CN104777551A - 一种低衰减大有效面积的单模光纤 - Google Patents
一种低衰减大有效面积的单模光纤 Download PDFInfo
- Publication number
- CN104777551A CN104777551A CN201510209916.2A CN201510209916A CN104777551A CN 104777551 A CN104777551 A CN 104777551A CN 201510209916 A CN201510209916 A CN 201510209916A CN 104777551 A CN104777551 A CN 104777551A
- Authority
- CN
- China
- Prior art keywords
- optical fiber
- layer
- micrometers
- wrapping layer
- fiber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明涉及一种具有低衰减大有效面积的单模光纤,包括有芯层和包层,其特征在于所述的芯层半径r1为4.8~6.5μm,芯层相对折射率Δ1为0.10%~0.24%,芯层外从内向外依次包覆内包层,下陷内包层,过渡外包层和外包层,所述的光纤的内包层半径r2为8.5~15μm,相对折射率Δ2为-0.3%~-0.05%,所述的下陷内包层半径r3为14~22μm,相对折射率Δ3为-0.45%~-0.2%,所述的过渡外包层半径r4为35~50μm,相对折射率Δ4范围为-0.25%~-0.05%;所述外包层为纯二氧化硅玻璃层。本发明降低了光纤的衰减参数;并通过对光纤各纤芯层剖面的合理设计,使光纤具有等于或大于100μm2的有效面积,本发明的截止波长、弯曲损耗、色散等综合性能参数在应用波段良好,光纤剖面采用多层阶梯状下陷包层结构,对光纤的弯曲损耗具有较好的改进作用。
Description
技术领域
本发明涉及光纤传输技术领域,具体涉及一种具有低衰减大有效面积的单模光纤。
背景技术
随着IP网络数据业务的迅速增长,运营商对于传输容量的需求不断提高,现网中单纤容量已逐渐在逼近极限值100Tbps。100G传输***已开始进入商用元年。如何在100G传输信号的基础上进一步增加传输容量,是各***设备商和运营商关注的焦点。
在100G和超100G***中,接收端采用相干接收及数字信号处理技术(DSP),能够在电域中数字补偿整个传输过程中累积的色散和偏振模色散(PMD);信号通过采用偏振模复用和各种高阶调制方式来降低信号的波特率,例如PM-QPSK、PDM-16QAM、PDM-32QAM,甚至PDM-64QAM和CO-OFDM。然而高阶调制方式对非线性效应非常敏感,因此对光信噪比(OSNR)提出了更高的要求。引入低损耗大有效面积光纤,能为***带来提高OSNR和降低非线性效应的效果当采用高功率密度***时,非线性系数是用于评估非线性效应造成的***性能优劣的参数,其定义为n2/Aeff。其中,n2是传输光纤的非线性折射指数,Aeff是传输光纤的有效面积。增加传输光纤的有效面积,能够降低光纤中的非线性效应。
目前,用于陆地传输***线路的普通单模光纤,其有效面积仅约80μm2左右。而在陆地长距离传输***中,对光纤的有效面积要求更高,一般的有效面积在100μm2以上。为了降低铺设成本,尽可能的减少中继器的使用,在无中继传输***,如海底传输***,传输光纤的有效面积最好在130μm2以上。然而,目前大有效面积光纤的折射率剖面的设计中,往往通过增大用于传输光信号的光学芯层的直径来获得大的有效面积。该类方案存在着一定的设计难点。一方面,光纤的芯层和靠近它的包层主要决定光纤的基本性能,并在光纤制造的成本中占据较大的比重,如果设计的径向尺寸过大,必然会提高光纤的制造成本,抬高光纤价格,将成为此类光纤普遍应用的障碍。另一方面,相比普通单模光纤,光纤有效面积的增大,会带来光纤其它一些参数的恶化:比如,光纤截止波长会增大,如果截止波长过大则难以保证光纤在传输波段中光信号的单模状态;此外,光纤折射率剖面如果设计不当,还会导致弯曲性能、色散等参数的恶化。
