CN104310902A - 一种环保保温砂浆 - Google Patents
一种环保保温砂浆 Download PDFInfo
- Publication number
- CN104310902A CN104310902A CN201410513974.XA CN201410513974A CN104310902A CN 104310902 A CN104310902 A CN 104310902A CN 201410513974 A CN201410513974 A CN 201410513974A CN 104310902 A CN104310902 A CN 104310902A
- Authority
- CN
- China
- Prior art keywords
- parts
- thermal insulation
- insulation mortar
- environment
- resistance
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种环保保温砂浆,包括以下重量份的组份:硅酸盐水泥40-65份、保温骨料10-20份、增强纤维5-10份、可再分散乳胶粉5-10份、填料10-20份、轻烧氧化镁1-5份、硅藻土5-10份。本发明保温砂浆抗裂性能优异,可克服保温砂浆开裂、起壳等通病,且粘结强度高,附着力强,具有良好的保温隔热性、耐候性、防火防水性、抗冻性等性能;保温砂浆的体积稳定性好,凝结硬化时产生体积微膨胀,不开裂、不空鼓,耐水性强,抗老化,使用寿命长;并且本发明的保温砂浆无毒、无味、无放射性,对人体无害,不污染环境,具有节能环保、吸收电磁辐射的优点。
Description
技术领域
本发明涉及一种保温砂浆,具体涉及一种环保保温砂浆,属于建筑领域。
背景技术
节能环保是我国的基本国策之一,因此国家正在推进对建筑物的环保节能要求,为了达到相关的节能标准,建筑物一般都要进行保温层的施工。传统的保温材料为膨胀聚苯板、挤塑聚苯板和发泡聚氨酯等,虽然其导热系数较小,保温性能优异,但是其作为有机保温材料,防火性能较差,近年来,我国发生了多起因引燃有机保温材料引起的严重火灾,因此,很多地区开始大力推广无机保温砂浆。
电磁污染是一种新型的环境污染源,随着社会的发展进步,电子设备的大量应用,电磁环境日益复杂 ;另一方面,随着人民生活水平的不断提高和环保意识的增强,人们开始越来越多的关注电磁波对环境的影响。
而为了应对日益严重的电磁波污染,提出了相应的解决方案,在保温砂浆中掺入一定量的吸收剂,对电磁波进行吸收处理,减弱电磁波的不利影响。但是,现有技术所针对的频段都在 18GHz 以下,而对更高频率的电磁波并没有提及其吸收效果。另外,选用的吸收剂多为碳基材料,比如导电石墨、炭黑等,这些材料作为吸收剂,强度低、导热系数高,若加入量过高,则会降低保温砂浆的强度,减弱保温砂浆的保温效果,同时,保温砂浆是一种轻质材料,对干密度有较为严格的限制,一般的要求都要在400kg/m3以下,吸收剂加入量过高,必然会提高保温砂浆的干密度。
发明内容
本发明所要解决的技术问题是针对现有技术的不足,提供一种抗开裂性能优异的保温保温砂浆,可克服保温砂浆开裂、起壳等通病,在提高保温性能的同时兼具吸收电磁波的功能。
为了达到上述目的,本发明采用的技术方案是:
一种环保保温砂浆,包括以下重量份的组份:硅酸盐水泥40-65份、保温骨料10-20份、增强纤维5-10份、可再分散乳胶粉5-10份、填料10-20份、轻烧氧化镁1-5份、硅藻土5-10份。
进一步的,所述的保温骨料为玻化微珠、膨胀珍珠岩和碳气凝胶的混合物。
进一步的,所述的保温骨料中玻化微珠、膨胀珍珠岩和碳气凝胶的的重量比为1-3:1-5:1。
进一步的,所述的增强纤维为聚丙烯纤维、纤维素醚、羟乙基纤维素醚、羟丙基甲基纤维素的混合物。
