CN104446176A - 一种水泥基复合材料及其压敏传感器 - Google Patents
一种水泥基复合材料及其压敏传感器 Download PDFInfo
- Publication number
- CN104446176A CN104446176A CN201410601109.0A CN201410601109A CN104446176A CN 104446176 A CN104446176 A CN 104446176A CN 201410601109 A CN201410601109 A CN 201410601109A CN 104446176 A CN104446176 A CN 104446176A
- Authority
- CN
- China
- Prior art keywords
- cement
- composite material
- graphene oxide
- carbon fiber
- base composite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
一种水泥基复合材料及其压敏传感器,涉及一种水泥基复合材料及其压敏传感器。本发明解决了碳纤维在基体中分散不均匀导致的水泥基复合材料电阻率和应力感知能力差,压敏传感器稳定性差和灵敏度低等问题。本发明的氧化石墨烯/碳纤维水泥基复合材料及其传感器由功能组分、水泥、分散剂、减水剂、消泡剂、细骨料和其它的矿物掺合料组成,功能组分为氧化石墨烯与碳纤维,其中氧化石墨烯占胶凝材料总质量的0.01%-5%,碳纤维占胶凝材料总质量的0.01-5%。本发明氧化石墨烯/碳纤维水泥基复合材料具有强度高、耐久性好、孔隙缺陷少、致密性好等优点,其压敏传感器具有初始电阻率稳定、应力感知能力高、传感器灵敏度高、稳定性好等优点,优于单独以碳纤维、氧化石墨烯、碳黑、钢渣等作为导电相的水泥基复合材料。
Description
【技术领域】
本发明涉及一种复合材料及其制备方法,具体讲涉及一种氧化石墨烯和碳纤维水泥基复合材料及其制备方法和应用。
【背景技术】
混凝土广泛应用于工业和民用建筑、道路与桥梁工程、机场、港口与水利工程。混凝土结构建筑物,特别是超大跨度桥梁、重点水利工程、重点体育场馆、大型海洋平台、核电站工程和高速铁路建设等重大工程结构设计寿命一般长达数十年,甚至上百年。其间长期反复承受各种荷载、酸雨等自然环境的长期侵蚀以及材质自身老化,不可避免地导致土木工程结构损伤,可能引起突发性灾难,给人民的生命财产安全造成极大的损失。为此已开展了诸如工程结构群体健康监测关键技术研究、材料安全服役行为和新型功能材料制备基础与性能调控相关方面的研究。重大土木工程结构实施健康监测与荷载控制技术已成为土木工程领域的热点研究课题,是未来经济建设和社会发展迫切需要解决的问题。
高性能智能传感元件是重大工程结构智能监测与健康诊断的重要组成部分。近年来,用作土木工程结构长期健康监测的传感器主要有光纤传感器和水泥基复合材料压敏传感器,光纤传感器虽然耐久性和稳定性较好,但是价格高昂,难以大规模推广使用。而水泥基复合材料压敏传感器由于埋设工艺简单,耐久性好,与土木工程结构相容性好,价格低等优点,成为土木工程结构监测与健康诊断领域的热点课题。