另一种限制长距离大容量传输的光纤特性就是衰减,目前常规的G.652.D光纤的衰减一般在0.20dB/km,激光能量在经过长距离传输后逐渐减小,所以需要采用中继的形式对信号再次放大。而相对与光纤光缆的成本,中继站相关设备和维护成本在整个链路***的70%以上,所以如果涉及一种低衰减或者超低衰减光纤,就可以有效的延长传输距离,减少建设和维护成本。经过相关计算,如果将光纤的衰减从0.20降低到0.16dB/km,整个链路的建设成本将总体降低30%左右。
综上所述,开发设计一种超低衰减大有效面积光纤成为光纤制造领域的一个重要课题。
对于低衰减大有效面积光纤剖面设计和工艺设计来说,主要的困难有两个,第一是如何获得较低的衰减;第二是在较低衰减的基础上,如何增加光纤的有效面积。
对于普通单模光纤而言,光纤衰减主要来源是瑞利散射,所以如何降低光纤的瑞利散射系数是剖面和工艺设计需要考虑的主要问题,通过有效的降低光纤芯层掺杂以及匹配各个部分的粘度设计,可以有效的降低光纤的瑞利系数。增加有效面积的主要方法是增加光纤的模场直径,其主要挑战是在降低光纤芯层折射率,增加芯层直径的情况下,保证光纤的基模传输,优化光纤的弯曲性能,保证基模截止。
文献US2010022533提出了一种大有效面积光纤的设计,为了得到更低的瑞利系数,其采用纯硅芯的设计,在芯层中没有进行锗和氟的共掺杂,并且其设计采用掺氟的二氧化硅作为外包层。对于这种纯硅芯的设计,其要求光纤内部必须进行复杂的粘度匹配,并要求在拉丝过程中采用极低的速度,避免高速拉丝造成光纤内部的缺陷引起的衰减增加,制造工艺及其复杂。
文献CN10232392A描述了一种具有更大有效面积的光纤。该发明所述光纤的有效面积虽然达到了150μm2以上,但却因为采用了常规的锗氟共掺方式的芯层设计,且通过牺牲了截止波长的性能指标实现的。其允许光缆截止波长在1450nm以上,在其所述实施例中,成缆截止波长甚至达到了1800nm以上。在实际应用当中,过高的截止波长难以保证光纤在应用波段中得到截止,便无法保证光信号在传输时呈单模状态。因此,该类光纤在应用中可能面临一系列实际问题。此外,该发明所列举的实施例中,下陷包层外径r3最小为16.3μm,同样有所偏大。该发明没有能够在光纤参数(如,有效面积、截止波长等)和光纤制造成本中得到最优组合。
发明内容
以下为本发明中涉及的一些术语的定义和说明:
从光纤纤芯轴线开始算起,根据折射率的变化,定义为最靠近轴线的那层为芯层,光纤的最外层即纯二氧化硅层定义为光纤外包层。
相对折射率Δni:
从光纤纤芯轴线开始算起,根据位置的变化,定义为最靠近轴线的那层为纤芯层,光纤的最外层即纯二氧化硅层定义为光纤外包层。
光纤各层相对折射率Δni由以下方程式定义,
其中ni为纤芯中某一位置的绝对折射率,而nc为包层绝对折射率,即没有Ge或F掺杂的纯二氧化硅绝对折射率。
光纤的有效面积Aeff:
其中,E是与传播有关的电场,R为轴心到电场分布点之间的距离。
光缆截止波长λcc:
IEC(国际电工委员会)标准60793-1-44中定义:光缆截止波长λcc是光信号在光纤中传播了22米之后不再作为单模信号进行传播的波长。在测试时需通过对光纤绕一个半径14cm的圈,两个半径4cm的圈来获取数据。
本发明所要解决的技术问题旨在提供一种低衰减大有效面积的单模光纤,其成缆截止波长小于1530nm,并且具有较好的弯曲损耗和色散性能,并具有较低制造成本。
本发明为解决上述提出的问题所采用的技术方案为:包括有芯层和包层,其特征在于所述的芯层半径r1为4.8~6.5μm,芯层相对折射率Δ1为0.10%~0.24%,芯层外从内向外依次包覆内包层,下陷内包层,过渡外包层和外包层,所述的光纤的内包层半径r2为8.5~15μm,相对折射率Δ2为-0.3%~-0.05%,所述的下陷内包层半径r3为14~22μm,相对折射率Δ3为-0.45%~-0.2%,所述的过渡外包层半径r4为35~50μm,相对折射率Δ4范围为-0.25%~-0.05%;所述外包层为纯二氧化硅玻璃层,最外层直径为125微米。
按上述方案,光纤的芯层为锗氟共掺的二氧化硅玻璃层,或为掺锗的二氧化硅玻璃层。
按上述方案,所述光纤在1550nm波长的有效面积为100~150μm2,优选条件下为110~135μm2。
按上述方案,所述光纤的成缆截止波长等于或小于1530nm。
按上述方案,所述光纤在波长1550nm处的色散等于或小于23ps/nm*km,所述光纤在波长1625nm处的色散等于或小于27ps/nm*km。
按上述方案,所述光纤的零色散点小于或等于1300nm。
按上述方案,所述光纤在波长1550nm处的衰耗等于或小于0.185dB/km;优选条件下等于或小于0.180dB/km。
