CN104291738A - Weather-resistant fireproof waterproof really stone paint and preparation method thereof - Google Patents
Weather-resistant fireproof waterproof really stone paint and preparation method thereof Download PDFInfo
- Publication number
- CN104291738A CN104291738A CN201410499982.3A CN201410499982A CN104291738A CN 104291738 A CN104291738 A CN 104291738A CN 201410499982 A CN201410499982 A CN 201410499982A CN 104291738 A CN104291738 A CN 104291738A
- Authority
- CN
- China
- Prior art keywords
- powder
- proof
- water
- calcite
- titanium dioxide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a coating and in particular relates to weather-resistant fireproof waterproof really stone paint. The weather-resistant fireproof waterproof really stone paint is prepared from silicone acrylic emulsion, hydroxypropyl methyl cellulose, amino acetic acid, polyvinyl formal, propylene glycol, hydroquinone, aids, quartz sand, iron oxide powder, titanium dioxide, calcite in powder, montmorillonite powder, anhydrous aluminum chloride, ferric trichloride, aluminum sulfate and tricresyl phosphate. According to the weather-resistant fireproof waterproof really stone paint provided by the invention, polyvinyl formal and other substances are subjected to a condensation reaction, the particles and powder substances such as the quartz sand, iron oxide powder, titanium dioxide, calcite in powder and montmorillonite powder are modified, the formed really stone paint is bright in color, vivid in texture and good in simulated effect. Meanwhile, due to the addition of an aluminum salt, a waterproof effect can be achieved, and tricresyl phosphate has a fireproof effect.
Description
Technical field
The present invention relates to a kind of coating, be specially the true mineral varnish of weathering resistance fire-proof and water-proof and preparation method.
Background technology
True mineral varnish is that a kind of decorative effect exactly likes marble, granitic exterior coating, and the main natural stone-powder of shades of colour that adopts is formulated.
Current true mineral varnish function ratio is more single, mainly play the effect of decoration, but its texture is more inferior again than water-water multicolor finish, simultaneously and modern architecture proposes with high requirement in the effect such as waterproof, fire prevention, the true mineral varnish that traditional function is single is difficult to meet this requirement.
Summary of the invention
For above-mentioned technical problem, the invention provides a kind of true mineral varnish of weathering resistance fire-proof and water-proof with fire-proof and water-proof function, and texture is more true to nature.Concrete technical scheme is:
The true mineral varnish of weathering resistance fire-proof and water-proof, is made up of according to parts by weight following raw materials according:
Organosilicon crylic acid latex 15 ~ 20 parts, Vltra tears 0.5 ~ 0.8, Padil 0.5 ~ 1.5, polyvinyl formal 0.05 ~ 0.10, propylene glycol 4.5 ~ 5.5, Resorcinol 0.05 ~ 0.08, mould inhibitor 0.3 ~ 1.5, polyurethane thickener 0.3 ~ 0.5, film coalescence aid 0.5 ~ 0.8, organic silicon surfactant 1 ~ 3, defoamer 0.05 ~ 0.1, solidifying agent 1 ~ 2, 40 ~ 100 order quartz sands 75 ~ 85, deionized water 3 ~ 5, brown iron oxide 0.5 ~ 1, titanium dioxide 1 ~ 2, calcite in powder 6 ~ 8, polynite powder 1 ~ 2, Aluminum chloride anhydrous 4 ~ 6, iron trichloride 2 ~ 4, Tai-Ace S 150 8 ~ 12, Tritolyl Phosphate 6 ~ 9,
The preparation method of described true mineral varnish, comprises the steps:
(1) Vltra tears and deionized water mix and blend form dispersant solution;
(2) quartz sand, brown iron oxide, titanium dioxide, calcite in powder, polynite powder mix formation compound;
(3) dispersant solution, compound are joined in Padil, polyvinyl formal, propylene glycol, Resorcinol, be heated to 50 degrees Celsius of insulations 1 hour;
(4) other raw materials of step (3) gained material are mixed together to stir and both obtain the true mineral varnish of weathering resistance fire-proof and water-proof.