以水泥(砂浆或混凝土)为基体的水泥基复合材料压敏传感器,复合部分是导电相,是借助电学性质的变化反映其力学特性变化的复合材料。现有技术已对包括碳纤维、纳米碳黑,碳纳米管等导电性能进行了不同角度的尝试。1993年,D.D.L.Chung教授及她的课题组提出了机敏混凝土(Smart concrete)的概念。1996年,李卓球等研究表明,碳纤维水泥基复合材料在逐渐加压直至破坏的过程中,其间的电阻率随压应力的增加呈现显著下降、平稳过渡和迅速上升三个阶段,这三个阶段分别与碳纤维混凝土的弹性、塑性及崩溃三个阶段相对应。2000年,欧进萍等提出开发小尺寸、精度高、可重复性好、造价低、耐久性好、埋设工艺简单的标准碳纤维水泥石传感器。将其埋设于混凝土构件中形成智能混凝土结构***,具有耐久性好、造价低、与混凝土相容性好等优点。
现有技术披露了用于水泥基体的纳米材料填充材料有:纳米SiO2,纳米CaCO3,纳米TiO2,碳纳米管,纳米炭黑和纳米Fe2O3等。揭示了纳米材料在水泥基体中的均匀分散以及对水泥基体微观结构和宏观性能的改善。
碳家族的新成员石墨烯,是一种二维的sp2杂化的碳的同素异形体,是最薄的材料-单原子厚度的材料。石墨烯具有优异的电学性能,热学性能,超高的比表面积,杨氏模量和断裂强度等一系列优异的性质。石墨烯作为一种高性能的聚合物填充材料,可以显著提高聚合物的导电性、导热性和机械性能。氧化石墨烯不仅是制备石墨烯及功能化石墨烯的一种重要起始原料,而且也是一种重要的石墨烯衍生材料。其含有丰富的表面含氧官能团,在水相体系中分散性能良好。
申请号为201310233476.5、名称为“一种氧化石墨烯水泥基复合材料应力传感器”的专利文件中公开了一种结构工程监测用应力传感器,此传感器部件是添加0.02%氧化石墨烯的氧化石墨烯水泥基复合材料制备的。但是,虽然石墨烯具有很强的导电能力,但是氧化石墨烯几乎没有导电能力,作为石墨烯的衍生物,表面含有大量的含氧官能团,π电子结构被破坏,导电能力几乎丧失。仅添在添加0.02%的氧化石墨烯下,水泥石的导电能力提高很少,氧化石墨烯水泥基复合材料无法发挥应力传感器的作用。
专利号为ZL200710072474.7、名称为“一种压敏水泥基复合材料”的发明专利公开了一种用于解决力-电耦合效应灵敏度低及受湿度影响大、基体极化易影响电学信号测试等缺陷的压敏水泥基复合材料,此材料为由含有1~80%的功能组分(镍粉、碳纤维、碳黑、石墨、钢渣中的一种或几种的混合物)与水泥基材料组成的复合材料,但用于制备水泥基智能材料时工艺复杂或加入量大、成本高或与水泥基体相容性差的缺陷严重制约了水泥基智能材料的应用。本发明人经长期观察、研究、分析发现需要提供一种对水泥基材的导电成分种类、分散性进一步优化的技术来克服现有技术存在的以下不足的技术方案:(1)碳纤维在水泥基体中的分散性差,填充物与基体相容性不好,初始电阻率和应力感知能力离散高等缺陷;(2)具有很高长径比的碳纳米管在水泥基体中容易缠绕,疏水的表面化学特性导致在水泥基体中的分散性差,最终导致微观结构和性能的均一性差;(3)纳米SiO2或纳米CaCO3虽然对改善水泥基体微观结构和力学性能有重要贡献,但是不能发挥水泥基复合材料的功能性,同时纳米材料的团聚性也可能导致基体强度下降。
【发明内容】
为解决碳纤维在基体材料中分散不均匀导致水泥基复合材料电阻率和应力感知能力差,压敏传感器稳定性差和灵敏度低等问题。本发明采用了具有两亲性质,能在水相体系中均匀分散的氧化石墨烯作为碳纤维的分散剂,不仅提高碳纤维在水泥基体中的分散性,而且还与碳纤维具有协同作用,增强增韧水泥基复合材料;协同利用氧化石墨烯残留电子和碳纤维的导电性,提高应力自感知水泥基复合材料的电学性能,降低初始电阻率和应力感知能力的离散性,可应用于混凝土构件的结构损伤监测。
为实现上述目的,本发明采用以下技术方案:
