CN104672945B - A kind of formula of fireplace charcoal bed and production technique thereof - Google Patents
A kind of formula of fireplace charcoal bed and production technique thereof Download PDFInfo
- Publication number
- CN104672945B CN104672945B CN201510107774.9A CN201510107774A CN104672945B CN 104672945 B CN104672945 B CN 104672945B CN 201510107774 A CN201510107774 A CN 201510107774A CN 104672945 B CN104672945 B CN 104672945B
- Authority
- CN
- China
- Prior art keywords
- charcoal bed
- charcoal
- slurry
- fireplace
- primary colors
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The present invention discloses a kind of formula and production technique thereof of fireplace charcoal bed, this fireplace formula of charcoal bed, be made up of following component by weight: the solidifying agent of the talcum powder of the soft resin of the yellow cream of 0.205 part, the red cream of 0.068 part, 15-25 part, the resinene of 75-85 part, 20-35 part, the scheelite powder of 75-90 part, the short-fibre silk of 2.1-4.2 part and 4.2-12.6 part, the gross weight X of this soft resin and resinene, the gross weight Y of this talcum powder and scheelite powder, X:Y=100:110.The production technique of this fireplace charcoal bed comprises condiment, and slip casting is poured into, and form removal also completed cure period through at least 48 hours, then natron cleaning, the step of repairing and colored drawing.The charcoal bed idiosome that the present invention produces has that charcoal fire quality is high, resistance to falls and effect that translucent effect is good.
Description
Technical field
The present invention relates to electric fireplace field, what be specifically related to is a kind of formula and production technique thereof of fireplace charcoal bed.
Background technology
In order to obtain antique decorative effect, the artificial product such as emulational electric fireplace and oven appears at each restaurant, restaurant and general family more and more.
Charcoal is a kind of traditional fuel, and the artificial products such as emulational electric fireplace and emulation oven naturally also be unable to do without and emulate charcoal, and existing emulation charcoal is substantially all be made up of resin material, and it can reach remarkably true to life in shape substantially, good enough to pass for genuine stage; And then artificial carbon bed interior luminescence component is set, and under the setting off by contrast of light, the artificial carbon bed visual effect that can produce fuel.
But, fireplace charcoal bed in the market in charcoal fire quality, resistance toly to fall, translucent effect and flame vivid effect still come with some shortcomings, improvement need be researched and developed further.
In view of this, the present inventor furthers investigate for fireplace charcoal bed in prior art, then has this case to produce.
Summary of the invention
Main purpose of the present invention is the formula providing a kind of fireplace charcoal bed, and its charcoal bed idiosome produced has that charcoal fire quality is high, resistance to falls and effect that translucent effect is good.
In order to reach above-mentioned purpose, solution of the present invention is:
A formula for fireplace charcoal bed, wherein, is made up of following component by weight:
Yellow cream: 0.205 part;
Red cream: 0.068 part;
Soft resin: 15-25 part;
Resinene: 75-85 part;
Talcum powder: 20-35 part;
Scheelite powder: 75-90 part;
Short-fibre silk: 2.1-4.2 part;
Solidifying agent: 4.2-12.6 part;
The gross weight X of this soft resin and resinene, the gross weight Y of this talcum powder and scheelite powder, X:Y=100:110.
Further, the component of this fireplace charcoal bed formula also increases the promotor having 0.42-1.05 weight part.
Further, this short-fibre silk adopts glass fibre.
Another object of the present invention is to the production technique that a kind of fireplace charcoal bed is provided, wherein, comprise the steps:
1. condiment: select the component of following weighing scale to mix slurry: the yellow cream of 0.205 part, the red cream of 0.068 part, the soft resin of 15-25 part, the resinene of 75-85 part, the talcum powder of 20-35 part, the scheelite powder of 75-90 part, the short-fibre silk of 2.1-4.2 part, the solidifying agent of 4.2-12.6 part, the gross weight X of this soft resin and resinene, the gross weight Y of this talcum powder and scheelite powder, X:Y=100:110;
2. slip casting perfusion, form removal also completed cure period through at least 48 hours, then natron cleaning;
3. repair: adopt primary colors slurry to repair, thicken 8-10mm in the charcoal fire edge thin location slurry scraping increasing a certain amount of short-fibre silk again, two needs lock screw part to thicken 12-15mm;
4. colored drawing: control sample colored drawing, obtains finished product after carrying out printing opacity detection in dark place.
