CN104529292A - 一种防腐高硬度砂浆及其制备方法 - Google Patents
一种防腐高硬度砂浆及其制备方法 Download PDFInfo
- Publication number
- CN104529292A CN104529292A CN201410793464.2A CN201410793464A CN104529292A CN 104529292 A CN104529292 A CN 104529292A CN 201410793464 A CN201410793464 A CN 201410793464A CN 104529292 A CN104529292 A CN 104529292A
- Authority
- CN
- China
- Prior art keywords
- parts
- mortar
- mixing
- auxiliary agent
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种防腐高硬度砂浆,由下列重量份的原料制成:十三氟辛基三甲氧基硅烷3-5、正硅酸乙酯5-7、白垩石70-80、氧化镁20-25、偏硼酸钡25-30、偏硅酸钠8-12、三聚磷酸钠4-6、水泥130-140、砂200-220、陶瓷微粉20-30、甲基醇胺1-2、壬基酚聚氧乙烯醚1-1.5、水适量、助剂20-25;本发明砂浆添加了陶瓷微粉、氧化镁等原料,使得砂浆密实性好,硬度高,耐磨性好,而且易和性、触变性、流平性好,施工速度快;通过使用本发明助剂,提高了砂浆的抗压、抗折强度,改善了和易性、抗流挂性、触变性和防沉降性;该砂浆适用于嵌缝、抹面、粘合等用途,经久耐用。
Description
技术领域
本发明属于建筑材料领域,特别涉及一种防腐高硬度砂浆及其制备方法。
背景技术
砂浆为建筑用普通材料,属于建筑施工中的必备材料。根据性能划分,砂浆分为很多种,有结合砂浆、嵌缝砂浆、保温砂浆等;按用途分为砌筑砂浆、抹面砂浆(包括装饰砂浆、防水砂浆)、粘结砂浆等。
目前砂浆的性能品质不一,影响着使用。具体来讲影响砂浆性能的因素包括新拌砂浆的和易性、流动性、保水性,还有就是硬化砂浆的强度。需要研究新的砂浆,使其具有优异的施工性和加工性、抗流挂性、触变性、防沉降性、贮存稳定性、改善泵送性和剪切稀化性,还需要寻找新的材料,以提高其使用性能和强度,以及降低综合成本。
发明内容
本发明的目的在于提供一种防腐高硬度砂浆及其制备方法,该砂浆密实性好,硬度高,耐磨性好,而且易和性、触变性、流平性好,施工速度快。
本发明的技术方案如下:
一种防腐高硬度砂浆,其特征在于由下列重量份的原料制成:十三氟辛基三甲氧基硅烷3-5、正硅酸乙酯5-7、白垩石70-80、氧化镁20-25、偏硼酸钡25-30、偏硅酸钠8-12、三聚磷酸钠4-6、水泥130-140、砂200-220、陶瓷微粉20-30、甲基醇胺1-2、壬基酚聚氧乙烯醚1-1.5、水适量、助剂20-25;
所述助剂由下列重量份的原料制成:木炭粉末1-2、虫胶树脂1-2、羧甲基纤维素2-3、乙醇3-5、不锈钢纤维6-7、双季戊四醇六丙烯酸酯4-5、E-12环氧树脂2-3、环氧丙烯酸酯3-4、硼酸锌1-1.4、膨润土3-4、10-15%氢氧化钠5-7、三聚磷酸钠1-1.5、硫酸钙晶须3-4、烟片胶1-2、196不饱和聚酯树脂3-4、亚硫酸钙2-3、异佛尔酮0.4-0.5、油酸钠0.2-0.3、过硫酸铵0.1-0.2、过硫酸钾0.1-0.2、水17-20;制备方法为:将膨润土放入煅烧炉中,在670-700℃下煅烧3-4小时,取出,放入10-15%氢氧化钠溶液中研磨至20-40μm浆料,调浆料PH值为中性,喷雾干燥得粉末;将水、油酸钠混合,加入羧甲基纤维素、乙醇、双季戊四醇六丙烯酸酯、E-12环氧树脂、环氧丙烯酸酯、196不饱和聚酯树,搅拌均匀,加热至70-80℃,加入过硫酸钾搅拌反应20-30分钟,再加入所述粉末以及其他剩余成分,加热至80-90℃,搅拌反应30-40分钟,即得。
所述的防腐高硬度砂浆的制备方法,其特征在于包括以下步骤:
(1)将白垩石、氧化镁、偏硼酸钡混合,粉碎成140-180目颗粒;
(2)将十三氟辛基三甲氧基硅烷、正硅酸乙酯、甲基醇胺、壬基酚聚氧乙烯醚、偏硅酸钠、三聚磷酸钠、水混合,搅拌均匀得到浆料;
