CN104178011A - Composite coating for outdoor tent and preparation method of composite coating - Google Patents
Composite coating for outdoor tent and preparation method of composite coating Download PDFInfo
- Publication number
- CN104178011A CN104178011A CN201410432455.0A CN201410432455A CN104178011A CN 104178011 A CN104178011 A CN 104178011A CN 201410432455 A CN201410432455 A CN 201410432455A CN 104178011 A CN104178011 A CN 104178011A
- Authority
- CN
- China
- Prior art keywords
- parts
- composite coating
- outdoor tent
- emulsion
- titanium dioxide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a composite coating for an outdoor tent. The composite coating comprises the following components in parts by weight: 25-35 parts of emulsion, 5-8 parts of calcined kaolin, 5-10 parts of titanium dioxide, 3-5 parts of a film-forming assistant, 15-20 parts of talcum powder, 8-12 parts of an anti-slip agent, 0.5-1 part of antibacterial nano titanium dioxide, 5-10 parts of lithopone, 0.2-0.3 part of a defoamer, 0.1-0.3 part of sodium hexametaphosphate, 0.8-1 part of a thickener, 0.05-0.1 part of AMP-95, 0.5-1 part of ethanediol and 35-45 parts of water. The invention further provides a preparation method of the coating. The preparation method comprises the following steps: selecting a proper formula as well as the emulsion, the film-forming assistant, the anti-slip agent and antibacterial nano titanium dioxide according to a proper ratio, adding AMP, the talcum powder, the lithopone and the defoamer, and interacting and coordinating the components. The prepared anti-slip coating has a remarkable sterilization effect while being waterproof, antifouling and wear-resistant, and can enable the tent to achieve the sterilization effect in light and even only faint light.
Description
Technical field
The present invention relates to coating material field, particularly, relate to a kind of outdoor tent composite coating and preparation method thereof.
Background technology
Along with the raising of people's living standard, outdoor activity become the main way that people loosen the sparetime, and it is more and more extensive that corresponding outdoor tent is also applied, and people require also more and more higher to the material of outdoor tent.Existing tent also mainly rests on the structure of tent and waterproof, antifouling property, but does not consider for the germ resistance of tent coating.
Summary of the invention
Goal of the invention: the technical problem to be solved in the present invention is to provide a kind of outdoor tent composite coating, this coating have waterproof, antifouling and wear-resisting in, also there is obvious sterilization effect, can make tent have light even be the effect that all can play sterilization under faint light.
The invention allows for the preparation method of above-mentioned outdoor tent composite coating.
Technique means: for realizing above-mentioned technical purpose, the invention provides a kind of outdoor tent composite coating, it comprises the component of following parts by weight: 35～45 parts, 25～35 parts of emulsions, 5～8 parts of calcined kaolins, 5～10 parts of titanium dioxides, 3～5 parts of film coalescence aid, 15～20 parts of talcum powder, 8～12 parts of slipproofing agents, 0.5～1 part of antimicrobial nano titanium dioxide, 5～10 parts, zinc sulfide white, 0.2～0.3 part of defoamer, 0.1～0.3 part of Sodium hexametaphosphate 99,0.8～1 part of thickening material, AMP-950.05～0.1 part, 0.5～1 part of ethylene glycol and water.
Preferably, described outdoor tent comprises the component of following parts by weight with composite coating: 40～45 parts, 30～35 parts of emulsions, 6～7 parts of calcined kaolins, 5～10 parts of titanium dioxides, 4～5 parts of film coalescence aid, 18～20 parts of talcum powder, 10～12 parts of slipproofing agents, 0.8～0.9 part of antimicrobial nano titanium dioxide, 7～8 parts, zinc sulfide white, 0.2～0.25 part of defoamer, 0.2～0.3 part of Sodium hexametaphosphate 99,0.9～1.0 part of thickening material, AMP-950.08～0.1 part, 0.6～0.8 part of ethylene glycol and water.
The most preferably, described outdoor tent comprises the component of following parts by weight with composite coating: 40 parts, 32 parts of emulsions, 7 parts of calcined kaolins, 8 parts of titanium dioxides, 5 parts of film coalescence aid, 19 parts of talcum powder, 11 parts of slipproofing agents, 0.8 part of antimicrobial nano titanium dioxide, 7 parts, zinc sulfide white, 0.25 part of defoamer, 0.2 part of Sodium hexametaphosphate 99,0.9～1.0 part of thickening material, AMP-950.09 part, 0.8 part of ethylene glycol and water.
