CN104231768A - 一种净味竹醋液乳胶漆 - Google Patents
一种净味竹醋液乳胶漆 Download PDFInfo
- Publication number
- CN104231768A CN104231768A CN201410445444.6A CN201410445444A CN104231768A CN 104231768 A CN104231768 A CN 104231768A CN 201410445444 A CN201410445444 A CN 201410445444A CN 104231768 A CN104231768 A CN 104231768A
- Authority
- CN
- China
- Prior art keywords
- bamboo vinegar
- liquid
- parts
- emulsion paint
- raw material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
本发明公开了一种净味竹醋液乳胶漆,它是由下述重量份的原料组成的:苯丙乳液40-45、竹醋净味液2-3、吡咯烷酮羟酸钠1-2、山梨醇1-2、羟乙基纤维素2-3、沉淀硫酸钡12-20、轻质碳酸钙24-30、成膜助剂5-7、去离子水31-40;本发明的乳胶漆强度高、有韧性,使用砂纸打磨不易脱粉,耐擦洗,吸附力强,不易爆裂,抗污性好,耐候性强,无污染,无毒,加入的竹醋净味液具有很好的净味效果。
Description
技术领域
本发明主要涉及涂料领域,尤其涉及一种净味竹醋液乳胶漆。
背景技术
以丙烯酸酯共聚乳液为代表的一大类合成树脂乳液涂料。乳胶漆是水分散性涂料,它是以合成树脂乳液为基料,填料经过研磨分散后加入各种助剂精制而成的涂料。乳胶漆具备了与传统墙面涂料不同的众多优点,如易于涂刷、干燥迅速、漆膜耐水、耐擦洗性好等;水溶性内墙乳胶漆无污染、无毒、无火灾隐患,易于涂刷、干燥迅速,漆膜耐水、耐擦洗性好,色彩柔和。水溶性内墙乳胶漆,以水作为分散介质,无有机溶剂性毒气体带来的环境污染问题,透气性好,避免了因涂膜内外温度压力差而导致的涂膜起泡弊病,适合未干透的新墙面涂装。
发明内容
本发明目的就是提供一种净味竹醋液乳胶漆。
本发明是通过以下技术方案实现的:
一种净味竹醋液乳胶漆,它是由下述重量份的原料组成的:
苯丙乳液40-45、竹醋净味液2-3、吡咯烷酮羟酸钠1-2、山梨醇1-2、羟乙基纤维素2-3、沉淀硫酸钡12-20、轻质碳酸钙24-30、成膜助剂5-7、去离子水31-40;
所述的竹醋净味液是由下述重量份的原料组成的:
竹醋液10-15、艾叶油1-2、三聚磷酸钠0.1-0.2、异噻唑啉酮0.1-0.3;
将上述三聚磷酸钠加入到竹醋液中,搅拌混合均匀后加入艾叶油、异噻唑啉酮,充分混合均匀,即得所述竹醋净味液;
所述的成膜助剂是由下述重量份的原料组成的:
硅丙乳液20-30、醋酸乙烯酯3-5、乙氧基化烷基硫酸铵1-2、磷酸二氢铝2-3、过硫酸铵0.5-2、去离子水10-20;
将乙氧基化烷基硫酸铵加入到上述去离子水中,搅拌得预混液;
将醋酸乙烯酯加热到40-50℃,加入磷酸二氢铝,保温搅拌混合20-30分钟,加入到上述预混液中,200-300转/分搅拌分散3-5分钟,得分散液;
将过硫酸铵加入到硅丙乳液中,搅拌混合均匀后与上述分散液混合,充分球磨,即得所述成膜助剂。
一种净味竹醋液乳胶漆的制备方法,包括以下步骤:
