CN104263176B - 纳米外墙装饰涂料 - Google Patents
纳米外墙装饰涂料 Download PDFInfo
- Publication number
- CN104263176B CN104263176B CN201410537182.6A CN201410537182A CN104263176B CN 104263176 B CN104263176 B CN 104263176B CN 201410537182 A CN201410537182 A CN 201410537182A CN 104263176 B CN104263176 B CN 104263176B
- Authority
- CN
- China
- Prior art keywords
- nano
- parts
- dispersant
- agent
- amount
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
一种纳米外墙装饰涂料,按重量份数计:451FQ纤维素0.2,多功能助剂AMP—95 0.1,分散剂SN‑5027 0.7,分散剂F200 0.4润湿剂X—405 0.1,消泡剂340 0.15,纳米复合材料0.5‑‑20,流平剂100 0.4,金红石钛白粉20,超细硫酸钡2.5,重钙10,煅烧高岭土7.5;纯丙5210 40,成膜助剂2,消泡剂340 0.2,杀菌剂623 0.25,多功能助剂AMP—95 0.1,增稠剂H380 0.4,增稠流变剂M161 0.2 和达到墙面涂料要求的水。有降解二氧化硫、一氧化氮,二氧化氮,防霉、吸收紫外线功能;所以,绿色环保。附着力强,硬度大。
Description
技术领域
本发明涉及一种纳米外墙装饰涂料。
背景技术
目前建筑装饰材料特别是房屋内墙的装饰材料,主要起到美化室内外的作用,使人感觉舒适温暖,房屋更加牢固,使用的材料一般是高岭土、硅石灰粉、滑石粉、云母粉、钛白粉等原料加入分散剂、润湿剂、丙二醇、乳液、水调和而成,起到了美化效果和保护墙体的作用但是人们对环保的要求越来越高,对墙面装饰材料提出来新的希望——装饰材料对人体健康的保护作用。但一般不具有杀死细菌、防霉、吸收紫外线功能。目前的装饰墙面的涂料的附着力差,易老化变暗,与墙体原有的水泥底层的粘合性不足,导致脱层剥落。
发明内容
本发明的目的是提供一种纳米外墙装饰涂料,以使装饰墙体的材料不仅起到装饰美化墙面的作用,还具有杀死细菌、防霉、吸收此外线效果。
技术方案:
一种纳米外墙装饰涂料,包括纳米原料和制作墙面涂料的通用原料,按重量份数计,步骤1,组成物中: 0.2份451FQ纤维素, 0.1份多功能助剂AMP-95, 分0.7份散剂SN-5027,0.4份分散剂F200,0.1份润湿剂X-405, 0.15份消泡剂340,2.0-20份纳米复合材料,0.4份流平剂100,20份金红石钛白粉,2.5份超细硫酸钡,10份重钙,7.5份煅烧高岭土和墙面涂料生产要求量的水,在搅拌机中搅拌得一组材料;步骤2,再取40份纯丙5210,2份成膜助剂,0.2份消泡剂340,0.25份杀菌剂623,0.1份多功能助剂AMP-95, 0.4份增稠剂H380,0.2份增稠流变剂M161和达到墙面涂料生产要求量的水得第二组材料,将第二组材料置入搅拌机中与第一组材料充分搅拌均匀即得成品。
按上述组分中各种原料取量,分两步在搅拌机中搅拌混合均匀即得到产品,第一步:依次将第一组材料置入搅拌机中,搅拌机转速每分钟450-550转,高速搅拌20分钟,经砂磨机砂磨,检验合格备用;第二步:在上步得到的混合料基础上,依次向搅拌机中加入第二组材料,以每分钟250-300的转速,搅拌20-30分钟,检验合格后,即为成品。
按重量份计,其中纳米复合材料中包括:纳米级二氧化硅10-25,纳米级二氧化钛15-30,451FQ纤维素,多功能助剂AMP-95,润湿剂X-405,分散剂WinSPerse4050,丙二醇;其中分散剂WinSPerse4050按纳米二氧化硅和纳米二氧化钛总量的35-40%取量,丙二醇按纳米二氧化硅和纳米二氧化钛总量的40-52%取量,再加入拟配制纳米复合材料总量0.15%的451FQ纤维素、0.1%的多功能助剂AMP-95 、0.15%的润湿剂X-405、不少于25%量的水。
按上述组分要求取足各种原料,依次把水,451FQ纤维素,多功能助剂AMP-95,润湿剂X-405,分散剂WinSPerse4050,丙二醇,纳米二氧化硅,纳米二氧化钛,置入搅拌机中,以不低于每分钟500转的转速搅拌25-30分钟即可制得纳米复合材料。