Preferred version is: be made up of according to parts by weight following raw materials according, organosilicon crylic acid latex 18 ~ 20 parts, Vltra tears 0.6 ~ 0.7, Padil 0.8 ~ 1.0, polyvinyl formal 0.06 ~ 0.08, propylene glycol 4.8 ~ 5.0, Resorcinol 0.05 ~ 0.07, mould inhibitor 1.0 ~ 1.2, polyurethane thickener 0.3 ~ 0.4, film coalescence aid 0.6 ~ 0.8, organic silicon surfactant 2 ~ 3, defoamer 0.08 ~ 0.1, solidifying agent 1.7 ~ 2, 40 ~ 100 order quartz sands 80 ~ 85, deionized water 3 ~ 4, brown iron oxide 0.8 ~ 1, titanium dioxide 1 ~ 1.8, calcite in powder 7 ~ 8, polynite powder 1.7 ~ 2, Aluminum chloride anhydrous 5 ~ 6, iron trichloride 3 ~ 4, Tai-Ace S 150 10 ~ 12, Tritolyl Phosphate 7 ~ 9.
The true mineral varnish of weathering resistance fire-proof and water-proof provided of the present invention, the material generation condensation reactions such as polyvinyl formal, to quartz sand, brown iron oxide, titanium dioxide, calcite in powder, these particulate matter of polynite powder and powder mass carry out modification, true mineral varnish beautiful in colour formed, texture is more true to nature, and simulated effect is better, simultaneously the adding and can play waterproof effect of aluminium salt, Tritolyl Phosphate plays fp effect.
Embodiment
The specific embodiment of the present invention is described in conjunction with the embodiments.
embodiment 1
The true mineral varnish of weathering resistance fire-proof and water-proof, be made up of according to parts by weight following raw materials according, organosilicon crylic acid latex 15 parts, Vltra tears 0.8, Padil 1.5, polyvinyl formal 0.10, propylene glycol 5.5, Resorcinol 0.06, mould inhibitor 1.5, polyurethane thickener 0.4, film coalescence aid 0.5, organic silicon surfactant 2, defoamer 0.08, solidifying agent 1,40 ~ 100 order quartz sand 80, deionized water 4, brown iron oxide 0.5, titanium dioxide 2, calcite in powder 6, polynite powder 2, Aluminum chloride anhydrous 5, iron trichloride 4, Tai-Ace S 150 12, Tritolyl Phosphate 6;
The preparation method of described true mineral varnish, comprises the steps:
(1) Vltra tears and deionized water mix and blend form dispersant solution;
(2) quartz sand, brown iron oxide, titanium dioxide, calcite in powder, polynite powder mix formation compound;
(3) dispersant solution, compound are joined in Padil, polyvinyl formal, propylene glycol, Resorcinol, be heated to 50 degrees Celsius of insulations 1 hour;
(4) other raw materials of step (3) gained material are mixed together to stir and both obtain the true mineral varnish of weathering resistance fire-proof and water-proof.
embodiment 2
The true mineral varnish of weathering resistance fire-proof and water-proof, be made up of according to parts by weight following raw materials according, organosilicon crylic acid latex 18 parts, Vltra tears 0.7, Padil 1.0, polyvinyl formal 0.06, propylene glycol 5.0, Resorcinol 0.07, mould inhibitor 1.2, polyurethane thickener 0.3, film coalescence aid 0.8, organic silicon surfactant 3, defoamer 0.08, solidifying agent 2, 40 ~ 100 order quartz sands 85, deionized water 3, brown iron oxide 0.8, titanium dioxide 1.8, calcite in powder 8, polynite powder 1.7, Aluminum chloride anhydrous 6, iron trichloride 4, Tai-Ace S 150 10, Tritolyl Phosphate 9.
