CN104611753A - Cable lacquering method and application thereof - Google Patents
Cable lacquering method and application thereof Download PDFInfo
- Publication number
- CN104611753A CN104611753A CN201510011618.2A CN201510011618A CN104611753A CN 104611753 A CN104611753 A CN 104611753A CN 201510011618 A CN201510011618 A CN 201510011618A CN 104611753 A CN104611753 A CN 104611753A
- Authority
- CN
- China
- Prior art keywords
- paint
- washing
- plated
- lacquered
- plating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a cable lacquering method and application thereof, wherein the method comprises the following steps: (1) placing and washing pieces to be lacquered in an acid solution; (2) soaking and washing the pieces to be lacquered after acid washing in step (1) in an alkali solution; (3) washing the pieces to be lacquered after alkali washing in step (2) with water and ethanol, so as to obtain a blank to be lacquered; (4) soaking and washing the blank to be lacquered in a surfactant, and then electroplating. According to the design above, the pieces to be lacquered are washed with water and ethanol after acid washing and alkali washing, the washed pieces to be lacquered is soaked in the surfactant for further removing impurities, and then the surfaces are lacquered, so that the lacquering quality is improved greatly, and the using effect is enhanced because the surfaces of the lacquered products almost have no impurity.
Description
Technical field
The present invention relates to cable and manufacture field, particularly, relate to a kind of cable plating paint method and application thereof.
Background technology
In daily production, at cable surface plating paint to reduce the mode that the corrosion on its surface is conventional use as far as possible, but in plating paint process, often make plating paint effect bad because paint part top layer to be plated has impurity etc., affect its actual use, and impurity may be had because of surface, make the product surface after plating paint rough, cause enamelled coating uneven, not only waste paint, and result of use is also poor.
Therefore, top layer impurity is less to provide one to ensure preferably, makes the cable plating paint method of plating paint better effects if be the problem that the present invention needs solution badly.
Summary of the invention
For above-mentioned prior art, the object of the invention is to overcome in prior art when plating paint because paint part surface impurity to be plated is more, thus effect is painted in impact plating greatly, even make the problem that the product result of use after plating paint is also poor, thus top layer impurity is less to provide one to ensure preferably, make the cable plating paint method of plating paint better effects if.
To achieve these goals, the invention provides a kind of cable plating paint method, wherein, described method comprises:
(1) paint part to be plated is placed in acidic solution to wash;
(2) the paint part to be plated after pickling in step (1) is soaked in alkali lye washs;
(3) by the paint part to be plated after alkali cleaning in step (2) through water and washing with alcohol, obtain paint blank to be plated;
(4) paint blank to be plated is soaked in tensio-active agent washs, then electroplate.
Preferably, in step (1), the pH value of acidic solution is 3-6.
Preferably, the pH value of step (2) neutral and alkali solution is 9-13.
Preferably, also comprise in step (3) and use water and ethanol to carry out alternately washing, and described alternately washing is washed for first using water.
Preferably, the number of times of described alternately washing is 2-6 time.
Preferably, also comprise in step (4) and use tensio-active agent to carry out secondary immersion after plating, and then carry out second time electroplating.
Preferably, described tensio-active agent is stearic acid and or Sodium dodecylbenzene sulfonate.
Preferably, described paint is insullac.
Present invention also offers a kind of application according to cable described above plating paint method.
Above-mentioned design is by after carrying out pickling and alkali cleaning respectively by paint part to be plated, wash at employing water and ethanol, then the paint part to be plated after washing is placed in tensio-active agent to soak, further removal impurity, carry out plated surface paint again, and then make the product surface after plating paint substantially increase its plating paint quality because of substantially free of impurities, add its result of use.
Other features and advantages of the present invention are described in detail in embodiment part subsequently.
Embodiment
Below the specific embodiment of the present invention is described in detail.Should be understood that, embodiment described herein, only for instruction and explanation of the present invention, is not limited to the present invention.