本发明提供了一种水泥基复合材料,包括水泥、减水剂和功能性组分,其中功能性组分为氧化石墨烯和碳纤维的组合物;功能性组分占水泥总质量的0.01-10%,得到的水泥基复合材料的抗压强度为30-100MPa,抗折强度为5-20MPa,灵敏度为0.5-1.0%/MPa。
本发明提供的水泥基复合材料中,功能性组分占水泥总质量的0.01%-5%。
本发明提供的水泥基复合材料中,功能性组分占水泥总质量的0.05-2%。
本发明提供的水泥基复合材料中,氧化石墨烯占水泥总质量的0.05-2%;碳纤维占水泥总质量的0.05-2%。
本发明提供的水泥基复合材料中,碳纤维为短切碳纤维。
本发明还提供了一种压敏传感器由本发明提供的水泥基复合材料制备而成。
本发明提供了一种制备压敏传感器的方法,包括下述步骤:
1)将经强酸浸泡2-12h的3mm-15mm的短切碳纤维用清水冲洗,离心,烘干;
2)称取氧化石墨烯制成水溶液水溶液,与减水剂充分混合后,倒入处理后的碳纤维,充分搅拌后,分批加入水泥和矿物掺合料,搅拌均匀,装模,在氧化石墨烯和碳纤维水泥基体与长度方向垂直的横截面上设置四层平行金属铜片,养护到一定龄期,即得;
制得的压敏传感器的抗压强度为30-100MPa,抗折强度为5-20MPa,灵敏度为0.5-1.0%/MPa。
本发明提供的制备方法中,酸为H2SO4或HNO3或KMnO4。优选浓度大于70%的H2SO4,质量分数为65%的市售浓硝酸。
本发明制得的压敏传感器在土木工程结构监测及荷载控制中的应用。
本发明提供的水泥基复合材料除了包括水泥,减水剂及功能性组分外,还可以根据需要加入消泡剂、细骨料或其它的矿物掺合料;矿物掺合料可选用硅灰、粉煤灰、矿粉、沸石粉等。
与现有技术相比,本发明提供的技术方案制得的氧化石墨烯/碳纤维水泥基复合材料具有强度高、耐久性好、孔隙缺陷少、致密性好等优点,其压敏传感器具有初始电阻率稳定、应力感知能力高、传感器灵敏度高、稳定性好等优点,优于单独以碳纤维、氧化石墨烯、碳黑、钢渣等作为导电相的水泥基复合材料。
本发明所述的氧化石墨烯和碳纤维水泥基复合材料抗压强度、抗折强度大,应力感知能力高,稳定性好,灵敏度高。
【附图说明】
图1为对照组水泥基复合材料试件;
图2.1为本发明实施例5氧化石墨烯和碳纤维水泥基复合材料的电镜扫描图;
图2.2为对照组2氧化石墨烯水泥基复合材料的电镜扫描图;
图2.3为对照组3碳纤维水泥基复合材料的电镜扫描图;
图3.1为本发明实施例5的电阻率曲线图,3.2为对照组2的电阻率曲线图,3.3为对照组3的电阻率曲线图。
【具体实施方式】
实施例1制备氧化石墨烯和碳纤维水泥基复合材料压敏传感器
将水泥质量1%的聚羧酸减水剂和0.03%的氧化石墨烯溶液加入200ml水中搅拌均匀后,加入水泥质量0.3%的经过HNO3氧化处理的短切碳纤维,充分搅拌,并加入消泡剂去泡;将分散均匀的碳纤维和水泥倒入砂浆搅拌机搅拌均匀,在此过程中,再加入剩余的水和适量的减水剂,控制拌合物的稠度和流动度。拌合均匀后,注入40×40×160mm胶砂标准力学试模(预先放入铜丝网电极),在振动台上振实3min,置于室内,1d后脱模,标准养护。
实施例2制备氧化石墨烯/碳纤维水泥基复合材料压敏传感器
将水泥质量1.2%的聚羧酸减水剂和0.1%的氧化石墨烯溶液加入200ml水中搅拌均匀后,加入水泥质量1%经过HNO3氧化处理的短切碳纤维,充分搅拌,使碳纤维均匀分散,并加入消泡剂去泡;将分散均匀的碳纤维和水泥倒入砂浆搅拌机搅拌均匀,在此过程中,再加入剩余的水和适量的减水剂,控制拌合物的稠度和流动度。拌合均匀后,注入40×40×160mm胶砂标准力学试模(预先放入铜丝网电极),在振动台上振实3min,置于室内,1d后脱模,标准养护。