本发明的特点是采用纳米复合材料制得的纳米外墙装饰涂料,具有降解无机污染物如;二氧化硫、一氧化氮,二氧化氮,防霉、吸收紫外线功能;所以,绿色环保,长期保护人体健康。该纳米涂料能够渗透到水泥墙面内与水泥构成一个整体,所以附着力特别强,硬度大;装饰后的墙面还具有耐老化,牢固不变形的特点。
具体实施方式
以下给出本发明的实施例:
例一、纳米外墙装饰涂料加工。
以生产100公斤外墙装饰涂料为例,说明本发明技术方案的实施方式。
1、备料:a、以重量计,取20.3公斤水,0.176公斤451FQ纤维素,0.09公斤多功能助剂AMP—95,0.61公斤分散剂SN-5027,0.352公斤分散剂F200,0.09公斤润湿剂X—405,0.13公斤消泡剂340,5公斤纳米复合材料,0.352公斤流平剂100,17.60公斤金红石钛白粉,2.2公斤超细硫酸钡,8.8公斤重钙,6.6公斤煅烧高岭土。
b、以重量计:取35.2公斤纯丙5210,1.76公斤成膜助剂,0.176公斤消泡剂340,0.22公斤杀菌剂623,0.09公斤多功能助剂AMP—95, 0.35公斤增稠剂H380,0.176公斤增稠流变剂M161,0.35公斤水。
2,加工:在涂料用搅拌机中搅拌混合均匀。
加工方式:
1、搅拌机转速500左右,依次加入上述步骤a备好的料:水, 451FQ纤维素, 多功能助剂AMP—95, 分散剂SN-5027,分散剂F200,润湿剂X—405,消泡剂340,纳米复合材料,流平剂100,金红石钛白粉,超细硫酸钡,重钙,煅烧高岭土后,高速搅拌20分钟,经砂磨机砂磨,检验合格后备用。
2、再向搅拌机中依次加入上述备料步骤b所述原料即:纯丙5210,成膜助剂,消泡剂340,杀菌剂623,多功能助剂AMP—95,增稠剂H380,水和增稠流变剂M161,以每分钟300转的速度,搅拌20-30分钟,检验合格后,进入包装机包装,成品入库。
例二、组合物中纳米复合材料的加工。
以生产125.55公斤纳米复合材料为例:
纳米级二氧化硅25公斤,纳米级二氧化钛30公斤,分散剂WinSPerse4050按纳米二氧化硅和纳米二氧化钛总量的20.4公斤,取量,丙二醇按纳米二氧化硅和纳米二氧化钛总量的24.75公斤取量,再加入拟配制纳米复合材料总重量0.15公斤的451FQ纤维素、0.1公斤的多功能助剂AMP-95 、0.15公斤的润湿剂X-405、25公斤水。前述原料,依次加入搅拌机中,以不低于每分钟500转的转速搅拌30分钟,即制得用于生产外墙面装饰涂料中用的纳米复合材料。
本发明的特点是采用纳米复合材料生产外墙面用的装饰涂料,具有降解无机污染物如;二氧化硫、一氧化氮,二氧化氮,防霉、吸收紫外线功能,绿色环保,长期居住,有利益保护人体健康,特别是该纳米涂料能够渗透到水泥墙面与水泥构成一个整体,所以附着力强,硬度大,坚实牢固,有较强的防渗透性能。与国家规定的优等品指标对照:a、干燥时间1.5小时,缩短了2小时;b、耐水性170小时无异常,国标96小时无异常,提高了74小时耐水性无异常性能;c、耐碱性90小时无异常,国标是48小时无异常;d、耐刷洗性12000次,国标是≥2000次;e、人工气候老化性1000小时不起泡、不剥落、无裂纹,国标是600小时不起泡、不剥落、无裂纹。
经济角度分析:使用本发明提供的技术产品作外墙装饰材料,每平方米成本增加1.5元左右,但环保、、分解有害气体、、抗老化、抗污等性能是市场上现有的传统涂料无法相比的。
Claims (1)
1.一种纳米外墙装饰涂料,包括纳米原料和制作墙面涂料的通用原料,其特征在于按重量份数计,步骤1,组成物中: 0.2份451FQ纤维素, 0.1份多功能助剂AMP-95, 0.7份分散剂SN-5027,0.4份分散剂F200,0.1份润湿剂X-405, 0.15份消泡剂340,2.0-20份纳米复合材料,0.4份流平剂100,20份金红石钛白粉,2.5份超细硫酸钡,10份重钙,7.5份煅烧高岭土和墙面涂料生产要求量的水,在搅拌机中搅拌得第一组材料;步骤2,再取40份纯丙5210,2份成膜助剂,0.2份消泡剂340,0.25份杀菌剂623,0.1份多功能助剂AMP-95, 0.4份增稠剂H380,0.2份增稠流变剂M161和达到墙面涂料生产要求量的水得第二组材料,将第二组材料置入搅拌机中与第一组材料充分搅拌均匀即得成品;按重量份计其中纳米复合材料中包括:纳米级二氧化硅10-25份,纳米级二氧化钛15-30份,分散剂WinSPerse4050按纳米二氧化硅和纳米二氧化钛总量的35-40%取量,丙二醇按纳米二氧化硅和纳米二氧化钛总量的40-52%取量,再加入拟配制纳米复合材料总量0.15%的451FQ纤维素、0.1%的多功能助剂AMP-95 、0.15%的润湿剂X-405、不少于25%量的水。