CN104386945A - 一种提高混凝土流动性的防冻减水剂及其制备方法 - Google Patents

一种提高混凝土流动性的防冻减水剂及其制备方法 Download PDF

Info

Publication number
CN104386945A
CN104386945A CN201410598188.4A CN201410598188A CN104386945A CN 104386945 A CN104386945 A CN 104386945A CN 201410598188 A CN201410598188 A CN 201410598188A CN 104386945 A CN104386945 A CN 104386945A
Authority
CN
China
Prior art keywords
parts
water reducer
concrete
synergistic agent
freezing water
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410598188.4A
Other languages
English (en)
Inventor
李磊
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ANHUI FUNAN LVYUAN CHEMICAL Co Ltd
Original Assignee
ANHUI FUNAN LVYUAN CHEMICAL Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ANHUI FUNAN LVYUAN CHEMICAL Co Ltd filed Critical ANHUI FUNAN LVYUAN CHEMICAL Co Ltd
Priority to CN201410598188.4A priority Critical patent/CN104386945A/zh
Publication of CN104386945A publication Critical patent/CN104386945A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种提高混凝土流动性的防冻减水剂，其特征在于，由下列重量份的原料制备制成：丙烯酸3-4、炭黑4-6、聚氧化乙烯基烯丙醇醚19-24、过硫酸铵0.6-0.8、2-丙烯酰胺基-2-甲基丙磺酸3.5-5、碳纤维2-3、海泡石纤维2-3、聚丙烯纤维3-5、甲基丙烯酸二甲氨乙酯2-4、树胶2-4、氯化钙2-3、硫化蓖麻油1.5-2.5、水28-30、增效剂2-3；本发明添加碳纤维、聚丙烯纤维等成分，配合增效剂的添加，分散性能好，提高了混凝土的强度以及耐久性；添加氯化钙、硫化蓖麻油，具有防冻、润滑的效果；本发明制成的减水剂具有较高的减水效果，改善混凝土的和易性，提高了可塑性、抗折强度，耐久性。

Description

一种提高混凝土流动性的防冻减水剂及其制备方法
技术领域
本发明涉及一种减水剂的制取方法，特别是一种提高混凝土流动性的防冻减水剂及其制备方法。
背景技术
水泥加水拌合后，由于水泥颗粒分子引力的作用，使水泥浆形成絮凝结构，使10%～30%的拌合水被包裹在水泥颗粒之中，不能参与自由流动和润滑作用，从而影响了混凝土拌合物的流动性，当加入减水剂后，由于减水剂分子能定向吸附于水泥颗粒表面，使水泥颗粒表面带有同一种电荷（通常为负电荷），形成静电排斥作用，促使水泥颗粒相互分散，絮凝结构破坏，释放出被包裹部分水，参与流动，从而有效地增加混凝土拌合物的流动性；同时减水剂空间位阻作用使得混凝土的坍落度保持良好，并控制坍落度损失。由于减水剂的应用，它的减水作用可以大大降低混凝土的水灰比，从而提高混凝土的强度。这样，就可以配制出更高强度等级的混凝土，在同等级的情况下，可以减少水泥用量，从而降低成本，提高经济效益。 
本发明添加碳纤维、聚丙烯纤维等多种纤维，添加到混凝土中具有良好的分散性，添加氯化钙、硫化蓖麻油等具有润滑防冻的效果，配合增效剂，进一步提高了分散效果，制成一种能够提高混凝土流动性的防冻减水剂。
发明内容
本发明的目的是提供一种提高混凝土流动性的防冻减水剂及其制备方法。
为了实现本发明的目的，本发明通过以下方案实施：
一种提高混凝土流动性的防冻减水剂，由下列重量份的原料制备制成：丙烯酸3-4、炭黑4-6、聚氧化乙烯基烯丙醇醚19-24、过硫酸铵0.6-0.8、2-丙烯酰胺基-2-甲基丙磺酸3.5-5、碳纤维2-3、海泡石纤维2-3、聚丙烯纤维3-5、甲基丙烯酸二甲氨乙酯2-4、树胶2-4、氯化钙2-3、硫化蓖麻油1.5-2.5、水28-30、增效剂2-3；
所述的增效剂由以下重量份的原料制备而成：松香甘油酯3-4、石英砂6-9、纳米石墨粉3-5、乙二醇丁醚1-1.5、微晶石蜡1.5-2.5、焦磷酸钠1-2、EVA乳胶12-15、水性环氧树脂8-11；制备方法是首先将松香甘油酯、微晶石蜡加热至软化，与石英砂、纳米石墨粉混合，保温研磨15-30分钟，然后控制温度在40℃-50℃，转速120-180转/分的条件下加入EVA乳胶、水性环氧树脂，继续搅拌20-30分钟后，最后加入其余剩余成分，提高转速到1000-1200转/分，搅拌40分钟，冷却至室温，即得所述增效剂。
本发明所述一种提高混凝土流动性的防冻减水剂，由以下具体步骤制成：
（1）将碳纤维、海泡石纤维、聚丙烯纤维粉碎与炭黑混合均匀，然后加入适量水搅拌研磨2-3小时；
（2）将丙烯酸、甲基丙烯酸二甲氨乙酯、聚氧化乙烯基烯丙醇醚、余量水、过硫酸铵混合，加热至50℃-70℃，反应20-30分钟，然后加入除增效剂之外的其余剩余成分，升温至80℃-85℃条件下恒温反应2-3小时；
（3）将步骤（1）产物与步骤（2）产物混合，加入增效剂，以600-800转/分的速度搅拌30-40分钟即得。
本发明的有益效果是：本发明添加碳纤维、聚丙烯纤维等成分，配合增效剂的添加，分散性能好，提高了混凝土的强度以及耐久性；添加氯化钙、硫化蓖麻油，具有防冻、润滑的效果；本发明制成的减水剂具有较高的减水效果，改善混凝土的和易性，提高了可塑性、抗折强度，耐久性。
具体实施方案
下面通过具体实例对本发明进行详细说明。
一种提高混凝土流动性的防冻减水剂，由下列重量份（公斤）的原料制备制成：丙烯酸3、炭黑4、聚氧化乙烯基烯丙醇醚19、过硫酸铵0.6、2-丙烯酰胺基-2-甲基丙磺酸3.5、碳纤维2、海泡石纤维2、聚丙烯纤维3、甲基丙烯酸二甲氨乙酯2、树胶2、氯化钙2、硫化蓖麻油1.5、水28、增效剂2；
所述的增效剂由以下重量份（公斤）的原料制备而成：松香甘油酯3、石英砂6、纳米石墨粉3、乙二醇丁醚1、微晶石蜡1.5、焦磷酸钠1、EVA乳胶12、水性环氧树脂8；制备方法是首先将松香甘油酯、微晶石蜡加热至软化，与石英砂、纳米石墨粉混合，保温研磨15-30分钟，然后控制温度在40℃-50℃，转速120-180转/分的条件下加入EVA乳胶、水性环氧树脂，继续搅拌20-30分钟后，最后加入其余剩余成分，提高转速到1000-1200转/分，搅拌40分钟，冷却至室温，即得所述增效剂。
本发明所述一种提高混凝土流动性的防冻减水剂，由以下具体步骤制成：
（1）将碳纤维、海泡石纤维、聚丙烯纤维粉碎与炭黑混合均匀，然后加入适量水搅拌研磨2-3小时；
（2）将丙烯酸、甲基丙烯酸二甲氨乙酯、聚氧化乙烯基烯丙醇醚、余量水、过硫酸铵混合，加热至50℃-70℃，反应20-30分钟，然后加入除增效剂之外的其余剩余成分，升温至80℃-85℃条件下恒温反应2-3小时；
（3）将步骤（1）产物与步骤（2）产物混合，加入增效剂，以600-800转/分的速度搅拌30-40分钟即得。
本发明制得的减水剂产品性能优异，减水率可达27.5%，本发明掺量为水泥用量的 1%-2%，在相同水灰比情况下，可使坍落度提高 15cm 以上，流动性大幅度增加。