实施例3制备氧化石墨烯和碳纤维水泥基复合材料压敏传感器
将水泥质量1.6%的聚羧酸减水剂和1%的氧化石墨烯溶液加入200ml水中搅拌均匀后,加入水泥质量2%经过HNO3氧化处理的碳纤维,充分搅拌,使碳纤维均匀分散,并加入消泡剂去泡;将分散均匀的碳纤维和水泥倒入砂浆搅拌机搅拌均匀,在此过程中,再加入剩余的水和适量的减水剂,控制拌合物的稠度和流动度。拌合均匀后,注入40×40×160mm胶砂标准力学试模(预先放入铜丝网电极),在振动台上振实3min,置于室内,1d后脱模,标准养护。
实施例4
将水泥质量0.8%的聚羧酸减水剂和0.01%的氧化石墨烯溶液加入200ml水中搅拌均匀后,加入水泥质量0.02%经过HNO3氧化处理的碳纤维,充分搅拌,使碳纤维均匀分散,并加入消泡剂去泡;将分散均匀的碳纤维和水泥倒入砂浆搅拌机搅拌均匀,在此过程中,再加入剩余的水和适量的减水剂,控制拌合物的稠度和流动度。拌合均匀后,注入40×40×160mm胶砂标准力学试模(预先放入铜丝网电极),在振动台上振实3min,置于室内,1d后脱模,标准养护。
实施例5
将水泥质量0.8%的聚羧酸减水剂和0.02%的氧化石墨烯溶液加入200ml水中搅拌均匀后,加入水泥质量0.2%经过HNO3氧化处理的碳纤维,充分搅拌,使碳纤维均匀分散,并加入消泡剂去泡;将分散均匀的碳纤维和水泥倒入砂浆搅拌机搅拌均匀,在此过程中,再加入剩余的水和适量的减水剂,控制拌合物的稠度和流动度。拌合均匀后,注入40×40×160mm胶砂标准力学试模(预先放入铜丝网电极),在振动台上振实3min,置于室内,1d后脱模,标准养护。
对比例1
制备氧化石墨烯水泥基复合材料压敏传感器
将水泥质量1%的聚羧酸减水剂和0.5%的氧化石墨烯溶液加入200ml水中搅拌均匀后,加入适量的水泥搅拌均匀;将分散均匀的氧化石墨烯水泥拌合物和剩余的水泥倒入砂浆搅拌机搅拌均匀,在此过程中,再加入剩余的水和适量的减水剂,控制拌合物的稠度和流动度。拌合均匀后,注入40×40×160mm胶砂标准力学试模(预先放入铜丝网电极),在振动台上振实3min,置于室内,1d后脱模,标准养护。
对比例2
制备氧化石墨烯水泥基复合材料压敏传感器
将水泥质量1%的聚羧酸减水剂和0.03%的氧化石墨烯溶液加入200ml水中搅拌均匀后,加入适量的水泥搅拌均匀;将分散均匀的氧化石墨烯水泥拌合物和剩余的水泥倒入砂浆搅拌机搅拌均匀,在此过程中,再加入剩余的水和适量的减水剂,控制拌合物的稠度和流动度。拌合均匀后,注入40×40×160mm胶砂标准力学试模(预先放入铜丝网电极),在振动台上振实3min,置于室内,1d后脱模,标准养护。
对比例3
制备碳纤维水泥基复合材料压敏传感器
先用烧杯盛100mL热水(60℃),将甲基纤维素加入水中搅拌,形成淤浆状物质,再加入水泥质量0.3%的经过HNO3氧化处理的碳纤维,并加入消泡剂搅拌;另外,将水泥、硅灰、减水剂、矿粉和水,拌和混匀,水胶比(水与胶凝材料的质量比)为0.35,以保持混合料适宜的流动性。将分散好的氧化石墨烯和拌合均匀的水泥拌合物分别倒入砂浆搅拌机搅拌均匀。配合料拌和均匀后,注入40×40×160mm胶砂标准力学试模(预先放入铜丝网电极),在振动台上振实3min,置于室内,1d后脱模,标准养护。
对比例4制备碳纤维水泥基复合材料压敏传感器
