CN104233809A - 一种皮肤衣面料 - Google Patents
一种皮肤衣面料 Download PDFInfo
- Publication number
- CN104233809A CN104233809A CN201410381803.6A CN201410381803A CN104233809A CN 104233809 A CN104233809 A CN 104233809A CN 201410381803 A CN201410381803 A CN 201410381803A CN 104233809 A CN104233809 A CN 104233809A
- Authority
- CN
- China
- Prior art keywords
- nylon
- cloth
- based cloth
- percent
- nylon based
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供了一种皮肤衣面料,其包括尼龙基布,所述尼龙基布经过下述步骤处理:A)将尼龙基布做防渗水处理;B)在防渗水处理后的尼龙基布上进行压光处理,使得布面干整;C))用0.3刀型在压光处理后的尼龙基布上涂上一层薄薄的抗紫外线胶水;D)烘干成型;其中,步骤C中所述抗紫外线胶水由下列成分组成:聚氨酯树脂70%~80%,溶剂20%~30%,抗UV1%~3%,交联剂1%~3%,促进剂1%~2%。本发明所述皮肤衣面料UPF达到50+,可以很好地保护皮肤不被晒伤。
Description
技术领域
本发明涉及一种皮肤衣面料,尤其涉及一种采用15D、20D尼龙超薄面料制成的皮肤衣面料。
背景技术
我们都知道,太阳光谱中的紫外线会使人体皮肤晒伤、老化,产生黑色素和色斑,更严重的是还会诱发癌变,危害人类健康。为了防止上述现象发生,皮肤衣也称防晒服因此诞生,皮肤衣大多采用轻薄面料然后添加助剂的原理,2011年1月1日,我国推出了最新的评定标准《纺织品防紫外线性能的评定》,防紫外线产品应该在标签上标有以下三个方面的内容:1.本标准的编号,即gb/t18830;2.UPF(紫外线透射程度)值:30+或者50+;3.长期使用以及在拉伸或者潮湿的情况下,该产品所提供的防护性能可能减少。现有的采用15D、20D这种轻薄的尼龙面料的皮肤衣,即使用亨斯迈助剂也很难达到UPF50+指数,本身这么轻薄的织物,密度一般在350T以上,属高密织物,因尼龙纤维本身的纱的切片空隙较细小,吸收紫外线助剂比较缓慢而且较少,并且渗透性相应较差,所以一般都达不到UPF40+,15D尼龙浅色面料甚至达不到UPF30+。
发明内容
为了克服现有技术的缺陷,本发明提供一种皮肤衣面料,通过在基布上涂设一层新型的抗紫外线胶水,从而达到UPF50+的效果。
为了实现上述目的,本发明提供以下技术方案:
一种皮肤衣面料,其包括尼龙基布,所述尼龙基布经过下述步骤处理:
A)将尼龙基布做防渗水处理;
B)在防渗水处理后的尼龙基布上进行压光处理,使得布面干整;
C)用0.3刀型在压光处理后的尼龙基布上涂上一层薄薄的抗紫外线胶水;
D)烘干成型;
其中,步骤C中所述抗紫外线胶水的成分及其质量百分比为:聚氨酯树脂70%~80%,溶剂DMF或甲苯20%~30%,抗紫外线助剂1%~3%,交联剂1%~3%,促进剂1%~2%。采用溶剂型中常用的交联剂和促进剂,可增加牢度的两种助剂。
作为优选技术方案,所述尼龙基布为15D或20D尼龙超薄棉料。
本发明所带来的有益效果是:UPF达到50+,可以很好地保护皮肤不被晒伤。
具体实施方式
下面对本发明的较佳实施例进行详细阐述,以使本发明的优点和特征能更易于被本领域技术人员理解,从而对本发明的保护范围做出更为清楚明确的界定。
一种皮肤衣面料,其包括尼龙基布,所述尼龙基布经过下述步骤处理:A)将尼龙基布做防渗水处理;
B)在防渗水处理后的尼龙基布上进行压光处理,使得布面干整;
C)用0.3刀型在压光处理后的尼龙基布上涂上一层薄薄的抗紫外线胶水;
D)烘干成型;
其中,步骤C中所述抗紫外线胶水的成分及其质量百分比为:聚氨酯树脂70%~80%,溶剂DMF或甲苯20%~30%,抗紫外线助剂1%~3%,交联剂1%~3%,促进剂1%~2%。采用溶剂型中常用的交联剂和促进剂,可增加牢度的两种助剂。
所述尼龙基布为15D或20D尼龙超薄棉料。
本发明所述实施例具有的优点是:UPF达到50+,可以很好地保护皮肤不被晒伤。
以上所述,仅为本发明的具体实施方式,但本发明的保护范围并不局限于此,任何熟悉本领域的技术人员在本发明所揭露的技术范围内,可不经过创造性劳动想到的变化或替换,都应涵盖在本发明的保护范围之内。因此,本发明的保护范围应该以权利要求书所限定的保护范围为准。
Claims (2)
1.一种皮肤衣面料,其包括尼龙基布,其特征在于,所述尼龙基布经过下述步骤处理:
A)将尼龙基布做防渗水处理;
B)在防渗水处理后的尼龙基布上进行压光处理,使得布面干整;
C)用0.3刀型在压光处理后的尼龙基布上涂上一层薄薄的抗紫外线胶水;
D)烘干成型;
其中,步骤C中所述抗紫外线胶水的成分及其质量百分比为:聚氨酯树脂70%~80%,溶剂DMF或甲苯20%~30%,抗紫外线助剂1%~3%,交联剂1%~3%,促进剂1%~2%。
2.根据权利要求1所述的一种皮肤衣面料,其特征在于,所述尼龙基布为15D或20D尼龙超薄面料。