进一步的,所述的增强纤维中聚丙烯纤维、纤维素醚、羟乙基纤维素醚、羟丙基甲基纤维素的重量比为1:1:1:1。
进一步的,所述的填料为水镁石粉、云母粉、高岭土、白云石粉以任意比例混合的混合物。
本发明保温砂浆,使用时,按照常规保温砂浆配置方法现场配置使用。
本发明保温砂浆抗裂性能优异,可克服保温砂浆开裂、起壳等通病,且粘结强度高,附着力强,具有良好的保温隔热性、耐候性、防火防水性、抗冻性等性能;保温砂浆的体积稳定性好,凝结硬化时产生体积微膨胀,不开裂、不空鼓,耐水性强,抗老化,使用寿命长;并且本发明的保温砂浆无毒、无味、无放射性,对人体无害,不污染环境,具有节能环保、吸收电磁辐射的优点。
具体实施方式
实施例1:
一种环保保温砂浆,包括以下重量份的组份:硅酸盐水泥40份、玻化微珠4份、膨胀珍珠岩4份、碳气凝胶2份、聚丙烯纤维1.5份、纤维素醚1.5份、羟乙基纤维素醚1.5份、羟丙基甲基纤维素1.5份、可再分散乳胶粉5份、轻烧氧化镁1份、硅藻土5份、水镁石粉3份、云母粉3份、高岭土2份、白云石粉2份。
实施例2:
一种环保保温砂浆,包括以下重量份的组份:硅酸盐水泥65份、玻化微珠8份、膨胀珍珠岩8份、碳气凝胶4份、聚丙烯纤维2.5份、纤维素醚2.5份、羟乙基纤维素醚2.5份、羟丙基甲基纤维素2.5份、可再分散乳胶粉10份、轻烧氧化镁5份、硅藻土10份、水镁石粉10份、云母粉5份、高岭土3份、白云石粉2份。
实施例3:
一种环保保温砂浆,包括以下重量份的组份:硅酸盐水泥50份、玻化微珠4份、膨胀珍珠岩8份、碳气凝胶2份、聚丙烯纤维2份、纤维素醚2份、羟乙基纤维素醚2份、羟丙基甲基纤维素2份、可再分散乳胶粉7份、轻烧氧化镁3份、硅藻土7份、水镁石粉5份、云母粉3份、高岭土2份、白云石粉2份。
实施例4:
一种环保保温砂浆,包括以下重量份的组份:硅酸盐水泥55份、玻化微珠4份、膨胀珍珠岩8份、碳气凝胶2份、聚丙烯纤维2份、纤维素醚2份、羟乙基纤维素醚2份、羟丙基甲基纤维素2份、可再分散乳胶粉8份、轻烧氧化镁2份、硅藻土8份、水镁石粉2份、云母粉5份、高岭土5份、白云石粉4份。
实施例5:
一种环保保温砂浆,包括以下重量份的组份:硅酸盐水泥60份、玻化微珠4份、膨胀珍珠岩8份、碳气凝胶2份、聚丙烯纤维2份、纤维素醚2份、羟乙基纤维素醚2份、羟丙基甲基纤维素2份、可再分散乳胶粉5份、轻烧氧化镁4份、硅藻土7份、水镁石粉2份、云母粉5份、高岭土5份、白云石粉4份。
验证试验:对本发明实施例1-5所得的保温砂浆进行性能验证,结果如表1所示:
表1:实施例1-5所得保温砂浆性能指标
同时对本发明的保温砂浆进行放电磁辐射性能检测,将本发明的保温砂浆与市售保温砂浆进行对比,涂抹于水泥板上干燥凝固后用200mT的辐射灯照射水泥板,检测另一侧的电磁辐射,检验结果如表2所示
上述实例只是为说明本发明的技术构思以及技术特点,并不能以此限制本发明的保护范围。凡根据本发明的实质所做的等效变换或修饰,都应该涵盖在本发明的保护范围之内。
Claims (6)
1.一种环保保温砂浆,包括以下重量份的组份:硅酸盐水泥40-65份、保温骨料10-20份、增强纤维5-10份、可再分散乳胶粉5-10份、填料10-20份、轻烧氧化镁1-5份、硅藻土5-10份。
2.根据权利要求1所述的保温砂浆,其特征在于,所述的保温骨料为玻化微珠、膨胀珍珠岩和碳气凝胶的混合物。
3.根据权利要求1所述的保温砂浆,其特征在于,所述的保温骨料中玻化微珠、膨胀珍珠岩和碳气凝胶的的重量比为1-3:1-5:1。
4.根据权利要求1所述的保温砂浆,其特征在于,所述的增强纤维为聚丙烯纤维、纤维素醚、羟乙基纤维素醚、羟丙基甲基纤维素的混合物。
5.根据权利要求1所述的保温砂浆,其特征在于,所述的增强纤维中聚丙烯纤维、纤维素醚、羟乙基纤维素醚、羟丙基甲基纤维素的重量比为1:1:1:1。
6.根据权利要求1所述的保温砂浆,其特征在于,所述的填料为水镁石粉、云母粉、高岭土、白云石粉以任意比例混合的混合物。