CN104671701B - 一种使用溶剂型合成胶制成的玩具砂及其制作方法 - Google Patents
一种使用溶剂型合成胶制成的玩具砂及其制作方法 Download PDFInfo
- Publication number
- CN104671701B CN104671701B CN201510062779.4A CN201510062779A CN104671701B CN 104671701 B CN104671701 B CN 104671701B CN 201510062779 A CN201510062779 A CN 201510062779A CN 104671701 B CN104671701 B CN 104671701B
- Authority
- CN
- China
- Prior art keywords
- parts
- sand
- rubber polymer
- solvent
- solid particle
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明实施例公开了一种使用溶剂型合成胶制成的玩具砂,包括固体颗粒、以及包裹于所述固体颗粒的溶剂合成胶,所述固体颗粒经甲基硅酸钠预混合烘干,所述溶剂合成胶包括硬脂酸、白蜡、十八醇处理剂。本发明实施例还公开了制作上述的玩具砂的方法。采用本发明,使用溶剂型合成胶制成的玩具砂,使用甲基硅酸钠和固体颗粒处理后,再和合成胶混合组成,所制成的玩具砂粘性好,可塑性强,所采用的材料环保、卫生,产生工艺简单、成本低,用途广泛,可以替代砂子类、砂盘类儿童乐园游戏等玩具的材料,可以砂滩玩具,厨房玩具,砂盘,艺术,教学,造型,砂雕等范围内应用。
Description
技术领域
本发明涉及一种玩具砂及其制作方法,尤其涉及一种使用溶剂型合成胶制成的玩具砂及其制作方法。
背景技术
目前现有技术中的砂滩玩具,需要在室外或有砂的地方才能玩耍,市面上所售的砂都是基于固体加热,采用多种添加材料,制造工艺复杂,不宜控制成本与环保安全,造成加工技术复杂,繁琐,价格昂贵,增加普通消费者的消费压力。
发明内容
本发明实施例所要解决的技术问题在于,提供一种使用溶剂型合成胶制成的玩具砂及其制作方法。可提供一种易加工、便宜、易于塑形的环保溶剂型合成胶做玩具砂。
为了解决上述技术问题,本发明实施例提供了一种使用溶剂型合成胶制成的玩具砂,包括固体颗粒、以及包裹于所述固体颗粒的溶剂合成胶,所述固体颗粒经甲基硅酸钠预混合烘干,所述溶剂合成胶包括硬脂酸、白蜡、十八醇处理剂;
所述的各成份的重量份为:
固体颗粒:100~600份;甲基硅酸钠10~15份;
硬脂酸:0.5~1.5份;白蜡:0.2~0.8份;十八醇处理剂:1.5~3.5份。
进一步地,所述固体颗粒为硅砂、保利龙发泡珠、木质纤维素、玻璃珠中的一种。
更进一步地,所述的各成份的重量份为:
硅砂:100份,甲基硅酸钠:12份;
硬脂酸:1份;白蜡:0.5份;十八醇处理剂:2.5份。
更进一步地,所述的各成份的重量份为:
保利龙发泡珠:200份,甲基硅酸钠:12份;
硬脂酸:1份;白蜡:0.5份;十八醇处理剂:2.5份;
所述保利龙发泡珠粒度为150~200目。
更进一步地,所述的各成份的重量份为:
木质纤维素:600份,甲基硅酸钠:12份;
