CN104389094A - 52%棉48%真丝单面大提花布及制备方法 - Google Patents
52%棉48%真丝单面大提花布及制备方法 Download PDFInfo
- Publication number
- CN104389094A CN104389094A CN201410546789.0A CN201410546789A CN104389094A CN 104389094 A CN104389094 A CN 104389094A CN 201410546789 A CN201410546789 A CN 201410546789A CN 104389094 A CN104389094 A CN 104389094A
- Authority
- CN
- China
- Prior art keywords
- fabric
- cotton
- percent
- real silk
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种面料的制备方法。52%棉48%真丝单面大提花布的制备方法,该方法包括以下的步骤:开幅、清水定型烘干、丝光、第二次定型、橡毯预缩、蒸呢和汽蒸预缩。制备的单面大提花布,同时具备棉和真丝的特性,具有吸湿力强、吸水性、护肤保健作用、透气性、保暖性、光泽润美、手感柔和耐用性。
Description
技术领域
本发明涉及一种面料的制备方法,尤其涉及一种单面大提花布的制备方法。
背景技术
棉的特点是吸湿力强---绵纤维是多孔性物质,内部分子排列很不规则,且分子中含有大量的亲水结构。保暖性----棉纤维是热的不良导体,棉纤维的内腔充满了不流动的空气,穿着舒适---不会产生静电,透气性良好,防敏感,容易清洗。
真丝具有良好的吸湿、透气性能,有护肤保健作用。手感柔软、滑爽、厚实、丰满,弹性优异。
发明内容
本发明的目的是提供一种52%棉48%真丝单面大提花布的制备方法,采用该方法制备的单面大提花布,同时具备棉和真丝的特性,具有吸湿力强、吸水性、护肤保健作用、透气性、保暖性、光泽润美、手感柔和耐用性。
为了实现上述的目的,本发明采用了以下的技术方案:
52%棉48%真丝单面大提花布的制备方法,该方法包括以下的步骤:
1)原料准备:135N/2丝24/棉52色纱,3股真丝色丝;
2)织造:在34寸30G单面提花机加装专用添梭三角,按48路排针,在电脑软件中编辑设计好花型,按电脑版图形及配色将色纱相应的接入进纱路数,其中3股真丝作添梭使用;
3)开幅;采用卧式开幅机,开幅辊线速度<60m/min;
4)清水定型烘干;
5)丝光工艺:干坯布开幅接头直接上机做轻碱丝光,丝光过程中先按100g/L加Fe3+螯合分散剂改善水质,NaOH浓度210-270g/L,0.2%丝光渗透剂,按25m/min常温丝光,碱液轧洗后在平洗时加90g/L冰醋酸进行酸碱中和,PH值≧7,并起固色作用;
6)二次定型:二次定型加40~65g/L蓬松柔软剂、冰凉整理剂50~65g/L、滑爽硅油120~160g/L,温度140~170℃,超喂25m/min;
7)橡毯预缩:橡毯温度应控制在55~70℃,车速在30~35m/min;
8)蒸呢及预缩工艺:对丝光及定型后织物进连续加压蒸呢机进行蒸呢,蒸汽压力6Pa以上,20m/min,蒸呢后面料由汽蒸预缩机及毛毯预缩机对面料的横向、纵向缩水率,织物花型、有效门幅作加工调整;
9)汽蒸预缩:机械速度,15-30m/min,饱和蒸汽3-3.5Bar,压缩空气5Bar,对面料的横向、纵向缩水率,织物花型、有效门幅作加工调整。
本发明的另外一个目的是提供采用上述的方法制备的单面大提花布。
本发明由于采用了上述的技术方案,制备的单面大提花布,同时具备棉和真丝的特性,具有吸湿力强、吸水性、护肤保健作用、透气性、保暖性、光泽润美、手感柔和耐用性。
具体实施方式
52%棉48%真丝单面大提花布的制备方法,该方法包括以下的步骤:
1) 原料准备:135N/2丝24/棉52色纱,3股真丝色丝;
2) 织造:在34寸30G单面提花机加装专用添梭三角,按48路排针,在电脑软件中编辑设计好花型,按电脑版图形及配色将色纱相应的接入进纱路数,其中3股真丝作添梭使用;
3) 开幅;采用卧式开幅机,开幅辊线速度<60m/min;
4) 清水定型烘干;
5) 丝光工艺:干坯布开幅接头直接上机做轻碱丝光,丝光过程中先按100g/L加Fe3+螯合分散剂改善水质,NaOH浓度250g/L,0.2%丝光渗透剂,按25m/min常温丝光,碱液轧洗后在平洗时加90g/L冰醋酸进行酸碱中和,PH值≧7,并起固色作用;
6) 二次定型:二次定型加55g/L蓬松柔软剂、冰凉整理剂60g/L、滑爽硅油140g/L,温度150℃,超喂25m/min;
7) 橡毯预缩:橡毯温度应控制在60℃,车速在33m/min;
8) 蒸呢及预缩工艺:对丝光及定型后织物进连续加压蒸呢机进行蒸呢,蒸汽压力6Pa以上,20m/min,蒸呢后面料由汽蒸预缩机及毛毯预缩机对面料的横向、纵向缩水率,织物花型、有效门幅作加工调整;
9) 汽蒸预缩:机械速度,25m/min,饱和蒸汽3.3Bar,压缩空气5Bar,对面料的横向、纵向缩水率,织物花型、有效门幅作加工调整。
上述的方法制备的单面大提花布经检测的项目如下表所示。检测标准GB/T 22849-2009、GB18401-20 03“ B” 类。
Claims (2)
1.52%棉48%真丝单面大提花布的制备方法,其特征在于该方法包括以下的步骤:
1)原料准备:135N/2丝24/棉52色纱,3股真丝色丝;
2)织造:在34寸30G单面提花机加装专用添梭三角,按48路排针,在电脑软件中编辑设计好花型,按电脑版图形及配色将色纱相应的接入进纱路数,其中3股真丝作添梭使用;
3)开幅:采用卧式开幅机,开幅辊线速度<60m/min;
4)清水定型烘干;
5)丝光工艺:干坯布开幅接头直接上机做轻碱丝光,丝光过程中先按100g/L加Fe3+螯合分散剂改善水质,NaOH浓度210-270g/L,0.2%丝光渗透剂,按25m/min常温丝光,碱液轧洗后在平洗时加90g/L冰醋酸进行酸碱中和,PH值≧7,并起固色作用;
6)二次定型:二次定型加40~65g/L蓬松柔软剂、冰凉整理剂50~65g/L、滑爽硅油120~160g/L,温度140~170℃,超喂25m/min;
7)橡毯预缩:橡毯温度应控制在55~70℃,车速在30~35m/min;
8)蒸呢及预缩工艺:对丝光及定型后织物进连续加压蒸呢机进行蒸呢,蒸汽压力6Pa以上,20m/min,蒸呢后面料由汽蒸预缩机及毛毯预缩机对面料的横向、纵向缩水率,织物花型、有效门幅作加工调整;
9)汽蒸预缩:机械速度,15-30m/min,饱和蒸汽3-3.5Bar,压缩空气5Bar,对面料的横向、纵向缩水率,织物花型、有效门幅作加工调整。
2.根据权利要求1所述的方法制备的单面大提花布。