CN104692735A - 防火a1级无机内外墙保温板及其制备方法 - Google Patents
防火a1级无机内外墙保温板及其制备方法 Download PDFInfo
- Publication number
- CN104692735A CN104692735A CN201310646450.3A CN201310646450A CN104692735A CN 104692735 A CN104692735 A CN 104692735A CN 201310646450 A CN201310646450 A CN 201310646450A CN 104692735 A CN104692735 A CN 104692735A
- Authority
- CN
- China
- Prior art keywords
- heat insulation
- insulation board
- water
- agent
- fiber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种防火A1级无机内外墙保温板及其制备方法,包括下列组分及其重量份数比:硅酸盐水泥60%-80%、矿渣粉0%-21%、粉煤灰10%-35%、防水剂1.4-2%、氧化铁黑1%-2%、纤维0.1%-0.34%、纤维素0.01%-0.8%、早强剂0.3%-1.2%、发泡剂7%-12%。本发明还提供其制备方法。本发明采用无机材料制备保温板,具备如下优点:具有一定抗压强度和抗拉强度的轻质防水、防火、防腐、隔音、隔热、无毒、无味、导热系数小、抗冻溶、耐候性好,与单位建筑体同寿命,是最为理性的外保温材料。避免了重复施工、重复投资、重复污染。其经济效益、社会效益和环保效益不容小觑。
Description
技术领域
本发明涉及保温板保温墙领域,具体涉及一种防火A1级无机内外墙保温板及其制备方法。
背景技术
2011年前有机保温材料占整个保温材料市场97%,这也是导致火灾高发的主要原因,并且有机材料本身就是一种经能源的转制(以能源为基料)的产品,所以存在诸多问题。浪费能源易老化、对环境的延续污染、易脱落、耐候性能差、寿命短、防火性能差、施工难度大,单位建筑体寿命期内重复2-4次施工,不可避免的导致了重复污染、重复施工、重复投资。目前国内外都在加紧研制替代产品,主要是无机材料产品,其中其他产品如珍珠岩产品、菱镁产品、玻化维珠产品、矿棉产品,在一般性能上,与硅酸盐产品相差无几,但就与建筑同寿命、防水、防火、抗冻融、耐候性上,其他无机产品对硅酸盐水泥为主料的保温材料是望尘莫及的,可以广泛用于建筑外墙保温***,此材料目前,日本市场占有率为16%,而我国仅占3%,市场之大,前景之广,不言而喻。
现有的保温材料基本是有机的,其主用材料以有机材料即能源材料为基料,并且使用寿命短、易燃、有毒、污染、耐冻融性差,使用寿命仅为15-20年,价格高。
发明内容
本发明的目的为了克服目前无奈而使用的有机保温材料,提供一种以硅酸盐水泥为主材料的防火外墙保温板,其可应用于①泡沫混凝土A1级防火外墙保温板,②组合式高强度轻型外墙体保温板,③组合式轻型发泡隔音隔断墙板等。
本发明提供一种防火保温板,包括下列组分及其重量份数比:52.5R硅酸盐水泥60%-80%、矿渣粉0%-21%、粉煤灰10%-35%、防水剂1.4-2%、氧化铁黑1%-2%、纤维0.1%-0.34%、纤维素0.01%-0.8%、早强剂0.3%-1.2%、发泡剂7%-12%。
本发明的有益效果。
由于硅酸盐水泥,和粉煤灰本身是无机材料,防火不燃的,经加入防水剂、纤维、早强剂、调泡剂、发泡剂后,使得材料本身从里到外形成孔径均等、壁厚均等、自封闭(氧离子含量近于零)的气泡并相互联磊,生成具有一定抗压强度和抗拉强度的轻质防水、防火、防腐、隔音、隔热、无毒、无味、导热系数小、抗冻溶、耐候性好,与单位建筑体同寿命,是最为理性的外保温材料。
本发明的保温板采用无机材料,材料来源取之不尽,且不燃、无毒无味、与建筑墙体亲和力好,与其同寿命,防水、防火、防腐、隔音、隔热、无毒、无味、导热系数小、抗冻溶、耐候性好,寿命为50-75年。避免了重复施工、重复投资、重复污染。其经济效益、社会效益和环保效益不容小觑。
具体实施方式
