CN104497881A - Water-based reflective insulation stone paint and manufacturing method thereof - Google Patents
Water-based reflective insulation stone paint and manufacturing method thereof Download PDFInfo
- Publication number
- CN104497881A CN104497881A CN201410724816.9A CN201410724816A CN104497881A CN 104497881 A CN104497881 A CN 104497881A CN 201410724816 A CN201410724816 A CN 201410724816A CN 104497881 A CN104497881 A CN 104497881A
- Authority
- CN
- China
- Prior art keywords
- spectral selectivity
- component
- water
- coating
- reflective insulation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses water-based reflective insulation stone paint and a manufacturing method thereof. The water-based reflective insulation stone paint comprises the following main components: a paint composition, a functional pigment and filler aid composition, a spectral selection powder composition, a spectral selection color paste composition and a spectral selection particle composition, wherein the spectral selection powder composition has a reflection effect. The paint has a reflection effect, can reflect lots of infrared light and ultraviolet light in sunlight and further has a thermal insulation effect; the paint is water-based stone paint and has the decorative effect of the traditional stone paint; and moreover, the paint is difficult to fade and does not have obvious fade marks within 8-10 years.
Description
Technical field
The present invention relates to coating and preparation method thereof Application Areas, particularly a kind of water-based reflective insulation stone-like coating and preparation method thereof.
Background technology
Carry out green building, pay attention to development building technology, for improving human settlement and solving energy shortage, the Sustainable Development realizing the mankind is significant.
At present as the coating of exterior-wall heat insulation basal plane and decorative effect, all adopt traditional true mineral varnish, although traditional true mineral varnish can play the effect of decoration, it can not play the effect of reflective insulation, especially during the broiling summer, sunlight intensity can directly be injected in the metope of true mineral varnish; Traditional true mineral varnish also easily fades, and after general 3-5, obviously has the vestige faded through rainwash, reduces its work-ing life.
Summary of the invention
For solving Problems existing in above-mentioned background technology, the object of the present invention is to provide a kind of water-based reflective insulation stone-like coating and preparation method thereof, making it can reach the effect of reflective insulation, possess again the effect of decoration simultaneously, and object not easy to fade.
For achieving the above object, technical scheme of the present invention is as follows:
A kind of water-based reflective insulation stone-like coating, its main component comprises coating composition, functional color stuffing adjuvant component, spectral selectivity powder component, spectral selectivity mill base component and spectral selectivity grain fraction, and described spectral selectivity powder component has reflex action.
Preferably, the mass fraction of described each main component is respectively: coating composition is 45-55 part, functional color stuffing adjuvant component is 0.5-1.5 part, spectral selectivity powder component is 10-15 part, spectral selectivity mill base component is 1.5-2.5 part, spectral selectivity grain fraction is 35-45 part.
A making method for water-based reflective insulation stone-like coating, comprises the following steps:
One, the making of coating composition: water, emulsion, titanium dioxide, barium sulfate, kaolin are added successively container for stirring dispersion, then through grinding, filter, then add functional color stuffing adjuvant component and disperse, finally measure its parameter, for subsequent use;
Two, the making of spectral selectivity powder component: water, spectral selectivity powder are added the dispersion of another container for stirring in the ratio of 1.5: 0.8, then add functional color stuffing adjuvant component film forming, finally measures its parameter, for subsequent use;
Three, the spectral selectivity powder component made in step 2 is added in the container in step one, fully mix with the coating composition made, dispersed with stirring, add spectral selectivity mill base component again to mix colours, measure its parameter again, finally add spectral selectivity grain fraction again, dispersed with stirring, and adjust its viscosity.
Pass through technique scheme, a kind of water-based reflective insulation stone-like coating provided by the invention and preparation method thereof, by the spectral selectivity powder component of adding, make it have the effect of reflection, it can a large amount of infrared lights and UV-light in reflected sunlight, and then making it have heat insulation effect, the intensity of sunlight is larger, and its reflective insulation effect is relatively more remarkable; This coating is water-based stone-like coating, and it possesses the decorative effect of traditional true mineral varnish coating simultaneously; Make this coating not fugitive color by the spectral selectivity mill base component of adding and spectral selectivity grain fraction, color and luster in 8-10 without obviously fading vestige.
