CN103991972A - 一种阻垢分散剂 - Google Patents
一种阻垢分散剂 Download PDFInfo
- Publication number
- CN103991972A CN103991972A CN201410216527.8A CN201410216527A CN103991972A CN 103991972 A CN103991972 A CN 103991972A CN 201410216527 A CN201410216527 A CN 201410216527A CN 103991972 A CN103991972 A CN 103991972A
- Authority
- CN
- China
- Prior art keywords
- scale inhibiting
- dispersion agent
- scale
- dispersant
- performance
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种阻垢分散剂,其由40wt.%~60wt.%α′,α-二氨基己二酸四亚甲基磷酸、20wt.%~30wt.%丙烯酸-2-丙烯酰胺-2-甲基丙磺酸共聚物、4wt.%~10wt.%乙酸锌、5wt.%~20wt.%去离子水组成。本发明阻垢分散剂对磷酸钙、碳酸钙都具有较好的阻垢效果,阻垢性能较好,同时具有较好的分散性能和较好的缓蚀性能,其用药量为5~10mg/L,在静态状况下,温度在80℃、pH值在9左右,阻垢性能能够达到93%以上,分散性能能够达到89%以上,与目前市售的阻垢分散剂相比性能比较优越,用药量少并且绿色环保。
Description
技术领域
本发明属于水处理技术领域,具体涉及一种绿色环保、使用于高温、高pH值的阻垢分散剂。
背景技术
在国内的许多化工厂或者电厂在处理灰水都存在管道结垢的问题,这不仅使得管道运输受到阻碍,而且对管道也有一定的腐蚀损害作用。目前处理阻垢的主要方法有酸洗法,酸洗法主要问题在于:第一,排出的污水不能够达标,对环境有污染。第二,该种方法对管道也有一定的腐蚀作用。还有一种清除方法就是机械清除法,管道内清洗刀在水里的作用下高速运转,强力切除阻垢,由于管道内碳酸钙等的厚度是不同的,所以断面是不均匀性的,清洗刀在管道内容易卡刀,并且切除的碎块容易堵塞管道,所以该种方法也不是能够很好的接受。并且上述两种方法费用高,应用范围不是很广泛。目前研究最热的就是阻垢分散剂,磷系阻垢剂对碳酸钙有较好的阻垢效果,但是一些常用的小分子磷系阻垢剂容易在水中分解,产生二次沉淀产物磷酸钙,不仅结垢对管道有一定的影响,而且外排污染环境,因此目前急需一种环保、高效的阻垢分散剂来解决现有的水处理领域中化工设备管道结垢的问题。
发明内容
本发明所要解决的技术问题在于克服现有阻垢分散剂存在的污染环境、阻垢效率低的缺点,提供一种绿色环保、阻垢性能和分散性能好的阻垢分散剂。
解决上述技术问题所采用的技术方案是所述的阻垢分散剂由下述质量百分配比的原料制成:
上述的阻垢分散剂最佳由下述质量百分配比的原料制成:
上述的α′,α-二氨基己二酸四亚甲基磷酸、丙烯酸-2-丙烯酰胺-2-甲基丙磺酸共聚物均由山东省枣庄泰和水处理有限公司提供,其中丙烯酸-2-丙烯酰胺-2-甲基丙磺酸共聚物的分子量为4000~5000道尔顿。
上述的阻垢分散剂的制备方法为:将α′,α-二氨基己二酸四亚甲基磷酸、丙烯酸-2-丙烯酰胺-2-甲基丙磺酸共聚物、乙酸锌加入去离子水中,在40℃搅拌至完全溶解,得到无色或琥珀色的阻垢分散剂。
