CN104947301A - 一种防卷边针织面料及其后整理方法 - Google Patents
一种防卷边针织面料及其后整理方法 Download PDFInfo
- Publication number
- CN104947301A CN104947301A CN201510284397.6A CN201510284397A CN104947301A CN 104947301 A CN104947301 A CN 104947301A CN 201510284397 A CN201510284397 A CN 201510284397A CN 104947301 A CN104947301 A CN 104947301A
- Authority
- CN
- China
- Prior art keywords
- fibre
- fiber
- protein
- knit fabric
- edge curl
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种防卷边针织面料及其后整理方法,面料由内中外三层分别由不同组份复合而成:三层分别选择合适的织物纤维进行复合,再进行纱织而成,加强了针织面料的牢固度,很大程度降低了其卷边现象的发生;此外采用柠檬酸和偏磷酸钠以及渗透剂的助剂进行后整理并结合进一步增强了面料的质感舒适度和定型程度。
Description
技术领域
本发明涉及服装的制作工艺,尤其涉及一种防卷边针织面料及其后整理方法。
背景技术
针织即是利用织针将纱线弯曲成圈并相互串套而形成的织物。针织面料与梭织面料的不同之处在于纱线在织物中的形态不同。针织分为纬编和经编;目前,针织面料广泛应用于服装面料及里料,家纺等产品中,受到广大消费者的喜爱。但是针织面料存在一个很常见的问题,就是在衣物加工的工程中容易发生卷边的现象,给生产者带来了很大的困扰。
因此,需要一种新的技术方案以解决上述问题。
发明内容
发明目的:为了解决现有技术所存在的问题,本发明提供了一种有效降低针织面料卷边现象发生的一种防卷边针织面料及其后整理方法。
技术方案:为达到上述目的,本发明的技术方案如下:一种防卷边针织面料,由三层纱线复合而成;其中各层由不同的织物组份复合而成:其中内层由以下两种成分复合组成:a1蛋白质纤维;b1莫代尔纤维;中层由以下三种成分复合组成:a2牛奶蛋白棉混纺纤维;b2纤维素纤维;c2腈纶纤维;外层由以下两种成分复合组成:a3再生蛋白纤维;b3天丝纤维,c3竹纤维;所述面料每平方米的重量为100-150g;所述面料的厚度为0.6-2.5mm;所述中层中a2牛奶蛋白棉混纺纤维;b2纤维素纤维;c2腈纶纤维重量比为4:3:1。
在一些实施方式中,所述a1蛋白质纤维为羊毛纤维或兔毛纤维。
在一些实施方式中,所述b2纤维素纤维为棉纤维、棉麻混纺纤维中的一种或两种。
在一些实施方式中,所述a3再生蛋白纤维为玉米纤维、大豆纤维中的一种或两种。
在一些实施方式中,所述a2牛奶蛋白棉混纺纤维中棉纤维含量不低于75%。
在一些实施方式中,所述内层中a1蛋白质纤维和b1莫代尔纤维的重量比为1:3。
在一些实施方式中,所述外层中a3再生蛋白纤维;b3天丝纤维,c3竹纤维的重量比为4:1:3。
上述一种防卷边针织面料的后整理方法,首先将面料成品装袋投入水洗机,加入4-8g/L质量比为2:1的柠檬酸和偏磷酸钠的混合物以及2-5g/L的渗透剂,浴比1:30-1:40,水洗时间30-40min,温度40-50℃,水洗完毕后脱水至5成干,清水中浸泡20-30min后取出自然晾干。
更为优选的,所述渗透剂为非离子型渗透剂。
有益效果:本发明所提供的一种防卷边针织面料及其后整理方法,面料由内中外三层分别由不同组份复合而成:三层分别选择合适的织物纤维进行复合,再进行纱织而成,加强了针织面料的牢固度,很大程度降低了其卷边现象的发生;此外采用柠檬酸和偏磷酸钠以及渗透剂的助剂进行后整理并结合进一步增强了面料的质感舒适度和定型程度。
具体实施方式
实施例1:
一种防卷边针织面料,由三层纱线复合而成;其中各层由不同的织物组份复合而成:其中内层由以下两种成分复合组成:a1蛋白质纤维;b1莫代尔纤维;中层由以下三种成分复合组成:a2牛奶蛋白棉混纺纤维;b2纤维素纤维;c2腈纶纤维;外层由以下两种成分复合组成:a3再生蛋白纤维;b3天丝纤维,c3竹纤维;所述面料每平方米的重量为100g;所述面料的厚度为0.6mm;所述内层中a1蛋白质纤维和b1莫代尔纤维的重量比为1:3;所述中层中a2牛奶蛋白棉混纺纤维、b2纤维素纤维以及c2腈纶纤维重量比为4:3:1;所述外层中a3再生蛋白纤维;b3天丝纤维,c3竹纤维的重量比为4:1:3。
其中,a1蛋白质纤维为羊毛纤维;b2纤维素纤维为棉纤维;a3再生蛋白纤维为玉米纤维;a2牛奶蛋白棉混纺纤维中棉纤维含量为75%。