Embodiment
Be clearly and completely described to the technical scheme in the embodiment of the present invention below.
Embodiment one:
A kind of water-based reflective insulation stone-like coating provided by the invention, its main component comprises coating composition, functional color stuffing adjuvant component, spectral selectivity powder component, spectral selectivity mill base component and spectral selectivity grain fraction, described spectral selectivity powder component has reflex action, and the mass fraction of each main component is respectively: coating composition is 45 parts, functional color stuffing adjuvant component is 0.5 part, spectral selectivity powder component is 10 parts, spectral selectivity mill base component is 1.5 parts, spectral selectivity grain fraction is 35 parts.
A making method for water-based reflective insulation stone-like coating, comprises the following steps:
One, the making of coating composition: water, emulsion, titanium dioxide, barium sulfate, kaolin are added successively container for stirring dispersion, then through grinding, filtration, the more functional color stuffing adjuvant component adding 0.25 part disperses, and finally measures its parameter, for subsequent use;
Two, the making of spectral selectivity powder component: water, spectral selectivity powder are added the dispersion of another container for stirring in the ratio of 1.5: 0.8, then add the functional color stuffing adjuvant component film forming of 0.25 part, finally measures its parameter, for subsequent use;
Three, the spectral selectivity powder component made in step 2 is added in the container in step one, fully mix with the coating composition made, dispersed with stirring, add spectral selectivity mill base component again to mix colours, measure its parameter again, finally add spectral selectivity grain fraction again, dispersed with stirring, and adjust its viscosity.
Embodiment two:
A kind of water-based reflective insulation stone-like coating provided by the invention, its main component comprises coating composition, functional color stuffing adjuvant component, spectral selectivity powder component, spectral selectivity mill base component and spectral selectivity grain fraction, described spectral selectivity powder component has reflex action, and the mass fraction of each main component is respectively: coating composition is 48 parts, functional color stuffing adjuvant component is 0.9 part, spectral selectivity powder component is 12 parts, spectral selectivity mill base component is 1.8 parts, spectral selectivity grain fraction is 38 parts.
The making method of a kind of water-based reflective insulation stone-like coating provided by the invention, comprises the following steps:
One, the making of coating composition: water, emulsion, titanium dioxide, barium sulfate, kaolin are added successively container for stirring dispersion, then through grinding, filtration, the more functional color stuffing adjuvant component adding 0.45 part disperses, and finally measures its parameter, for subsequent use;
Two, the making of spectral selectivity powder component: water, spectral selectivity powder are added the dispersion of another container for stirring in the ratio of 1.5: 0.8, then add the functional color stuffing adjuvant component film forming of 0.45 part, finally measures its parameter, for subsequent use;
Three, the spectral selectivity powder component made in step 2 is added in the container in step one, fully mix with the coating composition made, dispersed with stirring, add spectral selectivity mill base component again to mix colours, measure its parameter again, finally add spectral selectivity grain fraction again, dispersed with stirring, and adjust its viscosity.
Embodiment three:
A kind of water-based reflective insulation stone-like coating provided by the invention, its main component comprises coating composition, functional color stuffing adjuvant component, spectral selectivity powder component, spectral selectivity mill base component and spectral selectivity grain fraction, and described spectral selectivity powder component has reflex action.The mass fraction of each main component is respectively: coating composition is 52 parts, functional color stuffing adjuvant component is 1.2 parts, spectral selectivity powder component is 13.5 parts, spectral selectivity mill base component is 2.3 parts, spectral selectivity grain fraction is 42 parts.
The making method of a kind of water-based reflective insulation stone-like coating provided by the invention, comprises the following steps:
One, the making of coating composition: water, emulsion, titanium dioxide, barium sulfate, kaolin are added successively container for stirring dispersion, then through grinding, filtration, the more functional color stuffing adjuvant component adding 0.6 part disperses, and finally measures its parameter, for subsequent use;
Two, the making of spectral selectivity powder component: water, spectral selectivity powder are added the dispersion of another container for stirring in the ratio of 1.5: 0.8, then add the functional color stuffing adjuvant component film forming of 0.6 part, finally measures its parameter, for subsequent use;
Three, the spectral selectivity powder component made in step 2 is added in the container in step one, fully mix with the coating composition made, dispersed with stirring, add spectral selectivity mill base component again to mix colours, measure its parameter again, finally add spectral selectivity grain fraction again, dispersed with stirring, and adjust its viscosity.
