CN104529371A - 一种耐腐蚀砂浆及其制备方法 - Google Patents

一种耐腐蚀砂浆及其制备方法 Download PDF

Info

Publication number
CN104529371A
CN104529371A CN201410703428.2A CN201410703428A CN104529371A CN 104529371 A CN104529371 A CN 104529371A CN 201410703428 A CN201410703428 A CN 201410703428A CN 104529371 A CN104529371 A CN 104529371A
Authority
CN
China
Prior art keywords
parts
mortar
water
mixing
minute
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410703428.2A
Other languages
English (en)
Inventor
王新荣
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201410703428.2A priority Critical patent/CN104529371A/zh
Publication of CN104529371A publication Critical patent/CN104529371A/zh
Pending legal-status Critical Current

Abstract

一种耐腐蚀砂浆,由下列重量份的原料制成：三乙醇胺3-5、乙酸2-4、硫酸铝4-5、绞股蓝提取物7-10、二氯异氰尿酸钠2-4、三聚磷酸钠2-3、硅酸钠8-10、水适量、助剂20-25、水泥170-190、砂250-270、粉煤灰40-50；本发明砂浆具有优异的抗菌耐腐蚀性能，有效防止钢筋腐蚀，延长使用寿命，防止产生霉斑；该砂浆粘聚性、流动性、触变性适中，具有良好的施工性能；通过使用本发明助剂，提高了砂浆的抗压、抗折强度，改善了和易性、抗流挂性、触变性和防沉降性。

Description

一种耐腐蚀砂浆及其制备方法
技术领域
本发明属于建筑材料领域，特别涉及一种耐腐蚀砂浆及其制备方法。
背景技术
砂浆为建筑用普通材料，属于建筑施工中的必备材料。根据性能划分，砂浆分为很多种，有结合砂浆、嵌缝砂浆、保温砂浆等；按用途分为砌筑砂浆、抹面砂浆（包括装饰砂浆、防水砂浆）、粘结砂浆等。
目前砂浆的性能品质不一，影响着使用。具体来讲影响砂浆性能的因素包括新拌砂浆的和易性、流动性、保水性，还有就是硬化砂浆的强度。需要研究新的砂浆，使其具有优异的施工性和加工性、抗流挂性、触变性、防沉降性、贮存稳定性、改善泵送性和剪切稀化性，还需要寻找新的材料，以提高其使用性能和强度，以及降低综合成本。
发明内容
本发明的目的在于提供一种耐腐蚀砂浆及其制备方法，该砂浆具有优异的抗菌耐腐蚀性能，有效防止钢筋腐蚀，延长使用寿命，防止产生霉斑，粘聚性、流动性、触变性适中，具有良好的施工性能。
本发明的技术方案如下：
一种耐腐蚀砂浆,其特征在于由下列重量份的原料制成：三乙醇胺3-5、乙酸2-4、硫酸铝4-5、绞股蓝提取物7-10、二氯异氰尿酸钠2-4、三聚磷酸钠2-3、硅酸钠8-10、水适量、助剂20-25、水泥170-190、砂250-270、粉煤灰40-50；
    所述助剂由下列重量份的原料制成：高岭土2-3、20-25%氢氧化钠溶液4-5、纳米铁1-2、碳纤维6-7、可再分散性乳胶粉2-3、氰乙基纤维素0.4-0.5、双环戊二烯丙烯酸酯2-3、甲基丙烯酸酯2-3、硅酸钾1-2、硼酸镁晶须1-2、异氰脲酸三缩水甘油酯2-3、双酚A环氧树脂4-5、氧化镁4-5、艾叶油0.4-0.5、辛癸酸0.8-1.2、铝酸钙1-1.6、十二烷基苯磺酸钠0.2-0.3、过硫酸铵0.1-0.2、过硫酸钾0.1-0.2、水16-20；制备方法为：将高岭土放入煅烧炉中，在670-700℃下煅烧3-4小时，取出，放入20-25%氢氧化钠溶液中研磨至20-40μm浆料，调浆料PH值为中性，喷雾干燥得粉末；水、十二烷基苯磺酸钠、双环戊二烯丙烯酸酯、甲基丙烯酸酯、硅酸钾、异氰脲酸三缩水甘油酯、双酚A环氧树脂、辛癸酸混合，加热至70-80℃，加入过硫酸钾搅拌反应20-30分钟，再加入所述粉末以及其他剩余成分，加热至80-90℃，搅拌反应30-40分钟，即得。
所述的耐腐蚀砂浆的制备方法，其特征在于包括以下步骤：
（1）将乙酸、硫酸铝、三聚磷酸钠、硅酸钠、水混合，搅拌均匀得到浆料；
（2）将助剂、粉煤灰、三乙醇胺、绞股蓝提取物、二氯异氰尿酸混合，分散研磨20-30分钟，得到混合物料；
（3）将其他剩余成分与第（1）步、第（2）步得到的物料混合均匀，搅拌反应10-15分钟，即得。
本发明的有益效果
本发明砂浆具有优异的抗菌耐腐蚀性能，有效防止钢筋腐蚀，延长使用寿命，防止产生霉斑；该砂浆粘聚性、流动性、触变性适中，具有良好的施工性能；通过使用本发明助剂，提高了砂浆的抗压、抗折强度，改善了和易性、抗流挂性、触变性和防沉降性。
具体实施方式
一种耐腐蚀砂浆,由下列重量份（公斤）的原料制成：三乙醇胺4、乙酸3、硫酸铝4.5、绞股蓝提取物9、二氯异氰尿酸钠3、三聚磷酸钠2.5、硅酸钠9、水适量、助剂23、水泥180、砂260、粉煤灰45；
    所述助剂由下列重量份（公斤）的原料制成：高岭土2.5、20%氢氧化钠溶液4.5、纳米铁1.5、碳纤维6.5、可再分散性乳胶粉2.5、氰乙基纤维素0.5、双环戊二烯丙烯酸酯2.5、甲基丙烯酸酯2.5、硅酸钾1.5、硼酸镁晶须1.5、异氰脲酸三缩水甘油酯2.5、双酚A环氧树脂4.5、氧化镁4.5、艾叶油0.5、辛癸酸1、铝酸钙1.3、十二烷基苯磺酸钠0.2、过硫酸铵0.1、过硫酸钾0.1、水18；制备方法为：将高岭土放入煅烧炉中，在690℃下煅烧3.5小时，取出，放入20%氢氧化钠溶液中研磨至30μm浆料，调浆料PH值为中性，喷雾干燥得粉末；水、十二烷基苯磺酸钠、双环戊二烯丙烯酸酯、甲基丙烯酸酯、硅酸钾、异氰脲酸三缩水甘油酯、双酚A环氧树脂、辛癸酸混合，加热至75℃，加入过硫酸钾搅拌反应25分钟，再加入所述粉末以及其他剩余成分，加热至85℃，搅拌反应35分钟，即得。
所述的耐腐蚀砂浆的制备方法，包括以下步骤：
（1）将乙酸、硫酸铝、三聚磷酸钠、硅酸钠、水混合，搅拌均匀得到浆料；
（2）将助剂、粉煤灰、三乙醇胺、绞股蓝提取物、二氯异氰尿酸混合，分散研磨25分钟，得到混合物料；
（3）将其他剩余成分与第（1）步、第（2）步得到的物料混合均匀，搅拌反应13分钟，即得。
实验数据：
该实施例的砂浆28d的抗压强度为47MPa，抗折强度 15MPa。

