CN103131196A - High temperature-resistant colored asphalt - Google Patents
High temperature-resistant colored asphalt Download PDFInfo
- Publication number
- CN103131196A CN103131196A CN 201110376855 CN201110376855A CN103131196A CN 103131196 A CN103131196 A CN 103131196A CN 201110376855 CN201110376855 CN 201110376855 CN 201110376855 A CN201110376855 A CN 201110376855A CN 103131196 A CN103131196 A CN 103131196A
- Authority
- CN
- China
- Prior art keywords
- parts
- asphalt
- high temperature
- diatomite
- raw materials
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to the technical field of building materials, and particularly relates to high temperature-resistant colored asphalt. The high temperature-resistant colored asphalt is composed of the following raw materials of, by weight, 30-65 parts of asphalt, 10-25 parts of pigments, 10-30 parts of rubber powder and 10-20 parts of diatomite. Due to the adoption of the diatomite and the pigments as main raw materials, the color of the asphalt can be changed at will, and the high temperature-resistant colored asphalt with various colors can be produced. The asphalt can not only meet the requirements of various places and but also beautify the environment. Besides, the asphalt has color and increased performance of the asphalt. Due to the adoption of a large amount of the diatomite as the raw materials, the asphalt has the characteristic of resisting high temperature. Therefore, the asphalt has relatively low manufacturing cost, simple process and convenient production, so that the market price is relatively low, the asphalt can be widely used by building construction industry once being launched on the market, so that the product has good market application prospects and is suitable for large-scale popularization and application.
Description
Technical field
The present invention relates to a kind of technical field of material of construction, relate in particular to a kind of high temperature resistant color asphalt.
Background technology
[0002] well-known, due to advancing by leaps and bounds of present construction industry, therefore the demand of pitch for building is also thereupon in growth at full speed.Various pitches are also arranged on domestic market, simple low viscosity or full-bodied pitch are arranged, but because present domestic pitch is all single black, therefore after the process life-time service, the road surface can become a slice of ash ash, not only lacks aesthetic feeling, also driver's vision is caused bad impact, make the driver easily produce in the process of moving eye strain, thereby cause such-and-such traffic accident.
Summary of the invention
The objective of the invention is to be the technical problem for above-mentioned existence, and a kind of high temperature resistant color asphalt be provided, it have high temperature resistant and multicolour in the unusual effect of one.
The object of the present invention is achieved like this:
High temperature resistant color asphalt is comprised of following each raw materials by weight portion ratio:
Pitch: 30~65 parts;
Pigment: 10~25 parts;
Rubber powder: 10~30 parts;
Diatomite: 10~30 parts.
Described high temperature resistant color asphalt is comprised of following each raw materials by weight portion ratio:
Pitch: 30 parts;
Pigment: 10 parts;
Rubber powder: 30 parts;
Diatomite: 30 parts.
Described high temperature resistant color asphalt is comprised of following each raw materials by weight portion ratio:
Pitch: 65 parts;
Pigment: 15 parts;
Rubber powder: 10 parts;
Diatomite: 10 parts.
Described high temperature resistant color asphalt is comprised of following each raw materials by weight portion ratio:
Pitch: 35 parts;
Pigment: 25 parts;
Rubber powder: 20 parts;
Diatomite: 20 parts.
Described high temperature resistant color asphalt is comprised of following each raw materials by weight portion ratio:
Pitch: 50 parts;
Pigment: 15 parts;
Rubber powder: 15 parts;
Diatomite: 20 parts.
The present invention is main raw material owing to adopting diatomite to be equipped with pigment, therefore can change arbitrarily the color of pigment, produces the high temperature resistant color asphalt of various colors.Not only can satisfy the demand in various places, can also beautify the environment simultaneously.This pitch not only is with colored in addition, and has improved the performance of pitch, and adopting diatomite because they are a large amount of is raw material, therefore makes the present invention have resistant to elevated temperatures characteristics.It is simple that the present invention also has technique, characteristics convenient for production.Because the manufacturing cost of product of the present invention is lower, so its market sale price is also lower, and once putting goods on the market, namely widely building operation industry is used, so have good market application foreground, is suitable for large-scale popularization and uses.
Below in conjunction with specific embodiment to the present invention's detailed description in addition.
Embodiment
Embodiment 1:
High temperature resistant color asphalt of the present invention is comprised of following each raw materials by weight portion ratio:
Pitch: 30 parts;
Pigment: 10 parts;
Rubber powder: 30 parts;
Diatomite: 30 parts.
Manufacturing process of the present invention adopts conventional machining technique to get final product.
Embodiment 2:
High temperature resistant color asphalt of the present invention is comprised of following each raw materials by weight portion ratio:
Pitch: 65 parts;
Pigment: 15 parts;
Rubber powder: 10 parts;
Diatomite: 10 parts.
Embodiment 3:
High temperature resistant color asphalt of the present invention is comprised of following each raw materials by weight portion ratio:
Pitch: 35 parts;
Pigment: 25 parts;
Rubber powder: 20 parts;
Diatomite: 20 parts.
Embodiment 4:
High temperature resistant color asphalt of the present invention is characterized in that it is comprised of following each raw materials by weight portion ratio:
Pitch: 50 parts;
Pigment: 15 parts;
Rubber powder: 15 parts;
Diatomite: 20 parts.
Claims (5)
1. high temperature resistant color asphalt is characterized in that it is comprised of following each raw materials by weight portion ratio:
Pitch: 30~65 parts;
Pigment: 10~25 parts;
Rubber powder: 10~30 parts;
Diatomite: 10~30 parts.
2. high temperature resistant color asphalt according to claim 1 is characterized in that it is comprised of following each raw materials by weight portion ratio:
Pitch: 30 parts;
Pigment: 10 parts;
Rubber powder: 30 parts;
Diatomite: 30 parts.
3. high temperature resistant color asphalt according to claim 1 is characterized in that it is comprised of following each raw materials by weight portion ratio:
Pitch: 65 parts;
Pigment: 15 parts;
Rubber powder: 10 parts;
Diatomite: 10 parts.
4. high temperature resistant color asphalt according to claim 1 is characterized in that it is comprised of following each raw materials by weight portion ratio:
Pitch: 35 parts;
Pigment: 25 parts;
Rubber powder: 20 parts;
Diatomite: 20 parts.
5. high temperature resistant color asphalt according to claim 1 is characterized in that it is comprised of following each raw materials by weight portion ratio:
Pitch: 50 parts;
Pigment: 15 parts;
Rubber powder: 15 parts;
Diatomite: 20 parts.