Further, above-mentioned steps 2. in slip casting perfusion, when the length dimension of charcoal bed is at 25-45cm, charcoal bed need be divided do three operations, first time slurry brushing or bottoming of finding time, second time slurry adds short-fibre silk scraping and thickeies, third time slurry shake material to connect the end shaping, the short-fibre silk content wherein in second time slurry need be increased to 3 to 5 times of original content.
Further, above-mentioned steps 2. in slip casting perfusion, when the length dimension of charcoal bed is at 45-75cm, charcoal bed need be divided do three operations, first time slurry brushing or bottoming of finding time, second time is sticked by the cloth or fibrefelt of having cut moulding and uses paste compaction again in the place of charcoal bed plane, and after gel, slurry shakes uniformly thicken to connect the end shaping third time.
Further, above-mentioned steps 2. in slip casting perfusion, when the length dimension of charcoal bed is at 75-95cm, charcoal bed need be divided do three operations, for the first time with slurry brushing bottoming, second time is sticked by the cloth or fibrefelt of having cut moulding and uses paste compaction again in the place of charcoal bed plane, and after gel, slurry shakes uniformly thicken to connect the end shaping third time, and the length of this cloth or fibrefelt is 40-50cm.
Further, above-mentioned steps 2. in slip casting perfusion, when the length dimension of charcoal bed is greater than 95cm, need segmental machining, then in the steady conjunction of junction amendment, stick cloth or the fibrefelt that layer 2-3 is matched with charcoal bed plane sizes in the position of charcoal bed plane again, one deck cloth or fibrefelt are pasted in printing opacity position.
Further, 3. repairing in step in above-mentioned steps, be also included in dark place and carry out with standard core bulb the step that detects, standard printing opacity standard need be taken when detecting to carry out effect comparison.
Further, in above-mentioned steps 4. colored drawing step, it adopts and detects and shine sample colored drawing and intersect the mode of carrying out, and comprises again following three steps when colored drawing:
A: adopt and through diluted dirty oil paint, whole charcoal bed is sprayed first, spraying need allow the printing opacity position of charcoal bed leave over and suitable not be sprayed onto region, and not being sprayed onto area size need carry out contrasting judging with sample;
B: adopt the plane position of dirty oil paint to charcoal bed to carry out spray comprehensively black;
C: adopt white oil paint to spray on charcoal bed and form white point simulation ashes to paint at dirty oil.
After adopting said structure, the formula of a kind of fireplace charcoal bed that the present invention relates to and production technique thereof, it at least has following beneficial effect:
One, yellow cream and red cream select this number and proportioning, just can produce the charcoal bed idiosome that simulated effect in color is best;
Two, select the proportion relation of soft resin and resinene, it can improve the toughness of charcoal bed greatly, and then reduces the fracture rate of charcoal bed in transportation, reduces risk of carriage;
Three, selecting of scheelite powder is to reduce the transparent of whole charcoal bed and reduce whole charcoal bed resin demand, with the effect greatly reduced costs simultaneously; Talcum powder is then the toughness for increasing whole charcoal bed, and will reduce the mobility of deployed slurry, is able to industrialization realizes to allow follow-up employing swabbing explained hereafter;
Four, the selecting of short-fibre silk is the intensity for improving charcoal bed ensemble, and solidifying agent is then the indispensable auxiliary that resin material finally can be solidified;
Five, the present invention by condiment, slip casting perfusion and natron cleaning, to repair and after colored drawing, can obtain that charcoal fire quality highly, resistance to is fallen, simulate effect and all good artificial carbon bed of translucent effect.
Accompanying drawing explanation
Fig. 1 is the schema of the production technique that the present invention relates to a kind of fireplace charcoal bed.
Embodiment
In order to explain technical scheme of the present invention further, below by specific embodiment, the present invention will be described in detail.