将除了苯丙乳液以外的各原料混合,1000-1200转/分搅拌分散10-20分钟,将分散好的浆料进行砂磨,转速为800-1200转/分,砂磨30-60min,加入剩余各原料,600-800转/分搅拌分散20-30分钟,即得所述乳胶漆。
本发明的优点是:
本发明的乳胶漆强度高、有韧性,使用砂纸打磨不易脱粉,耐擦洗,吸附力强,不易爆裂,抗污性好,耐候性强,无污染,无毒,加入的竹醋净味液具有很好的净味效果。
具体实施方式
实施例1
一种净味竹醋液乳胶漆,它是由下述重量份(公斤)的原料组成的:
苯丙乳液45、竹醋净味液2、吡咯烷酮羟酸钠1、山梨醇1、羟乙基纤维素3、沉淀硫酸钡20、轻质碳酸钙30、成膜助剂5、去离子水40;
所述的竹醋净味液是由下述重量份的原料组成的:
竹醋液15、艾叶油2、三聚磷酸钠0.2、异噻唑啉酮0.3;
将上述三聚磷酸钠加入到竹醋液中,搅拌混合均匀后加入艾叶油、异噻唑啉酮,充分混合均匀,即得所述竹醋净味液;
所述的成膜助剂是由下述重量份的原料组成的:
硅丙乳液30、醋酸乙烯酯5、乙氧基化烷基硫酸铵2、磷酸二氢铝2、过硫酸铵0.5、去离子水20;
将乙氧基化烷基硫酸铵加入到上述去离子水中,搅拌得预混液;
将醋酸乙烯酯加热到50℃,加入磷酸二氢铝,保温搅拌混合20分钟,加入到上述预混液中,300转/分搅拌分散5分钟,得分散液;
将过硫酸铵加入到硅丙乳液中,搅拌混合均匀后与上述分散液混合,充分球磨,即得所述成膜助剂。
一种净味竹醋液乳胶漆的制备方法,包括以下步骤:
将除了苯丙乳液以外的各原料混合,1200转/分搅拌分散20分钟,将分散好的浆料进行砂磨,转速为1200转/分,砂磨60min,加入剩余各原料,800转/分搅拌分散20分钟,即得所述乳胶漆。
性能测试:
漆膜外观平整、无硬块、手感好、光泽度好;
耐洗刷性试验:5000 次通过,漆膜无破损;
耐人工老化性试验:2000小时不起泡、不剥落、无裂纹;
耐水性:140h漆膜无破损;
耐碱性:120h漆膜无破损。
Claims (2)
1.一种净味竹醋液乳胶漆,其特征在于它是由下述重量份的原料组成的:
苯丙乳液40-45、竹醋净味液2-3、吡咯烷酮羟酸钠1-2、山梨醇1-2、羟乙基纤维素2-3、沉淀硫酸钡12-20、轻质碳酸钙24-30、成膜助剂5-7、去离子水31-40;
所述的竹醋净味液是由下述重量份的原料组成的:
竹醋液10-15、艾叶油1-2、三聚磷酸钠0.1-0.2、异噻唑啉酮0.1-0.3;
将上述三聚磷酸钠加入到竹醋液中,搅拌混合均匀后加入艾叶油、异噻唑啉酮,充分混合均匀,即得所述竹醋净味液;
所述的成膜助剂是由下述重量份的原料组成的:
硅丙乳液20-30、醋酸乙烯酯3-5、乙氧基化烷基硫酸铵1-2、磷酸二氢铝2-3、过硫酸铵0.5-2、去离子水10-20;
将乙氧基化烷基硫酸铵加入到上述去离子水中,搅拌得预混液;
将醋酸乙烯酯加热到40-50℃,加入磷酸二氢铝,保温搅拌混合20-30分钟,加入到上述预混液中,200-300转/分搅拌分散3-5分钟,得分散液;
将过硫酸铵加入到硅丙乳液中,搅拌混合均匀后与上述分散液混合,充分球磨,即得所述成膜助剂。
2.一种如权利要求1所述的净味竹醋液乳胶漆的制备方法,其特征在于包括以下步骤:
将除了苯丙乳液以外的各原料混合,1000-1200转/分搅拌分散10-20分钟,将分散好的浆料进行砂磨,转速为800-1200转/分,砂磨30-60min,加入剩余各原料,600-800转/分搅拌分散20-30分钟,即得所述乳胶漆。