The invention provides a kind of cable plating paint method, wherein, described method comprises:
(1) paint part to be plated is placed in acidic solution to wash;
(2) the paint part to be plated after pickling in step (1) is soaked in alkali lye washs;
(3) by the paint part to be plated after alkali cleaning in step (2) through water and washing with alcohol, obtain paint blank to be plated;
(4) paint blank to be plated is soaked in tensio-active agent washs, then electroplate.
Above-mentioned design is by after carrying out pickling and alkali cleaning respectively by paint part to be plated, wash at employing water and ethanol, then the paint part to be plated after washing is placed in tensio-active agent to soak, further removal impurity, carry out plated surface paint again, and then make the product surface after plating paint substantially increase its plating paint quality because of substantially free of impurities, add its result of use.
In order to make the corrosion avoiding causing it to paint part to be plated because acidity is too high in acid cleaning process, or the too low impurity not washing clean surface of acidity, one of the present invention preferred embodiment in, the pH value of acidic solution can be 3-6 in step (1).
Similarly, in order to make alkali cleaning effect better and reduce as far as possible in alkaline cleaning procedure, of the present invention another preferred embodiment in, the pH value of step (2) neutral and alkali solution can be set to 9-13.
Can be removed better to make the acid solution on surface and alkali lye and impurity, one of the present invention preferred embodiment in, can also comprise in step (3) and use water and ethanol to carry out alternately washing, and described alternately washing is washed for first using water.
Described alternately washing can operate according to the mode of washing of this area routine, washing times can not limit, certainly, in order to make washing effect better and economize on resources as far as possible, one of the present invention more preferred embodiment in, the number of times of described alternately washing can be 2-6 time.
Certainly, in order to make the cleaning effect of tensio-active agent to paint part surface to be plated better, one of the present invention preferred embodiment in, can also comprise in step (4) and use tensio-active agent to carry out secondary immersion after plating, and then carry out second time electroplating.
Described tensio-active agent can be this area routine use type, such as, one of the present invention preferred embodiment in, described tensio-active agent can be stearic acid and/or Sodium dodecylbenzene sulfonate.
Described paint can be this area routine use paint, such as, one of the present invention preferred embodiment in, in order to make its surface have good insulating property, described paint can be insullac.
Present invention also offers a kind of application according to cable described above plating paint method.
More than describe the preferred embodiment of the present invention in detail; but the present invention is not limited to the detail in above-mentioned embodiment, within the scope of technical conceive of the present invention; can carry out multiple simple variant to technical scheme of the present invention, these simple variant all belong to protection scope of the present invention.
It should be noted that in addition, each concrete technical characteristic described in above-mentioned embodiment, in reconcilable situation, can be combined by any suitable mode, in order to avoid unnecessary repetition, the present invention illustrates no longer separately to various possible array mode.
In addition, also can carry out arbitrary combination between various different embodiment of the present invention, as long as it is without prejudice to thought of the present invention, it should be considered as content disclosed in this invention equally.
Claims (9)
1. a cable plating paint method, it is characterized in that, described method comprises:
(1) paint part to be plated is placed in acidic solution to wash;
(2) the paint part to be plated after pickling in step (1) is soaked in alkali lye washs;
(3) by the paint part to be plated after alkali cleaning in step (2) through water and washing with alcohol, obtain paint blank to be plated;
(4) paint blank to be plated is soaked in tensio-active agent washs, then electroplate.
2. method according to claim 1, is characterized in that, in step (1), the pH value of acidic solution is 3-6.
3. method according to claim 1, is characterized in that, the pH value of step (2) neutral and alkali solution is 9-13.
4. according to the method in claim 1-3 described in any one, it is characterized in that, also comprise in step (3) and use water and ethanol to carry out alternately washing, and described alternately washing is washed for first using water.
5. method according to claim 4, is characterized in that, the number of times of described alternately washing is 2-6 time.
6. method according to claim 1, is characterized in that, also comprises and uses tensio-active agent to carry out secondary immersion after plating, and then carry out second time electroplating in step (4).
7. method according to claim 1, is characterized in that, described tensio-active agent is stearic acid and/or Sodium dodecylbenzene sulfonate.
8. method according to claim 1, is characterized in that, described paint is insullac.
9. the application according to the cable plating paint method in claim 1-8 described in any one.