将水泥质量1%的聚羧酸减水剂加入200ml水中搅拌均匀后,加入水泥质量1%经过HNO3氧化处理的碳纤维,充分搅拌,再加入适量的硅灰充分搅拌,使碳纤维均匀分散,并加入消泡剂去泡;将分散均匀的碳纤维和水泥倒入砂浆搅拌机搅拌均匀,在此过程中,再加入剩余的水和适量的减水剂,控制拌合物的稠度和流动度。拌合均匀后,注入40×40×160mm胶砂标准力学试模(预先放入铜丝网电极),在振动台上振实3min,置于室内,1d后脱模,标准养护。
氧化石墨烯/碳纤维水泥基复合材料和碳纤维水泥基复合材料压敏试验对比结果见表1。
表1 性能稳定性对比结果
实施例1 | 实施例2 | 实施例3 | 实施例4 | 实施例5 | |
电阻率 | 109 | 75 | 49 | 1280 | 420 |
变异系数(%) | 0.031 | 0.028 | 0.074 | 0.083 | 0.068 |
对比例1 | 对比例2 | 对比例3 | 对比例4 | ||
电阻率 | 21900 | 25000 | 519 | 65 | |
变异系数(%) | 1.73 | 1.34 | 0.198 | 0.178 |
图3.1是同时添加氧化石墨烯和碳纤维的水泥石在非破坏荷载下电阻的变化情况。
图3.2是仅添加氧化石墨烯的水泥石在非破坏荷载下电阻的变化情况。
图3.3是仅添加碳纤维的水泥石在非破坏荷载下电阻的变化情况。
由图3.1可知,仅掺加NGO的普通水泥石的电阻虽然也有变化,但变化幅度基本可以忽略,在从0KN匀速加载到15KN时,电阻的变化只有1.20%。说明仅添加氧化石墨烯的水泥石压敏性不明显。
与之对比的是,在同时掺入氧化石墨烯和碳纤维后,水泥石在变化的应力下的电阻变化幅度大幅增加,增加到26.6%,而图3.2仅为1.2%,图3.3为13.54%。
尽管本申请结合优选实施例对本发明进行了说明,但本发明并不局限于上述实施例当中,应该理解,在本发明构思的引导下,本领域技术人员可进行各种修改和改进,这些变更和修改均在申请待批的权利要求保护范围之内。
Claims (10)
1.一种水泥基复合材料,包括水泥、减水剂和功能性组分,按质量百分比计,其特征在于:所述功能性组分为由氧化石墨烯和碳纤维组成;
所述功能性组分占水泥总质量的0.01-10%。
2.根据权利要求1所述的水泥基复合材料,其特征在于:所述水泥基复合材料的抗压强度为30-100MPa,抗折强度为5-20MPa,灵敏度为0.5-1.0%/MPa。
3.根据权利要求1所述的水泥基复合材料,其特征在于:所述功能性组分占水泥总质量的0.01%-5%。
4.根据权利要求3所述的水泥基复合材料,其特征在于:所述功能性组分占水泥总质量的0.05-2%。
5.根据权利要求1所述的水泥基复合材料,其特征在于:所述氧化石墨烯占水泥总质量的0.05-2%;所述碳纤维占水泥总质量的0.05-2%。
6.根据权利要求1所述的水泥基复合材料,其特征在于:所述碳纤维为短切碳纤维。
7.一种压敏传感器,其特征在于:由权利要求6所述水泥基复合材料制备而成。
8.一种制备如权利要求7所述压敏传感器的方法,包括下述步骤:
1)将经酸浸泡2-12h的3mm-15mm的短切碳纤维用清水冲洗,离心,烘干;
2)将称取氧化石墨烯水溶液与减水剂充分混合后,加入短切碳纤维充分搅拌后,分批加入水泥搅拌均匀,装模,在氧化石墨烯和碳纤维水泥基体与长度方向垂直的横截面上设置四层平行金属铜片,养护,即得;
所述压敏传感器的抗压强度为30-100MPa,抗折强度为5-20MPa,灵敏度为0.5-1.0%/MPa。
9.根据权利要求8所述的制备方法,其特征在于:所述酸为H2SO4、KMnO4或HNO3。
10.根据权利要求8所述方法制得的压敏传感器在土木工程结构监测及荷载控制中的应用。