CN104788624A - 阻燃型透光板材树脂及其制备方法 - Google Patents
阻燃型透光板材树脂及其制备方法 Download PDFInfo
- Publication number
- CN104788624A CN104788624A CN201510168165.4A CN201510168165A CN104788624A CN 104788624 A CN104788624 A CN 104788624A CN 201510168165 A CN201510168165 A CN 201510168165A CN 104788624 A CN104788624 A CN 104788624A
- Authority
- CN
- China
- Prior art keywords
- parts
- ethylene glycol
- propylene glycol
- flame retardant
- dilution
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明涉及一种阻燃型透光板材树脂。其原料配方质量份组成为：HET酸40-50份、丙二醇12-19份、乙二醇9-13份、顺酐10-15份、邻苯二甲酸酐15-20份、苯乙烯40-70份、氢醌0.01-0.03份。制备时，将HET酸、丙二醇、乙二醇、氢醌、顺酐加入反应釜中，加热到200℃，反应脱水直到酸值到45mgKOH/g，反应过程中通氮气保护；停止通氮气，抽真空进一步脱水，直到酸值到30mgKOH/g；冷却到160℃，将反应完成的聚酯抽入已经加入含苯乙烯的稀释釜中稀释；确保稀释温度不超过80℃。其阻燃性能好、高透光性、与玻璃纤维折射率接近、工艺性好。
Description
技术领域
本发明涉及一种阻燃型透光板材树脂及其制备方法，该树脂主要用于制造采光瓦。
背景技术
工业厂房屋面墙面采光，农业蔬菜大棚保温采光，公共体育场馆屋面采光，特殊要求的建筑物阻燃防腐隔热等场所；还有仓库、温室、车站、码头、航空港、商业建筑、钢结构等诸多采光领域均需要使用采光瓦。
现有的彩光瓦都不具有阻燃性，而随着安全生产规范的实施，阻燃防火将变成强制性指标之一，但是常规的彩光瓦用树脂，为提高其阻燃性能，通常采取以下措施：
1、在树脂体系中添加氢氧化铝，但是这种做法会使树脂粘度升高，后续制成采光瓦过程中，与玻璃纤维浸润性不好，工艺性差。
2、在树脂体系中添加DCPP（苯基二氯化磷），阻燃性提高，但是降低的最终产品的强度；
3、在树脂体系中添加三氧化二锑，树脂透光性变差，且粘度升高、工艺性差。
发明内容
本发明的目的之一在于克服上述不足，提供一种阻燃性能好、高透光性、与玻璃纤维折射率接近、工艺性好的阻燃型透光板材树脂。
本发明目的之二在于提供一种阻燃型透光板材树脂的制备方法。
本发明的目的是这样实现的：
一种阻燃型透光板材树脂，其原料配方质量份组成为：
HET酸（海特酸） 40-50份
丙二醇 12-19份
乙二醇 9-13份
顺酐 10-15份
邻苯二甲酸酐 15-20份
苯乙烯 40-70份
氢醌 0.01-0.03份。
其中：
HET酸给予树脂阻燃性能，丙二醇、乙二醇、苯酐、顺酐为反应生产长链聚酯分子结构组成，其中顺酐给予树脂交联可反应性，苯乙烯起稀释交联作用，氢醌为防止生产树脂过程中发生胶凝，并调整树脂产品在使用过程中的凝胶时间。
作为本发明阻燃型透光板材树脂优选方案，其原料配方质量份组成为：
HET酸 44.6份
丙二醇 16.5份
乙二醇 10.7份
顺酐 11.2份
邻苯二甲酸酐 17.0份
苯乙烯 50份
氢醌 0.015份。
一种阻燃型透光板材树脂的制备方法：将计量准确的HET酸、丙二醇、乙二醇、氢醌、顺酐加入反应釜中，加热到200±5℃，反应脱水直到酸值到45±2mgKOH/g，反应过程中通氮气保护。停止通氮气，抽真空进一步脱水，直到酸值到30±1mgKOH/g。冷却到160±5℃，将反应完成的聚酯抽入已经加入计量准确苯乙烯的稀释釜中稀释。确保稀释温度不超过80℃。检验产品，合格后出料。
与现有技术相比，本发明的有益效果是：
1、制成的采光瓦氧指数达32，反应性阻燃，阻燃元素添加在树脂分子链上；
2、透光率高，做成1.5mm厚的玻璃钢，透光率达95%；
3、固化后树脂折光率接近无碱玻璃纤维折光率，界面效应小，透光率高。
4、与玻璃纤维浸润性好，工艺性好。
具体实施方式
实施例1：