Particularly, described emulsion is any one in polyaminoester emulsion, benzene emulsion, organosilicon crylic acid latex, and wherein, the solid content of described emulsion is 55～60%.Preferably, described emulsion is benzene emulsion.
Described film coalescence aid is diethylene glycol monomethyl ether or ethylene glycol monomethyl ether.
Described slipproofing agent is any one or a few in rubber particles, hollow glass micropearl and polyurethane particles, and wherein, the particle diameter of described slipproofing agent is 120～200 orders.Be preferably hollow glass micropearl.Use hollow glass micropearl, constantly exposing new surface when coating because wearing and tearing is that pressurized makes surperficial bead break and forms new pit, has strengthened surperficial roughness, increases friction resistance, even skidproof effect is also fine under water hygrometric state.
Preferably, described defoamer is polydimethylsiloxane; Described thickening material is Natvosol.
Nano titanium oxide has sterilizing function, under action of ultraviolet radiation, can effectively kill the unwanted bacteria such as intestinal bacteria, yellow glucose fungus, can purify air simultaneously, has deodorization functions.General aseptic sterilant, as silver, copper etc. can make cell lose activity, but after bacterium kills, corpse can discharge harmful component, as intracellular toxin.And nano titanium oxide can not only affect bacterial reproduction power, and can attack bacteria organic constituent in cell, the membrane structure of penetration cell film destroy bacterium, reaches thorough bacterium for degrading, prevents that intracellular toxin from causing the object of secondary pollution.
The preparation method who the invention allows for above-mentioned outdoor tent composite coating, comprises the steps: said components to mix, and constant temperature at the uniform velocity stirs, and each component is uniformly distributed.
Preferably, the condition that described constant temperature average rate stirs is that the speed of 80～100r/min at 25～28 DEG C stirs 4～5h.
Beneficial effect: compared with prior art, the present invention is by selecting emulsion, film coalescence aid, slipproofing agent and the antimicrobial nano titanium dioxide of suitable formula and ratio, and coordinate the use of AMP, talcum powder, zinc sulfide white and defoamer, by interaction and the coordination of each component, prepared skid-resistant coating has waterproof, antifouling and wear-resisting time, also there is obvious sterilization effect, can make tent have light even be the effect that all can play sterilization under faint light.
Embodiment
According to following embodiment, the present invention may be better understood.But, those skilled in the art will readily understand, the described content of embodiment is only for the present invention is described, and should also can not limit the present invention described in detail in claims.The antimicrobial nano titanium dioxide using in the present invention is KN-100A type nano titanium oxide.
Embodiment 1
A kind of outdoor tent composite coating, comprises the component of following parts by weight: 40 parts, 32 parts of benzene emulsions, 7 parts of calcined kaolins, 8 parts of titanium dioxides, 5 parts of ethylene glycol monomethyl ethers, 19 parts of talcum powder, 11 parts of hollow glass micropearls, 0.8 part of antimicrobial nano titanium dioxide, 7 parts, zinc sulfide white, 0.25 part of polydimethylsiloxane, 0.2 part of Sodium hexametaphosphate 99,0.9 part of Natvosol, AMP-950.09 part, 0.8 part of ethylene glycol and water.Said components is mixed, and the speed with 100r/min at 25 DEG C stirs 5h, to obtain final product.
Embodiment 2
A kind of outdoor tent composite coating, comprises the component of following parts by weight: 45 parts, 30 parts of polyaminoester emulsions, 6 parts of calcined kaolins, 5 parts of titanium dioxides, 4 parts of diethylene glycol monomethyl ethers, 18 parts of talcum powder, 10 parts of rubber particles, 0.9 part of antimicrobial nano titanium dioxide, 8 parts, zinc sulfide white, 0.2 part of polydimethylsiloxane, 0.3 part of Sodium hexametaphosphate 99,1.0 parts of Natvosols, AMP-950.08 part, 0.6 part of ethylene glycol and water.Said components is mixed, and the speed with 100r/min at 28 DEG C stirs 5h, to obtain final product.
Embodiment 3
A kind of outdoor tent composite coating, comprises the component of following parts by weight: 43 parts, 35 parts of organosilicon crylic acid latexs, 7 parts of calcined kaolins, 10 parts of titanium dioxides, 5 parts of diethylene glycol monomethyl ethers, 18 parts of talcum powder, 12 parts of polyurethane particles, 0.8 part of antimicrobial nano titanium dioxide, 7 parts, zinc sulfide white, 0.25 part of polydimethylsiloxane, 0.2 part of Sodium hexametaphosphate 99,0.9 part of Natvosol, AMP-950.1 part, 0.8 part of ethylene glycol and water.Said components is mixed, and the speed with 100r/min at 25 DEG C stirs 5h, to obtain final product.