The formula of a kind of fireplace charcoal bed that the present invention relates to, is made up of following component by weight:
Yellow cream: 0.205 part;
Red cream: 0.068 part;
Soft resin: 15-25 part;
Resinene: 75-85 part;
Talcum powder: 20-35 part;
Scheelite powder: 75-90 part;
Short-fibre silk: 2.1-4.2 part;
Solidifying agent: 4.2-12.6 part;
The gross weight X of this soft resin and resinene, the gross weight Y of this talcum powder and scheelite powder, X:Y=100:110, in order to ensure molded artificial carbon bed final quality, the ratio of this X and Y can be floated at most in the scope of ± 5%, and what this soft resin and resinene all adopted is unsaturated polyester.
Above-mentioned yellow cream and red cream select this number and proportioning, just can produce the charcoal bed idiosome that simulated effect in color is best; For the proportion relation between soft resin and resinene, it can improve the toughness of charcoal bed greatly, and then reduces the fracture rate of charcoal bed in transportation, reduces risk of carriage; For selecting of scheelite powder, be that the transparency in order to reduce whole charcoal bed also reduces whole charcoal bed resin demand, with the effect greatly reduced costs simultaneously; Talcum powder is then the toughness for increasing whole charcoal bed, and will reduce the mobility of deployed slurry, is able to industrialization realizes to allow follow-up employing swabbing explained hereafter; Selecting of short-fibre silk is the intensity for improving charcoal bed ensemble, and solidifying agent is then the indispensable auxiliary that resin material finally can be solidified, and preferred employing is glass fibre.
It should be noted that, in the winter that temperature is comparatively low, the component of this fireplace charcoal bed formula also increases the promotor having 0.42-1.05 weight part.
In addition, the present invention also provides a kind of production technique of fireplace charcoal bed, comprises the steps:
1. condiment: select the component of following weighing scale to mix slurry: the yellow cream of 0.205 part, the red cream of 0.068 part, the soft resin of 15-25 part, the resinene of 75-85 part, the talcum powder of 20-35 part, the scheelite powder of 75-90 part, the short-fibre silk of 2.1-4.2 part, the solidifying agent of 4.2-12.6 part, the gross weight X of this soft resin and resinene, the gross weight Y of this talcum powder and scheelite powder, X:Y=100:110;
2. slip casting perfusion, form removal also completed cure period through at least 48 hours, then natron cleaning; The object of natron is to take out grease, and employing paper mill wastewater is 15%mol/L;
3. repair: adopt primary colors slurry to repair, thicken 8-10mm in the charcoal fire edge thin location slurry scraping increasing a certain amount of short-fibre silk again, two needs lock screw part to thicken 12-15mm; When specifically repairing, film line effect nature, inner chamber and the certain round and smooth nature of all burrs, lines want straight, keep product style; Charcoal bed also needs after fixing to detect with testing tool, mainly detects and whether there is needle-holding hand position, size of product and the vertical goodness of fit of group; Finally in dark place, can also carrying out with standard core bulb detect step, standard printing opacity standard need be taken when detecting to carry out effect comparison;
4. colored drawing: control sample colored drawing, obtains finished product after carrying out printing opacity detection in dark place.
Above-mentioned steps 2. in slip casting perfusion, when the length dimension of charcoal bed is at 25-45cm, charcoal bed need be divided do three operations, first time slurry brushing or bottoming of finding time, second time slurry adds short-fibre silk scraping and thickeies, slurry shook material to connect the end shaping third time, and the short-fibre silk content wherein in second time slurry need be increased to 3 to 5 times of original content.
Above-mentioned steps 2. in slip casting perfusion, when the length dimension of charcoal bed is at 45-75cm, charcoal bed need be divided do three operations, first time slurry brushing or bottoming of finding time, second time is sticked by the cloth or fibrefelt of having cut moulding and uses paste compaction again in the place of charcoal bed plane, and after gel, slurry shakes uniformly thicken to connect the end shaping third time.
Above-mentioned steps 2. in slip casting perfusion, when the length dimension of charcoal bed is at 75-95cm, charcoal bed need be divided do three operations, for the first time with slurry brushing bottoming, second time is sticked by the cloth or fibrefelt of having cut moulding and uses paste compaction again in the place of charcoal bed plane, after gel, slurry shakes uniformly thicken to connect the end shaping third time, and the length of this cloth or fibrefelt is 40-50cm.
