CN104562029A - 高频调谐器框架冲压件表面处理工艺 - Google Patents
高频调谐器框架冲压件表面处理工艺 Download PDFInfo
- Publication number
- CN104562029A CN104562029A CN201410821384.3A CN201410821384A CN104562029A CN 104562029 A CN104562029 A CN 104562029A CN 201410821384 A CN201410821384 A CN 201410821384A CN 104562029 A CN104562029 A CN 104562029A
- Authority
- CN
- China
- Prior art keywords
- surface treatment
- parts
- mass parts
- stamping part
- treatment process
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种高频调谐器框架冲压件表面处理工艺,包括如下步骤:1)取7.5质量份硝酸锌、2.1质量份月桂酸聚氧乙烯酯、1.8质量份氟化氢钠、3.4质量份钼酸钠、2.6质量份椰子油脂肪酸二乙醇酰胺、0.3份质量植酸、1.9质量份聚硅氧烷聚醚共聚物混合,于105℃反应125min,制得金属表面处理剂;2)在将8.5质量份金属表面处理剂与32质量份水混合,制得表面处理工作液;3)将表面处理工作液升温至65℃,将金属冲压件置入表面处理工作液35分钟。本发明高频调谐器框架冲压件表面处理工艺,能提高金属冲压件的抗氧化、防腐蚀能力。
Description
技术领域
本发明涉及高频调谐器框架冲压件表面处理工艺。
背景技术
现有金属冲压件的抗氧化、防腐蚀能力有待提高。
发明内容
本发明的目的在于提供一种高频调谐器框架冲压件表面处理工艺,提高金属冲压件的抗氧化、防腐蚀能力。
为实现上述目的,本发明的技术方案是设计一种高频调谐器框架冲压件表面处理工艺,包括如下步骤:
1)取7.5质量份硝酸锌、2.1质量份月桂酸聚氧乙烯酯、1.8质量份氟化氢钠、3.4质量份钼酸钠、2.6质量份椰子油脂肪酸二乙醇酰胺、0.3份质量植酸、1.9质量份聚硅氧烷聚醚共聚物混合,于105℃反应125min,制得金属表面处理剂;
2)在将8.5质量份金属表面处理剂与32质量份水混合,制得表面处理工作液;
3)将表面处理工作液升温至65℃,将金属冲压件置入表面处理工作液35分钟。
本发明的优点和有益效果在于:提供一种高频调谐器框架冲压件表面处理工艺,提高金属冲压件的抗氧化、防腐蚀能力。
具体实施方式
下面结合实施例,对本发明的具体实施方式作进一步描述。以下实施例仅用于更加清楚地说明本发明的技术方案,而不能以此来限制本发明的保护范围。
本发明具体实施的技术方案是:
一种高频调谐器框架冲压件表面处理工艺,包括如下步骤:
1)取7.5质量份硝酸锌、2.1质量份月桂酸聚氧乙烯酯、1.8质量份氟化氢钠、3.4质量份钼酸钠、2.6质量份椰子油脂肪酸二乙醇酰胺、0.3份质量植酸、1.9质量份聚硅氧烷聚醚共聚物混合,于105℃反应125min,制得金属表面处理剂;
2)在将8.5质量份金属表面处理剂与32质量份水混合,制得表面处理工作液;
3)将表面处理工作液升温至65℃,将金属冲压件置入表面处理工作液35分钟。
以上所述仅是本发明的优选实施方式,应当指出,对于本技术领域的普通技术人员来说,在不脱离本发明技术原理的前提下,还可以做出若干改进和润饰,这些改进和润饰也应视为本发明的保护范围。
Claims (1)
1.高频调谐器框架冲压件表面处理工艺,其特征在于,包括如下步骤:
1)取7.5质量份硝酸锌、2.1质量份月桂酸聚氧乙烯酯、1.8质量份氟化氢钠、3.4质量份钼酸钠、2.6质量份椰子油脂肪酸二乙醇酰胺、0.3份质量植酸、1.9质量份聚硅氧烷聚醚共聚物混合,于105℃反应125min,制得金属表面处理剂;
2)在将8.5质量份金属表面处理剂与32质量份水混合,制得表面处理工作液;
3)将表面处理工作液升温至65℃,将金属冲压件置入表面处理工作液35分钟。