一种阻燃型透光板材树脂，其原料配方质量份组成为：
HET酸（海特酸） 44.6份
丙二醇 16.5份
乙二醇 10.7份
顺酐（顺丁烯二酸酐） 11.2份
邻苯二甲酸酐 17.0份
苯乙烯 50份
氢醌 0.015份
制备方法为：将计量准确的HET酸、丙二醇、乙二醇、氢醌、顺酐加入反应釜中，加热到200摄氏度，反应脱水直到酸值到45mgKOH/g，反应过程中通氮气保护。停止通氮气，抽真空进一步脱水，直到酸值到30 mgKOH/g。冷却到160℃，将反应完成的聚酯抽入已经加入计量准确苯乙烯的稀释釜中稀释。确保稀释温度不超过80℃。检验产品，合格后出料。
使用实施例1制备的阻燃型透光板材树脂制成的采光瓦，其氧指数达32；做成1.5mm厚的玻璃钢，透光率达95%；与玻璃纤维浸润性好，工艺性好。固化后树脂折光率接近无碱玻璃纤维折光率，界面效应小，透光率高。
实施例2
一种阻燃型透光板材树脂，其原料配方质量份组成为：
HET酸（海特酸） 47份
丙二醇 18份
乙二醇 12份
顺酐 13份
邻苯二甲酸酐 18份
苯乙烯 60份
氢醌 0.02份
制备方法与实施例1中的方法相同。
使用实施例2制备的阻燃型透光板材树脂制成的采光瓦，其氧指数达31；做成1.5mm厚的玻璃钢，透光率达94%；与玻璃纤维浸润性好，工艺性好。固化后树脂折光率接近无碱玻璃纤维折光率，界面效应小，透光率高。
实施例3
一种阻燃型透光板材树脂，其原料配方质量份组成为：
HET酸（海特酸） 50份
丙二醇 19份
乙二醇 13份
顺酐 15份
邻苯二甲酸酐 20份
苯乙烯 70份
氢醌 0.03份
制备方法：将计量准确的HET酸、丙二醇、乙二醇、氢醌、顺酐加入反应釜中，加热到205摄氏度，反应脱水直到酸值到47mgKOH/g，反应过程中通氮气保护。停止通氮气，抽真空进一步脱水，直到酸值到31 mgKOH/g。冷却到165℃，将反应完成的聚酯抽入已经加入计量准确苯乙烯的稀释釜中稀释。确保稀释温度不超过80℃。检验产品，合格后出料。
使用实施例3制备的阻燃型透光板材树脂制成的采光瓦，其氧指数达32；做成1.5mm厚的玻璃钢，透光率达93%；与玻璃纤维浸润性好，工艺性好。固化后树脂折光率接近无碱玻璃纤维折光率，界面效应小，透光率高。
实施例4
一种阻燃型透光板材树脂，其原料配方质量份组成为：
HET酸（海特酸） 40份
丙二醇 12份
乙二醇 9份
顺酐 10份
邻苯二甲酸酐 15份
苯乙烯 40份
氢醌 0.01份
制备方法：将计量准确的HET酸、丙二醇、乙二醇、氢醌、顺酐加入反应釜中，加热到195摄氏度，反应脱水直到酸值到43mgKOH/g，反应过程中通氮气保护。停止通氮气，抽真空进一步脱水，直到酸值到29 mgKOH/g。冷却到155℃，将反应完成的聚酯抽入已经加入计量准确苯乙烯的稀释釜中稀释。确保稀释温度不超过80℃。检验产品，合格后出料。
使用实施例4制备的阻燃型透光板材树脂制成的采光瓦，其氧指数达32；做成1.5mm厚的玻璃钢，透光率达93%；与玻璃纤维浸润性好，工艺性好。固化后树脂折光率接近无碱玻璃纤维折光率，界面效应小，透光率高。
Claims (4)
1.一种阻燃型透光板材树脂，其特征在于，其原料配方质量份组成为：
HET酸 40-50份
丙二醇 12-19份
乙二醇 9-13份
顺酐 10-15份
邻苯二甲酸酐 15-20份
苯乙烯 40-70份
氢醌 0.01-0.03份。
2.根据权利要求1所述的一种阻燃型透光板材树脂，其特征在于，其原料配方质量份组成为：
HET酸 44.6份
丙二醇 16.5份
乙二醇 10.7份
顺酐 11.2份
邻苯二甲酸酐 17.0份
苯乙烯 50份
氢醌 0.015份。
3.制备权利要求1所述的阻燃型透光板材树脂的方法，其特征在于：将HET酸、丙二醇、乙二醇、氢醌、顺酐加入反应釜中，加热到200±5℃，反应脱水直到酸值到45±2mgKOH/g，反应过程中通氮气保护；停止通氮气，抽真空进一步脱水，直到酸值到30±1mgKOH/g；冷却到160±5℃，将反应完成的聚酯抽入已经加入含苯乙烯的稀释釜中稀释；确保稀释温度不超过80℃。
4.根据权利要求3所述的阻燃型透光板材树脂的制备方法：其特征在于：将HET酸、丙二醇、乙二醇、氢醌、顺酐加入反应釜中，加热到200℃，反应脱水直到酸值到45mgKOH/g，反应过程中通氮气保护；停止通氮气，抽真空进一步脱水，直到酸值到30mgKOH/g；冷却到160℃，将反应完成的聚酯抽入已经加入含苯乙烯的稀释釜中稀释；确保稀释温度不超过80℃。