上述一种防卷边针织面料的后整理方法,首先将面料成品装袋投入水洗机,加入4g/L质量比为2:1的柠檬酸和偏磷酸钠的混合物以及2g/L的非离子型渗透剂,浴比1:30,水洗时间30min,温度40℃,水洗完毕后脱水至5成干,清水中浸泡20min后取出自然晾干。
实施例2:
一种防卷边针织面料,由三层纱线复合而成;其中各层由不同的织物组份复合而成:其中内层由以下两种成分复合组成:a1蛋白质纤维;b1莫代尔纤维;中层由以下三种成分复合组成:a2牛奶蛋白棉混纺纤维;b2纤维素纤维;c2腈纶纤维;外层由以下两种成分复合组成:a3再生蛋白纤维;b3天丝纤维,c3竹纤维;所述面料每平方米的重量为150g;所述面料的厚度为2.5mm;所述内层中a1蛋白质纤维和b1莫代尔纤维的重量比为1:3;所述中层中a2牛奶蛋白棉混纺纤维、b2纤维素纤维以及c2腈纶纤维重量比为4:3:1;所述外层中a3再生蛋白纤维;b3天丝纤维,c3竹纤维的重量比为4:1:3。
其中,a1蛋白质纤维为兔毛纤维;b2纤维素纤维为棉麻混纺纤维;a3再生蛋白纤维为大豆纤维;a2牛奶蛋白棉混纺纤维中棉纤维含量为85%。
上述一种防卷边针织面料的后整理方法,首先将面料成品装袋投入水洗机,加入8g/L质量比为2:1的柠檬酸和偏磷酸钠的混合物以及5g/L的非离子型渗透剂,浴比1:40,水洗时间40min,温度50℃,水洗完毕后脱水至5成干,清水中浸泡30min后取出自然晾干。
实施例3:
一种防卷边针织面料,由三层纱线复合而成;其中各层由不同的织物组份复合而成:其中内层由以下两种成分复合组成:a1蛋白质纤维;b1莫代尔纤维;中层由以下三种成分复合组成:a2牛奶蛋白棉混纺纤维;b2纤维素纤维;c2腈纶纤维;外层由以下两种成分复合组成:a3再生蛋白纤维;b3天丝纤维,c3竹纤维;所述面料每平方米的重量为130g;所述面料的厚度为1.5mm;所述内层中a1蛋白质纤维和b1莫代尔纤维的重量比为1:3;所述中层中a2牛奶蛋白棉混纺纤维、b2纤维素纤维以及c2腈纶纤维重量比为4:3:1;所述外层中a3再生蛋白纤维;b3天丝纤维,c3竹纤维的重量比为4:1:3。
其中,a1蛋白质纤维为羊毛纤维;b2纤维素纤维为棉纤维、棉麻混纺纤维两者质量比为1:3的混合物;a3再生蛋白纤维为玉米纤维、大豆纤维质量比为4:3的混合物;a2牛奶蛋白棉混纺纤维中棉纤维含量为95%。
上述一种防卷边针织面料的后整理方法,首先将面料成品装袋投入水洗机,加入6g/L质量比为2:1的柠檬酸和偏磷酸钠的混合物以及4g/L的非离子型渗透剂,浴比1:35,水洗时间35min,温度45℃,水洗完毕后脱水至5成干,清水中浸泡25min后取出自然晾干。
应当指出,以上具体实施方式仅用于说明本发明而不用于限制本发明的范围,在阅读了本发明之后,本领域技术人员对本发明的各种等价形式的修改均落于本申请所附权利要求所限定的范围。
Claims (9)
1.一种防卷边针织面料,其特征在于由三层纱线复合而成;其中各层由不同的织物组份复合而成:其中内层由以下两种成分复合组成:a1蛋白质纤维;b1莫代尔纤维;中层由以下三种成分复合组成:a2牛奶蛋白棉混纺纤维;b2纤维素纤维;c2腈纶纤维;外层由以下两种成分复合组成:a3再生蛋白纤维;b3天丝纤维,c3竹纤维;所述面料每平方米的重量为100-150g;所述面料的厚度为0.6-2.5mm;所述中层中a2牛奶蛋白棉混纺纤维;b2纤维素纤维;c2腈纶纤维重量比为4:3:1。
2.根据权利要求1所述的一种防卷边针织面料,其特征在于:所述a1蛋白质纤维为羊毛纤维或兔毛纤维。
3.根据权利要求1所述的一种防卷边针织面料,其特征在于:所述b2纤维素纤维为棉纤维、棉麻混纺纤维中的一种或两种。
4.根据权利要求1所述的一种防卷边针织面料,其特征在于:所述a3再生蛋白纤维为玉米纤维、大豆纤维中的一种或两种。
5.根据权利要求1所述的一种防卷边针织面料,其特征在于:所述a2牛奶蛋白棉混纺纤维中棉纤维含量不低于75%。
6.根据权利要求1所述的一种防卷边针织面料,其特征在于:所述内层中a1蛋白质纤维和b1莫代尔纤维的重量比为1:3。
7.根据权利要求1所述的一种防卷边针织面料,其特征在于:所述外层中a3再生蛋白纤维;b3天丝纤维,c3竹纤维的重量比为4:1:3。
8.如权利要求1所述的一种防卷边针织面料的后整理方法,其特征在于:首先将面料成品装袋投入水洗机,加入4-8g/L质量比为2:1的柠檬酸和偏磷酸钠的混合物以及2-5g/L的渗透剂,浴比1:30-1:40,水洗时间30-40min,温度40-50℃,水洗完毕后脱水至5成干,清水中浸泡20-30min后取出自然晾干。
9.根据权利要求8所述的一种防卷边针织面料的后整理方法,其特征在于:所述渗透剂为非离子型渗透剂。