本发明选用分子量相对较大的磷系阻垢剂α′,α-二氨基己二酸四亚甲基磷酸,其在水中不易分解,阻垢性能较好,同时选用丙烯酸-2-丙烯酰胺-2-甲基丙磺酸共聚物,其对磷酸钙具有较好的阻垢效果,并且磺酸根基团具有较好的分散性能,另外选用乙酸锌与丙烯酸-2-丙烯酰胺-2-甲基丙磺酸共聚物复配使用,具有较好的缓蚀性能。本发明阻垢分散剂的用药量为5~10mg/L,用药量较少,在静态状况下,温度在80℃、pH值在9左右,阻垢性能能够达到93%以上,分散性能能够达到89%以上,与目前市售的阻垢分散剂相比性能比较优越,并且绿色环保。
具体实施方式
下面结合实施例对本发明进一步详细说明,但本发明的保护范围不仅限于这些实施例。
实施例1
以制备100g阻垢分散剂为例,其组成如下:
其制备方法为:将50gα′,α-二氨基己二酸四亚甲基磷酸、25g丙烯酸-2-丙烯酰胺-2-甲基丙磺酸共聚物、8g乙酸锌加入17g去离子水中,在40℃条件下搅拌30分钟,得到阻垢分散剂。
本实施例的α′,α-二氨基己二酸四亚甲基磷酸、丙烯酸-2-丙烯酰胺-2-甲基丙磺酸共聚物均由山东省枣庄泰和水处理有限公司提供,其中丙烯酸-2-丙烯酰胺-2-甲基丙磺酸共聚物的分子量为4000~5000道尔顿。
实施例2
以制备100g阻垢分散剂为例,其组成如下:
其制备方法与实施例1相同。
实施例3
以制备100g阻垢分散剂为例,其组成如下:
其制备方法与实施例1相同。
实施例4
以制备100g阻垢分散剂为例,其组成如下:
其制备方法与实施例1相同。
实施例5
以制备100g阻垢分散剂为例,其组成如下:
其制备方法与实施例1相同。
为了验证本发明的有益效果,发明人采用EDTA滴定法和分光光度计对本发明实施例1~5制备的阻垢剂分散剂的阻垢性能和分散性能进行了测定,测试结果见表1,具体测试方法如下:
(1)阻垢性能测试方法
向100mL容量瓶中加入50mL去离子水和4mL6mg/mL的CaCl2水溶液,摇匀,然后加入阻垢剂分散剂,摇匀,用滴定管缓慢加入4mL18.3mg/mL NaHCO3水溶液(边加边摇匀),再加入38mL去离子水,用硼酸调节其pH值为9左右,所得溶液中阻垢剂分散剂的浓度为7mg/L,将容量瓶置于80℃水浴锅中反应10小时,同时做空白试验(空白试验除了不加阻垢分散剂外,其它条件都一样),然后用EDTA滴定法测阻垢性能。
(2)分散性能测试方法
向100mL锥形瓶中加入50mL去离子水和4mL6mg/mL的CaCl2水溶液,摇匀,然后加入阻垢剂分散剂,摇匀,用滴定管缓慢加入4mL18.3mg/mL NaHCO3水溶液(边加边摇匀),再加入4mL10mg/L的Fe2+(以FeSO4计),最后加入34mL去离子水,用硼酸调节其pH值为9左右,所得溶液中阻垢剂分散剂的浓度为7mg/L,将锥形瓶置于80℃水浴锅中反应5小时,用分光光度计于420nm处测定吸光度,同时做空白试验(空白试验除了不加阻垢分散剂外,其它条件都一样)。
表1本发明阻垢分散剂的阻垢和分散性能
阻垢分散剂 | 温度(℃) | 用药量(mg/L) | pH值 | 阻垢性能 | 分散性能 |
实施例1 | 80 | 7 | 9.14 | 96% | 92% |
实施例2 | 80 | 7 | 9.14 | 95% | 89% |
实施例3 | 80 | 7 | 9.14 | 94% | 90% |
实施例4 | 80 | 7 | 9.14 | 93% | 90% |
实施例5 | 80 | 7 | 9.14 | 93% | 91% |
由表1可以看出,本发明阻垢分散剂的阻垢性能能够达到93%以上,分散性能能够在89%以上。
Claims (3)
1.一种阻垢分散剂,其特征在于它由下述质量百分配比的原料制成:
2.根据权利要求1所述的阻垢分散剂,其特征在于它由下述质量百分配比的原料制成:
3.根据权利要求1或2所述的阻垢分散剂,其特征在于:所述的丙烯酸-2-丙烯酰胺-2-甲基丙磺酸共聚物的分子量为4000~5000道尔顿。