CN104530741A - Environment-friendly resin crafts and preparation method thereof - Google Patents
Environment-friendly resin crafts and preparation method thereof Download PDFInfo
- Publication number
- CN104530741A CN104530741A CN201410806311.7A CN201410806311A CN104530741A CN 104530741 A CN104530741 A CN 104530741A CN 201410806311 A CN201410806311 A CN 201410806311A CN 104530741 A CN104530741 A CN 104530741A
- Authority
- CN
- China
- Prior art keywords
- parts
- environment
- resin
- weight
- artwork
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses environment-friendly resin crafts and a preparation method thereof. The environment-friendly resin crafts consist of the following components in parts by weight: 100 parts of resin, 50-65 parts of aluminum trioxide, 10-17 parts of aluminum hydroxide, 35-45 parts of crystal sand and 0.3-0.5 part of a curing agent. A preparation process comprises the following steps: (1) fully stirring and mixing 50-65 weight parts of aluminum trioxide powder, 10-17 weight parts of aluminum hydroxide powder and 35-45 weight parts of crystal sand particles to form a mixture; (2) putting the mixture into 100 parts of the resin, then adding 0.3-0.5 part of the curing agent, and uniformly stirring to form a resin solution; (3) injecting the resin solution into a manufactured mold, and performing vacuum pumping and slurry shaking processes according to models of products; and (4) demolding, and then performing blank finishing and bottom grinding to form the environment-friendly resin crafts. The environment-friendly resin crafts disclosed by the invention have the characteristics of low labor force cost, environmental protection and high product grade.
Description
Technical field
The invention belongs to resin craft field, that be specifically related to is a kind of environment-friendly resin artwork and preparation technology thereof.
Background technology
Resin craft is known by people, and it take resin as main raw material, shaping by die casting, makes the personage of various lifelike image handsome in appearance, animal, elder brother bird, scenery with hills and waters etc., and can be made into various simulated effect.
Current its general complete processing of ordinary resin artwork is on the market: calcium carbonate, resin are mixed with certain proportion, for subsequent use after fully stirring, get suitable slurry again and add appropriate solidifying agent again, mould is inserted after stirring, carry out vacuumizing and shaking sizing process according to product demand, the shaping rear demoulding can obtain preliminary process product, then repaiies embryo and the mill end to preliminary process product, namely obtains the resin craft of finished product after finally spraying the layer of ink that oils.
Above-mentioned traditional resin craft, at least there is following defect in it:
One, due to after repairing embryo to preliminary process product and grinding the end, also need the processing carrying out ink layer can obtain qualified resin craft, so must need some labor forces in ink layer construction process, and relate to ink due to it, then enterprise can be allowed to face the problem of discharge and contaminate environment;
Two, because preliminary process product are in quality and aesthetically poor, the quality aesthetic feeling of whole resin craft is mainly derived from ink layer, and in use for some time, especially after exposing to the sun and rain, the problem that ink comes off can be there is unavoidably, so have a strong impact on the sight of whole resin craft, and then have influence on the class of resin craft.
In view of this, the present inventor, for above-mentioned defect further investigation of the prior art, has this case to produce then---a kind of environment-friendly resin artwork and preparation technology thereof.
Summary of the invention
Main purpose of the present invention is to provide a kind of environment-friendly resin artwork and preparation technology thereof, with solve prior art exist labor cost higher, easily face problem of environmental pollution and use the problem that class glides after for some time.
In order to reach above-mentioned purpose, primary solutions of the present invention is:
A kind of environment-friendly resin artwork, wherein, is made up of following component by weight:
Resin, 100 parts;
Aluminium sesquioxide, 50 ~ 65 parts;
Aluminium hydroxide, 10 ~ 17 parts;
Chalazie, 35 ~ 45 parts;
Solidifying agent, 0.3 ~ 0.5 part.
Further, this environment-friendly resin artwork is made up of following component by weight:
Resin, 100 parts;
Aluminium sesquioxide, 55 parts;
Aluminium hydroxide, 10 parts;
Chalazie, 35 parts;
Solidifying agent, 0.4 part.
The present invention also provides a kind of preparation technology of environment-friendly resin artwork, wherein, comprises the steps:
1. by the chalazie particle of the aluminium sesquioxide powder of 50 ~ 65 weight parts, the aluminium-hydroxide powder of 10 ~ 17 weight parts and 35 ~ 45 weight parts through being fully uniformly mixed, formed mixture;
2. said mixture is inserted in 100 parts of resins, then the solidifying agent adding 0.3 ~ 0.5 part forms resin solution after stirring;
3. above-mentioned resin solution is injected in the middle of the mould made, carry out vacuumizing and shaking sizing process according to the moulding of product;
4. carry out after the demoulding repairing embryo and the mill end, form environment-friendly resin artwork.
Further, this chalazie particle is selected from 40 ~ 60 orders.
Further, step 1. in aluminium sesquioxide adopt 55 weight parts, this aluminium hydroxide adopts 10 weight parts, and chalazie adopts 35 parts.
Further, step 2. in solidifying agent adopt 0.4 weight part.
After adopting said structure, a kind of environment-friendly resin artwork that the present invention relates to and preparation technology thereof, it at least has following beneficial effect:
One, the present invention adopts aluminium sesquioxide to be used for allowing the environment-friendly resin artwork formed out have white and the transparent feature of texture, substantially increases the aesthetics of whole artwork; Aluminium hydroxide is adopted to be then to produce inclined yellow on artwork, and then improve the change of whole artwork in color, chalazie is then the intensity promoting whole artwork, based crystal sand is in particulate state simultaneously, so also relatively good operation in die molding process, be convenient to rapid shaping, the cost of chalazie is also lower simultaneously, greatly reduces the cost of whole artwork.
