分混合均匀为A组分；
B、按配方精确称取另一半的107液体硅橡胶、另一半的气相法白炭黑以及正硅酸乙酯，高速搅拌下充分混合均匀为B组分。
本发明在所述的高速搅拌为1000-2000转/分钟下搅拌1-3小时。
使用时按A组分:B组分为1:2-2:1混合均匀。
本发明带来的有益技术效果：
本发明解决了现有技术中有机硅灌封胶无法在室温下快速固化的问题。本发明硅橡胶可在较宽温度范围内长期保持弹性，并具有优良的化学稳定性，耐水性。特别适宜于要求深层固化的应用场合，而且室温下固化速度较快，适合电子产品的灌封。
具体实施方式
实施例1
一种室温快速固化灌封用硅橡胶，包括以下按照重量份数计的原料：
107液体硅橡胶71份
甲基三丙酮肟基硅烷25份
正硅酸乙酯8份
二月桂酸丁基锡4份
添加剂KH-5500.3份
气相法白炭黑10份。
实施例2
一种室温快速固化灌封用硅橡胶，包括以下按照重量份数计的原料：
107液体硅橡胶80份
甲基三丙酮肟基硅烷35份
正硅酸乙酯12份
二月桂酸丁基锡6份
添加剂KH-5502份
气相法白炭黑15份。
实施例3
一种室温快速固化灌封用硅橡胶，包括以下按照重量份数计的原料：
107液体硅橡胶75.5份
甲基三丙酮肟基硅烷30份
正硅酸乙酯10份
二月桂酸丁基锡5份
添加剂KH-5501.1份
气相法白炭黑12.5份。
实施例4
一种室温快速固化灌封用硅橡胶，包括以下按照重量份数计的原料：
107液体硅橡胶78份
甲基三丙酮肟基硅烷27份
正硅酸乙酯11份
二月桂酸丁基锡5.5份
添加剂KH-5500.7份
气相法白炭黑11份。
实施例5
一种室温快速固化灌封用硅橡胶的制备方法，包括以下工艺步骤：
A、按配方精确称取一半的107液体硅橡胶、一半的气相法白炭黑、二月桂酸丁基锡以及甲基三丙酮肟基硅烷，高速搅拌下充分混合均匀为A组分；
B、按配方精确称取另一半的107液体硅橡胶、另一半的气相法白炭黑以及正硅酸乙酯，高速搅拌下充分混合均匀为B组分。
优选的，在所述的高速搅拌为1000转/分钟下搅拌1小时。
实施例6
一种室温快速固化灌封用硅橡胶的制备方法，包括以下工艺步骤：
A、按配方精确称取一半的107液体硅橡胶、一半的气相法白炭黑、二月桂酸丁基锡以及甲基三丙酮肟基硅烷，高速搅拌下充分混合均匀为A组分；
B、按配方精确称取另一半的107液体硅橡胶、另一半的气相法白炭黑以及正硅酸乙酯，高速搅拌下充分混合均匀为B组分。
优选的，在所述的高速搅拌为2000转/分钟下搅拌3小时。
实施例7
一种室温快速固化灌封用硅橡胶的制备方法，包括以下工艺步骤：
A、按配方精确称取一半的107液体硅橡胶、一半的气相法白炭黑、二月桂酸丁基锡以及甲基三丙酮肟基硅烷，高速搅拌下充分混合均匀为A组分；
B、按配方精确称取另一半的107液体硅橡胶、另一半的气相法白炭黑以及正硅酸乙酯，高速搅拌下充分混合均匀为B组分。
优选的，在所述的高速搅拌为1500转/分钟下搅拌2小时。
实施例8
一种室温快速固化灌封用硅橡胶的制备方法，包括以下工艺步骤：
A、按配方精确称取一半的107液体硅橡胶、一半的气相法白炭黑、二月桂酸丁基锡以及甲基三丙酮肟基硅烷，高速搅拌下充分混合均匀为A组分；
B、按配方精确称取另一半的107液体硅橡胶、另一半的气相法白炭黑以及正硅酸乙酯，高速搅拌下充分混合均匀为B组分。
优选的，在所述的高速搅拌为1200转/分钟下搅拌2.5小时。
Claims (3)
1.一种室温快速固化灌封用硅橡胶，其特征在于：包括以下按照重量份数计的原料：
107液体硅橡胶71-80份
甲基三丙酮肟基硅烷25-35份
正硅酸乙酯8-12份
二月桂酸丁基锡4-6份
添加剂KH-5500.3-2份
气相法白炭黑10-15份。
2.根据权利要求1所述的一种室温快速固化灌封用硅橡胶的制备方法，其特征在于：包括以下工艺步骤：
A、按配方精确称取一半的107液体硅橡胶、一半的气相法白炭黑、二月桂酸丁基锡以及甲基三丙酮肟基硅烷，高速搅拌下充分混合均匀为A组分；
B、按配方精确称取另一半的107液体硅橡胶、另一半的气相法白炭黑以及正硅酸乙酯，高速搅拌下充分混合均匀为B组分。
3.根据权利要求2所述的一种室温快速固化灌封用硅橡胶的制备方法，其特征在于：在所述的高速搅拌为1000-2000转/分钟下搅拌1-3小时。