The preparation method of described true mineral varnish, comprises the steps:
(1) Vltra tears and deionized water mix and blend form dispersant solution;
(2) quartz sand, brown iron oxide, titanium dioxide, calcite in powder, polynite powder mix formation compound;
(3) dispersant solution, compound are joined in Padil, polyvinyl formal, propylene glycol, Resorcinol, be heated to 50 degrees Celsius of insulations 1 hour;
(4) other raw materials of step (3) gained material are mixed together to stir and both obtain the true mineral varnish of weathering resistance fire-proof and water-proof.
embodiment 3
The true mineral varnish of weathering resistance fire-proof and water-proof, be made up of according to parts by weight following raw materials according, organosilicon crylic acid latex 20 parts, Vltra tears 0.6, Padil 0.8, polyvinyl formal 0.08, propylene glycol 4.8, Resorcinol 0.05, mould inhibitor 1.0, polyurethane thickener 0.4, film coalescence aid 0.6, organic silicon surfactant 2, defoamer 0.1, solidifying agent 1.7,40 ~ 100 order quartz sand 80, deionized water 4, brown iron oxide 1, titanium dioxide 1, calcite in powder 7, polynite powder 2, Aluminum chloride anhydrous 5, iron trichloride 3, Tai-Ace S 150 12, Tritolyl Phosphate 7.
The preparation method of described true mineral varnish, comprises the steps:
(1) Vltra tears and deionized water mix and blend form dispersant solution;
(2) quartz sand, brown iron oxide, titanium dioxide, calcite in powder, polynite powder mix formation compound;
(3) dispersant solution, compound are joined in Padil, polyvinyl formal, propylene glycol, Resorcinol, be heated to 50 degrees Celsius of insulations 1 hour;
(4) other raw materials of step (3) gained material are mixed together to stir and both obtain the true mineral varnish of weathering resistance fire-proof and water-proof.
Claims (2)
1. the true mineral varnish of weathering resistance fire-proof and water-proof, it is characterized in that: be made up of according to parts by weight following raw materials according, organosilicon crylic acid latex 15 ~ 20 parts, Vltra tears 0.5 ~ 0.8, Padil 0.5 ~ 1.5, polyvinyl formal 0.05 ~ 0.10, propylene glycol 4.5 ~ 5.5, Resorcinol 0.05 ~ 0.08, mould inhibitor 0.3 ~ 1.5, polyurethane thickener 0.3 ~ 0.5, film coalescence aid 0.5 ~ 0.8, organic silicon surfactant 1 ~ 3, defoamer 0.05 ~ 0.1, solidifying agent 1 ~ 2, 40 ~ 100 order quartz sands 75 ~ 85, deionized water 3 ~ 5, brown iron oxide 0.5 ~ 1, titanium dioxide 1 ~ 2, calcite in powder 6 ~ 8, polynite powder 1 ~ 2, Aluminum chloride anhydrous 4 ~ 6, iron trichloride 2 ~ 4, Tai-Ace S 150 8 ~ 12, Tritolyl Phosphate 6 ~ 9,
The preparation method of the true mineral varnish of described weathering resistance fire-proof and water-proof, comprises the steps:
(1) Vltra tears and deionized water mix and blend form dispersant solution;
(2) quartz sand, brown iron oxide, titanium dioxide, calcite in powder, polynite powder mix formation compound;
(3) dispersant solution, compound are joined in Padil, polyvinyl formal, propylene glycol, Resorcinol, be heated to 50 degrees Celsius of insulations 1 hour;
(4) other raw materials of step (3) gained material are mixed together to stir and both obtain the true mineral varnish of weathering resistance fire-proof and water-proof.
2. the true mineral varnish of weathering resistance fire-proof and water-proof according to claim 1, it is characterized in that: be made up of according to parts by weight following raw materials according, organosilicon crylic acid latex 18 ~ 20 parts, Vltra tears 0.6 ~ 0.7, Padil 0.8 ~ 1.0, polyvinyl formal 0.06 ~ 0.08, propylene glycol 4.8 ~ 5.0, Resorcinol 0.05 ~ 0.07, mould inhibitor 1.0 ~ 1.2, polyurethane thickener 0.3 ~ 0.4, film coalescence aid 0.6 ~ 0.8, organic silicon surfactant 2 ~ 3, defoamer 0.08 ~ 0.1, solidifying agent 1.7 ~ 2, 40 ~ 100 order quartz sands 80 ~ 85, deionized water 3 ~ 4, brown iron oxide 0.8 ~ 1, titanium dioxide 1 ~ 1.8, calcite in powder 7 ~ 8, polynite powder 1.7 ~ 2, Aluminum chloride anhydrous 5 ~ 6, iron trichloride 3 ~ 4, Tai-Ace S 150 10 ~ 12, Tritolyl Phosphate 7 ~ 9.