一种防火保温板,包括下列组分及其重量份数比:水泥60%-80%、矿渣粉0%-21%、粉煤灰10%-35%、防水剂1.4-2%、氧化铁黑1%-2%、纤维0.1%-0.34%、纤维素0.01%-0.8%、早强剂0.3%-1.2%、发泡剂7%-12%。
所述水泥可以是市售52.5R特种硅酸盐水泥、也可以是42.5硅酸盐水泥;所述矿渣粉可以是市售一级矿渣粉,所述粉煤灰可以是市售二级粉煤灰,所述防水剂可以是有机硅防水剂,该防水剂的成分可以是硬脂酸钙和硅酸钠混合剂,所述纤维可以是市售6-12mm普通工业用纤维;所述早强剂可以为市售氯化钠系列;所述发泡剂可以为市售普通工业用27.2%双氧水。所述纤维素可以为20万单位植物纤维素,所述纤维素也称为调泡剂。
实施例一
一种防火保温板,包括下列组分及其重量份数比:52.5R特种硅酸盐水泥60%、矿渣粉10.19%、粉煤灰20%、防水剂1.4%、氧化铁黑1%、纤维0.1%、纤维素0.01%、早强剂0.3%、发泡剂7%。
实施例二
一种防火保温板,包括下列组分及其重量份数比:52.5R特种硅酸盐水泥80%、粉煤灰10%、防水剂1.4%、氧化铁黑1%、纤维0.1%、纤维素0.01%、旱强剂0.49%、发泡剂7%。
实施例三
一种防火保温板,包括下列组分及其重量份数比:42.5级硅酸盐水泥60%、矿渣粉1.66%、粉煤灰20%、防水剂2%、氧化铁黑2%、纤维0.34%、纤维素0.8%、早强剂1.2%、发泡剂12%。
实施例四
一种防火保温板,包括下列组分及其重量份数比:42.5级硅酸盐水泥60%、矿渣粉20.19%、粉煤灰10%、防水剂1.4%、氧化铁黑1%、纤维0.1%、纤维素0.01%、早强剂0.3%、发泡剂7%。
实施例五
一种防火保温板,包括下列组分及其重量份数比:52.5R级硅酸盐水泥60%、粉煤灰30.19%、防水剂1.4%、氧化铁黑1%、纤维0.1%、纤维素0.01%、早强剂0.3%、发泡剂7%。
实施例六
一种防火保温板,包括下列组分及其重量份数比:52.5R级硅酸盐水泥60%、矿渣粉7.15%、粉煤灰20%、防水剂1.8%、氧化铁黑1.5%、纤维0.25%、纤维素0.5%、早强剂0.8%、发泡剂8%。
实施例七
一种防火保温板,包括下列组分及其重量份数比:42.5级硅酸盐水泥80%、粉煤灰10%、防水剂1.59%、氧化铁黑1%、纤维0.1%、纤维素0.01%、早强剂0.3%、发泡剂7%。
一种保温板制备方法,包括下述步骤:
1)取上述实施例中的重量份数比的组分备用;
2)按重量份数比计算,将硅酸盐水泥、矿渣粉、粉煤灰、早强剂、进行混合,采用干粉搅拌机搅拌均匀。加入早强剂是为了提高保温板的前期强度,促进保温板早期强度的发展,使保温板在较短的时间内脱模,以提高生产效率。
3)按重量份数比计算,适量水中加入防水剂、纤维、早强剂、纤维素、发泡剂。发泡的目的是在水泥浆内产生大量的空气气泡,增加保温板的保温效果;。
4)将步骤2)和步骤3)中混合均匀的物料在发泡机中搅拌3-5分钟后,通过专用搅拌机进行搅拌,制成浆料。
5)将上述浆料注入模具。
6)浆料在模具内,进行蒸养。根据现场条件步骤6)可省略。
7)将成品切割制成所需要的大小。
Claims (5)
1.一种防火保温板,包括下列组分及其重量份数比:硅酸盐水泥60%-80%、矿渣粉0%-21%、粉煤灰10%-35%、防水剂1.4-2%、氧化铁黑1%-2%、纤维0.1%-0.34%、纤维素0.01%-0.8%、早强剂0.3%-1.2%、发泡剂7%-12%。
2.如权利要求1所述的防火保温板,其中:所述硅酸盐水泥是52.5R特种硅酸盐水泥;所述矿渣粉是一级矿渣粉;所述粉煤灰是二级粉煤灰;所述防水剂是有机硅防水剂;所述纤维是6-12mm普通工业用纤维;所述早强剂为氯化钠系列;所述发泡剂为普通工业用27.2%双氧水;所述纤维素为20万单位植物纤维素。
3.如权利要求2所述的防火保温板,其中:所述防水剂的成分是硬脂酸钙和硅酸钠混合剂。
4.一种制备权利要求1-3所述防火保温板的方法,包括以下步骤:
1)取所述的重量份数比的组分备用;
2)按重量份数比计算,将硅酸盐水泥、矿渣粉、粉煤灰、早强剂、进行混合,采用干粉搅拌机搅拌均匀;
3)按重量份数比计算,适量水中加入防水剂、纤维、纤维素、发泡剂;
4)将步骤2)和步骤3)中混合均匀的物料在发泡机中搅拌3-5分钟后,通过专用搅拌机进行搅拌,制成浆料;
5)将上述浆料注入模具;
6)浆料在模具内,进行蒸养;
7)将成品切割制成所需要的大小。
5.如权利要求4所述的方法,其中省略步骤6)。