Claims (2)

1.一种耐腐蚀砂浆,其特征在于由下列重量份的原料制成：三乙醇胺3-5、乙酸2-4、硫酸铝4-5、绞股蓝提取物7-10、二氯异氰尿酸钠2-4、三聚磷酸钠2-3、硅酸钠8-10、水适量、助剂20-25、水泥170-190、砂250-270、粉煤灰40-50；
    所述助剂由下列重量份的原料制成：高岭土2-3、20-25%氢氧化钠溶液4-5、纳米铁1-2、碳纤维6-7、可再分散性乳胶粉2-3、氰乙基纤维素0.4-0.5、双环戊二烯丙烯酸酯2-3、甲基丙烯酸酯2-3、硅酸钾1-2、硼酸镁晶须1-2、异氰脲酸三缩水甘油酯2-3、双酚A环氧树脂4-5、氧化镁4-5、艾叶油0.4-0.5、辛癸酸0.8-1.2、铝酸钙1-1.6、十二烷基苯磺酸钠0.2-0.3、过硫酸铵0.1-0.2、过硫酸钾0.1-0.2、水16-20；制备方法为：将高岭土放入煅烧炉中，在670-700℃下煅烧3-4小时，取出，放入20-25%氢氧化钠溶液中研磨至20-40μm浆料，调浆料PH值为中性，喷雾干燥得粉末；水、十二烷基苯磺酸钠、双环戊二烯丙烯酸酯、甲基丙烯酸酯、硅酸钾、异氰脲酸三缩水甘油酯、双酚A环氧树脂、辛癸酸混合，加热至70-80℃，加入过硫酸钾搅拌反应20-30分钟，再加入所述粉末以及其他剩余成分，加热至80-90℃，搅拌反应30-40分钟，即得。
2.根据权利要求1所述的耐腐蚀砂浆的制备方法，其特征在于包括以下步骤：
（1）将乙酸、硫酸铝、三聚磷酸钠、硅酸钠、水混合，搅拌均匀得到浆料；
（2）将助剂、粉煤灰、三乙醇胺、绞股蓝提取物、二氯异氰尿酸混合，分散研磨20-30分钟，得到混合物料；
（3）将其他剩余成分与第（1）步、第（2）步得到的物料混合均匀，搅拌反应10-15分钟，即得。
CN201410703428.2A 2014-11-26 2014-11-26 一种耐腐蚀砂浆及其制备方法 Pending CN104529371A (zh)