Two, the environment-friendly resin artwork that forms out of the present invention, after it mixes based on said components, the outward appearance and quality that meet sale demand can be molded, do not need again at outer surface one deck ink layer, so eliminate the processing of ink layer, not only greatly reduce labor cost, and based on without the need to ink layer, it also avoid the problem that ink causes environmental pollution; Moreover due to consistent inside and outside environment-friendly resin artwork, the part that come off after exposing to the weather epidermis, Nei Biao and appearance are consistently, so overcome the problem that conventional art uses for some time class to glide.
Embodiment
In order to explain technical scheme of the present invention further, below by specific embodiment, the present invention will be described in detail.
The present invention relates to a kind of environment-friendly resin artwork, it is made up of following component by weight: the solidifying agent of the resin of 100 parts, the aluminium sesquioxide of 50 ~ 65 parts, the aluminium hydroxide of 10 ~ 17 parts, the chalazie of 35 ~ 45 parts and 0.3 ~ 0.5 part.
More preferably, what this resin adopted is 100 parts, and what this aluminium sesquioxide adopted is 55 parts, and what this aluminium hydroxide adopted is 10 parts, and what this chalazie adopted is 35 parts, this fixing agent 0.4 part.
Particularly, the present invention relates to the preparation technology of environment-friendly resin artwork, comprise the steps:
1. by the chalazie particle of the aluminium sesquioxide powder of 50 ~ 65 weight parts, the aluminium-hydroxide powder of 10 ~ 17 weight parts and 35 ~ 45 weight parts through being fully uniformly mixed, formed mixture; More preferably, aluminium sesquioxide adopts 55 weight parts, and this aluminium hydroxide adopts 10 weight parts, and chalazie adopts 35 parts;
2. said mixture is inserted in 100 parts of resins, then the solidifying agent adding 0.3 ~ 0.5 part forms resin solution after stirring; Preferably, solidifying agent adopts 0.4 weight part;
3. above-mentioned resin solution is injected in the middle of the mould made, carry out vacuumizing and shaking sizing process according to the moulding of product;
4. carry out after the demoulding repairing embryo and the mill end, form environment-friendly resin artwork.
Particularly, this chalazie particle is selected from 40 ~ 60 orders, and so this chalazie can promote the intensity of whole environment-friendly resin artwork preferably, and when the whole artwork of mould molding, based crystal sand has certainweight, and more convenient operation when shaping, operation efficiency is high.
In addition, it should be noted that, the aluminium sesquioxide that the present invention adopts, when selecting number to be less than 50 parts, whole artwork by poor, cannot reach certain appreciation effect in the transparency; When selecting number to be greater than 65 parts, when mould molding, operation is not too convenient, and operating time bad control, and the artwork obtained even can be allowed to there is the defect of easily cracking.
The aluminium hydroxide that the present invention adopts, it is yellow for producing in white, and be less than 10 parts according to number, yellow is almost invisible to the naked eye, poor effect; Once number is greater than 17 parts, too can turns yellow again, affect whole structure.
The chalazie that the present invention adopts, when adopting number to be less than 35 parts, the cost of whole resin craft will be higher, once be greater than 45 parts, that can have influence on again the texture of whole resin craft.
Above-described embodiment non-limiting product form of the present invention and style, any person of an ordinary skill in the technical field, to its suitable change done or modification, all should be considered as not departing from patent category of the present invention.
Claims (6)
1. an environment-friendly resin artwork, is characterized in that, is made up of following component by weight:
Resin, 100 parts;
Aluminium sesquioxide, 50 ~ 65 parts;
Aluminium hydroxide, 10 ~ 17 parts;
Chalazie, 35 ~ 45 parts;
Solidifying agent, 0.3 ~ 0.5 part.
2. a kind of environment-friendly resin artwork as claimed in claim 1, is characterized in that, this environment-friendly resin artwork is made up of following component by weight:
Resin, 100 parts;
Aluminium sesquioxide, 55 parts;
Aluminium hydroxide, 10 parts;
Chalazie, 35 parts;
Solidifying agent, 0.4 part.
3. a preparation technology for environment-friendly resin artwork, is characterized in that, comprises the steps:
1. by the chalazie particle of the aluminium sesquioxide powder of 50 ~ 65 weight parts, the aluminium-hydroxide powder of 10 ~ 17 weight parts and 35 ~ 45 weight parts through being fully uniformly mixed, formed mixture;
2. said mixture is inserted in 100 parts of resins, then the solidifying agent adding 0.3 ~ 0.5 part forms resin solution after stirring;
3. above-mentioned resin solution is injected in the middle of the mould made, carry out vacuumizing and shaking sizing process according to the moulding of product;
4. carry out after the demoulding repairing embryo and the mill end, form environment-friendly resin artwork.
4. the preparation technology of a kind of environment-friendly resin artwork as claimed in claim 3, is characterized in that, this chalazie particle is selected from 40 ~ 60 orders.
5. the preparation technology of a kind of environment-friendly resin artwork as claimed in claim 3, is characterized in that, step 1. in aluminium sesquioxide adopt 55 weight parts, this aluminium hydroxide adopts 10 weight parts, and chalazie adopts 35 parts.
6. the preparation technology of a kind of environment-friendly resin artwork as claimed in claim 3, is characterized in that, step 2. middle solidifying agent adopts 0.4 weight part.