CN104263176B - Nano outer wall decorative paint - Google Patents
Nano outer wall decorative paint Download PDFInfo
- Publication number
- CN104263176B CN104263176B CN201410537182.6A CN201410537182A CN104263176B CN 104263176 B CN104263176 B CN 104263176B CN 201410537182 A CN201410537182 A CN 201410537182A CN 104263176 B CN104263176 B CN 104263176B
- Authority
- CN
- China
- Prior art keywords
- nano
- parts
- dispersant
- agent
- amount
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
A kind of nano outer wall decorative paint, meter by weight: 451FQ cellulose 0.2, multifunctional assistant AMP 95 0.1, dispersant SN 5,027 0.7, dispersant F200 0.4 wetting agent X 405 0.1, defoamer 340 0.15, nano composite material 0.5 20, levelling agent 100 0.4, rutile titanium white lead 20, ultra-fine barium sulfate 2.5, triple superphosphate 10, calcined kaolin 7.5；Pure third 5,210 40, coalescents 2, defoamer 340 0.2, antibacterial 623 0.25, multifunctional assistant AMP 95 0.1, thickening agent H380 0.4, thickener rheology agent M161 0.2 and the water reaching wall covering requirement.There are degraded sulfur dioxide, nitric oxide, nitrogen dioxide, mildew-resistant, absorption ultraviolet function；So, environmental protection.Adhesive force is strong, and hardness is big.
Description
Technical field
The present invention relates to a kind of nano outer wall decorative paint.
Background technology
The ornament materials of building and ornament materials particularly house inner wall at present; primarily serve the effect beautifying indoor and outdoor; make people feel comfortable warm; house is more firm; raw material addition dispersant, wetting agent, propylene glycol, emulsion, the water such as the material usually Kaolin of use, Silicon stone ashes, Pulvis Talci, mica powder, titanium dioxide are in harmonious proportion and form; the effect still people serving landscaping effect and protection body of wall are more and more higher to the requirement of environmental protection, and decorative material for wall surface puts forward the protective effect to health of the new hope ornament materials.But typically do not have and kill antibacterial, mildew-resistant, absorption ultraviolet function.The poor adhesive force of the coating of current decorated wall surface, easy to be aging dimmed, the cohesive of cement bottom layer original with body of wall is not enough, causes delamination to be peeled off.
Summary of the invention
It is an object of the invention to provide a kind of nano outer wall decorative paint, so that the material of decorating wall not only acts as the effect of decoration metope, also have and kill antibacterial, mildew-resistant, absorb this outside line effect.
Technical scheme:
A kind of nano outer wall decorative paint, including nano raw material and the general raw material of making wall covering, count by weight, step 1, in constituent: 0.2 part of 451FQ cellulose, 0.1 part of multifunctional assistant AMP-95, divide 0.7 part of powder SN-5027, 0.4 part of dispersant F200, 0.1 part of wetting agent X-405, 0.15 part of defoamer 340, 2.0-20 part nano composite material, 0.4 part of levelling agent 100, 20 parts of rutile titanium white lead, 2.5 parts of ultra-fine barium sulfates, 10 parts of triple superphosphate, 7.5 parts of calcined kaolins and the water of wall covering production requirement amount, one group of material is stirred to obtain in blender；Step 2, take 40 parts pure third 5210 again, 2 parts of coalescents, 0.2 part of defoamer 340,0.25 part of antibacterial 623,0.1 part of multifunctional assistant AMP-95,0.4 part of thickening agent H380,0.2 part of thickener rheology agent M161 and reach the water of wall covering production requirement amount and obtain second group of material, inserts second group of material to stir with first group of material in blender and gets product.
By raw material taken amounts various in said components, it is uniformly mixed in blender in two steps and i.e. obtains product, the first step: successively first group of material is inserted in blender, blender rotating speed 450-550 per minute turns, high-speed stirred 20 minutes, through sand mill sand milling, checks qualified standby；Second step: on the basis of the compound that upper step obtains, adds second group of material successively in blender, with the rotating speed of 250-300 per minute, stirs 20-30 minute, after the assay was approved, is finished product.
By weight, wherein nano composite material includes: nanometer grade silica 10-25, Nano titanium dioxide 15-30,451FQ cellulose, multifunctional assistant AMP-95, wetting agent X-405, dispersant WinSPerse4050, propylene glycol；Wherein dispersant WinSPerse4050 presses the 35-40% taken amount of nano silicon and nano titanium oxide total amount, the 40-52% taken amount of nano silicon and nano titanium oxide total amount pressed by propylene glycol, adds and intends the 451FQ cellulose of preparation of nano composite total amount 0.15%, the multifunctional assistant AMP-95 of 0.1%, the wetting agent X-405 of 0.15%, water no less than 25% amount.
Various raw material is taken fully by said components requirement, successively water, 451FQ cellulose, multifunctional assistant AMP-95, wetting agent X-405, dispersant WinSPerse4050, propylene glycol, nano silicon, nano titanium oxide, insert in blender, be not less than 500 turns per minute rotating speed stir within 25-30 minute, can be prepared by nano composite material.
It is characteristic of the invention that the nano outer wall decorative paint using nano composite material to prepare, there is degraded inorganic pollution such as；Sulfur dioxide, nitric oxide, nitrogen dioxide, mildew-resistant, absorption ultraviolet function；So, environmental protection, digital preservation health.This nano paint constitutes an entirety with cement in can penetrating into cement wall surface, so adhesive force is strong especially, hardness is big；Metope after decoration also has ageing-resistant, firm indeformable feature.
Detailed description of the invention
Embodiments of the invention given below:
Example one, nano outer wall decorative paint are processed.