Embodiment four:
A kind of water-based reflective insulation stone-like coating provided by the invention, its main component comprises coating composition, functional color stuffing adjuvant component, spectral selectivity powder component, spectral selectivity mill base component and spectral selectivity grain fraction, and described spectral selectivity powder component has reflex action.The mass fraction of each main component is respectively: coating composition is 55 parts, functional color stuffing adjuvant component is 1.5 parts, spectral selectivity powder component is 15 parts, spectral selectivity mill base component is 2.5 parts, spectral selectivity grain fraction is 45 parts.
The making method of a kind of water-based reflective insulation stone-like coating provided by the invention, comprises the following steps:
One, the making of coating composition: water, emulsion, titanium dioxide, barium sulfate, kaolin are added successively container for stirring dispersion, then through grinding, filtration, the more functional color stuffing adjuvant component adding 0.75 part disperses, and finally measures its parameter, for subsequent use;
Two, the making of spectral selectivity powder component: water, spectral selectivity powder are added the dispersion of another container for stirring in the ratio of 1.5: 0.8, then add the functional color stuffing adjuvant component film forming of 0.75 part, finally measures its parameter, for subsequent use;
Three, the spectral selectivity powder component made in step 2 is added in the container in step one, fully mix with the coating composition made, dispersed with stirring, add spectral selectivity mill base component again to mix colours, measure its parameter again, finally add spectral selectivity grain fraction again, dispersed with stirring, and adjust its viscosity.
A kind of water-based reflective insulation stone-like coating disclosed by the invention and preparation method thereof, by the spectral selectivity powder component of adding, make it have the effect of reflection, it can a large amount of infrared lights and UV-light in reflected sunlight, and then make it have heat insulation effect, the intensity of sunlight is larger, and its reflective insulation effect is relatively more remarkable; This coating is water-based stone-like coating, and it possesses the decorative effect of traditional true mineral varnish coating simultaneously; Make this coating not fugitive color by the spectral selectivity mill base component of adding and spectral selectivity grain fraction, color and luster in 8-10 without obviously fading vestige.The not only energy-conserving and environment-protective of this coating, also have stable freedom from cracking performance, also have weathering resistance, resistance to acids and bases, self-cleaning simultaneously, its short construction period, greatly save engineering time and cost of labor.
To the above-mentioned explanation of the disclosed embodiments, professional and technical personnel in the field are realized or uses the present invention.To be apparent for those skilled in the art to the multiple amendment of these embodiments, General Principle as defined herein can without departing from the spirit or scope of the present invention, realize in other embodiments.Therefore, the present invention can not be restricted to these embodiments shown in this article, but will meet the widest scope consistent with principle disclosed herein and features of novelty.
Claims (3)
1. a water-based reflective insulation stone-like coating, it is characterized in that, its main component comprises coating composition, functional color stuffing adjuvant component, spectral selectivity powder component, spectral selectivity mill base component and spectral selectivity grain fraction, and described spectral selectivity powder component has reflex action.
2. a kind of water-based reflective insulation stone-like coating according to claim 1, it is characterized in that, the mass fraction of described each main component is respectively: coating composition is 45-55 part, functional color stuffing adjuvant component is 0.51.5 part, spectral selectivity powder component is 1015 parts, spectral selectivity mill base component is 1.52.5 part, spectral selectivity grain fraction is 35-45 part.
3. a making method for water-based reflective insulation stone-like coating, is characterized in that, comprises the following steps:
One, the making of coating composition: water, emulsion, titanium dioxide, barium sulfate, kaolin are added successively container for stirring dispersion, then through grinding, filter, then add functional color stuffing adjuvant component and disperse, finally measure its parameter, for subsequent use;
Two, the making of spectral selectivity powder component: water, spectral selectivity powder are added the dispersion of another container for stirring in the ratio of 1.5: 0.8, then add functional color stuffing adjuvant component film forming, finally measures its parameter, for subsequent use;
Three, the spectral selectivity powder component made in step 2 is added in the container in step one, fully mix with the coating composition made, dispersed with stirring, add spectral selectivity mill base component again to mix colours, measure its parameter again, finally add spectral selectivity grain fraction again, dispersed with stirring, and adjust its viscosity.