(3)将助剂、陶瓷微粉混合,分散研磨20-30分钟,得到混合物料;
(4)将其他剩余成分与第(1)步、第(2)步、第(3)步得到的物料混合均匀,搅拌反应10-15分钟,即得。
本发明的有益效果
本发明砂浆添加了添加了陶瓷微粉、氧化镁等原料,使得砂浆密实性好,硬度高,耐磨性好,而且易和性、触变性、流平性好,施工速度快;通过使用本发明助剂,提高了砂浆的抗压、抗折强度,改善了和易性、抗流挂性、触变性和防沉降性;该砂浆适用于嵌缝、抹面、粘合等用途,经久耐用。
具体实施方式
一种防腐高硬度砂浆,由下列重量份(公斤)的原料制成:十三氟辛基三甲氧基硅烷4、正硅酸乙酯6、白垩石75、氧化镁23、偏硼酸钡27、偏硅酸钠10、三聚磷酸钠5、水泥135、砂210、陶瓷微粉25、甲基醇胺1.5、壬基酚聚氧乙烯醚1.3、水适量、助剂23;
所述助剂由下列重量份(公斤)的原料制成:木炭粉末1.5、虫胶树脂1.5、羧甲基纤维素2.5、乙醇4、不锈钢纤维6.5、双季戊四醇六丙烯酸酯4.5、E-12环氧树脂2.5、环氧丙烯酸酯3.5、硼酸锌1.2、膨润土3.5、15%氢氧化钠6、三聚磷酸钠1.3、硫酸钙晶须3.5、烟片胶1.5、196不饱和聚酯树脂3.5、亚硫酸钙2.5、异佛尔酮0.5、油酸钠0.3、过硫酸铵0.1、过硫酸钾0.2、水19;制备方法为:将膨润土放入煅烧炉中,在690℃下煅烧3.5小时,取出,放入15%氢氧化钠溶液中研磨至30μm浆料,调浆料PH值为中性,喷雾干燥得粉末;将水、油酸钠混合,加入羧甲基纤维素、乙醇、双季戊四醇六丙烯酸酯、E-12环氧树脂、环氧丙烯酸酯、196不饱和聚酯树,搅拌均匀,加热至75℃,加入过硫酸钾搅拌反应25分钟,再加入所述粉末以及其他剩余成分,加热至85℃,搅拌反应35分钟,即得。
所述的防腐高硬度砂浆的制备方法,包括以下步骤:
(1)将白垩石、氧化镁、偏硼酸钡混合,粉碎成150目颗粒;
(2)将十三氟辛基三甲氧基硅烷、正硅酸乙酯、甲基醇胺、壬基酚聚氧乙烯醚、偏硅酸钠、三聚磷酸钠、水混合,搅拌均匀得到浆料;
(3)将助剂、陶瓷微粉混合,分散研磨25分钟,得到混合物料;
(4)将其他剩余成分与第(1)步、第(2)步、第(3)步得到的物料混合均匀,搅拌反应13分钟,即得。
实验数据:
该实施例的砂浆28d的抗压强度为51MPa,抗折强度 17MPa,吸水率2.6%。
Claims (2)
1.一种防腐高硬度砂浆,其特征在于由下列重量份的原料制成:十三氟辛基三甲氧基硅烷3-5、正硅酸乙酯5-7、白垩石70-80、氧化镁20-25、偏硼酸钡25-30、偏硅酸钠8-12、三聚磷酸钠4-6、水泥130-140、砂200-220、陶瓷微粉20-30、甲基醇胺1-2、壬基酚聚氧乙烯醚1-1.5、水适量、助剂20-25;
所述助剂由下列重量份的原料制成:木炭粉末1-2、虫胶树脂1-2、羧甲基纤维素2-3、乙醇3-5、不锈钢纤维6-7、双季戊四醇六丙烯酸酯4-5、E-12环氧树脂2-3、环氧丙烯酸酯3-4、硼酸锌1-1.4、膨润土3-4、10-15%氢氧化钠5-7、三聚磷酸钠1-1.5、硫酸钙晶须3-4、烟片胶1-2、196不饱和聚酯树脂3-4、亚硫酸钙2-3、异佛尔酮0.4-0.5、油酸钠0.2-0.3、过硫酸铵0.1-0.2、过硫酸钾0.1-0.2、水17-20;制备方法为:将膨润土放入煅烧炉中,在670-700℃下煅烧3-4小时,取出,放入10-15%氢氧化钠溶液中研磨至20-40μm浆料,调浆料PH值为中性,喷雾干燥得粉末;将水、油酸钠混合,加入羧甲基纤维素、乙醇、双季戊四醇六丙烯酸酯、E-12环氧树脂、环氧丙烯酸酯、196不饱和聚酯树,搅拌均匀,加热至70-80℃,加入过硫酸钾搅拌反应20-30分钟,再加入所述粉末以及其他剩余成分,加热至80-90℃,搅拌反应30-40分钟,即得。
2.根据权利要求1所述的防腐高硬度砂浆的制备方法,其特征在于包括以下步骤:
(1)将白垩石、氧化镁、偏硼酸钡混合,粉碎成140-180目颗粒;
(2)将十三氟辛基三甲氧基硅烷、正硅酸乙酯、甲基醇胺、壬基酚聚氧乙烯醚、偏硅酸钠、三聚磷酸钠、水混合,搅拌均匀得到浆料;
(3)将助剂、陶瓷微粉混合,分散研磨20-30分钟,得到混合物料;
(4)将其他剩余成分与第(1)步、第(2)步、第(3)步得到的物料混合均匀,搅拌反应10-15分钟,即得。