Claims (2)

1.一种提高混凝土流动性的防冻减水剂，其特征在于，由下列重量份的原料制备制成：丙烯酸3-4、炭黑4-6、聚氧化乙烯基烯丙醇醚19-24、过硫酸铵0.6-0.8、2-丙烯酰胺基-2-甲基丙磺酸3.5-5、碳纤维2-3、海泡石纤维2-3、聚丙烯纤维3-5、甲基丙烯酸二甲氨乙酯2-4、树胶2-4、氯化钙2-3、硫化蓖麻油1.5-2.5、水28-30、增效剂2-3；
所述的增效剂由以下重量份的原料制备而成：松香甘油酯3-4、石英砂6-9、纳米石墨粉3-5、乙二醇丁醚1-1.5、微晶石蜡1.5-2.5、焦磷酸钠1-2、EVA乳胶12-15、水性环氧树脂8-11；制备方法是首先将松香甘油酯、微晶石蜡加热至软化，与石英砂、纳米石墨粉混合，保温研磨15-30分钟，然后控制温度在40℃-50℃，转速120-180转/分的条件下加入EVA乳胶、水性环氧树脂，继续搅拌20-30分钟后，最后加入其余剩余成分，提高转速到1000-1200转/分，搅拌40分钟，冷却至室温，即得所述增效剂。
2.根据权利要求1所述一种提高混凝土流动性的防冻减水剂，其特征在于，由以下具体步骤制成：
（1）将碳纤维、海泡石纤维、聚丙烯纤维粉碎与炭黑混合均匀，然后加入适量水搅拌研磨2-3小时；
（2）将丙烯酸、甲基丙烯酸二甲氨乙酯、聚氧化乙烯基烯丙醇醚、余量水、过硫酸铵混合，加热至50℃-70℃，反应20-30分钟，然后加入除增效剂之外的其余剩余成分，升温至80℃-85℃条件下恒温反应2-3小时；
（3）将步骤（1）产物与步骤（2）产物混合，加入增效剂，以600-800转/分的速度搅拌30-40分钟即得。
CN201410598188.4A 2014-10-31 2014-10-31 一种提高混凝土流动性的防冻减水剂及其制备方法 Pending CN104386945A (zh)