As a example by producing 100 kilograms of exterior wall decorating coatings, the embodiment of technical solution of the present invention is described.
1, get the raw materials ready: a, by weight, take 20.3 kg of water, 0.176 kilogram of 451FQ cellulose, 0.09 kilogram of multifunctional assistant AMP 95,0.61 kilogram of dispersant SN-5027,0.352 kilogram of dispersant F200,0.09 kilogram of wetting agent X 405,340,5 kilograms of nano composite materials of 0.13 kilogram of defoamer, 0.352 kilogram of levelling agent 100,17.60 kilogram rutile titanium white lead, 2.2 kilograms of ultra-fine barium sulfates, 8.8 kilograms of triple superphosphate, 6.6 kilograms of calcined kaolins.
B, by weight: take 35.2 kilograms pure third 5210,1.76 kilograms of coalescents, 0.176 kilogram of defoamer 340,0.22 kilogram of antibacterial, 95,0.35 kilogram of thickening agent H380 of 623,0.09 kilogram of multifunctional assistant AMP, 0.176 kilogram of thickener rheology agent M161,0.35 kg of water.
2, processing: be uniformly mixed in coating blender.
Processing mode:
1, blender rotating speed about 500, is sequentially added into the material that above-mentioned steps a is got ready: water, 451FQ cellulose, multifunctional assistant AMP 95, dispersant SN-5027, dispersant F200, wetting agent X 405, defoamer 340, nano composite material, levelling agent 100, rutile titanium white lead, ultra-fine barium sulfate, triple superphosphate, after calcined kaolin, high-speed stirred 20 minutes, through sand mill sand milling, the most standby.
2, in blender, raw material described in above-mentioned material preparation step b it is sequentially added into more i.e.: pure the third 5210, coalescents, defoamer 340, antibacterial 623, multifunctional assistant AMP 95, thickening agent H380, water and thickener rheology agent M161, with the speed of 300 turns per minute, stir 20-30 minute, after the assay was approved, entering packer packaging, finished product is put in storage.
The processing of nano composite material in example two, compositions.
As a example by producing 125.55 kilograms of nano composite materials:
Nanometer grade silica 25 kilograms, Nano titanium dioxide 30 kilograms, dispersant WinSPerse4050 presses 20.4 kilograms of nano silicon and nano titanium oxide total amount, taken amount, 24.75 kilograms of taken amounts of nano silicon and nano titanium oxide total amount pressed by propylene glycol, add plan the 451FQ cellulose of preparation of nano composite gross weight 0.15 kilogram, the multifunctional assistant AMP-95 of 0.1 kilogram, the wetting agent X-405 of 0.15 kilogram, 25 kg of water.Aforementioned base materials, is sequentially added in blender, be not less than 500 turns per minute rotating speed stir 30 minutes, i.e. prepare for producing the nano composite material in exterior wall surface decorative coating.
It is characteristic of the invention that the decorative paint using nano composite material to produce wall face, there is degraded inorganic pollution such as；Sulfur dioxide, nitric oxide; nitrogen dioxide; mildew-resistant, absorption ultraviolet function, environmental protection, hang up one's hat; there is interest protection health; particularly this nano paint can penetrate into cement wall surface and cement one entirety of composition, so adhesive force is strong, hardness is big; solid firmly, have stronger anti-permeability.Compare with the high-class product index of national regulation: a, drying time 1.5 hours, shorten 2 hours；B, resistance to water 170 hours are without exception, and GB 96 hours is without exception, improves 74 hours resistance to water performances without exception；C, alkali resistance 90 hours are without exception, GB be 48 hours without exception；D, brushing resistance 12000 times, GB is >=2000 times；E, artificial weathering aging 1000 hours is non-foaming, do not peel off, flawless, GB be 600 hours non-foaming, do not peel off, flawless.
Economic angle is analyzed: the technical products using the present invention to provide makees external wall decorative material, and every square metre of cost increases about 1.5 yuan, but environmental protection, resolving harmful gas, the performance such as aging resistance, anti-soil be that on market, existing traditional coating cannot be compared.
Claims (1)
1. a nano outer wall decorative paint, including nano raw material and the general raw material of making wall covering, it is characterized in that counting by weight, step 1, in constituent: 0.2 part of 451FQ cellulose, 0.1 part of multifunctional assistant AMP-95, 0.7 part of dispersant SN-5027, 0.4 part of dispersant F200, 0.1 part of wetting agent X-405, 0.15 part of defoamer 340, 2.0-20 part nano composite material, 0.4 part of levelling agent 100, 20 parts of rutile titanium white lead, 2.5 parts of ultra-fine barium sulfates, 10 parts of triple superphosphate, 7.5 parts of calcined kaolins and the water of wall covering production requirement amount, first group of material is stirred to obtain in blender；Step 2, take 40 parts pure third 5210 again, 2 parts of coalescents, 0.2 part of defoamer 340,0.25 part of antibacterial 623,0.1 part of multifunctional assistant AMP-95,0.4 part of thickening agent H380,0.2 part of thickener rheology agent M161 and reach the water of wall covering production requirement amount and obtain second group of material, inserts second group of material to stir with first group of material in blender and gets product；Wherein nano composite material includes: nanometer grade silica 10-25 part, Nano titanium dioxide 15-30 part, dispersant WinSPerse4050 presses the 35-40% taken amount of nano silicon and nano titanium oxide total amount, the 40-52% taken amount of nano silicon and nano titanium oxide total amount pressed by propylene glycol, adds and intends the 451FQ cellulose of preparation of nano composite total amount 0.15%, the multifunctional assistant AMP-95 of 0.1%, the wetting agent X-405 of 0.15%, water no less than 25% amount.