硬脂酸:1份;白蜡:0.5份;十八醇处理剂:2.5份;
所述木质纤维素粒度为100~200目。
更进一步地,所述的各成份的重量份为:
玻璃珠100份,甲基硅酸钠12份;
硬脂酸:1份;白蜡:0.5份;十八醇处理剂:2.5份;
所述玻璃珠粒度为70~200目。
相应地,本发明实施例还提供了制作上述的玩具砂的方法,包括以下步骤:
(1)将所述固体颗粒先用甲基硅酸钠混合并烘干;
(2)溶剂合成胶以溶剂石油醚,硬脂酸,白蜡,十八醇混合后搅拌;
(3)将上述固体颗粒与溶剂合成胶进行搅拌揉合处理,同时烘干挥发掉石油醚达到软固相。
进一步地,所采用的石油醚重量份为8~12份。
实施本发明实施例,具有如下有益效果:本发明使用溶剂型合成胶制成的玩具砂,使用甲基硅酸钠和固体颗粒处理后,再和合成胶混合组成,所制成的玩具砂粘性好,可塑性强,所采用的材料环保、卫生,产生工艺简单、成本低,用途广泛,可以替代砂子类、砂盘类儿童乐园游戏等玩具的材料,可以砂滩玩具,厨房玩具,砂盘,艺术,教学,造型,砂雕等范围内应用。
具体实施方式
为使本发明的目的、技术方案和优点更加清楚,下面将对本发明作进一步地详细描述。
实施例1:
在本实施例中,一种使用溶剂型合成胶制成的玩具砂,使用的各成份的重量份为:固体颗粒硅砂100份,构成溶剂合成胶的石油醚10份,硬脂酸1份,白蜡0.5份,十八醇处理剂2.5份。
将上述成份按以下步骤进行制作。
(1)将固体颗粒硅砂先用甲基硅酸钠12份混合并烘干;
(2)溶剂合成胶以溶剂石油醚,硬脂酸,白蜡,十八醇混合后搅拌;
(3)将上述固体颗粒与溶剂合成胶进行搅拌揉合处理,同时烘干挥发掉石油醚达到软固相。
当固体颗粒被揉合到合成胶达到软固相时,同时大部分的固体颗粒被合成胶所覆盖,并有分离倾向时,即放在手里成松散状,就可以达到所要的效果,即砂状材料特性,并且回到室温时,就可以获得包含软固相粘的溶剂型合成胶做玩具砂,其性质柔软,可以用手进行操作,更佳的是,材料是有粘性的,而不是像河里,海里砂料的松散的形状。
制得溶剂型合成胶做玩具砂在室温(24摄氏度),储藏温度(大于10摄氏度)和手工操作温度(35摄氏度)时保持柔软状态。因此,溶剂型合成胶做玩具砂对温度的反映不敏感。可以在较大的温度范围内保持良好的工作特性。 无论制作过程中的工作强度有多大,工作时间有多久,能够保持溶剂型合成胶做玩具砂含有合适的柔软度。
实施例2:
在本实施例中,一种使用溶剂型合成胶制成的玩具砂,使用的各成份的重量份为:固体颗粒保利龙发泡珠200份,构成溶剂合成胶的石油醚10份,硬脂酸1份,白蜡0.5份,十八醇处理剂2.5份。
将上述成份按以下步骤进行制作。
(1)将固体颗粒保利龙发泡珠先用甲基硅酸钠12份混合并烘干;
(2)溶剂合成胶以溶剂石油醚,硬脂酸,白蜡,十八醇混合后搅拌;
(3)将上述固体颗粒与溶剂合成胶进行搅拌揉合处理,同时烘干挥发掉石油醚达到软固相。
需要进行说明的,保丽龙发泡珠粒度在150-200目之间。
实施例3:
在本实施例中,一种使用溶剂型合成胶制成的玩具砂,使用的各成份的重量份为:固体颗粒木质纤维素600份,构成溶剂合成胶的石油醚10份,硬脂酸1份,白蜡0.5份,十八醇处理剂2.5份。
将上述成份按以下步骤进行制作。
(1)将固体颗粒木质纤维素先用甲基硅酸钠12份混合并烘干;
(2)溶剂合成胶以溶剂石油醚,硬脂酸,白蜡,十八醇混合后搅拌;
