CN102277059A - Novel stone paint - Google Patents
Novel stone paint Download PDFInfo
- Publication number
- CN102277059A CN102277059A CN2011102114075A CN201110211407A CN102277059A CN 102277059 A CN102277059 A CN 102277059A CN 2011102114075 A CN2011102114075 A CN 2011102114075A CN 201110211407 A CN201110211407 A CN 201110211407A CN 102277059 A CN102277059 A CN 102277059A
- Authority
- CN
- China
- Prior art keywords
- stone
- parts
- propylene glycol
- weight parts
- weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to the field of paint, and in particular relates to novel stone paint. The novel stone paint comprises 80-120 parts of water, 3-10 parts of film-forming auxiliary, 1-3 parts of cellulose, 1-3 parts of corrosion inhibitor, 1-5 parts of mildewproof agent, 10-15 parts of propylene glycol, 100-200 parts of silicone-acrylic emulsion and 650-800 parts of stone powder by weight. A preparation process of the stone paint comprises the following steps: firstly weighing all the materials according to weight, then separately grinding the stone wastes in different colors into powder with fineness being 60-100 meshes, firstly adding water to a mixing bucket, then adding the film-forming auxiliary, the cellulose, the corrosion inhibitor, the mildewproof agent, propylene glycol, the silicone-acrylic emulsion and the stone powder while stirring and finally stirring the materials uniformly, thus obtaining the finished product. The stone paint prepared by the process solves the problem of environmental pollution of the stone wastes, has real simulation effect, has the same textures and look as the natural stone, is water-based, environment-friendly, non-toxic and non-combustible, saves energy, is simple and convenient to construct; and the color change of the stone paint is easy.
Description
Technical field
The present invention relates to the paint field, be specifically related to a kind of novel true mineral varnish.
Background technology
Lacquer on the market mostly exists the texture impression relatively poor at present, and mainly be to make with industrial chemicals, every kind of industrial chemicals all forms through deep processing, all can produce pollution, problems such as prestige evil environment, not only there are potential safety hazard in power consumption and cost height, and the cost height, imitative stone weak effect, inflammable poisonous, and construction inconvenience, the colour changing difficulty.
Summary of the invention
The purpose of this invention is to provide a kind of novel true mineral varnish, imitative stone is effective and cost is low.
A kind of novel true mineral varnish contains: water 80～120 weight parts, film coalescence aid 3～10 weight parts, Mierocrystalline cellulose 1～3 weight part, sanitas 1～3 weight part, mould inhibitor 1～5 weight part, propylene glycol 10～15 weight parts, organosilicon crylic acid latex 100～200 weight parts, stone flour 650～800 weight parts.
Described film coalescence aid claims coalescing aid again, is a kind of evanescent softening agent; The macromolecular polysaccharide that described Mierocrystalline cellulose is made up of glucose, water insoluble and common organic solvents is the main component of plant cell wall; Described sanitas is meant natural or the synthetic chemical ingredients; Described mould inhibitor main component: quaternary ammonium salt derivative, card pine, tensio-active agent, synergistic agent etc.Can prevent that microorganism from causing mouldy medicament; Described propylene glycol is the important source material of unsaturated polyester, Resins, epoxy, urethane resin; Described organosilicon crylic acid latex is selected import special addition agent and features monomer for use, and introduces extraordinary organosilicon, adopts seed emulsion, coats polymerization technique by nucleocapsid and synthesizes; Described stone flour is to be commonly referred to as stone dust the lime carbonate limestone powder is arranged, and also has silica powder etc.
Its preparation technology is: take by weighing each material at first by weight, just the stone material waste material of different colours separates grinding and processing again, grinding to form fineness is 45-100 purpose powder, earlier water is added in the mixer, then add film coalescence aid, Mierocrystalline cellulose, sanitas, mould inhibitor, propylene glycol, organosilicon crylic acid latex, stone flour while stirring, stir at last, be finished product.
Adopt the true mineral varnish of above prepared, solved the problem of environmental pollution of stone material waste material; Simulated effect is true to nature, and texture impression and lithotome are as good as; Aqueous, environmental protective is nontoxic not to fire energy-conserving and environment-protective; Easy construction, colour changing is easy.
Embodiment
Implement 1
Its preparation technology is: take by weighing each material at first by weight: water 80～120 weight parts, film coalescence aid 3～10 weight parts, Mierocrystalline cellulose 1～3 weight part, sanitas 1～3 weight part, mould inhibitor 1～5 weight part, propylene glycol 10～15 weight parts, organosilicon crylic acid latex 100～200 weight parts, stone flour 650～800 weight parts.Just the stone material waste material of different colours separates grinding and processing again, grinding to form fineness is 45-100 purpose powder, earlier water is added in the mixer, then adds film coalescence aid, Mierocrystalline cellulose, sanitas, mould inhibitor, propylene glycol, organosilicon crylic acid latex, stone flour while stirring, stir at last, be finished product.
Implement 2
Its preparation technology is: take by weighing each material at first by weight: water 90 weight parts, film coalescence aid 10 weight parts, Mierocrystalline cellulose 2 weight parts, sanitas 3 weight parts, mould inhibitor 5 weight parts, propylene glycol 10 weight parts, organosilicon crylic acid latex 130 weight parts, stone flour 750 weight parts.Stone material waste material with different colours separates grinding and processing again, grinding to form fineness is 100 purpose powder, earlier water is added in the mixer, then adds film coalescence aid, Mierocrystalline cellulose, sanitas, mould inhibitor, propylene glycol, organosilicon crylic acid latex, stone flour while stirring, stir at last, be finished product.