本发明的有益效果在于:1、采用掺有锗的芯层设计,合理的设计了光纤内部的粘度匹配,减少光纤制备过程中缺陷,降低光纤的衰减参数;2、设计了合理的光纤氟掺杂下陷结构,并通过对光纤各纤芯层剖面的合理设计,使光纤具有等于或大于100μm2的有效面积,在较佳参数范围下,可以达到等于或大于130μm2的有效面积;3、本发明的截止波长、弯曲损耗、色散等综合性能参数在应用波段良好,足够小的的成缆截止波长,以保证该类光纤在C波段传输应用中光信号的单模状态,光纤剖面采用多层阶梯状下陷包层结构,具有较宽的下陷包层结构用于限制基模泄露,对光纤的弯曲损耗具有较好的改进作用;4、最外层的外包层结构采用了纯二氧化硅的设计,降低了氟掺杂玻璃在光纤中的比重,从而降低了光纤制造生产成本。
附图说明
图1为本发明一个实施例的相对折射率剖面结构分布图。
具体实施方式
以下结合实施例对本发明进行详细描述。
包括有芯层和包层,所述的芯层为锗氟共掺的二氧化硅玻璃层,或为掺锗的二氧化硅玻璃层,芯层外从内向外依次包覆内包层,下陷内包层,过渡外包层和外包层。所述外包层为纯二氧化硅玻璃层,外包层的半径为125微米。
表一所列为本发明优选的实施例的折射率剖面参数,表二为表一所述光纤所对应的光传输特性。
表一、本发明实施例的光纤剖面参数
序号 | r1[μm] | Δ1[%] | r2[μm] | Δ2[%] | r3[μm] | Δ3[%] | r4[μm] | Δ4[%] |
1 | 4.8 | 0.18 | 11.8 | -0.1 | 14.5 | -0.42 | 42 | -0.18 |
2 | 5.2 | 0.16 | 11.5 | -0.15 | 15.5 | -0.32 | 48 | -0.18 |
3 | 5.5 | 0.13 | 12.5 | -0.2 | 15.5 | -0.45 | 45 | -0.23 |
4 | 5.7 | 0.18 | 11 | -0.14 | 14.5 | -0.32 | 38 | -0.28 |
5 | 4.9 | 0.24 | 9.5 | -0.03 | 14 | -0.23 | 41 | -0.07 |
6 | 6.1 | 0.2 | 15 | -0.07 | 16 | -0.45 | 40 | -0.15 |
7 | 4.8 | 0.1 | 10 | -0.2 | 16.8 | -0.41 | 46 | -0.24 |
8 | 6.3 | 0.15 | 13 | -0.16 | 16.5 | -0.38 | 47 | -0.13 |
9 | 6.1 | 0.12 | 12 | -0.12 | 19 | -0.4 | 44 | -0.15 |
10 | 5.6 | 0.13 | 14 | -0.13 | 16.5 | -0.31 | 42 | -0.3 |
表二、本发明实施例的光纤参数
Claims (7)
1.一种低衰减大有效面积的单模光纤,包括有芯层和包层,其特征在于所述的芯层半径r1为4.8~6.5μm,芯层相对折射率Δ1为0.10%~0.24%,芯层外从内向外依次包覆内包层,下陷内包层,过渡外包层和外包层,所述的光纤的内包层半径r2为8.5~15μm,相对折射率Δ2为-0.3%~-0.05%,所述的下陷内包层半径r3为14~22μm,相对折射率Δ3为-0.45%~-0.2%,所述的过渡外包层半径r4为35~50μm,相对折射率Δ4范围为-0.25%~-0.05%;所述外包层为纯二氧化硅玻璃层。
2.按权利要求1所述的低衰减大有效面积的单模光纤,其特征在于光纤的芯层为锗氟共掺的二氧化硅玻璃层,或为掺锗的二氧化硅玻璃层。
3.按权利要求1或2所述的低衰减大有效面积的单模光纤,其特征在于所述光纤在1550nm波长的有效面积为100~150μm2。
4.按权利要求1或2所述的低衰减大有效面积的单模光纤,其特征在于所述光纤的成缆截止波长等于或小于1530nm。
5.按权利要求1或2所述的低衰减大有效面积的单模光纤,其特征在于所述光纤在波长1550nm处的色散等于或小于 23ps/nm*km,所述光纤在波长1625nm处的色散等于或小于27ps/nm*km。
6.按权利要求1或2所述的低衰减大有效面积的单模光纤,其特征在于所述光纤的零色散点小于或等于1300nm。
7.按权利要求1或2所述的低衰减大有效面积的单模光纤,其特征在于所述光纤在波长1550nm处的衰耗等于或小于0.185dB/km。