(3)将上述固体颗粒与溶剂合成胶进行搅拌揉合处理,同时烘干挥发掉石油醚达到软固相。
需要进行说明的,木质纤维素粒度在100-200目之间。
实施例4:
在本实施例中,一种使用溶剂型合成胶制成的玩具砂,使用的各成份的重量份为:固体颗粒玻璃珠600份,构成溶剂合成胶的石油醚10份,硬脂酸1份,白蜡0.5份,十八醇处理剂2.5份。
将上述成份按以下步骤进行制作。
(1)将固体颗粒玻璃珠先用甲基硅酸钠12份混合并烘干;
(2)溶剂合成胶以溶剂石油醚,硬脂酸,白蜡,十八醇混合后搅拌;
(3)将上述固体颗粒与溶剂合成胶进行搅拌揉合处理,同时烘干挥发掉石油醚达到软固相。
需要进行说明的,玻璃珠粒度在70-200目之间。
实施例5:
在本实施例中,一种使用溶剂型合成胶制成的玩具砂,使用的各成份的重量份为:固体颗粒硅砂300份,甲基硅酸钠10份,构成溶剂合成胶的石油醚12份,硬脂酸0.5份,白蜡0.8份,十八醇处理剂1.5份。所采用的制作方法与实施例1一致,本实施例在此不做重复性说明。
实施例6:
在本实施例中,一种使用溶剂型合成胶制成的玩具砂,使用的各成份的重量份为:固体颗粒玻璃珠400份,甲基硅酸钠15份,构成溶剂合成胶的石油醚8份,硬脂酸1.5份,白蜡0.2份,十八醇处理剂3.5份。所采用的制作方法与实施例1一致,本实施例在此不做重复性说明。
以上所述是本发明的优选实施方式,应当指出,对于本技术领域的普通技术人员来说,在不脱离本发明原理的前提下,还可以做出若干改进和润饰,这些改进和润饰也视为本发明的保护范围。
Claims (7)
1.一种使用溶剂型合成胶制成的玩具砂,其特征在于,包括固体颗粒、以及包裹于所述固体颗粒的溶剂合成胶,所述固体颗粒经甲基硅酸钠预混合烘干,所述溶剂合成胶包括硬脂酸、白蜡、十八醇处理剂,所述固体颗粒为硅砂、保利龙发泡珠、木质纤维素、玻璃珠中的一种;
所述的各成份的重量份为:
固体颗粒:100~600份;甲基硅酸钠10~15份;
硬脂酸:0.5~1.5份;白蜡:0.2~0.8份;十八醇处理剂:1.5~3.5份。
2.根据权利要求1所述的玩具砂,其特征在于,所述的各成份的重量份为:
硅砂:100份,甲基硅酸钠:12份;
硬脂酸:1份;白蜡:0.5份;十八醇处理剂:2.5份。
3.根据权利要求1所述的玩具砂,其特征在于,所述的各成份的重量份为:
保利龙发泡珠:200份,甲基硅酸钠:12份;
硬脂酸:1份;白蜡:0.5份;十八醇处理剂:2.5份;
所述保利龙发泡珠粒度为150~200目。
4.根据权利要求1所述的玩具砂,其特征在于,所述的各成份的重量份为:
木质纤维素:600份,甲基硅酸钠:12份;
硬脂酸:1份;白蜡:0.5份;十八醇处理剂:2.5份;
所述木质纤维素粒度为100~200目。
5.根据权利要求1所述的玩具砂,其特征在于,所述的各成份的重量份为:
玻璃珠100份,甲基硅酸钠12份;
硬脂酸:1份;白蜡:0.5份;十八醇处理剂:2.5份;
所述玻璃珠粒度为70~200目。
6.一种制作如权利要求1所述的玩具砂的方法,其特征在于,包括以下步骤:
(1)将所述固体颗粒先用甲基硅酸钠混合并烘干;
(2)溶剂合成胶以溶剂石油醚,硬脂酸,白蜡,十八醇混合后搅拌;
(3)将上述固体颗粒与溶剂合成胶进行搅拌揉合处理,同时烘干挥发掉石油醚达到软固相。
7.根据权利要求6所述的制作玩具砂的方法,其特征在于,所采用的石油醚重量份为8~12份。