CN104529539A - Peacock blue glaze and preparation method thereof - Google Patents
Peacock blue glaze and preparation method thereof Download PDFInfo
- Publication number
- CN104529539A CN104529539A CN201410702571.XA CN201410702571A CN104529539A CN 104529539 A CN104529539 A CN 104529539A CN 201410702571 A CN201410702571 A CN 201410702571A CN 104529539 A CN104529539 A CN 104529539A
- Authority
- CN
- China
- Prior art keywords
- parts
- glaze
- roe
- blue glaze
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a peacock blue glaze. The peacock blue glaze comprises, by weight, 5-8 parts of PbO, 58-63 parts of K2O, 2-3 parts of Al2O3, 4-5 parts of SiO2, 15-19 parts of CuO, 18-22 parts of CaO, 9-12 parts of MgO and 1-3 parts of FeCl. The glaze layer of the peacock blue glaze prepared in the invention has sorghum seed size fish roe crackle, so the peacock blue glaze is exquisite and elegant.
Description
Technical field
The present invention relates to ceramic glaze technical field, more specifically, relate to a kind of roe blue glaze and preparation method thereof.
Background technology
Roe blue glaze, also known as peacock blue glaze, belongs to traditional glaze colours of west Asia, is brought to Central Plains and makes successively in gold, first common cave when the commerce and trade of its goods during the Tang and Song Dynasty are come and gone.The peacock blue goods that a pair peacock blue-black Hua Yu Hu Chunpingshi China that Yan De source, Jin Dynasty, Datong District tomb is unearthed is more early stage.From gold, first Product Process, the Cizhouyao in 13rd century is that bright blue device level is relatively high, has exquisite " the bright blue black flower " device of many drawing to deposit generation so far.
Summary of the invention
The object of this invention is to provide a kind of roe blue glaze, the roe line of jowar grain size can be appeared in glaze layer, exquisite air.
Another object of the present invention is to provide a kind of preparation method of described roe blue glaze.
The object of the invention is achieved by the following technical programs:
A kind of roe blue glaze is provided, is made up of each component of following weight fraction: PbO 5 ~ 8 parts, K
2o 58 ~ 63 parts, Al
2o
32 ~ 3 parts, SiO
24 ~ 5 parts, CuO 15 ~ 19 parts, CaO 18 ~ 22 parts, MgO 9 ~ 12 parts, FeCl 1 ~ 3 part.
Preferably, described roe blue glaze is made up of each component of following weight fraction: PbO 7 parts, K
2o 66 parts, Al
2o
32 parts, SiO
24 parts, CuO 16 parts, CaO 19 parts, MgO 11 parts, FeCl 2 parts.
Present invention also offers the preparation method of described roe blue glaze, comprise the following steps:
S1. get starting material by weight ratio, add 30% water and enter ball milling, obtain glaze slip;
S2. glazing on biscuit, enters kiln oxidizing atmosphere and burns till.
Preferably, the enameling method in S2 is for watering glaze or being coated with glaze.
Preferably, the glazing thickness in S2 is 2mm.
Preferably, the firing temperature in S2 is 980 ~ 1020 DEG C.
Compared with prior art, the present invention has following beneficial effect:
The invention provides a kind of roe blue glaze, the roe line of jowar grain size can be appeared in its glaze layer, exquisite air.
Embodiment
Below in conjunction with specific embodiment, the present invention is further illustrated.
Embodiment 1
Present embodiment discloses a kind of roe blue glaze, be made up of each component of following weight fraction: PbO 7 parts, K
2o 66 parts, Al
2o
32 parts, SiO
24 parts, CuO 16 parts, CaO 19 parts, MgO 11 parts, FeCl 2 parts.
Embodiment 2
Present embodiment discloses a kind of roe blue glaze, be made up of each component of following weight fraction: PbO 5 parts, K
2o 63 parts, Al
2o
33 parts, SiO
25 parts, CuO 19 parts, CaO 22 parts, MgO 12 parts, FeCl 3 parts.
Embodiment 3
Present embodiment discloses a kind of roe blue glaze, be made up of each component of following weight fraction: PbO 8 parts, K
2o 58 parts, Al
2o
32 parts, SiO
24 parts, CuO 15 parts, CaO 18 parts, MgO 11 parts, FeCl 1.5 parts.
Embodiment 4
Present embodiment discloses a kind of roe blue glaze, be made up of each component of following weight fraction: PbO 6 parts, K
2o 59 parts, Al
2o
32.5 parts, SiO
24.5 parts, CuO 17 parts, CaO 21 parts, MgO 10 parts, FeCl 2.5 parts.
Embodiment 5
The components by weight percent of Example 1 ~ 4 any embodiment prepares roe blue glaze, and preparation process is as follows:
S1. get starting material by weight ratio, add 30% water and enter ball milling 2h, obtain glaze slip;
S2. on biscuit, water glaze, glazed thickness is 2mm, enters kiln oxidizing atmosphere and burns till, and firing temperature is 1000 DEG C.
The roe line of jowar grain size can be appeared, exquisite air in its glaze layer of products obtained therefrom.
Embodiment 6
The components by weight percent of Example 1 ~ 4 any embodiment prepares roe blue glaze, and preparation process is as follows:
S1. get starting material by weight ratio, add 30% water and enter ball milling 2h, obtain glaze slip;
S2. on biscuit, be coated with glaze, glazed thickness is 2mm, enters kiln oxidizing atmosphere and burns till, and firing temperature is 1020 DEG C.
The roe line of jowar grain size can be appeared, exquisite air in its glaze layer of products obtained therefrom.
Claims (6)
1. a roe blue glaze, is characterized in that, is made up of each component of following weight fraction: PbO 5 ~ 8 parts, K
2o 58 ~ 63 parts, Al
2o
32 ~ 3 parts, SiO
24 ~ 5 parts, CuO 15 ~ 19 parts, CaO 18 ~ 22 parts, MgO 9 ~ 12 parts, FeCl 1 ~ 3 part.
2. roe blue glaze according to claim 1, is characterized in that, is made up of each component of following weight fraction: PbO 7 parts, K
2o 66 parts, Al
2o
32 parts, SiO
24 parts, CuO 16 parts, CaO 19 parts, MgO 11 parts, FeCl 2 parts.
3. the preparation method of roe blue glaze according to claim 1 or 2, is characterized in that, comprise the following steps:
S1. get starting material by weight ratio, add 30% water and enter ball milling, obtain glaze slip;
S2. glazing on biscuit, enters kiln oxidizing atmosphere and burns till.
4. the preparation method of roe blue glaze according to claim 3, is characterized in that, the enameling method in S2 is for watering glaze or being coated with glaze.
5. the preparation method of roe blue glaze according to claim 3, it is characterized in that, the glazing thickness in S2 is 2mm.
6. the preparation method of roe blue glaze according to claim 3, it is characterized in that, the firing temperature in S2 is 980 ~ 1020 DEG C.