Above-mentioned steps 2. in slip casting perfusion, when the length dimension of charcoal bed is greater than 95cm, need segmental machining, then in the steady conjunction of junction amendment, stick cloth or the fibrefelt that layer 2-3 is matched with charcoal bed plane sizes in the position of charcoal bed plane again, one deck cloth or fibrefelt are pasted in printing opacity position.
No matter the charcoal bed of which kind of length, its slurry brushing or find time bottoming time be all adopt second half of first forming charcoal bed, then the mode that two halves charcoal bed shaping respectively combined before not condensing is shaped to charcoal bed idiosome.
More preferably, in above-mentioned steps 4. colored drawing step, it adopts and detects and shine sample colored drawing and intersect the mode of carrying out, and comprises again following three steps when colored drawing:
A: adopt and through diluted dirty oil paint, whole charcoal bed is sprayed first, spraying need allow the printing opacity position of charcoal bed leave over and suitable not be sprayed onto region, and not being sprayed onto area size need carry out contrasting judging with sample;
B: adopt the plane position of dirty oil paint to charcoal bed to carry out spray comprehensively black;
C: adopt white oil paint to spray on charcoal bed and form white point simulation ashes to paint at dirty oil.
It should be noted that, the printing opacity position of this charcoal bed is mainly made up of simulation charcoal, simulation charcoal is processed to roughness when slip casting form, namely the dell position of a greater number can be there is on simulation charcoal, in step, it preferably adopts spray gun to carry out ink-jet back and forth, generally back and forth once, in course of injection, dell position is based on not being directly injected to more ink, it mainly still presents the color after slip casting form, and so under light-illuminating, whole simulation charcoal can demonstrate preferably simulated flame effect.
Compared with prior art, the formula of a kind of fireplace charcoal bed that the present invention relates to and production technique thereof, its by condiment, slip casting perfusion and natron cleaning, to repair and after colored drawing, can obtain that charcoal fire quality highly, resistance to is fallen, simulate effect and all good artificial carbon bed of translucent effect.
Above-described embodiment and graphic and non-limiting product form of the present invention and style, any person of an ordinary skill in the technical field, to its suitable change done or modification, all should be considered as not departing from patent category of the present invention.
Claims (2)
1. a fireplace production technique for charcoal bed, is characterized in that, comprise the steps:
1. condiment: select the component of following weighing scale to mix primary colors slurry: the yellow cream of 0.205 part, the red cream of 0.068 part, the soft resin of 15-25 part, the resinene of 75-85 part, the talcum powder of 20-35 part, the scheelite powder of 75-90 part, the short-fibre silk of 2.1-4.2 part, the solidifying agent of 4.2-12.6 part, the gross weight X of this soft resin and resinene, the gross weight Y of this talcum powder and scheelite powder, X:Y=100:110;
2. slip casting perfusion, form removal also completed cure period through at least 48 hours, then natron cleaning; Above-mentioned steps 2. in slip casting perfusion, when the length dimension of charcoal bed is at 25-45cm, charcoal bed need be divided do three operations, first time primary colors slurry brushing or bottoming of finding time, second time primary colors slurry adds short-fibre silk scraping and thickeies, primary colors slurry shook material to connect the end shaping third time, and the short-fibre silk content wherein in second time slurry need be increased to 3 to 5 times of primary colors slurry middle short fiber silk content;
3. repair: adopt primary colors slurry to repair, thicken 8-10mm in the charcoal fire edge thin location primary colors slurry scraping increasing a certain amount of short-fibre silk again, two needs lock screw part to thicken 12-15mm;
4. colored drawing: control sample colored drawing, obtains finished product after carrying out printing opacity detection in dark place.
2. the production technique of a kind of fireplace charcoal bed as claimed in claim 1, is characterized in that, 3. repair in step in above-mentioned steps, is also included in dark place and carries out with standard core bulb the step that detects, and standard printing opacity standard need be taken when detecting to carry out effect comparison.