Embodiment 4
A kind of outdoor tent composite coating, comprises the component of following parts by weight: 42 parts, 25 parts of benzene emulsions, 8 parts of calcined kaolins, 5 parts of titanium dioxides, 3 parts of ethylene glycol monomethyl ethers, 15 parts of talcum powder, 8 parts of hollow glass micropearls, 0.5 part of antimicrobial nano titanium dioxide, 5 parts, zinc sulfide white, 0.2 part of polydimethylsiloxane, 0.1 part of Sodium hexametaphosphate 99,0.8 part of Natvosol, AMP-950.08 part, 0.6 part of ethylene glycol and water.Said components is mixed, and the speed with 100r/min at 25 DEG C stirs 5h, to obtain final product.
Embodiment 5
A kind of outdoor tent composite coating, comprises the component of following parts by weight: 43 parts, 35 parts of polyaminoester emulsions, 8 parts of calcined kaolins, 9 parts of titanium dioxides, 4 parts of ethylene glycol monomethyl ethers, 19 parts of talcum powder, 12 parts of polyurethane particles, 0.9 part of antimicrobial nano titanium dioxide, 10 parts, zinc sulfide white, 0.3 part of polydimethylsiloxane, 0.3 part of Sodium hexametaphosphate 99,0.9 part of Natvosol, AMP-950.09 part, 0.9 part of ethylene glycol and water.Said components is mixed, and the speed with 100r/min at 25 DEG C stirs 5h, to obtain final product.
Embodiment 6
Outdoor tent to embodiment 1～5 preparation carries out performance test with composite coating, and its result is as shown in table 1:
Table 1 outdoor tent composite coating performance index
Note: alkali-proof evaluation is coating to be placed in to 10%NaOH solution soaking detect.
Claims (9)
1. an outdoor tent composite coating, it is characterized in that, comprise the component of following parts by weight: 35～45 parts, 25～35 parts of emulsions, 5～8 parts of calcined kaolins, 5～10 parts of titanium dioxides, 3～5 parts of film coalescence aid, 15～20 parts of talcum powder, 8～12 parts of slipproofing agents, 0.5～1 part of antimicrobial nano titanium dioxide, 5～10 parts, zinc sulfide white, 0.2～0.3 part of defoamer, 0.1～0.3 part of Sodium hexametaphosphate 99,0.8～1.0 part of thickening material, AMP-950.05～0.1 part, 0.5～1 part of ethylene glycol and water.
2. outdoor tent composite coating according to claim 1, it is characterized in that, comprise the component of following parts by weight: 40～45 parts, 30～35 parts of emulsions, 6～7 parts of calcined kaolins, 5～10 parts of titanium dioxides, 4～5 parts of film coalescence aid, 18～20 parts of talcum powder, 10～12 parts of slipproofing agents, 0.8～0.9 part of antimicrobial nano titanium dioxide, 7～8 parts, zinc sulfide white, 0.2～0.25 part of defoamer, 0.2～0.3 part of Sodium hexametaphosphate 99,0.9～0.1 part of thickening material, AMP-950.08～0.1 part, 0.6～0.8 part of ethylene glycol and water.
3. outdoor tent composite coating according to claim 1 and 2, is characterized in that, described emulsion is any one in polyaminoester emulsion, benzene emulsion, organosilicon crylic acid latex, and wherein, the solid content of described emulsion is 55～60%.
4. outdoor tent composite coating according to claim 1 and 2, is characterized in that, described film coalescence aid is diethylene glycol monomethyl ether or ethylene glycol monomethyl ether.
5. outdoor tent composite coating according to claim 1 and 2, is characterized in that, described slipproofing agent is any one or a few in rubber particles, hollow glass micropearl and polyurethane particles, and wherein, the particle diameter of described slipproofing agent is 120～200 orders.
6. outdoor tent composite coating according to claim 1 and 2, is characterized in that, described defoamer is polydimethylsiloxane.
7. outdoor tent composite coating according to claim 1 and 2, is characterized in that, described thickening material is Natvosol.
8. the preparation method of composite coating for outdoor tent claimed in claim 1, is characterized in that, comprise the steps: said components to mix, constant temperature at the uniform velocity stirs, and each component is uniformly distributed.
9. preparation method according to claim 8, is characterized in that, the condition that described constant temperature average rate stirs is that the speed of 80～100r/min at 25～28 DEG C stirs 4～5h.