Implement 3
Its preparation technology is: take by weighing each material at first by weight: 90 kilograms in water, 10 kilograms of film coalescence aid, 2 kilograms of Mierocrystalline celluloses, 3 kilograms of sanitass, 5 kilograms of mould inhibitors, 10 kilograms of propylene glycol, 130 kilograms of organosilicon crylic acid latexs, 750 kilograms of stone flours.Stone material waste material with different colours separates grinding and processing again, grinding to form fineness is 60 purpose powder, earlier water is added in the mixer, then adds film coalescence aid, Mierocrystalline cellulose, sanitas, mould inhibitor, propylene glycol, organosilicon crylic acid latex, stone flour while stirring, stir at last, be finished product.Described film coalescence aid claims coalescing aid again.Can promote macromolecular compound plastic flow and recoverable deformation, improve coalescent performance, can be at film forming material in the construction temperature scope extensively.It is a kind of evanescent softening agent.Commonly used is the strong solvent of ether alcohol class superpolymer, as propylene glycol butyl ether, 1-Methoxy-2-propyl acetate etc.The macromolecular polysaccharide that described Mierocrystalline cellulose (cellulose) is made up of glucose.Water insoluble and common organic solvents.It is the main component of plant cell wall.Mierocrystalline cellulose is a kind of polysaccharide that the occurring in nature distribution is the widest, content is maximum, accounts for more than 50% of vegitabilia's carbon content.The content of cellulose of cotton is near 100%, is natural pure cellulose source.In the general timber, cellulose comprises 40～50%, 10～30% hemicellulose and 20～30% xylogen in addition.Described sanitas is meant natural or the synthetic chemical ingredients, is used to add food, medicine, pigment, biological sample etc., to postpone the corruption that microorganism growth or chemical transformation cause.Nitrite and sulfurous gas are one of sanitass of using always.Described mould inhibitor main component: quaternary ammonium salt derivative, card pine, tensio-active agent, synergistic agent etc.Can prevent that microorganism from causing mouldy medicament.Phenols (as phenol), chlorophenols (as Pentachlorophenol), organic mercury salt (as phenyl mercury oleate), organic copper salt (as copper 8-quinolinolate), organic tin salt (as chlorination three second or tributyl tin etc.) are arranged, reach inorganic salt copper sulfate, mercury chloride, Sodium Fluoride etc.Be used for plastics, rubber, textiles, paint and insulating material etc.Described propylene glycol is the important source material of unsaturated polyester, Resins, epoxy, urethane resin, and the consumption of this respect accounts for about 45% of propylene glycol aggregate consumption, and this unsaturated polyester is used for topcoating and reinforced plastics in a large number.The viscosity of propylene glycol and good hygroscopicity, and nontoxic, thereby in food, medicine and cosmetic industry, be widely used as moisture adsorbent, antifreezing agent, lubricant and solvent.Propylene glycol is the fine solvent of seasonings and pigment.Described organosilicon crylic acid latex is selected import special addition agent and features monomer for use, and introduces extraordinary organosilicon, adopts seed emulsion, coats synthetic, water-fast, acidproof, alkaline-resisting, the anti-contamination of polymerization technique by nucleocapsid; Pure third silicon is formed, the not yellowing of filming, and UV resistant, anti-aging; The glued membrane densification, tough and tensile, hardness is high, anti-water-white voltinism is fabulous; The gloss height, true mineral varnish color developing is good.Described stone flour is to be commonly referred to as stone dust, and the kind of stone is a lot, divide according to mineralogical composition to have a large amount in variety, and might not be lime carbonate.Lime carbonate is Wingdale, and just a kind of in the stone flour also has talcum powder in the stone flour, and putty uses as making.Also have silica powder, as bearing glass.The rock that also has a lot of mineralogical compositions can be clayed into power, as different technology and purposes.
Claims (3)
1. a novel true mineral varnish is characterized in that: contain: water 80～120 weight parts, film coalescence aid 3～10 weight parts, Mierocrystalline cellulose 1～3 weight part, sanitas 1～3 weight part, mould inhibitor 1～5 weight part, propylene glycol 10～15 weight parts, organosilicon crylic acid latex 100～200 weight parts, stone flour 650～800 weight parts.
2. a kind of novel true mineral varnish according to claim 1, it is characterized in that: described film coalescence aid claims coalescing aid again, is a kind of evanescent softening agent; The macromolecular polysaccharide that described Mierocrystalline cellulose is made up of glucose is the main component of plant cell wall; Described sanitas is meant natural or the synthetic chemical ingredients; Described mould inhibitor main component: quaternary ammonium salt derivative, card pine, tensio-active agent, synergistic agent etc. can prevent that microorganism from causing mouldy medicament; Described propylene glycol is the important source material of unsaturated polyester, Resins, epoxy, urethane resin; Described organosilicon crylic acid latex is selected import special addition agent and features monomer for use, and introduces extraordinary organosilicon, adopts seed emulsion, coats polymerization technique by nucleocapsid and synthesizes; Described stone flour is to be commonly referred to as stone dust the lime carbonate limestone powder is arranged, and also has silica powder etc.
3. a kind of novel true mineral varnish according to claim 1, it is characterized in that: its preparation technology is: take by weighing each material at first by weight, just the stone material waste material of different colours separates grinding and processing again, grinding to form fineness is 45-100 purpose powder, earlier water is added in the mixer, then add film coalescence aid, Mierocrystalline cellulose, sanitas, mould inhibitor, propylene glycol, organosilicon crylic acid latex, stone flour while stirring, stir at last, be finished product.