CN104592599A - 一种橡胶输送带 - Google Patents

一种橡胶输送带 Download PDF

Info

Publication number
CN104592599A
CN104592599A CN201510001317.1A CN201510001317A CN104592599A CN 104592599 A CN104592599 A CN 104592599A CN 201510001317 A CN201510001317 A CN 201510001317A CN 104592599 A CN104592599 A CN 104592599A
Authority
CN
China
Prior art keywords
parts
conveyor belt
rubber
good
aging agent
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510001317.1A
Other languages
English (en)
Inventor
吴远滨
冯红明
朱汉华
叶扬政
高丽锋
邱孝仲
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
DOUBLE ARROW RUBBER Co Ltd
Original Assignee
DOUBLE ARROW RUBBER Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by DOUBLE ARROW RUBBER Co Ltd filed Critical DOUBLE ARROW RUBBER Co Ltd
Priority to CN201510001317.1A priority Critical patent/CN104592599A/zh
Publication of CN104592599A publication Critical patent/CN104592599A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种橡胶制品技术领域；尤其是一种橡胶输送带；本发明的目的是提供一种耐磨性好、导热效果好、强度好和伸长率好的一种橡胶输送带；它由100份丁苯胶1500、5～15份纳米氧化锌、0.5～3份硬脂酸、0.5～5份防老剂RD、0.5～5份防护蜡RP-3、0.5～5份防老剂4010NA、1～15份防老剂MB、0.5～65份炭黑N234、0～3份分散剂AT-C、0～15份石油树脂、1～10份癸二酸二辛酯、0.5～3份促进剂CZ、0.5～3.5份促进剂DTDM和0.5～2份促进剂TMTD构成；本发明所得的一种橡胶输送带，在长时间使用过后，输送带的两侧耐磨强度高，输送带的导热性好，且输送带在老化后，该输送带的强度变化率和扯断伸长变化率性能更好。

Description

一种橡胶输送带
技术领域
本发明涉及了一种橡胶制品技术领域；尤其是一种橡胶输送带。
背景技术
目前市面上普通的橡胶输送带在使用过程中存在以下几点缺点：（1）在长时间使用过后输送带的两侧磨耗较为严重；（2）输送带的导热性不好；（3）输送带在老化后，该输送带的强度变化率≤-30%，扯断伸长变化率≤-50%。
针对以上问题，急需我们解决。
发明内容
本发明的目的在于克服现有技术的不足，提供一种耐磨性好、导热效果好、强度好和伸长率好的一种橡胶输送带。
为了达到上述目的，本发明所设计的一种橡胶输送带，它由100份丁苯胶1500、5～15份纳米氧化锌、0.5～3份硬脂酸、0.5～5份防老剂RD、0.5～5份防护蜡RP-3、0.5～5份防老剂4010NA、1～15份防老剂MB、0.5～65份炭黑N234、0～3份分散剂AT-C、0～15份石油树脂、1～10份癸二酸二辛酯、0.5～3份促进剂CZ、0.5～3.5份促进剂DTDM和0.5～2份促进剂TMTD构成。
该橡胶输送带在混栋工艺中的制备工艺流程如下：
    第一步，在60℃～80℃时加入丁苯胶1500，然后在85℃～90℃时依次加入纳米氧化锌、硬脂酸、防老剂RD、防护蜡RP-3、防老剂MB、分散剂AT-C和石油树脂；
第二步，再在95℃～135℃时加入炭黑N234和癸二酸二辛酯；
第三步，最后在85℃～105℃时加入促进剂CZ、促进剂DTDM和促进剂TMTD。
本发明所得的一种橡胶输送带，在长时间使用过后，输送带的两侧耐磨强度高，输送带的导热性好，且输送带在老化后，该输送带的强度变化率和扯断伸长变化率性能更好。
具体实施方式
本实施例描述的一种橡胶输送带，它由100份丁苯胶1500、6份纳米氧化锌、2.份硬脂酸、1.5份防老剂RD、1份防护蜡RP-3、1份防老剂4010NA、1.5份防老剂MB、53份炭黑N234、2份分散剂AT-C、6份石油树脂、2.5份葵二酸二辛酯、2.5份促进剂CZ、2份促进剂DTDM和1份促进剂TMTD制成。
本发明所述的一种橡胶输送带在混栋工艺中的制备工艺流程如下：
    第一步，在70℃时加入丁苯胶1500，然后在90℃时依次加入纳米氧化锌、硬脂酸、防老剂RD、防护蜡RP-3、防老剂MB、分散剂AT-C和石油树脂；
第二步，再在110℃时加入炭黑N234和癸二酸二辛酯；
第三步，最后在100℃时加入促进剂CZ、促进剂DTDM和促进剂TMTD。
本发明所得的一种橡胶输送带的性能指标如下：

Claims (2)

1.一种橡胶输送带，其特征在于：它由100份丁苯胶1500、5～15份纳米氧化锌、0.5～3份硬脂酸、0.5～5份防老剂RD、0.5～5份防护蜡RP-3、0.5～5份防老剂4010NA、1～15份防老剂MB、0.5～65份炭黑N234、0～3份分散剂AT-C、0～15份石油树脂、1～10份癸二酸二辛酯、0.5～3份促进剂CZ、0.5～3.5份促进剂DTDM和0.5～2份促进剂TMTD构成。
2.根据权利要求1所述的一种橡胶输送带，其特征在于：该橡胶输送带在混栋工艺中的制备工艺流程如下：
第一步，在60℃～80℃时加入丁苯胶1500，然后在85℃～90℃时依次加入纳米氧化锌、硬脂酸、防老剂RD、防护蜡RP-3、防老剂MB、分散剂AT-C和石油树脂；
第二步，再在95℃～135℃时加入炭黑N234和癸二酸二辛酯；
第三步，最后在85℃～105℃时加入促进剂CZ、促进剂DTDM和促进剂TMTD。
CN201510001317.1A 2015-01-05 2015-01-05 一种橡胶输送带 Pending CN104592599A (zh)