CN103862832A - 纯棉凉爽麻纱针织复合面料的生产方法 - Google Patents
纯棉凉爽麻纱针织复合面料的生产方法 Download PDFInfo
- Publication number
- CN103862832A CN103862832A CN201210547427.4A CN201210547427A CN103862832A CN 103862832 A CN103862832 A CN 103862832A CN 201210547427 A CN201210547427 A CN 201210547427A CN 103862832 A CN103862832 A CN 103862832A
- Authority
- CN
- China
- Prior art keywords
- fabric
- cool
- cloth
- production method
- cotton
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种纯棉凉爽麻纱针织复合面料的生产方法,选择强捻纯棉棉纱织造面料进行水洗处理,再进行丝光处理、上色,丝光处理之后对布料进行预缩、定型处理,用熨斗熨烫布料平整定型;最后进行布料复合,取热塑性聚氨酯TPU薄膜涂胶,预热,之后与所得布料进行热压合,冷却之后即得成品。处理工艺简单,成产成本低,流程短,布料质地轻薄、透气性强、导湿快、麻感强、凉爽舒适、防水透气、无刺激。
Description
技术领域
本发明属于面料技术领域,具体涉及一种生产纯棉凉爽麻纱针织复合面料的方法。
背景技术
苎麻具有凉爽、透气、挺括、干爽、利汗、天然抗菌防腐性能等优良性能,据报道,苎麻针织物的通透性特别好,穿用苎麻针织物制作的夏季装针织服装可使人体体表温度降低2—3℃。
然而,高档芝麻针织面料品种却很少,本发明的目的在于研发一种麻纱针织复合面料的生产方法。
发明内容
为了克服现有技术领域存在的上述技术问题,本发明的目的在于,提供一种纯棉凉爽麻纱针织复合面料的生产方法,处理工艺简单,成产成本低,流程短,布料质地轻薄、透气性强、导湿快、麻感强、凉爽舒适。
本发明提供的纯棉凉爽麻纱针织复合面料的生产方法,包括以下生产步骤:
1)选择强捻纯棉棉纱织造面料进行水洗处理, 采用工业用的全自动洗衣机进行水洗,助剂采用浴比为1:1000,水温为常温,水洗时间采用40~60分钟后漂洗,漂洗之后用离心甩干机进行脱水,然后用烘干机烘干;
2)丝光处理、上色,所述丝光处理NaOH浓度为260g/L,温度为20℃;
3)丝光处理之后对布料进行预缩、定型处理,用熨斗熨烫布料平整定型;
4)布料复合,取热塑性聚氨酯TPU薄膜涂胶,预热,之后与所得布料进行热压合,冷却之后即得成品。
本发明提供的纯棉凉爽麻纱针织复合面料的生产方法,其有益效果在于,生产工艺简单,成产成本低,流程短,生产效率高,可实现批量生产;选用布料质地轻薄、透气性强、导湿快、麻感强、凉爽舒适;采用热塑性聚氨酯TPU薄膜复合,防水透气,无刺激,抑菌抗菌。
具体实施方式
下面结合一个实施例,对本发明提供的纯棉凉爽麻纱针织复合面料的生产方法,进行详细的说明。
实施例
本实施例的纯棉凉爽麻纱针织复合面料的生产方法,包括以下生产步骤:
1)选择强捻纯棉棉纱织造面料进行水洗处理, 采用工业用的全自动洗衣机进行水洗,助剂采用浴比为1:1000,水温为常温,水洗时间采用40~60分钟后漂洗,漂洗之后用离心甩干机进行脱水,然后用烘干机烘干;
2)丝光处理、上色,所述丝光处理NaOH浓度为260g/L,温度为20℃;
3)丝光处理之后对布料进行预缩、定型处理,用熨斗熨烫布料平整定型;
4)布料复合,取热塑性聚氨酯TPU薄膜涂胶,预热,之后与所得布料进行热压合,冷却之后即得成品。
选用布料质地轻薄、透气性强、导湿快、麻感强、凉爽舒适;采用热塑性聚氨酯TPU薄膜复合,防水透气,无刺激,抑菌抗菌。
Claims (1)
1.一种纯棉凉爽麻纱针织复合面料的生产方法,其特征在于包括以下生产步骤:
1)选择强捻纯棉棉纱织造面料进行水洗处理, 采用工业用的全自动洗衣机进行水洗,助剂采用浴比为1:1000,水温为常温,水洗时间采用40~60分钟后漂洗,漂洗之后用离心甩干机进行脱水,然后用烘干机烘干;
2)丝光处理、上色,所述丝光处理NaOH浓度为260g/L,温度为20℃;
3)丝光处理之后对布料进行预缩、定型处理,用熨斗熨烫布料平整定型;
4)布料复合,取热塑性聚氨酯TPU薄膜涂胶,预热,之后与所得布料进行热压合,冷却之后即得成品。